CN1640834A - Colour glass brown colouring pigment and its preparing process - Google Patents
Colour glass brown colouring pigment and its preparing process Download PDFInfo
- Publication number
- CN1640834A CN1640834A CN 200410023538 CN200410023538A CN1640834A CN 1640834 A CN1640834 A CN 1640834A CN 200410023538 CN200410023538 CN 200410023538 CN 200410023538 A CN200410023538 A CN 200410023538A CN 1640834 A CN1640834 A CN 1640834A
- Authority
- CN
- China
- Prior art keywords
- preparation
- pigment
- fusing assistant
- colorant
- crucible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is colorant for color glass and its preparation process. The granular brown colorant for color glass is prepared with Pb and B as basic components, Ni, Cd and Fe as basic color components and added Zn and Li as added color components, and through the technological process including compounding flux, preparing glaze melting powder, compounding pigment, preparing colorant and other steps. The new type of colorant has stable quality, good use effect and low production cost.
Description
Technical field
The present invention relates to a kind of glass coloring immunomodulator compounds and preparation method.
Background technology
Late 1960s, coloured glass begins to occur abroad, China began one's study the seventies, originally be in the road, to add Powdered pigment, dye melts is after stirring action, make itself and parent glass be mixed into the material of homogeneous, through the homogenizing postforming, yet this coloured glass is had to limited popularization.The first, when in glass metal, adding tinting material, can produce many difficulties, the second, glass metal is carried out second-heating detrimentally affect, and subject matter is reboil bubble to occur.U.S.'s import particulate state tinting material is used in the back, and this tinting material external product generally adopts chromium painted, though improvement is arranged, but still have unstable product quality, defectives such as look road, bubble, color lump very easily appear, and the product import, cost an arm and a leg, be badly in need of substitute products.
Summary of the invention
Cost an arm and a leg in order to overcome prior art, unstable product quality, effect is undesirable, defectives such as look road, bubble, color lump very easily occur, the invention provides a kind of new coloured glass tinting material and production technique.
New coloured glass brown colouring additive provided by the present invention adopts plumbous boron prescription, and nickel, cadmium, iron are painted, and add zinc, lithium composition in prescription, and its chemical ingredients is as follows: SiO
225-30%; AI
2O
33-6%; PbO35-40%; B
2O
35-8%; R
2O10-20%; Ni
2O3-7%; CdS2-4%; ZnO10-12%; Se1-3%; Fe
2O
30.5-1%.
Above-mentioned compound can prepare by following method.
(a) preparation of fusing assistant: the fusing assistant proportioning raw materials is SiO
230-35%; AI
2O
36-10%; CaO0.5-2%; MgO0.2-1%; PbO45-50%; B2O
34-8%; K
2O+Na
2O10-15%.
(b) preparation of melted glaze powder: fusing assistant is heated in crucible 1100-1200 ℃ by above-mentioned chemical constitution batching back and is founded, soak 40-60min, and through shrend, ball milling, drying, sieving obtains melted glaze powder.
(c) preparation of pigment, it is toner that bronzing agent adopts nickel, cadmium, iron, its composition of raw materials: Ni
2O20-30%; CdS8-12%; Fe
2O
31-2%; ZnO20-30%; Li
2CO
316-20%; Se2-4%; B
2O
36-10%.Borax is earlier soluble in water, and powder adds behind all the other raw material blendings, mixes oven dry thoroughly, and ball milling sieves, and obtains pigment
(d) preparation of tinting material: fusing assistant and pigment by fusion in crucible after 2: 1 mixed, are injected the cold water hardening crack then, and dry back fragmentation is sieved, the brown particle agent.
Embodiment
The invention will be further described below in conjunction with embodiment
The preparation of the coloured glass brown colouring additive of indication of the present invention realizes by following processing method.
One, the preparation of fusing assistant
In order to adapt to the processing temperature of expecting the road and the chemical constitution and the chemical property of glass basestocks.Reduce PbO, B
2O
3Deng the volatile quantity of raw material, fusing assistant is selected following raw materials according proportioning: SiO for use
230-35%; AI
2O
36-10%; CaO0.5-2%; MgO0.2-1%; PbO45-50%; B2O
34-8%; K
2O+Na
2O10-15%.
Two, the preparation of melted glaze powder
Fusing assistant is formed the batching back by its said ratio and found into vitreum in crucible, and glass melting temperature is about 1180 ℃, and top temperature keeps 50min, pours into then and carries out shrend in the water, the molten glaze ball milling after the shrend 28 hours.Sieve on the 80th is crossed in dry back, obtains powdered frit.
Three, the preparation of pigment
It is toner that brown colouring additive adopts nickel, cadmium, iron, its pigment raw material proportioning: Ni
2O20-30%; CdS8-12%; Fe
2O
31-2%; ZnO20-30%; Li
2CO
316-20%; Se2-4%; B
2O
36-10%.The raw materials used chemical pure raw material that all adopts of pigment requires steady quality, and borax is earlier soluble in water, and powder behind all the other raw material blendings is added, mixes thoroughly oven dry, and ball milling was crossed 280 mesh sieves about 25 hours, obtained pigment.
Four, the preparation of tinting material
Fusing assistant and pigment by fusion in crucible after 2: 1 mixed, are injected the cold water hardening crack then, broken 4 orders of crossing in dry back, 10 mesh sieves, intermediate particle is the particulate state brown colouring additive, its main chemical compositions: SiO
225-30%; AI
2O
33-6%; PbO35-40%; B
2O
35-8%; R
2O10-20%; Ni
2O3-7%; CdS2-4%; ZnO10-12%; Se1-3%; Fe
2O
30.5-1%.
Claims (1)
1, a kind of coloured glass brown colouring additive and preparation technology is characterized in that: adopt plumbous boron prescription, nickel, cadmium, iron are painted, and add zinc, lithium composition in prescription, and its chemical ingredients is as follows: SiO
225-30%; AI
2O
33-6%; PbO35-40%; B
2O
35-8%; R
2O10-20%; Ni
2O3-7%; CdS2-4%; ZnO10-12%; Se1-3%; Fe
2O
30.5-1%.
Above-mentioned compound can prepare by following method:
(a) preparation of fusing assistant: the fusing assistant proportioning raw materials is: SiO
230-35%; AI
2O
36-10%; CaO0.5-2%; MgO0.2-1%; PbO45-50%; B
2O
34-8%; K
2O+Na
2O10-15%.
(b) preparation of melted glaze powder: fusing assistant is heated in crucible 1100-1200 ℃ by above-mentioned chemical constitution batching back and is founded, soak 40-60min, and through shrend, ball milling, drying, sieving obtains melted glaze powder.
(c) preparation of pigment, it is toner that bronzing agent adopts nickel, cadmium, iron, its composition of raw materials: Ni
2O20-30%; CdS8-12%; Fe
2O
31-2%; ZnO20-30%; Li
2CO
316-20%; Se2-4%; B
2O
36-10%, borax is earlier soluble in water, and powder adds behind all the other raw material blendings, mixes oven dry thoroughly, and ball milling sieves, and obtains pigment.
(d) preparation of tinting material: fusing assistant and pigment by fusion in crucible after 2: 1 mixed, are injected the cold water hardening crack then, and dry back fragmentation is sieved, the brown particle agent.