CN1757431A - Visualized aquogel, and its preparing method - Google Patents
Visualized aquogel, and its preparing method Download PDFInfo
- Publication number
- CN1757431A CN1757431A CN 200510094400 CN200510094400A CN1757431A CN 1757431 A CN1757431 A CN 1757431A CN 200510094400 CN200510094400 CN 200510094400 CN 200510094400 A CN200510094400 A CN 200510094400A CN 1757431 A CN1757431 A CN 1757431A
- Authority
- CN
- China
- Prior art keywords
- hydrogel
- visualized
- sensitive
- aquogel
- molecule
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A visualized aqueogel used for analyzing metal ions, nucleic acid and protein is composed of a sensitive aqueogel layer and a non-sensitive aqueogel layer. Its preparing process includes such steps as proportionally dissolving aqueogel, cross-linking agent, sensing element and trigger in solvent, polymerizing to obtain sensitive aqueogel, proportionally dissolving aqueogel, cross-linking agent and trigger in water, polymerizing to obtain non-sensitive aqueogel, and adhering them together.
Description
Technical field
The present invention relates to a kind of visual double-deck hydrogel and preparation method thereof.Utilize sensitive aquagel response external environment and produce deformation.Specifically, the present invention relates in hydrogel fixedly that sensitive molecule (group) forms sensitive aquagel, again sensitive aquagel and non-sensitive hydrogel are bonded together, promptly get a kind of visualized aquogel.The technical field that belongs to.
Background technology
Hydrogel is the hydrophilic high molecular polymer of a class, it has certain biocompatibility, have because of osmotic pressure cause to such an extent that expand and shrink character, also has memory function, properties such as environment pattern before can replica polymerization, therefore hydrogel has been applied to application studies such as tissue repair, medicament slow release, template imprinting.
Because hydrogel can response environment must be changed and be applied to sensing Study of An, PAHG for example, under alkali condition, amide groups is hydrolyzed into carboxyl group---can induced environment in pH be worth changing and volume takes place must change, in hydrogel fixing on behind specific molecular (antibody etc.) and its corresponding aglucon (antigen etc.), hydrogel can respond the environment that contains this specific molecular or corresponding aglucon, a little less than the Volume Changes naked eyes resolution capability of these responses.With forming crystal colloid array gel behind the neutral water gel locking crystal colloid array, in crystal colloid array gel, fix specific molecule, be intelligent crystal colloid array gel.The Bragg peak value that its deformation that induction of environment is caused can show the crystal colloid that locks in the gel moves.The color that perusal shows as intelligent crystal colloid array gel changes, but the variation naked eyes of Bragg peak value in certain wave-length coverage can not be distinguished.For example in the 600-700nm scope, change, all show as redness.
Summary of the invention
Technical problem: the purpose of this invention is to provide visual double-deck hydrogel that a kind of naked eyes of quick deformation can distinguish and preparation method thereof.
Technical scheme: the present invention adopts following technical scheme:
Visual double-deck hydrogel of the present invention is about to sensitive aquagel and non-non-sensitive hydrogel and is bonded together the visual double-deck hydrogel of the deformation of formation.
The method of the visual double-deck hydrogel of preparation of the present invention, that is: 1, with monomer, crosslinking agent, sensing element, the initator of hydrogel, in 100～10: 1～0.1: 10～1: 1～0.1 ratio be dissolved in the solvent to w/v be 4～30%, polymerization forms sensitive aquagel
2, with the monomer of hydrogel, crosslinking agent, initator, in 100～10: 1～0.1: 10～0.1 ratio soluble in water to w/v be 4～30%, polymerization forms non-sensitive hydrogel,
3, sensitive aquagel that above-mentioned steps 1 is obtained and step 2 to non-sensitive hydrogel be bonded together, promptly form visual double-deck hydrogel.
Described hydrogel monomer can be acrylamide or amido substituted acrylamide,
Described crosslinking agent can be a methylene diacrylamide,
Described sensing element can be the molecule of chemical synthesis such as the molecule that identification can take place with other molecule for 4-vinyl benzene-18-hat-6,4-propenylbenzene-18-hat-6 and 3-aminobenzene boric acid etc., also can be natural biomolecule such as antibody, nucleic acid strand and enzyme
Described solvent
Beneficial effect: compared with prior art, the present invention has following advantage:
1, visualized aquogel of the present invention and intelligent crystal colloid array gel phase ratio, fixedly the condition of sensing element is not harsh, can former polymerization fix, and can fix after the polymerization yet again, and can directly fixedly resemble the large biological molecule of this class of antigen antibody complex.
2, visualized aquogel of the present invention and intelligent crystal colloid array gel phase ratio, polymerization single polymerization monomer can be neutral monomers, also can not be neutral monomer, and intelligent crystal colloid array gel intelligence can only be neutral polymerization single polymerization monomers.
3, the great advantage of visualized aquogel of the present invention is that the deformation that environmental response is produced is the variation that bends, and can observe intuitively by naked eyes, and is highly sensitive.
The hydrogel of visual analyzing of the present invention, the hydrogel of prepared visual analyzing can detect metal ion, nucleic acid and albumen etc.
The specific embodiment
Embodiment 1: the preparation method who is used to prepare the visualized aquogel that detects lead ion of the present invention follows these steps to carry out successively:
1) with 4-vinyl benzene-18-hat-6 or 4-propenylbenzene-18-hat-6, acrylamide, methene acrylamide (mol ratio is 1: 20: 1)) to be dissolved in w/v be in 1.5: 10 water, to be added to (clamp bar thickness is 160 microns) polymerization film formation in the mould.
2) with acrylamide: it is in 1.5: 10 water, to be added to (clamp bar thickness is 160 microns) polymerization film formation in the mould that methene acrylamide (mol ratio is 30: 1) is dissolved in w/v.
3) above-mentioned two kinds of glued membranes are placed dry dehydration 80% on the glass plate, form mould with 320 microns clamp bar again, add step 2) described acrylamide and the polymerization of methene acrylamide solution, and form the visualized aquogel that detects lead ion.
Embodiment 2: the preparation method who is used to prepare the visualized aquogel that detects hepatitis B surface antigen of the present invention follows these steps to carry out successively:
1) acrylamide: methene acrylamide (mol ratio is 30: 1)) being dissolved in w/v is in 3: 10 water, to be added to (clamp bar thickness is 160 microns) polymerization film formation in the mould;
2) above-mentioned glued membrane places dry dehydration 90% on the glass plate, and the clamp bar that adds a flat glass plate thickness again and be 320 microns is formed mould;
3) activate acrylic acid with active ester method, form the acrylic acid of activation;
4) modify hepatitis B surface antigen with the acrylic acid of activation and form the acrylic hepatitis B surface antigen, modify the antibody of the antibody formation acrylic anti-hepatitis B surface antigen of anti-hepatitis B surface antigen with the acrylic acid of activation, (mol ratio is 1: 1: 20: 1) be dissolved in w/v and be in 3: 10 water for the antibody of acrylic hepatitis B surface antigen, acrylic anti-hepatitis B surface antigen, acrylamide and methene acrylamide, be added to 2 again) polymerization film formation in the mould, and form the visualized aquogel that detects hepatitis B surface antigen.
Embodiment 3: the preparation method who is used to prepare the visualized aquogel that detects the random nucleic acid segment of the present invention follows these steps to carry out successively:
1) N-isopropylacrylamide: it is in 3: 10 water, to be added to (clamp bar thickness is 160 microns) polymerization film formation in the mould that methene acrylamide (mol ratio is 30: 1) is dissolved in w/v;
2) above-mentioned glued membrane is placed dry dehydration 90% on the glass plate, the clamp bar that adds a flat glass plate thickness again and be 320 microns is formed mould;
3) activate acrylic acid with active ester method, form the acrylic acid of activation;
4) modify amidized nucleic acid fragment with the acrylic acid of activation and form the acrylic nucleic acid fragment, modify the complementary fragment of anti-amidized nucleic acid fragment with the acrylic acid of activation and form the complementary fragment of acrylic nucleic acid fragment, (mol ratio is 3: 3: 30: 1) be dissolved in w/v and be in 3: 10 water for the complementary fragment of acrylic nucleic acid fragment, acrylic nucleic acid fragment, acrylamide and methene acrylamide, be added to 2 again) polymerization film formation in the mould, and form the visualized aquogel that detects the random nucleic acid segment.
Embodiment 4: the preparation method who is used to prepare the visualized aquogel that detects organophosphorus insecticide of the present invention follows these steps to carry out successively:
1) acrylamide: it is in 3: 10 water, to be added to (clamp bar thickness is 160 microns) polymerization film formation in the mould that methene acrylamide (mol ratio is 30: 1) is dissolved in w/v;
2) above-mentioned glued membrane is placed dry dehydration 90% on the glass plate, the clamp bar that adds a flat glass plate thickness again and be 320 microns is formed mould;
3) activate acrylic acid with active ester method, form the acrylic acid of activation, modify acetylcholinesterase with the acrylic acid of activation again;
4) acetylcholinesterase, acrylamide and the methene acrylamide (mol ratio is 1: 100: 4) modified of acrylic acid to be dissolved in w/v be in 1: 10 water, to be added to 2 again) polymerization film formation in the mould, and form the visualized aquogel that detects organophosphorus insecticide.
Claims (5)
1. visualized aquogel is characterized in that this hydrogel is bonded together by one deck sensitive aquagel and the non-sensitive hydrogel of one deck to constitute.
2. preparation method who is used for the described visualized aquogel of claim 1 is characterized in that the method for preparing is:
1). with monomer, crosslinking agent, sensing element, the initator of hydrogel, in 100～10: 1～0.1: 10～1: 1～0.1 ratio be dissolved in the solvent to w/v be 4～30%, polymerization forms sensitive aquagel;
2). with the monomer of hydrogel, crosslinking agent, initator, in 100～10: 1～0.1: 10～0.1 ratio soluble in water to w/v be 4～30%, polymerization forms non-sensitive hydrogel;
3) with above-mentioned steps 1) sensitive aquagel and the step 2 that obtain) to non-sensitive hydrogel be bonded together, promptly form visual double-deck hydrogel.
3. the method for visualized aquogel as claimed in claim 2, the monomer that it is characterized in that hydrogel is acrylamide or amido substituted acrylamide, and crosslinking agent is a methylene diacrylamide, and sensing element is. the molecule of chemical synthesis.
4. the method for visualized aquogel as claimed in claim 3, the molecule that it is characterized in that chemical synthesis is the molecule that identification can take place with other molecule of 4-vinyl benzene-18-hat-6,4-propenylbenzene-18-hat-6 and 3-aminobenzene boric acid, also can be natural biomolecule such as antibody, nucleic acid strand and enzyme.
5. as the method for claim 2 or 3 described visualized aquogels, it is characterized in that sensing element in the hydrogel is that the branch period of the day from 11 p.m. to 1 a.m of chemical synthesis is: 4-vinyl benzene-18-hat-6 and 3-aminobenzene boric acid when being natural biomolecule is: enzyme, antibody and nucleic acid fragment.