CN1693391A - 亮化泛光漆 - Google Patents
亮化泛光漆 Download PDFInfo
- Publication number
- CN1693391A CN1693391A CN 200510025692 CN200510025692A CN1693391A CN 1693391 A CN1693391 A CN 1693391A CN 200510025692 CN200510025692 CN 200510025692 CN 200510025692 A CN200510025692 A CN 200510025692A CN 1693391 A CN1693391 A CN 1693391A
- Authority
- CN
- China
- Prior art keywords
- flood
- polish
- paint
- pigment
- paint according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种具有亮化效果的丙烯酸类漆,具体地说是一种亮化泛光漆。一种亮化泛光漆由石英、丙烯酸树脂、颜料、助剂、填充料在常温下按一定比例配制而成,其特征在于其组成(按重量计)的百分比为:石英20-40%,丙烯酸树脂40-60%,颜料10-14%,助剂1-3%,填充料5-7%。同现有技术相比,本发明所述的泛光漆不是边涂刷,边撒微珠的产品,是一次成型的产品。从而大大简化了操作。本发明所述的泛光漆可以手工涂刷,喷枪喷涂,施工简单方便。而使用了泛光光亮涂层技术的广播电视塔就不会出现这种现象,通过灯光的照射,整体结构便能显现光芒四射的玻璃质感。同时使用亮化泛光漆以后,还可使灯光功率降低,达到节电目的。
Description
[技术领域]
本发明涉及一种具有亮化效果的丙烯酸类漆,具体地说是一种亮化泛光漆。
[背景技术]
现有技术中,泛光漆在实际的操作中均有许多不便之处,要分两道工序完成。一种泛光漆是先须喷涂反光底漆,待底漆表干后,再喷涂反光面漆而成型;另一种泛光漆更为低陋,先将反光底漆喷上,再在的漆面喷涂沾附上反光玻璃微珠,不仅浪费大,而且漆面难看,亮化效果不均匀。因为这种操作上的不便,许多曾采用泛光漆的单位被迫放弃了使用,正在使用的,也希望能出现操作更为简便的泛光漆。
[发明内容]
本发明的目的是在背景技术基础上,通过调整其组份、配比及生产工艺,以达到提高泛光漆的反光性能的目的。
为实现上述目的,本发明采用以下方案来实现:一种亮化泛光漆由石英、丙烯酸树脂、颜料、助剂、填充料在常温下按一定比例配制而成,其特征在于其组成(按重量计)的百分比为:
石英 20-40%
丙烯酸树脂 40-60%
颜料 10-14%
助剂 1-3%
填充料 5-7%
该亮化泛光漆的优选的组成(按重量计)的百分比为:
石英 30%
丙烯酸树脂 50%
颜料 12%
助剂 2%
填充料 6%
所述的助剂为分散防沉剂、流平剂、催干剂、增稠剂、消泡剂中的一种或几种。还可以根据具体的工艺的要求,添加不同的添加剂。
所述的石英为六角的、八角的或者是十二角的。为了能保证最佳的泛光效果,最好采用十二角的石英。而所采用的填充料为轻钙、硫酸钡、滑石粉等等及其他本领域常用的填充料。
而所用的颜料为BASF所生产的颜料,主要有普灵黄、普灵宝红、海丽晶蓝、丽色宝黄、丽色宝橙、丽色宝黑等等。根据需要的色彩可进行调配,以满足需要。同时,所用的颜料也可以采用质量比较好的其他颜料。
一种亮化泛光漆,其特征在于其制备工艺是:
(1)预混:将石英、填料、部分消泡剂加入配料罐中高速搅拌均匀
(2)分散:将上述物料送入分散罐,向其中加入增稠剂,搅匀进行分散
(3)后混:在上述物料中加入丙烯酸树脂,部分助剂搅匀
(4)调色:在上述物料中加入颜料进行调色
(5)过滤
(6)包装
该泛光漆能用于广播电视塔、桥梁、高架道路,以及其他的城市的景观建筑和标志性建筑。
由于调整其组份、配比及生产工艺,及根据光的各向同性的原理,本泛光漆能显著增加在夜间的亮化效果。同时,本泛光漆具有反光率高,能防止紫外线光波照射、防止颜色淡化剥离,能抗极强的盐雾、抗酸碱等性能。
同现有技术相比,本发明所述的泛光漆不是边涂刷,边撒微珠的产品,是一次成型的产品。从而大大简化了操作。本发明所述的泛光漆可以手工涂刷,喷枪喷涂,施工简单方便。而使用了泛光光亮涂层技术的广播电视塔就不会出现这种现象,通过灯光的照射,整体结构便能显现光芒四射的玻璃质感。同时使用亮化泛光漆以后,还可使灯光功率降低,达到节电目的。
[附图说明]
图1是本发明创造的工艺流程图:参见图1。
1为预混,2为分散,3为后混,4为调色,5为过滤,6为包装
[具体实施例]
以下结合具体实例对本发明作进一步具体描述,但不局限于此。这种制造技术对本专业的人员来说还是清楚地
例1采用以下配方制备泛光漆
石英 22%
丙烯酸树脂 59%
颜料 10%
助剂 2%
填充料 7%
该泛光漆的附着力为一级,硬度为2H,耐冲击性为45kg,柔韧性为1,耐磨性为0.046。
例2采用以下配方制备泛光漆
石英 38%
丙烯酸树脂 43%
颜料 10%
助剂 2%
填充料 7%
该泛光漆的附着力为一级,硬度为4H,耐冲击性为50kg,柔韧性为1,耐磨性为0.044。
例3采用以下配方制备泛光漆
石英 30%
丙烯酸树脂 50%
颜料 12%
助剂 2%
填充料 6%
该泛光漆的附着力为一级,硬度为2H,耐冲击性为50,柔韧性为1,耐磨性为0.046。
Claims (7)
1、一种亮化泛光漆由石英、丙烯酸树脂、颜料、助剂、填充料在常温下按一定比例配制而成,其特征在于其组成(按重量计)的百分比为:
石英 20-40%
丙烯酸树脂 40-60%
颜料 10-14%
助剂 1-3%
填充料 5-7%
2、根据权利要求1所述的一种亮化泛光漆,其特征在于其组成(按重量计)的百分比为:
石英 30%
丙烯酸树脂 50%
颜料 12%
助剂 2%
填充料 6%
3、根据权利要求1或2所述的一种亮化泛光漆,其特征在于所述的助剂为分散防沉剂、流平剂、催干剂、增稠剂、消泡剂中的一种或几种。
4、根据权利要求1或2所述的一种亮化泛光漆,其特征在于所述的石英为六角的、八角的或者是十二角的。
5、根据权利要求1或2所述的一种亮化泛光漆,其特征在于所述的石英为十二角的。
6、根据权利要求1或2所述的一种亮化泛光漆,其特征在于其制备工艺是:
(1)预混:将石英、填料、部分消泡剂加入配料罐中高速搅拌均匀
(2)分散:将上述物料送入分散罐,向其中加入增稠剂,搅匀进行分散
(3)后混:在上述物料中加入丙烯酸树脂,部分助剂搅匀
(4)调色:在上述物料中加入颜料进行调色
(5)过滤
(6)包装。
7、根据权利要求1或2所述的一种亮化泛光漆,其特征在于该泛光漆可用于广播电视塔、桥梁、高架道路及城市亮化的景观建筑和标志性建筑。