CN1654419A - Process for preparing alumina ceramic foil materials with penetrative nanohole - Google Patents
Process for preparing alumina ceramic foil materials with penetrative nanohole Download PDFInfo
- Publication number
- CN1654419A CN1654419A CN 200510032663 CN200510032663A CN1654419A CN 1654419 A CN1654419 A CN 1654419A CN 200510032663 CN200510032663 CN 200510032663 CN 200510032663 A CN200510032663 A CN 200510032663A CN 1654419 A CN1654419 A CN 1654419A
- Authority
- CN
- China
- Prior art keywords
- foil
- aluminium
- aluminium foil
- conductive material
- electro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The alumina ceramic foil material with nanometer level through pores is prepared adhering aluminum foil onto the surface of some conductive material to form electric contact; setting the conductive material as anode inside electrochemical anode oxidizing solution to oxidize the aluminum foil into alumina foil with through pores in thickness direction; and separating the alumina ceramic foil from the conductive material to obtain pure alumina ceramic foil material with through pores. The alumina ceramic foil material may be used directly in fine filtering of gas and liquid. The present invention can make compact alumina ceramic foil material with nanometer level through pores effectively in low cost and high efficiency, and has wide industrial application foreground.
Description
Technical field
The present invention relates to aluminium sesquioxide ceramic foil materials field, specifically be meant a kind of aluminium foil to be changed into the preparation method with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous by electrochemical anodic oxidation.
Background technology
Aluminium sheet and aluminium block are when carrying out electrochemical anodic oxidation, the surface can generate one deck di-aluminium trioxide film, and this layer di-aluminium trioxide film is porous, and diameter is less than 100nm, thickness can reach 30 μ m, the hole be axially perpendicular to material surface, and distribute very evenly (" destruction of carrying out---metallic corrosion silently ", Cao Chunan is write, press of Tsing-Hua University, press is learned by Board Nanjing University, in June, 2000 first version, P77~80).Application number is that 01107430.2 Chinese invention patent discloses a sharp aluminum pot fast anode hardening oxidation method, it is characterized in that the aluminum pot is activated with surfactant under 40 ℃~50 ℃ temperature condition after the decontamination in normal temperature alkali lye, carrying out hard anodizing again handles, use chemical hole sealing agent and pure water to surface-sealing at last, prepare the oxide film protection layer; Application number is that the Chinese invention patent of 90101981.X discloses a kind of metallized film chemical oxidization method, and technological process is: at first prepare aluminium plating membrane at base material, produce the oxide film protection layer on the aluminium plating membrane surface with phosphoric acid, chromic salt oxidation style then.The aluminium sesquioxide ceramic membrane material for preparing by the above-mentioned materials process for treating surface is always attached to the surface of substrate (or part), be actually surface film, always combine with substrate, the thickness of substrate material can't use aluminium sesquioxide ceramic membrane material separately in this case much larger than the thickness of thin-film material.But under many circumstances, simple film is widely used in industrial production with different attached to the performance on the substrate surface, is not attached to the aluminium sesquioxide ceramic foil materials on the substrate material and prior art still can't prepare simple.
Summary of the invention
The objective of the invention is to overcome the shortcoming of prior art, a kind of preparation method with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous is provided.
Purpose of the present invention is achieved through the following technical solutions: a kind of preparation method with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous comprises the steps and processing condition: at first the surface with aluminium foil and electro-conductive material fits, aluminium foil is kept between aluminium foil and the electro-conductive material and is conducted electricity with after the surface of electro-conductive material contacts; The electro-conductive material that will be fitted with aluminium foil again places electrochemical anodic oxidation solution to carry out oxidizing reaction as anode, thereby aluminium foil is transformed into aluminium sesquioxide, and form the micropore penetrate at thickness direction, with aluminium sesquioxide ceramic foil after separating from the electro-conductive material surface, then obtain to have the simple aluminium sesquioxide ceramic foil materials that evenly penetrates micropore.
For realizing the present invention better, the method that the surface of aluminium foil and electro-conductive material is fitted is for to be fitted in described aluminium foil on the metal plate with conductive resin; Can also overlay on the cylindrical member described aluminum foil coil is wrapped, the outside surface of aluminium foil and cylindrical member is fitted.
For realizing the present invention better, can work as when aluminum foil coil is wrapped to overlay on nonconducting cylindrical member, the outer field aluminium foil of coating formation and the aluminium foil of internal layer are contacted with each other.
For realizing the present invention better, described anode can be placed electrochemical anodic oxidation solution, electrochemical anodic oxidation solution only contacts with the one side of aluminium foil, and electrochemical anodization reaction is only carried out from the outside surface of aluminium foil.
For realizing the present invention better, on aluminium foil, circularize with the adhesive tape subsides, in the electrochemical anodic oxidation process, pasted the part that circularizes by adhesive tape and do not participate in chemical reaction, still be aluminium foil, the middle area portions of aluminium foil is converted to aluminium sesquioxide, thereby area portions is an aluminium sesquioxide and periphery is the foil material of aluminium in the middle of forming.
Action principle of the present invention is: aluminium sheet and aluminium block are when carrying out electrochemical anodic oxidation, and the surface can generate one deck di-aluminium trioxide film, and this layer di-aluminium trioxide film is porous, diameter is less than 100nm, thickness can reach 30 μ m, the hole be axially perpendicular to material surface, and distribute very evenly.Because aluminium sheet or aluminium block are thicker, its surperficial di-aluminium trioxide film is thinner, and the micropore of formation does not penetrate unitary piece of material.Di-aluminium trioxide film on aluminium sheet or the aluminium block intactly can't be separated from aluminium sheet or aluminium block, so can't utilize aluminium sesquioxide to filter with micropore.When electrochemical anodic oxidation is carried out on the surface of adopting aluminium foil to be fitted in electro-conductive material, can guarantee the electroconductibility of aluminium foil, because aluminium foil is thinner, aluminium foil can change into aluminium sesquioxide fully, the micropore that forms can penetrate whole foil material, thereby can be applicable to the fine filtering of gas or liquid.
The present invention compared with prior art has following advantage and effect:
1, the aluminium sesquioxide ceramic foil materials of the present invention's preparation has micron order thickness, nano through holes, and micropore is even;
2, adopt the present invention can guarantee the electroconductibility of aluminium foil in the electrochemical anodic oxidation process;
3, the aluminium sesquioxide ceramic foil of the present invention's acquisition can be applicable to the fine filtering of gas or liquid, has market outlook preferably, uses in industrial production and can bring huge economic benefit;
4, technology of the present invention is simple, the preparation efficiency height, and Financial cost is low, is suitable for suitability for industrialized production.
Embodiment
The present invention is described in further detail below in conjunction with embodiment, but embodiments of the present invention are not limited thereto.
Embodiment 1
With thickness is that the pure aluminum foil of 30 μ m is evenly reeled and is coated on the PVC cylindrical member, gently draws aluminium foil that the outside surface of aluminium foil and cylindrical member is fitted, and outer field aluminium foil is contacted with the aluminium foil of internal layer.Again with aluminium foil edge rubber belt sealing, in the electrochemical anodic oxidation process, do not make solution enter aluminium foil and be fitted in internal surface on the PVC cylindrical member.Coiling is coated on aluminium foil places electrochemical anodic oxidation solution as anode on the PVC cylindrical member, electrochemical anodic oxidation solution is only contacted with the one side of aluminium foil, thereby electrochemical anodization reaction carried out from a surface of aluminium foil.The concentration of electrochemical anodic oxidation solution is in the sulfuric acid electrolytic solution of 1mol/L, and the temperature of sulfuric acid electrolytic solution is 3 ℃, and anodic current density is 4A/dm
2, the voltage of electrolyzer is 100V; In this process, aluminium foil generation oxidizing reaction changes into aluminium sesquioxide, the blocking layer that will not form through hole is transferred on the aluminium foil of bottom, thereby the thickness direction at the aluminium foil on top layer forms the through hole crack, with the aluminium sesquioxide ceramic foil on top layer after separating from the aluminium foil of bottom, then obtain to have the simple aluminium sesquioxide ceramic foil materials that evenly penetrates micropore.The present invention is transformed into the aluminium sesquioxide ceramic foil materials with micro-through-hole crack through anodic oxidation with pure aluminum foil, can be used for the fine filtering of gas and liquid.
Embodiment 2
Present embodiment is identical with embodiment 1 except that following process: is that the pure aluminum foil of 10 μ m evenly is fitted on the aluminium sheet with conductive resin with thickness, again with aluminium foil edge rubber belt sealing, so that solution is entered between aluminium foil and the aluminium sheet coating surface.After the electrochemical anodic oxidation process is finished, the aluminium sesquioxide ceramic foil is separated from surface of aluminum plate, and after removing photoresist, then obtain to have the simple aluminium sesquioxide ceramic foil materials that evenly penetrates micropore.
Embodiment 3
Present embodiment is identical with embodiment 1 except that following process: with thickness is that the pure aluminum foil of 10 μ m evenly is fitted on the aluminium sheet, again with aluminium foil edge rubber belt sealing, and on aluminium foil, paste into an annular with adhesive tape, in the electrochemical anodic oxidation process, the aluminium foil of area is oxidized to the aluminium sesquioxide ceramic foil materials in the middle of the annular, being pasted the part circularize by adhesive tape and do not participate in chemical reaction, still be aluminium foil, thereby area portions is an aluminium sesquioxide and peripherally be the foil material of aluminium in the middle of forming.The aluminium toughness of periphery is better, and the retained part in the time of can installing as foil material in use just can not destroy more crisp aluminium sesquioxide easily.
Claims (6)
1, the preparation method who has the aluminium sesquioxide ceramic foil materials that penetrates nanoporous, it is characterized in that comprising the steps and processing condition: at first the surface with aluminium foil and electro-conductive material fits, aluminium foil is kept between aluminium foil and the electro-conductive material and is conducted electricity with after the surface of electro-conductive material contacts; The electro-conductive material that will be fitted with aluminium foil again places electrochemical anodic oxidation solution to carry out oxidizing reaction as anode, thereby aluminium foil is transformed into aluminium sesquioxide, and form the micropore penetrate at thickness direction, with aluminium sesquioxide ceramic foil after separating from the electro-conductive material surface, then obtain to have the simple aluminium sesquioxide ceramic foil materials that evenly penetrates micropore.
2, the preparation method with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous according to claim 1 is characterized in that: the method that the surface of aluminium foil and electro-conductive material is fitted is for to be fitted in aluminium foil on the metal plate with conductive resin.
3, the preparation method with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous according to claim 1 is characterized in that: the method that the surface of aluminium foil and electro-conductive material is fitted is for overlaying on the cylindrical member aluminum foil coil is wrapped.
4, according to claim 1 or the 3 described methods that the surface of aluminium foil and electro-conductive material is fitted, it is characterized in that: when aluminum foil coil is wrapped when overlaying on nonconducting cylindrical member, coats the outer field aluminium foil that forms and the aluminium foil of internal layer and contact with each other.
5, according to the described preparation method of claim 1 with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous, it is characterized in that: described anode is placed electrochemical anodic oxidation solution, electrochemical anodic oxidation solution only contacts with the one side of aluminium foil, and electrochemical anodization reaction is only carried out from the outside surface of aluminium foil.
6, according to the described preparation method of claim 1 with the aluminium sesquioxide ceramic foil materials that penetrates nanoporous, it is characterized in that: on aluminium foil, circularize with the adhesive tape subsides, in the electrochemical anodic oxidation process, pasted the part that circularizes by adhesive tape and do not participate in chemical reaction, still be aluminium foil, the middle area portions of aluminium foil is converted to aluminium sesquioxide, thereby area portions is an aluminium sesquioxide and periphery is the foil material of aluminium in the middle of forming.