CN1721035A - Method for manufacturing puffy glass fiber filtration material - Google Patents
Method for manufacturing puffy glass fiber filtration material Download PDFInfo
- Publication number
- CN1721035A CN1721035A CNA2005100350006A CN200510035000A CN1721035A CN 1721035 A CN1721035 A CN 1721035A CN A2005100350006 A CNA2005100350006 A CN A2005100350006A CN 200510035000 A CN200510035000 A CN 200510035000A CN 1721035 A CN1721035 A CN 1721035A
- Authority
- CN
- China
- Prior art keywords
- glass
- puffy
- filtration material
- fiber filtration
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The preparation method for puff glass fiber filtration material concerns to that sprays the fused glass under pressure through micropore and form filament, adds cementing agent for stick; after superposition with many layers, takes puffzation at high temperature and form smooth skin-type coat on two surfaces; finally, adds to fire retarding agent on surface. This material has little resistance and high oil catching rate; it has good fire retardant property, low cost, simple technique, convenient to use and has wide functions.
Description
Technical field
The present invention relates to the air purifying process field, more specifically to a kind of manufacture method of glass fiber filter material.
Background technology
At present, be widely used in conventional equipments such as air filtration element such as baking finish for car room exhaust air discharge equipment, family expenses and industrial air regulator, air freshener, dust catcher, ventilation fan, smoke exhaust ventilator and not only have higher resistance with the filtering material in the air handling system, the oil capture rate is not high, and fire resistance is poor.People utilize the aluminium net of individual layer to be used as containing the air filting material of organic substances such as oil smoke always, but because screen pack is more sparse, oil trap collection poor efficiency, most oil smoke just all can't fully capture and discharge, and the result causes very big pollution to environment on every side.Simultaneously, present screen pack does not all have the good flame performance, if when having Mars to jump to screen pack, the oil that adheres to above just has the danger of being lighted, and manufacturing cost is also higher.Be not suitable for promoting the use of on a large scale.Chinese patent " glass fibre air cleaner ", the patent No.: 86201469, it discloses a kind of air cleaner.Filter element adopts glass fibre as filter medium, and the filter medium layer thickness can be realized by regulating nut, can transform use on existing equipment.Degerming ability is 10#+[15] individual bacterium/batch, gas resistant pressure is reduced to 0.15～0.2 kg/cm, and safe handling reached more than 200 days, and used repeatedly after can handling by regeneration, and expense is low, and is heat-resisting, withstand voltage.Be specially adapted to filter filtrated air for antibiotic fermentation production.But filter clogging effect is not high yet.
Summary of the invention
Technical problem to be solved by this invention be overcome provide in existing deficiency a kind of method simply, cost is lower, have good oil trap collection efficient, resistance is little, the manufacture method of nonflammable puffy glass fiber filtration material
The present invention can take following technical measures to solve:
By above-mentioned purpose, a kind of manufacture method of puffy glass fiber filtration material, be that glass is ejected the formation filament by micropore under pressure after fusion, add that then binding agent bonds, through fluffyization of high temperature again behind the multilayer build-up, and form smooth skin shape epidermis on two surfaces, add fire retardant on its surface at last.
Above-mentioned glass can be simple glass, borate glass, lead glass, cobalt glass, coloured glass or safety glass.
Above-mentioned adhesive can be phenolic resin, epoxy resin, Lauxite, anline resin, polyurethane resin or unsaturated-resin
Above-mentioned fire retardant can be the chemical substance of the halogen-containing phosphorus-containing matter of organic matter, also can be inorganic substances, as aluminium oxide, magnesia.
Outstanding effect of the present invention is:
1) puffy glass fiber filtration material of the present invention not only has lower resistance, and has oily preferably capture rate.
2) puffy glass fiber filtration material of the present invention has good flame retardancy, low cost of manufacture;
3) manufacture craft of the present invention is simple, makes easily.
4) the present invention is easy to use, and purposes is wide, applicable to conventional equipments such as air filtration element such as baking finish for car room exhaust air discharge equipment, family expenses and industrial air regulator, air freshener, dust catcher, ventilation fan, smoke exhaust ventilators with in the air handling system.
The specific embodiment
Embodiment 1
A kind of manufacture method of puffy glass fiber filtration material, be with simple glass through after the fusion under normal pressure the effect by self gravitation eject the formation filament by 3 micron pore size, be that 30% epoxy resin acetone soln binding agent bonds according to 50 parts of concentration of 100 parts of glass fibres then, through spending dry oven dry and fluffyization in the baking ovens 100 again behind the multilayer build-up, make goods form smooth skin shape epidermis on two surfaces subsequently by two rollers that press, at last soak oven dry subsequently with 5% fire retardant alumina solution by weight percentage on its surface.
Embodiment 2
A kind of manufacture method of puffy glass fiber filtration material, be through under 8 atmospheric effects, ejecting the formation filament after the fusion with safety glass by little 30 micron pore size, be that 70% phenolic resin solution bonds according to 40 parts of concentration of 100 parts of glass fibres then, through spending dry oven dry and fluffyization in the baking ovens 200 again behind the multilayer build-up, and make goods form smooth skin shape epidermis by two rollers that press on two surfaces, using by weight percentage on its surface at last, 30% fire retardant magnesia sprays.
Claims (6)
1, a kind of manufacture method of puffy glass fiber filtration material, it is characterized in that: be that glass is ejected the formation filament by micropore under pressure after fusion, add that then binding agent bonds, through fluffyization of high temperature again behind the multilayer build-up, and form smooth skin shape epidermis on two surfaces, add fire retardant on its surface at last;
Above-mentioned glass can be simple glass, borate glass, lead glass, cobalt glass, coloured glass or safety glass;
Above-mentioned adhesive can be phenolic resin, epoxy resin, Lauxite, anline resin, polyurethane resin or unsaturated-resin;
Above-mentioned fire retardant can be the chemical substance of the halogen-containing phosphorus-containing matter of organic matter, also can be inorganic substances, as aluminium oxide, magnesia.
2, the manufacture method of a kind of puffy glass fiber filtration material according to claim 1 is characterized in that: the effective diameter of above-mentioned glass fibre is the 3-30 micron.
3, the manufacture method of a kind of puffy glass fiber filtration material according to claim 1 is characterized in that: the temperature of above-mentioned fluffyization of high temperature is the 100-200 degree.
4, the manufacture method of a kind of puffy glass fiber filtration material according to claim 1 is characterized in that: above-mentioned interpolation fire retardant is with fire retardant use immersion or the spraying method of 5%-30% are added on its surface by weight percentage.
5, the manufacture method of a kind of puffy glass fiber filtration material according to claim 2 is characterized in that: the effective diameter of above-mentioned glass fibre is the 16-24 micron.
6, the manufacture method of a kind of puffy glass fiber filtration material according to claim 2 is characterized in that: above-mentioned glass is through ejecting the formation filament by micropore after the fusion under 1-10 atmospheric pressure effect.