CN1752290A - Multifunctional maintaniing agent for defatting, washing and forming oright film on surface of stainless steel products - Google Patents
Multifunctional maintaniing agent for defatting, washing and forming oright film on surface of stainless steel products Download PDFInfo
- Publication number
- CN1752290A CN1752290A CN 200510094865 CN200510094865A CN1752290A CN 1752290 A CN1752290 A CN 1752290A CN 200510094865 CN200510094865 CN 200510094865 CN 200510094865 A CN200510094865 A CN 200510094865A CN 1752290 A CN1752290 A CN 1752290A
- Authority
- CN
- China
- Prior art keywords
- film
- stainless steel
- functional
- minutes
- degreasing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A multifunctional maintenance agent of stainless steel products for generating a firm film to degrease, clean and brighten the surface contains 14 chemical compounds including phosphoric acid, sodium alkylphenylsulfonate, acetone, non-ionic surfactant, methyl silica oil, emulsifying stabilizer OP-22, etc.
Description
Technical field
The present invention relates to the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods.
Background technology
Goods at present stainless steel are very universal, in the process of producing and using, be easy to by various organic dirts, mineral contaminants, dust, pollute and damage than heavy-gravity grease stain, micronic dust, acid micropartical and alkaline micropartical, so need a kind of multi-functional maintaniing agent of surperficial cleaning by degreasing forming oright film of stainless steel goods because of static focus.
Summary of the invention:
The object of the present invention is to provide a kind of multi-functional maintaniing agent of surperficial cleaning by degreasing forming oright film of stainless steel goods.
Technical scheme of the present invention: the present invention is a kind of multi-functional maintaniing agent of surperficial cleaning by degreasing forming oright film of stainless steel goods, and the composition that can realize surperficial cleaning by degreasing effect of this multi-functional maintaniing agent is: the two dodecyl dimethyl ammonia of phosphoric acid, sodium alkyl benzene sulfonate, acetone, Sodium dodecylbenzene sulfonate and chlorination; The composition that can realize surperficial forming oright film effect of this multi-functional maintaniing agent is: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate; The composition of other of this multi-functional maintaniing agent is: OP-10 emulsifying agent and an amount of essence; The part by weight of the prescription of the mentioned component of the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods is: 5% to 35% phosphoric acid, 3% to 30% sodium alkyl benzene sulfonate, 1% to 10% acetone, 1% to 10% Sodium dodecylbenzene sulfonate, the two dodecyl dimethyl ammonia of 0.5% to 8% chlorination, 1.5% to 15% nonionogenic tenside, 1.5% to 15% methyl-silicone oil, 0.5% to 8% dimethyl silicone oil, 0.5% to 8% fatty acid alcohol acid amides, 0.5% to 8% tricresyl phosphate methyl fat, 0.5% to 8% tricresyl phosphite butyl phenyl ester, 1% to 10% methyl methacrylate, 1% to 10% OP-22 emulsion stabilizer, 0.5% to 8% essence.
Above-mentioned phosphoric acid, sodium alkyl benzene sulfonate and acetone have the various organic dirts, mineral contaminants, dust on surface that can cleaning by degreasing stainless steel goods and than the function of heavy-gravity grease stain; The two dodecyl dimethyl ammonia of above-mentioned Sodium dodecylbenzene sulfonate and chlorination have the micronic dust because of static focus, acid micropartical and the alkaline atomic function on surface that can cleaning by degreasing stainless steel goods.
Above-mentioned nonionogenic tenside has can play the function of elimination because of the static focus micronic dust on the surface of stainless steel goods; Above-mentioned methyl-silicone oil, dimethyl silicone oil and fatty acid alcohol acid amides have the function that can form one deck composite lubricating film on the surface of stainless steel goods, and the thickness of this composite lubricating film can be 50 nanometer to 5000 nanometers; Above-mentioned tricresyl phosphate methyl fat and tricresyl phosphite butyl phenyl ester have can form the anti-function of sending out black the phosphatization film of one deck at the table of stainless steel goods, and the thickness of this prevents sending out black phosphatization film can be 50 nanometer to 5000 nanometers; Above-mentioned methyl methacrylate has and can form the function that one deck is refused the water mildewproof film on the surface of stainless steel goods, and this thickness of refusing the water mildewproof film can be 50 nanometer to 5000 nanometers.
Above-mentioned OP-22 emulsion stabilizer has can make the various compositions of this multi-functional maintaniing agent keep stable function.
The composition that can realize surperficial cleaning by degreasing effect with this above-mentioned multi-functional maintaniing agent: the two dodecyl dimethyl ammonia of phosphoric acid, sodium alkyl benzene sulfonate, acetone, Sodium dodecylbenzene sulfonate and chlorination mix in selected ratio, carry out 5 minutes to 400 minutes evenly stir fully then in the stirred vessel of entry altitude sealing, afterwards in 15 minutes to 40 minutes time demulcent be heated to 40 ℃ to 65 ℃ standby; The composition that can realize surperficial forming oright film effect with this above-mentioned multi-functional maintaniing agent: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate mix in selected ratio, carry out 15 minutes to 700 minutes evenly stir fully then in the stirred vessel of entry altitude sealing, afterwards in 15 minutes to 70 minutes time demulcent be heated to 35 ℃ to 55 ℃ standby; Can mix the two this moment, carries out 25 minutes to 300 minutes evenly stir fully then in the stirred vessel of entry altitude sealing, treats that temperature-stable can obtain work in-process at 30 ℃ between 40 ℃; After this above-mentioned OP-22 emulsion stabilizer and an amount of essence can be mixed with work in-process in selected ratio, carry out 5 minutes to 400 minutes evenly stirring fully then in the stirred vessel of entry altitude sealing, can leave standstill at last stablize 10 minutes to 900 minutes after, treat that temperature-stable can obtain finished product in normal temperature; Can detect finished product afterwards; After detecting, can carry out quantitative filling at finished product, after the process wrapping machine is finished packing at last, promptly can be made into product.
The multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods can be packaged as liquid agent; Or the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods can be packaged as aerosol.
The present invention has positive result of use: because the composition that can realize surperficial cleaning by degreasing effect of this multi-functional maintaniing agent is: the two dodecyl dimethyl ammonia of phosphoric acid, sodium alkyl benzene sulfonate, acetone, Sodium dodecylbenzene sulfonate and chlorination; The composition that can realize surperficial forming oright film effect of this multi-functional maintaniing agent is: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate; The composition of other of this multi-functional maintaniing agent is: OP-22 emulsion stabilizer and an amount of essence; Above-mentioned phosphoric acid, sodium alkyl benzene sulfonate and acetone have the various organic dirts, mineral contaminants, dust on surface that can cleaning by degreasing stainless steel goods and than the function of heavy-gravity grease stain; The two dodecyl dimethyl ammonia of above-mentioned Sodium dodecylbenzene sulfonate and chlorination have the micronic dust because of static focus, acid micropartical and the alkaline atomic function on surface that can cleaning by degreasing stainless steel goods; Above-mentioned nonionogenic tenside has can play the function of elimination because of the static focus micronic dust on the surface of stainless steel goods; Above-mentioned methyl-silicone oil, dimethyl silicone oil and fatty acid alcohol acid amides have the function that can form one deck composite lubricating film on the surface of stainless steel goods, and the thickness of this composite lubricating film can be 50 nanometer to 5000 nanometers; Above-mentioned tricresyl phosphate methyl fat and tricresyl phosphite butyl phenyl ester have can form the anti-function of sending out black the phosphatization film of one deck on the surface of stainless steel goods, and the thickness of this prevents sending out black phosphatization film can be 50 nanometer to 5000 nanometers; Above-mentioned methyl methacrylate has and can form the function that one deck is refused the water mildewproof film on the surface of stainless steel goods, and this thickness of refusing the water mildewproof film can be 50 nanometer to 5000 nanometers; Above-mentioned OP-22 emulsion stabilizer has can make the various compositions of this multi-functional maintaniing agent keep stable function.The present invention be safe and reliable, effect is obvious, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of widely used a kind of stainless steel goods.
Embodiment
The multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of a kind of stainless steel goods of present embodiment of the present invention meets relevant technological standard; Present embodiment of the present invention is owing to the composition that can realize surperficial cleaning by degreasing effect of this multi-functional maintaniing agent is: the two dodecyl dimethyl ammonia of phosphoric acid, sodium alkyl benzene sulfonate, acetone, Sodium dodecylbenzene sulfonate and chlorination; The composition that can realize surperficial forming oright film effect of this multi-functional maintaniing agent is: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate; The composition of other of this multi-functional maintaniing agent is: OP-10 emulsifying agent and an amount of essence; The part by weight of the prescription of the mentioned component of the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods is: 5% to 35% phosphoric acid, 3% to 30% sodium alkyl benzene sulfonate, 1% to 10% acetone, 1% to 10% Sodium dodecylbenzene sulfonate, the two dodecyl dimethyl ammonia of 0.5% to 8% chlorination, 1.5% to 15% nonionogenic tenside, 1.5% to 15% methyl-silicone oil, 0.5% to 8% dimethyl silicone oil, 0.5% to 8% fatty acid alcohol acid amides, 0.5% to 8% tricresyl phosphate methyl fat, 0.5% to 8% tricresyl phosphite butyl phenyl ester, 1% to 10% methyl methacrylate, 1% to 10% OP-22 emulsion stabilizer, 0.5% to 8% essence, in the present embodiment, can select the part by weight of prescription of mentioned component of multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods of using to be: 25% phosphoric acid, 13% sodium alkyl benzene sulfonate, 6.5% acetone, 3.5% Sodium dodecylbenzene sulfonate, the two dodecyl dimethyl ammonia of 2.5% chlorination, 6.5% nonionogenic tenside, 7.5% methyl-silicone oil, 1.5% dimethyl silicone oil, 1.5% fatty acid alcohol acid amides, 2.5% tricresyl phosphate methyl fat, 1.5% tricresyl phosphite butyl phenyl ester, 5% methyl methacrylate, 3.5% OP-22 emulsion stabilizer, 1.5% essence; Above-mentioned phosphoric acid, sodium alkyl benzene sulfonate and acetone have the various organic dirts, mineral contaminants, dust on surface that can cleaning by degreasing stainless steel goods and than the function of heavy-gravity grease stain; The two dodecyl dimethyl ammonia of above-mentioned Sodium dodecylbenzene sulfonate and chlorination have the micronic dust because of static focus, acid micropartical and the alkaline atomic function on surface that can cleaning by degreasing stainless steel goods; Above-mentioned nonionogenic tenside has can play the function of elimination because of the static focus micronic dust on the surface of stainless steel goods; Above-mentioned methyl-silicone oil, dimethyl silicone oil and fatty acid alcohol acid amides have the function that can form one deck composite lubricating film on the surface of stainless steel goods, the thickness of this composite lubricating film can be 50 nanometer to 5000 nanometers, in the present embodiment, the thickness of this composite lubricating film may be controlled to about 350 nanometers; Above-mentioned tricresyl phosphate methyl fat and industry tricresyl phosphate butyl phenyl ester have can form the anti-function of sending out the phosphatization film black of one deck on the surface of stainless steel goods, the thickness that should anti-send out the phosphatization film black can be 50 nanometer to 5000 nanometers, in the present embodiment, this anti-thickness of sending out the phosphatization film black may be controlled to about 550 nanometers; Above-mentioned methyl methacrylate has and can form the function that one deck is refused the water mildewproof film on the surface of stainless steel goods, this thickness of refusing the water mildewproof film can be 50 nanometer to 5000 nanometers, in the present embodiment, this thickness of refusing the water mildewproof film may be controlled to about 500 nanometers; Above-mentioned OP-22 emulsion stabilizer has can make the various compositions of this multi-functional maintaniing agent keep stable function; The composition that can realize surperficial cleaning by degreasing effect with this above-mentioned multi-functional maintaniing agent: phosphoric acid, sodium alkyl benzene sulfonate, acetone, the two dodecyl dimethyl ammonia of Sodium dodecylbenzene sulfonate and chlorination mix in selected ratio, carry out 5 minutes to 400 minutes evenly stirring fully then in the stirred vessel of entry altitude sealing, afterwards in 15 minutes to 40 minutes time demulcent be heated to 40 ℃ to 65 ℃ standby, in the present embodiment, can entry altitude carry out 40 minutes evenly stir fully in the stirred vessel of sealing, afterwards in 25 minutes time demulcent be heated to 47.5 ℃ standby; The composition that can realize surperficial forming oright film effect with this above-mentioned multi-functional maintaniing agent: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, the fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate mix in selected ratio, carry out 15 minutes to 700 minutes evenly stirring fully then in the stirred vessel of entry altitude sealing, afterwards in 15 minutes to 70 minutes time demulcent be heated to 35 ℃ to 55 ℃ standby, in the present embodiment, can entry altitude carry out 70 minutes evenly stir fully in the stirred vessel of sealing, afterwards in 35 minutes time demulcent be heated to 45 ℃ standby; Can mix the two this moment, carry out 25 minutes to 300 minutes evenly stirring fully then in the stirred vessel of entry altitude sealing, treat that temperature-stable can obtain work in-process at 30 ℃ between 40 ℃, in the present embodiment, can carry out 50 minutes evenly stirring fully in the stirred vessel of entry altitude sealing, treat that temperature-stable can obtain work in-process in 35 ℃; After this above-mentioned OP-22 emulsion stabilizer and an amount of essence can be mixed with work in-process in selected ratio, carry out 5 minutes to 400 minutes evenly stirring fully then in the stirred vessel of entry altitude sealing, can leave standstill at last stablize 10 minutes to 900 minutes after, treat that temperature-stable can obtain finished product in normal temperature, in the present embodiment, can carry out 40 minutes evenly stirring fully in the stirred vessel of entry altitude sealing, can leave standstill at last stablize 200 minutes after, treat that temperature-stable can obtain finished product in normal temperature; Can detect finished product afterwards; After detecting, can carry out quantitative filling at finished product, after the process wrapping machine is finished packing at last, promptly can be made into product; In the present embodiment, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods can be packaged as liquid agent; In other embodiments, or the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods can be packaged as aerosol.The present invention be safe and reliable, effect is obvious, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of widely used a kind of stainless steel goods.
Claims (6)
1, a kind of multi-functional maintaniing agent of surperficial cleaning by degreasing forming oright film of stainless steel goods is characterized in that: the composition that can realize surperficial cleaning by degreasing effect of this multi-functional maintaniing agent is: the two dodecyl dimethyl ammonia of phosphoric acid, sodium alkyl benzene sulfonate, acetone, Sodium dodecylbenzene sulfonate and chlorination; The composition that can realize surperficial forming oright film effect of this multi-functional maintaniing agent is: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate; The composition of other of this multi-functional maintaniing agent is: OP-22 emulsion stabilizer and an amount of essence; The part by weight of the prescription of the mentioned component of the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods is: 5% to 35% phosphoric acid, 3% to 30% sodium alkyl benzene sulfonate, 1% to 10% acetone, 1% to 10% Sodium dodecylbenzene sulfonate, the two dodecyl dimethyl ammonia of 0.5% to 8% chlorination, 1.5% to 15% nonionogenic tenside, 1.5% to 15% methyl-silicone oil, 0.5% to 8% dimethyl silicone oil, 0.5% to 8% fatty acid alcohol acid amides, 0.5% to 8% tricresyl phosphate methyl fat, 0.5% to 8% tricresyl phosphite butyl phenyl ester, 1% to 10% methyl methacrylate, 1% to 10% OP-22 emulsion stabilizer, 0.5% to 8% essence.
2, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods according to claim 1 is characterized in that: above-mentioned phosphoric acid, sodium alkyl benzene sulfonate and acetone have the various organic dirts, mineral contaminants, dust on surface that can cleaning by degreasing stainless steel goods and than the function of heavy-gravity grease stain; The two dodecyl dimethyl ammonia of above-mentioned Sodium dodecylbenzene sulfonate and chlorination have the micronic dust because of static focus, acid micropartical and the alkaline atomic function on surface that can cleaning by degreasing stainless steel goods.
3, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods according to claim 1 is characterized in that: above-mentioned nonionogenic tenside has can play the function of elimination because of the static focus micronic dust on the surface of stainless steel goods; Above-mentioned methyl-silicone oil, dimethyl silicone oil and fatty acid alcohol acid amides have the function that can form one deck composite lubricating film on the surface of stainless steel goods, and the thickness of this composite lubricating film can be 50 nanometer to 5000 nanometers; Above-mentioned tricresyl phosphate methyl fat and tricresyl phosphite butyl phenyl ester have can form the anti-function of sending out black the phosphatization film of one deck on the surface of stainless steel goods, and the thickness of this prevents sending out black phosphatization film can be 50 nanometer to 5000 nanometers; Above-mentioned methyl methacrylate has and can form the function that one deck is refused the water mildewproof film on the surface of stainless steel goods, and this thickness of refusing the water mildewproof film can be 50 nanometer to 5000 nanometers.
4, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods according to claim 1 is characterized in that: above-mentioned OP-22 emulsion stabilizer has can make the various compositions of this multi-functional maintaniing agent keep stable function.
5, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods according to claim 1, it is characterized in that: with the composition that can realize surperficial cleaning by degreasing effect of this above-mentioned multi-functional maintaniing agent: phosphoric acid, sodium alkyl benzene sulfonate, acetone, the two dodecyl dimethyl ammonia of Sodium dodecylbenzene sulfonate and chlorination mix in selected ratio, carry out 5 minutes to 400 minutes evenly stir fully then in the stirred vessel of entry altitude sealing, afterwards in 15 minutes to 40 minutes time demulcent be heated to 40 ℃ to 65 ℃ standby; The composition that can realize surperficial forming oright film effect with this above-mentioned multi-functional maintaniing agent: nonionogenic tenside, methyl-silicone oil, dimethyl silicone oil, fatty acid alcohol acid amides, tricresyl phosphate methyl fat, tricresyl phosphite butyl phenyl ester and methyl methacrylate mix in selected ratio, carry out 15 minutes to 700 minutes evenly stir fully then in the stirred vessel of entry altitude sealing, afterwards in 15 minutes to 70 minutes time demulcent be heated to 35 ℃ to 55 ℃ standby; Can mix the two this moment, carries out 25 minutes to 300 minutes evenly stir fully then in the stirred vessel of entry altitude sealing, treats that temperature-stable can obtain work in-process at 30 ℃ between 40 ℃; After this above-mentioned OP-22 emulsion stabilizer and an amount of essence can be mixed with work in-process in selected ratio, carry out 5 minutes to 400 minutes evenly stirring fully then in the stirred vessel of entry altitude sealing, can leave standstill at last stablize 10 minutes to 900 minutes after, treat that temperature-stable can obtain finished product in normal temperature; Can detect finished product afterwards; After detecting, can carry out quantitative filling at finished product, after the process wrapping machine is finished packing at last, promptly can be made into product.
6, the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of stainless steel goods according to claim 1 is characterized in that: the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods can be packaged as liquid agent; Or the multi-functional maintaniing agent of the surperficial cleaning by degreasing forming oright film of these stainless steel goods can be packaged as aerosol.