CN1661355A - Probe unit of microscope with atomic force and manufacturing method - Google Patents
Probe unit of microscope with atomic force and manufacturing method Download PDFInfo
- Publication number
- CN1661355A CN1661355A CN 200410015593 CN200410015593A CN1661355A CN 1661355 A CN1661355 A CN 1661355A CN 200410015593 CN200410015593 CN 200410015593 CN 200410015593 A CN200410015593 A CN 200410015593A CN 1661355 A CN1661355 A CN 1661355A
- Authority
- CN
- China
- Prior art keywords
- plane
- atomic force
- force microscope
- hole
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to an atomic force microscope probe device and its making method. It includes a probe seat, a cantilever which is fixed on the probe seat and has at least a tail end on which a probe point can be set and a carbon nano tube which is set on the tail end of said cantilever and used as probe point, in which the top portion of said probe cantilever tail end is formed into a plane with hole, and said carbon nano tube can be grown out from said hole which is basically perpendicular to said plane.
Description
[technical field]
The present invention relates to a kind of atomic force microscope (Atomic Force Microscopy is hereinafter to be referred as AFM) probe unit and manufacture method thereof, relate in particular to a kind of atomic force microscope probe device and manufacture method thereof that adopts carbon nano-tube to make needle point.
[background technology]
In recent years, along with the densification of devices such as CD, magnetic recording, semiconductor, highly integrated, expand day by day with the range of application of the AFM of the following precision determination sample surface of nanometer form.Its principle of work is to utilize that the dependence of power and distance obtains material surface structure and character between its probe and the sample.Typical A FM has three kinds of imaging patterns: contact, contactless and rap formula.And probe is the core component of AFM, costs an arm and a leg, and is very easily impaired.
Favorable elasticity and the most advanced and sophisticated characteristic of utilizing carbon nano-tube to possess early have report with its AFM as probe tip.Dai Hongjie etc. are disclosing a kind of method that forms carbon nano-tube point on the probe cantilever of using at AFM in the 6th, 346, No. 189 United States Patent (USP)s " carbon nano tube structure that utilizes the catalyzer island to make " of bulletin on February 12nd, 2002.This method step is as follows: a cantilever that can be used for AFM is provided; Free end (Free End) deposition one catalyst granules at this cantilever; Make this catalyst granules at high temperature contact carbon-containing atmosphere to grow carbon nano-tube.
Yet this method is directly in the carbon nano-tube of the cantilever tip of AFM growth as needle point, and the carbon nano-tube poor orientation of gained certainly will influence the accuracy of whole AFM.
Therefore, be necessary to provide a kind of AFM probe unit and manufacture method thereof with high orientation carbon nano-tube point.
[summary of the invention]
For solving the low problem of orientation that is used as the carbon nano-tube of AFM probe tip in the prior art, first purpose of the present invention is to provide a kind of AFM probe unit with high orientation carbon nano-tube point.
Second purpose of the present invention is to provide the method for making above-mentioned AFM probe unit.
For realizing first purpose of the present invention, AFM probe unit provided by the present invention comprises: a probe base; One be fixed in probe base, have at least one cantilever that the end of needle point is set; And be arranged at this cantilevered distal end as the carbon nano-tube of needle point.Wherein, the top of this probe cantilevered distal end is formed with a plane with hole, and this carbon nano-tube is basically perpendicular to this plane by this hole and grows.
For realizing second purpose of the present invention, the manufacture method of above-mentioned AFM probe unit provided by the present invention comprises step: provide one to have the AFM cantilever that at least one need are provided with the end of needle point; Form a plane at this terminal top; Adopt the deep electroforming model of X-ray (be LithographyElectroforming Micro Molding, be called for short LIGA) processing procedure to form a hole on this plane; It is basic vertical with the carbon nano-tube as needle point with this plane to adopt chemical vapour deposition technique to be grown by this hole.
The aperture of above-mentioned hole can be 20~100 nanometers.
Above-mentioned LIGA processing procedure comprises step: the photoresist layer that forms the tool predetermined pattern on this plane; This plane of etching is so that its formation and the corresponding predetermined pattern of photoresist layer; Remove the photoresist layer.
Above-mentioned employing chemical vapour deposition technique is grown with the step of the vertical substantially carbon nano-tube in this plane by this hole and comprises step: at this planar depositions catalyzer; One carbon source gas is provided, and it is contacted with catalyzer at predetermined temperature make that being basically perpendicular to this plane during carbon nano-tube is by hole grows.
With respect to prior art, the present invention adopts the LIGA fabrication process that the AFM probe cantilever of carbon nano-tube point need be set, make its terminal top form the nano aperture structure, utilize " template effect " of this pore space structure to adopt chemical vapour deposition technique again at this cantilevered distal end carbon nano-tube.Because the hole diameter of LIGA fabrication process gained is even and the degree of depth is easily controlled, makes the carbon nano-tube favorable orientation that makes as template, thereby guarantee and improves the accuracy of the AFM instrument of this probe of use.
[description of drawings]
Fig. 1 is the synoptic diagram of AFM probe unit of the present invention;
Fig. 2 is the schematic flow sheet of the method for the above-mentioned AFM probe unit of manufacturing of the present invention;
Fig. 3 is the schematic flow sheet of LIGA processing procedure provided by the invention 57 ' formation hole 58 ' in the plane;
Fig. 4 is the schematic flow sheet of chemical vapour deposition technique provided by the invention in hole 58 ' carbon nano-tube.
[embodiment]
The present invention is described in further detail below in conjunction with accompanying drawing.
See also Fig. 1, AFM probe unit 5 provided by the present invention comprises: a probe base 50; One is fixed in the cantilever 52 of probe base 50, has an end 54; Be arranged at this cantilevered distal end 54, as the carbon nano-tube 60 of needle point.Wherein, the top 56 of cantilevered distal end 54 is formed with a plane 57, and this plane 57 has a hole 58.Carbon nano-tube 60 is grown by this hole 58, and is basically perpendicular to this plane 57.
In the present embodiment, the aperture of hole 58 is preferably 20~100 nanometers.Cantilever 52 can be made by silicon nitride.
See also Fig. 2, the manufacture method 7 of above-mentioned AFM probe unit 5 provided by the present invention comprises step:
(2a) provide the cantilever 52 ' that can be used for AFM, its tool one need be provided with the end 54 ' of needle point, and this end 54 ' has a pointed top 56 ';
(2b) can form a plane 57 ' in this terminal top 56 ' by modes such as cutting polishings;
(2c) adopt the LIGA processing procedure to form a hole 58 ' on this plane 57 ';
It is basic vertical with the carbon nano-tube 60 as needle point with this plane 57 ' (2d) to adopt chemical vapour deposition technique to grow in this hole 58 '.
See also Fig. 3, described LIGA processing procedure comprises that step is as follows:
(3a) 57 ' coating one photoresist layer 80 (as polymethylmethacrylate, Polyvinylchloride or polycarbonate etc.) on the plane, again a light shield (figure does not show) that is provided with predetermined pattern being placed on the photoresist layer 80 and at X-ray and exposes certain hour to the open air, is that developer adopts the wet corrosion method to make the photoresist layer manifest predetermined pattern with alkaline solutions such as potassium hydroxide;
(3b) adopt reactive ion-etching etching plane 57 ' to form and photoresist layer 80 corresponding predetermined pattern;
(3c) with an organic solvent as removal photoresist layers 80 such as acetone.
57 ' form hole 58 ' on the plane thus.
In addition, adopting the LIGA method that object is carried out the concrete processing procedure of micromachined can be with reference to the 6,245, and No. 849, the 6th, 472, No. 459 and the 6th, 455, the related content of No. 233 United States Patent (USP)s.
See also Fig. 4, utilize chemical vapour deposition technique can adopt step in the carbon nano-tube 60 that hole 58 ' growth is used as needle point:
(4a) 57 ' deposited catalyst on the plane.Methods such as available electron bundle evaporation, sputter or coating on the plane 57 ' with hole 58 ', make it form the thick catalyst film 82 of 4~10nm, one or more materials of catalyzer chosen from Fe, cobalt, nickel and oxide thereof catalyst deposit.
(4b) provide a carbon source gas, and it is contacted with catalyzer at predetermined temperature make that being basically perpendicular to plane 57 ' during carbon nano-tube is by hole 58 ' grows.300 ℃~500 ℃ of temperature, under the air atmosphere, catalyst film 82 is carried out 8~12 hours annealing in process, make its nano-scale particle that is punctured into separation (figure do not show), and the cantilever 52 ' that will have a catalyst granules is put reacting furnace (figure does not show) simultaneously into; Feed blanket gas (not indicating) air is caught up with to the greatest extent fully, reacting furnace is heated to 550~1000 ℃ simultaneously; Feed blanket gas and carbon source gas (not indicating) then, blanket gas can be argon, nitrogen or helium etc., and carbon source gas can be acetylene, methane, ethene etc.; After about 15 seconds~40 minutes, highly certain carbon nano-tube 60 is grown by hole 58 '.
Certainly, catalyst film 82 also can only be distributed in the hole 58 ', and the carbon nano-tube 60 of gained can be carbon nano-tube tube bank, and should not exceed with present embodiment.
The employing chemical vapour deposition technique also can be with reference to the related content of above-mentioned the 6th, 346, No. 189 United States Patent (USP)s at the concrete steps and the reaction conditions of cantilevered distal end carbon nano-tube 60.
In addition, those skilled in the art should understand that the concrete steps of LIGA fabrication process cantilevered distal end provided by the invention and chemical vapour deposition technique carbon nano-tube are and illustrate the present invention, should not limit with specific embodiment.Be understandable that when adopting different fixed positions, the probe cantilever also has two ends that are used to be provided with needle point.This manufacture method 7 can comprise further that probe cantilever 52 ' that a step is about to gained is fixed in the probe base 50 of AFM.
The present invention adopts the LIGA fabrication process that the AFM probe cantilever of carbon nano-tube point need be set, and makes its terminal top form the nano aperture structure, utilizes " template effect " of this pore space structure to adopt chemical vapour deposition technique at this cantilevered distal end carbon nano-tube again.Because the hole diameter of LIGA fabrication process gained is even and the degree of depth is easily controlled, makes the carbon nano-tube favorable orientation that makes as template, thereby guarantee and improves the accuracy of the AFM instrument of this probe of use.
Claims (10)
1. an atomic force microscope probe device comprises: a probe base; One be fixed in probe base, have at least one cantilever that the end of needle point is set; And be arranged at this cantilevered distal end as the carbon nano-tube of needle point, and it is characterized in that the top of this probe cantilevered distal end is formed with a plane with hole, this carbon nano-tube is basically perpendicular to this plane by this hole and grows.
2. described according to claim 1 atomic force microscope probe device is characterized in that the aperture of above-mentioned hole is 20~100 nanometers.
3. the manufacture method of an atomic force microscope probe device comprises step: provide at least one need of a tool that the atomic force microscope cantilever of the end of needle point is set; Form a plane at this terminal top; Adopt the deep electroforming model of X-ray processing procedure to form a hole on this plane; It is basic vertical with the carbon nano-tube as needle point with this plane to adopt chemical vapour deposition technique to grow in this hole.
4. as the manufacture method of described atomic force microscope probe device as described in the claim 3, it is characterized in that, adopt the cutting polishing process to form a plane at this terminal top.
5. the manufacture method of atomic force microscope probe device as claimed in claim 3 is characterized in that, the deep electroforming model of above-mentioned X-ray processing procedure comprises step: form the photoresist layer with predetermined pattern on this plane; This plane of etching forms and the corresponding predetermined pattern of photoresist layer; Remove the photoresist layer.
6. the manufacture method of atomic force microscope probe device as claimed in claim 5 is characterized in that, above-mentioned formation method with photoresist layer of predetermined pattern comprises step: a light shield that is provided with predetermined pattern is provided; Form a photoresist layer on this plane; Light shield placed on the photoresist layer and in X-ray expose certain hour to the open air; Adopt treating fluid to make the photoresist layer manifest predetermined pattern.
7. the manufacture method of atomic force microscope probe device as claimed in claim 3 is characterized in that, the aperture of above-mentioned hole is 20~100 nanometers.
8. the manufacture method of atomic force microscope probe device as claimed in claim 3 is characterized in that, above-mentioned employing chemical vapour deposition technique is grown with the step of the vertical substantially carbon nano-tube in this plane by this hole and comprises step: at this planar depositions catalyzer; One carbon source gas is provided, and it is contacted with catalyzer at predetermined temperature make that being basically perpendicular to this plane during carbon nano-tube is by hole grows.
9. the manufacture method of atomic force microscope probe device as claimed in claim 8 is characterized in that, above-mentioned catalyzer only is distributed in the hole at top.
10. the manufacture method of atomic force microscope probe device as claimed in claim 3 is characterized in that, this manufacture method further comprises the step that the probe cantilever of gained is fixed in the atomic force microscope probe seat.