CN1709662A

CN1709662A - Punching tool manufacturing method for puncher

Info

Publication number: CN1709662A
Application number: CN 200410059429
Authority: CN
Inventors: 黄建铨
Original assignee: Individual
Current assignee: Individual
Priority date: 2004-06-18
Filing date: 2004-06-18
Publication date: 2005-12-21
Anticipated expiration: 2024-06-18
Also published as: CN1326675C

Abstract

A manufacture method for making punching tool of eyelet machine is to make a columned curly metal continuity raw material stretched and lined, and then cut it by the length needed by the punching tool to form a single type raw material; and then put it into shaped module and then use the clash head dash out a flute on one end for at least one time clash, clash the flute to a prospective cutting edge, while the other end clash the brim of upper face to form the first pre-shape material; clash a orientation hole or orientation ring slot on each of pre-shape material to form a second pre-shape material; and through heat treatment, surface whetting and antirust dispose we can get a stiletto knife finished product which has the characters of steady quality, lower cost, laborsaving.

Description

The punching cutter manufacture method of puncher

Technical field

The present invention is relevant with a kind of puncher, particularly relates to the punching cutter manufacture method of puncher.

Background technology

Consult Fig. 1,2, the punching cutter 10 of known puncher is when making, mainly be earlier with the cylindrical vertical bar iron material 11 in a cross section as type embryo material in advance, and give machined into according to the Len req of punching cutter 10 and cut, pre-sections material 11 after this cuts is bestowed lead angle turning in an end support surface 12, to form a lead angle edge 13, and can be according to the difference of punching cutter 10 installings, in go ahead of the rest turning one location annular groove 14 or be drilled with a locating hole 15 of its external diameter edge, pre-sections material 11 after with the cutting blade 20 of toolroom machine each being cut again is with respect to the end in addition of support surface 12, form a cutting cutting edge 16 according to required cutting angle milling, at last, the pre-sections material 11 of soft materials is heat-treated, to improve its rigidity material characteristic, carry out again grinding and antirust processing on the embryo material surface, to finish manufacturing of punching cutter 10.

But the manufacture method of known punching cutter has following many scarce frauds and waits to solve:

1, known punching cutter 10 utilizes the cylindrical vertical bar iron material 11 in a cross section to be cut for pre-type embryo material carries out size, so the production place needs long spatial accommodation, to hold or to put this rectangular iron material 10, and because iron material 11 its length of this long vertical bar shaped can not infinitely be extended, therefore, each 11 of cylinder iron material can provide the negligible amounts of manufacturing punching cutter 10, operating personnel's essential frequent replacing in work is carried out installed the iron material of producing 11, and causes production efficiency not high.

2, the cutting edge 16 of known punching cutter 10 is that cutting blade 20 with toolroom machine cuts, because that cutting operation needs is incremental, so need the long cutting time, be the not high first cause of cutter shaping efficiency in fact.

3, as mentioned above, because the cutting edge 16 of known punching cutter 10 must be dependent on cutting operation fully, therefore, cutting blade 20 consumes of this toolroom machine are exceedingly fast, and in the working angles, the injection of break flour is easily caused in this workplace, the working environment vulnerable to pollution, and cause the health that influences operating personnel; Again,, need to be changed cutting blade 20 regularly, improve, do not meet the economical production benefit in fact and cause the cost of deriving for guaranteeing the quality of cutting edge 16 cuttings.

4, the cutting edge 16 after cutting, it is the cutting face of a plane formula, so the reaction force that is produced during paper punching, make its to the required application of force of paper punching also relatively for greatly.

Summary of the invention

Main purpose of the present invention provides a kind of punching cutter manufacture method of puncher, it will be cylindric curling metal continuity embryo material and cut, cooperate mould punching and punching press and form cutting edge and support surface lead angle edge respectively in two ends, make it have high manufacturing speed and efficient, and with low cost, the moulding quality is good, punching is more laborsaving.

The punching cutter manufacture method of puncher of the present invention mainly is to be cylindric curling metal continuity embryo material with one, is cut according to the punching cutter Len req after stretching through extending, to form the pre-type embryo of monomer material again; Again the pre-type embryo of this monomer material is inserted in the mould, and utilize ram head at one end portion at least once dash to establish and form a shrinkage pool, the continuous cutting edge that again the shrinkage pool punching press is formed expection, the end is then carried out the lead angle edge of this support surface of punching press simultaneously in addition, to mold first preshaping body; Establish a locating hole or spreading one location annular groove in each first preshaping body upper punch again, to form one second preshaping body; Heat-treat in regular turn again, surface grinding and antirust processing, to obtain required punching cutter finished product.

Manufacture method provided by the present invention, not only processing procedure is more quick and cutting edge stay in grade and punching are laborsaving, thus can effectively reduce production costs, and meet the economical production benefit.

Description of drawings

Fig. 1 is that the punching cutter of known puncher is made process block diagram.

Fig. 2 is the making schematic flow sheet of known punching cutter.

Fig. 3 makes process block diagram for the punching cutter of puncher of the present invention.

Fig. 4 is the making schematic flow sheet of punching cutter of the present invention.

Fig. 5 is the stereoscopic figure of punching cutter of the present invention.

Fig. 6 is the stereoscopic figure of another punching cutter of the present invention.

The main element symbol description

Conventional construction

10...... punching cutter 11...... iron material

12...... support surface 13...... lead angle edge

14...... positioning ring groove 15...... locating hole

16...... cutting edge 20...... cutting blade

The present invention

30...... the pre-type embryo of continuity embryo material 31...... monomer material

311...... shrinkage pool 32...... first preshaping body

321...... cutting edge 322...... support surface

323...... lead angle edge 33...... second preshaping body

331...... locating hole 332...... positioning ring groove

40...... guide wheel 50...... mould

51...... die cavity 52...... ram head

53...... ram head 54...... ram head

60...... punching cutter

The specific embodiment

Consult Fig. 3,4, the cutter manufacture method of puncher of the present invention, its step includes:

(a) be equipped with material: be to be equipped with one to be cylindric curling metal continuity embryo material 30, and this continuity embryo material 30 is furled the location supply;

(b) cut: the guide wheel 40 of this metal continuity embryo material 30 by a correspondence given roll extrusion extend stretchingly, and cut, to form the pre-type embryo of monomer material 31 respectively according to punching cutter 60 Len reqs;

(c) moulding of cutting edge and support surface lead angle edge: the pre-type embryo of each monomer material 31 is inserted in the die cavity 51 of mould 50 in regular turn, and the one end carried out one-off hole-piercing operation at least with ram head 52 according to the degree of depth of required cutting, after making this end form the shrinkage pool 311 of a desired depth, automatically change the ram head 53 of the mould 50 of another form again, these shrinkage pool 311 punching presses are formed cutting edge 321 V-shaped without exception and that have depression, and support surface 322 punching press in the same time of other end formed a lead angle edge 323, to be shaped to first preshaping body 32 respectively;

(d) moulding of locating hole or positioning ring groove: hold in addition suitably radially to locate to dash at the cutting edge 321 of each first preshaping body 32 respectively and establish a locating hole 331, or according to the difference of punching cutter 60 installing, and can be in its external diameter edge spreading one location annular groove 332, to form one second preshaping body 33;

(e) heat treatment: each second preshaping body 33 is heat-treated, to improve rigidity material characteristic;

(f) grind: each second preshaping body, 33 outer peripheral edges is carried out surface grinding, make its punching cutter 60 have a preferable smooth surface and an out of roundness, and make the outer peripheral edges of cutting edge 321 form sharpness;

(g) antirust: as each second preshaping body 33 to be carried out antirust processing, to prevent corrosion, to obtain a punching cutter 60 finished products respectively, shown in Fig. 5,6.

What need special instruction is, the pre-type embryo of monomer of the present invention material 31 is in mould 50 inside, when carrying out the punching operation with ram head 52, its length can be slightly elongated because of the punching extruding, and when carrying out the punch forming of cutting edge 321 with another ram head 53, its length is with the answer of appropriateness, use the physical change that the pre-type embryo material 31 of conduct dashes when establishing, simultaneously, in this mould 50, it can be gone out die cavity 51 with each preshaping body after the moulding by another ram head 54.

At last, characteristic of the present invention and the arrangement of attainable effect is as follows:

1, punching cutter 60 of the present invention cuts to be cylindric curling metal continuity embryo material 30, therefore, the continuity embryo material 30 that should curl does not only more take up space, and can continuously supply long pre-type embryo material, can reduce pre-type embryo material and change the time of installing, so can promote whole production efficiency according to this.

2, the cutting edge 321 of punching cutter 60 of the present invention can be in the same time with the lead angle edge 323 of support surface 322, finish with punching faster and punch forming mode by mould 50, so its shaping speed is fast far beyond the method for known employing grinding operation, makes efficient so can promote integral production.

3, as mentioned above, because the cutting edge 321 of punching cutter 60 of the present invention utilizes mould 50 punchings and punch forming, in its forming process, go out shrinkage pool 311 earlier, be beneficial to again shrinkage pool 311 punching presses are formed cutting edge 321, thus this mould 50 and respectively this

ram head

52,53 have the space of low cost and non-environmental-pollution doubt compared to known cutting blade 20, plastic more punching cutter 60 meets the production economic benefit really.

4, because the cutting edge 321 of this punching cutter 60, be to establish shrinkage pool 311 through dashing earlier, give the cutting edge that punching press is V-shaped without exception and tool caves in again, so its cutting edge 321 has the space of a buffering when paper punching, can reduce paper to the reaction force that cutting edge produces, make the required application of force of its punching operation also laborsaving relatively.

But the above only is of the present invention one preferable possible embodiments, so use the equivalent structure variation that the present invention does such as, ought to be included in the claim of the present invention.

Claims

1, a kind of punching cutter manufacture method of puncher is characterized in that, its step comprises:

(a) be equipped with a cylindrical metal continuity embryo material, and this continuity embryo material is furled the location supply;

(b) this metal continuity embryo material is extended stretching after, and cut, to form the pre-type embryo of monomer material respectively according to the punching cutter Len req;

(c) the pre-type embryo of each monomer material is inserted in the mould in regular turn, and carry out one-off hole-piercing at least,, again this shrinkage pool punching press is formed a cutting cutting edge, to mold first preshaping body respectively to form the shrinkage pool of a desired depth in an end;

(d) respectively the cutting edge of each first preshaping body in addition end suitably radially locate to dash and establish a locating hole, or according to the difference of punching cutter installing, and can be in its external diameter edge spreading one location annular groove, to form one second preshaping body;

(e) each second preshaping body is heat-treated;

(f) each second preshaping body outer peripheral edges is carried out surface grinding;

(g) each second preshaping body is carried out antirust processing, and obtain a punching cutter finished product respectively.

2, the punching cutter manufacture method of puncher according to claim 1 is characterized in that, the guide wheel of this metal continuity embryo material by at least one correspondence gives roll extrusion and extend stretching.

3, the punching cutter manufacture method of puncher according to claim 1 is characterized in that, the pre-type embryo of this monomer material during the forming and cutting cutting edge, can hold other the support surface punching press to form a lead angle edge in mould simultaneously.

4, the punching cutter manufacture method of puncher according to claim 1 is characterized in that, this cutting edge is generally V-shaped.