CN1654571A - Functional primer and its preparing process - Google Patents

Functional primer and its preparing process Download PDF

Info

Publication number
CN1654571A
CN1654571A CN 200510038218 CN200510038218A CN1654571A CN 1654571 A CN1654571 A CN 1654571A CN 200510038218 CN200510038218 CN 200510038218 CN 200510038218 A CN200510038218 A CN 200510038218A CN 1654571 A CN1654571 A CN 1654571A
Authority
CN
China
Prior art keywords
resin
mixed solvent
butanone
sebacic acid
isoamyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510038218
Other languages
Chinese (zh)
Other versions
CN1290950C (en
Inventor
李永安
周立军
徐根华
徐金官
柏金枝
李晓霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHONGJIN MEDICINE PAKING CO Ltd LIANYUNGANG
Original Assignee
ZHONGJIN MEDICINE PAKING CO Ltd LIANYUNGANG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHONGJIN MEDICINE PAKING CO Ltd LIANYUNGANG filed Critical ZHONGJIN MEDICINE PAKING CO Ltd LIANYUNGANG
Priority to CN 200510038218 priority Critical patent/CN1290950C/en
Publication of CN1654571A publication Critical patent/CN1654571A/en
Application granted granted Critical
Publication of CN1290950C publication Critical patent/CN1290950C/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The functional bottom paint has glycol-paraphthalic acid-sebacic acid polymer as main adhering resin, mixed nitrocellulose-acrylic acid resin, glycol-paraphthalic acid-sebacic acid-isopentyl diol polymer, and mixed solvent of butanone, ethyl acetate, isopropanol, etc. It is painted onto aluminum foil and may have hot melt adhesive painted on it. The coating the paint forms has high density, hard dissolving and other performance of thermosetting resin as well as high surface tension like thermoplastic resin, and thus may be painted for the second time effectively. The present invention is used to coat blister packing aluminum foil to protect medicine effectively.

Description

A kind of functional primer and preparation method thereof
Technical field
The present invention relates to a kind of silane coupling agent, particularly a kind of silane coupling agent that is used for Blister Package with the internal layer functional type that covers aluminium foil.
The invention still further relates to the making method of the silane coupling agent of this functional type.
Background technology
Existing normally used Blister Package is to be basal layer with the pure aluminum foil with covering aluminium foil, is attached with protective layer and printed layers or matcoveredn only at the aluminium foil outside surface; Adhere at the aluminium foil layer internal surface printed layers is arranged, hot melt adhesive layer or have only hot melt adhesive layer.In the prior art be 93111514.0 Chinese patent as the patent No., it discloses a kind of aluminium-plastics hot-fusible binder: it is to be mixed by mixed solvent, ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer, vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin.When the aluminium foil packing that use is coated with this aluminium-plastics hot-fusible binder contains the medicine of volatile matter; at first be that hot melt adhesive layer is in a short time promptly by molten and come off again; not only polluted medicine; and influenced the stopping property of packing; to destroy aluminium foil when secondly the volatile matter activity is big, and make it can't reach provide protection.
Summary of the invention
The technical problem to be solved in the present invention is at the deficiencies in the prior art, a kind of silane coupling agent that is used for Blister Package with the internal layer functional type that covers aluminium foil has been proposed, it can prevent volatile matter to hot melt adhesive layer destructive metal silane coupling agent, and effectively stops the destruction of certain material to aluminium foil.
Another technical problem that will solve of the present invention is the making method that has proposed the silane coupling agent of this functional type.
The technical problem to be solved in the present invention is achieved through the following technical solutions; a kind of functional primer; be coated on Blister Package with aluminium foil after; after aluminium foil contains the medicine of volatile matter as the tectum packing; should do not destroyed and play the effect of effective protection medicine by activity, the assurance hot melt adhesive layer was not come off by swelling in the maintenance phase of medicine in the specified period again.
The technical problem to be solved in the present invention is achieved through the following technical solutions, and a kind of functional primer is characterized in, it be by:
The mixed solvent 75-80% of butanone, vinyl acetic monomer, Virahol
The hybrid resin 2-5% of nitrocotton, acrylic resin
Ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer 8-12%
Vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 5-9%
The solvent-borne type glue of making, wherein per-cent is mass percent.
The quality proportioning of butanone, vinyl acetic monomer, Virahol is 2~3.5: 5~7 in the described mixed solvent: 1~2; The quality proportioning of nitrocotton, acrylic resin is 4~6: 1~3 in the described hybrid resin.
Wherein, the making method of ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer is: the ethylene glycol that will wait mass parts, the isoamyl glycol, terephthalate is mixed, add Butyl Phthalate and make catalyzer, under 140 ℃~180 ℃ temperature, carry out transesterify, after removing by-product carbinol, be cooled to 120 ℃~140 ℃, the sebacic acid of mass parts such as adding adds butyl (tetra) titanate again and makes catalyzer, under 230 ℃~250 ℃ temperature, pressure is to carry out polyreaction 2~5 hours under 130Pa~150Pa pascal's the condition, and the back adds after ketone and the dissolving of ester class mixed solvent thorough mixing promptly.
The technical problem to be solved in the present invention can also come to realize that further the quality proportioning of butanone, vinyl acetic monomer, Virahol is 3: 6: 1 in the described mixed solvent by the following technical programs.
The technical problem to be solved in the present invention can also come to realize that further the quality proportioning of nitrocotton, acrylic resin is 5: 2 in the described hybrid resin by the following technical programs.
The making method of functional silane coupling agent of the present invention, be characterized in: stir and the answering in the still of backflow functionality having, under 40 ℃ of conditions, add butanone, vinyl acetic monomer, isopropyl alcohol mixed solvent, add nitrocotton, acrylic resin dissolving 2 hours, adding waits the ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer of ratio reaction again, stirring and refluxing adds vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin again after 1 hour, stirring and refluxing 1.5 hours promptly gets the glue of transparent or little Huang.
Compared with prior art, the present invention is main adhering resin by ethylene glycol-terephthalic acid-multipolymers such as sebacic acid, be equipped with the hybrid resin and the ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer of nitrocotton, acrylic resin, use mixed solvents such as butanone, vinyl acetic monomer, Virahol to make the solvent-borne type glue.It is the coating agent of using as metal such as aluminium foil with certain function, and the performances such as highly dense, indissoluble that it applies the existing thermosetting resin of film that the back generates have the high surfaces tension force of thermoplastic resin again, promptly can carry out secondary coating efficiently on the film of its generation.The present invention be coated on Blister Package with aluminium foil after; after promptly using the aluminium foil packing of this silane coupling agent to contain the medicine of volatile matter; can either do not destroyed and play the effect of effective protection medicine by activity, the assurance hot melt adhesive layer was not come off by swelling in the maintenance phase of medicine in the specified period again.
Embodiment
Embodiment 1: a kind of functional primer, it be by:
The mixed solvent 75% of butanone, vinyl acetic monomer, Virahol
The hybrid resin 5% of nitrocotton, acrylic resin
Ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer 12%
Vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 8%
The solvent-borne type glue of making, wherein per-cent is mass percent.
The quality proportioning of butanone, vinyl acetic monomer, Virahol is 3: 6: 1 in the described mixed solvent; The quality proportioning of nitrocotton, acrylic resin is 5: 2 in the described hybrid resin.
Wherein, the making method of ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer is: the ethylene glycol that will wait mass parts, the isoamyl glycol, terephthalate is mixed, add Butyl Phthalate and make catalyzer, under 140 ℃~180 ℃ temperature, carry out transesterify, after removing by-product carbinol, be cooled to 120 ℃~140 ℃, the sebacic acid of mass parts such as adding adds butyl (tetra) titanate again and makes catalyzer, under 230 ℃~250 ℃ temperature, pressure is to carry out polyreaction 2~5 hours under 130Pa~150Pa pascal's the condition, and the back adds after ketone and the dissolving of ester class mixed solvent thorough mixing promptly.
Its making method of this functional primer is: in the little reactor of 50 liters tools stirrings and backflow, under 40 ℃ of environment, add mixed solvent 20kg such as butanone, vinyl acetic monomer, Virahol, add nitrocotton, acrylic resin 0.7kg dissolving 2 hours, ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer the 4kg of ratios such as adding reaction, stirring and refluxing adds vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 2kg again after 1 hour, stirring and refluxing 1.5 hours promptly gets the glue of transparent or little Huang.
Embodiment 2: a kind of functional primer, it be by:
The mixed solvent 80% of butanone, vinyl acetic monomer, Virahol
The hybrid resin 3% of nitrocotton, acrylic resin
Ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer 8%
Vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 9%
The solvent-borne type glue of making, wherein per-cent is mass percent.
The quality proportioning of butanone, vinyl acetic monomer, Virahol is 2: 7: 1 in the described mixed solvent; The quality proportioning of nitrocotton, acrylic resin is 4: 1 in the described hybrid resin.
In the little reactor of 200 liters tools stirrings and backflow, ratio in 3: 6: 1 under 40 ℃ of environment adds mixed solvent 100kg such as butanone, vinyl acetic monomer, Virahol, dissolved 4 hours by 5: 2 adding nitrocottons, acrylic resin 4kg earlier, ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer the 15kg of ratios such as adding reaction, stirring and refluxing adds vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 12kg again after 1 hour, stirring and refluxing 1.5 hours promptly gets the glue of transparent or little Huang.
Embodiment 3: a kind of functional primer, it be by:
The mixed solvent 78% of butanone, vinyl acetic monomer, Virahol
The hybrid resin 2% of nitrocotton, acrylic resin
Ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer 11%
Vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 9%
The solvent-borne type glue of making, wherein per-cent is mass percent.
The quality proportioning of butanone, vinyl acetic monomer, Virahol is 3.5: 5: 2 in the described mixed solvent; The quality proportioning of nitrocotton, acrylic resin is 6: 3 in the described hybrid resin.
In the little reactor of 200 liters tools stirrings and backflow, ratio in 3: 6: 1 under 40 ℃ of environment adds mixed solvent 100kg such as butanone, vinyl acetic monomer, Virahol, dissolved 3 hours by 5: 2 adding nitrocottons, acrylic resin 1.4kg earlier, ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer the 20kg of ratios such as adding reaction, stirring and refluxing adds vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 10kg again after 1 hour, stirring and refluxing 1.5 hours promptly gets the glue of transparent or little Huang.
Embodiment 4: a kind of functional primer, it be by:
The mixed solvent 80% of butanone, vinyl acetic monomer, Virahol
The hybrid resin 3% of nitrocotton, acrylic resin
Ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer 12%
Vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 5%
The solvent-borne type glue of making, wherein per-cent is mass percent.
The quality proportioning of butanone, vinyl acetic monomer, Virahol is 2: 5: 2 in the described mixed solvent; The quality proportioning of nitrocotton, acrylic resin is 4: 3 in the described hybrid resin.
In the little reactor of 500 liters tools stirrings and backflow, ratio in 3: 6: 1 under 40 ℃ of environment adds mixed solvent 300kg such as butanone, vinyl acetic monomer, Virahol, dissolved 3.5 hours by 5: 2 adding nitrocottons, acrylic resin 10kg earlier, ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer the 80kg of ratios such as adding reaction, stirring and refluxing adds vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 30kg again after 1 hour, stirring and refluxing 1.5 hours promptly gets the glue of transparent or little Huang.

Claims (5)

1. a functional primer is characterized in that, it be by:
The mixed solvent 75-80% of butanone, vinyl acetic monomer, Virahol,
The hybrid resin 2-5% of nitrocotton, acrylic resin,
Ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer 8-12%,
Vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin 5-9%,
The solvent-borne type glue of making, wherein per-cent is mass percent,
The quality proportioning of butanone, vinyl acetic monomer, Virahol is 2~3.5: 5~7 in the described mixed solvent: 1~2; The quality proportioning of nitrocotton, acrylic resin is 4~6: 1~3 in the described hybrid resin.
2. functional primer according to claim 1 is characterized in that, the quality proportioning of butanone, vinyl acetic monomer, Virahol is 3: 6: 1 in the described mixed solvent.
3. functional primer according to claim 1 is characterized in that, the quality proportioning of nitrocotton, acrylic resin is 5: 2 in the described hybrid resin.
4. functional primer according to claim 1, it is characterized in that, the making method of ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer is: the ethylene glycol that will wait mass parts, the isoamyl glycol, terephthalate is mixed, add Butyl Phthalate and make catalyzer, under 140 ℃~180 ℃ temperature, carry out transesterify, after removing by-product carbinol, be cooled to 120 ℃~140 ℃, the sebacic acid of mass parts such as adding adds butyl (tetra) titanate again and makes catalyzer, under 230 ℃~250 ℃ temperature, pressure is to carry out polyreaction 2~5 hours under the condition of 130Pa~150Pa, and the back adds after ketone and the dissolving of ester class mixed solvent thorough mixing promptly.
5. the described functional primer of claim 1, it is characterized in that, its making method is: in the reactor with stirring and backflow functionality, under 40 ℃ of conditions, add butanone, vinyl acetic monomer, isopropyl alcohol mixed solvent, add nitrocotton, acrylic resin dissolving 2~4 hours, adding waits the ethylene glycol-terephthalate-sebacic acid-isoamyl diol copolymer of ratio reaction again, stirring and refluxing adds vinylchlorid-maleic anhydride-vinyl acetate between to for plastic terpolymer resin again after 1 hour, stirring and refluxing 1.5 hours promptly gets the glue of transparent or little Huang.
CN 200510038218 2005-01-24 2005-01-24 Functional primer and its preparing process Active CN1290950C (en)