CN1640831A - Colour hollow glass brick production process - Google Patents
Colour hollow glass brick production process Download PDFInfo
- Publication number
- CN1640831A CN1640831A CN 200410023536 CN200410023536A CN1640831A CN 1640831 A CN1640831 A CN 1640831A CN 200410023536 CN200410023536 CN 200410023536 CN 200410023536 A CN200410023536 A CN 200410023536A CN 1640831 A CN1640831 A CN 1640831A
- Authority
- CN
- China
- Prior art keywords
- stirring
- area
- temperature
- brick
- hollow glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The color hollow glass brick producing process is completed in an improved production apparatus with material channel coloring system separated into five areas with individual temperature regulators, including color material melting area, stirring area, cooling area, temperature regulating area and material basin. The melting area has color material throwing unit, and the stirring area has five separate detachable propeller stirrers. The production process has raised temperature of the work part and the different areas of the coloring system and regulated flame atmosphere for obtaining high quality color hollow glass brick product.
Description
Technical field
The present invention relates to the production technique of a kind of glass and colorant combination.
Background technology
Glass hollow block is heat insulation with it, sound insulation, anti-pressure and abrasion-proof,, printing opacity and not having an X-rayed, especially coloured glass tile, it decorates the favor that luxurious, elegant advantage is subjected to people at present day by day.Current coloured glass tile is produced coloring process three kinds of methods, and A, tank furnace are painted.B, the material road painted.C, cold process spray colouration.Tank furnace is painted to form a large amount of intermediate color glass when changing color, cause the colour changing time long, the production cost height.Though the cold process spray colouration can obtain chromatic colour, the cost height, color is fragile to come off with heat.The road is painted makes a kiln produce multiple decorative terra cotta for material, cost is low, the colour changing time is short, existing domestic its stirring area of German equipment that adopts is provided with four groups of stirring arms more, but the operative technique difficulty is big, exists to produce instability, and product is prone to color lump, bubble, reach not easy coloring, painted inhomogenous problem.
Summary of the invention
The painted production technology difficulty in existing stained glass hollow brick material road is big, production is unstable in order to overcome, be prone to color lump, bubble reaches not easy coloring, painted inhomogenous problem, the invention provides the painted production technique in a kind of stained glass hollow brick material road, this production technique has not only reduced technical difficulty, and has constant product quality, easy coloring, the advantage of uniform coloring.
The technical solution adopted for the present invention to solve the technical problems is: will expect coloring system transformation, whole material road is divided into the colorant fusing, stirring, cooling, temperature adjustment, five districts of feed basin, material road upper space is separated entirely, each district establishes thermosistor separately, at material top, melting area, the road material throwing device of filling in colors on a sketch, stirring area is provided with five groups can distinguish relative movement, and the helical stir that can dismantle is at any time starched.Every group of agitating unit revolves each other, revolves about each other in the agitating unit, and the stirring arm diameter suitably strengthens, and the eddy current that produces when relying on the rotation of paddle slurry stirs tinting material; Form the glass metal of color homogeneous.Its production technique:
1, selects materials: select suitable parent glass composition and material side.
2, operation system: the operate portions temperature is improved 10-40 ℃.Improve melting area, the stirring area of expecting the road, the temperature that reaches feed basin simultaneously, and beginning heats up gradually before azulejo is produced four days.
3, flame atmosphere: production pink colour brick generally adopts neutral atmosphere, and green brick adopts weak reducing atmosphere, and brown and blue brick adopts oxidizing atmosphere.
4, intensification is stirred, and throws colorant, presses brick
Employing the invention has the beneficial effects as follows (1) operation rapidly, the colorant input can be produced the color of qualified product (2) colored brick and can arbitrarily adjust according to demand after one hour, (3), change the line of production easily, stop to add that colorant is very fast can produce other color product, avoided a large amount of transition.(4), be suitable for many kinds, masstone, big small serial production.It is easy to have production technique, the advantage of constant product quality.
Embodiment
One, material road development
To expect coloring system transformation, its material road uses width 660mm, length 8640mm, and will expect to be divided into 5 districts, enter the material pipeline joint, 1 district is the colorant melting area, and 2 districts are stirring area, 3 districts are the cooling zone, 4 districts are the damping district, and 5 districts are feed basin, and material road upper space is separated entirely, each district all establishes independent thermosistor, is provided with the colorant throwing device on top, melting area.Stirring area is provided with the relative movement respectively of 10 stirring arms of 5 groups of agitators, the spiral stirring arm of diamond spar mullite that can dismantle at any time, the stirring arm diameter is increased to 170mm by 145mm, and the eddy current that produces when relying on the rotation of paddle slurry stirs tinting material, forms the glass metal of color even.
Two, production technique
1, selects suitable parent glass
Since adopt the material road painted, not tight to the glass ingredient requirement, so adopt former height to expect material side in vain.
2, operation system
Because adopt the material road painted, toner fusing difficulty is big, so in azulejo is produced, the temperature of operate portions is improved 10-40C °.Material pipeline joint temperature is reached more than 1270 ℃, improve material melting area, road, stirring area, feed basin simultaneously temperature 10-30 ℃.
3, flame atmosphere
For making decorative terra cotta better painted, material road flame atmosphere there is certain requirement, when producing the powder brick, generally adopt neutral atmosphere, when producing green brick, adopt weakly reducing atmosphere.When producing brown and blue brick, adopt oxidizing atmosphere.
Concrete operations technology:
(1) stirring arm is at least in production lifting baking in preceding 4 days, must the stirring arm surface cleaning is clean before the lifting, produce azulejo preceding 2 stirring arm all over the world, initial rotating speed is 4 rev/mins, produce and began to increase rotating speed in preceding 5 hours and once increase by 4 rev/mins, stablize half an hour, quicken one by one, reach 26 rev/mins of regulation rotating speeds.
(2), stirring velocity carries to the productive capacity 2 hours, the production azulejo that begins to feed intake, stirring arm is kept normally in the transient process
(3), transit time presses brick or blowing with normal engine speed, forbids big blowing.
Claims (1)
1, a kind of colorful hollow plate glass production technique, it is characterized in that: will expect coloring system transformation, whole material road is divided into colorant, fusing, stirring, cooling, temperature adjustment and 5 subregions of feed basin, material road upper space is separated entirely, each district all establishes independent thermosistor, be provided with the colorant throwing device on top, melting area, stirring area is provided with relative movement respectively, the spiral stirring arm that can dismantle at any time, the corresponding increasing of stirring arm size, the eddy current that produces during the rotation of stirring arm paddle slurry stirs tinting material, forms the glass metal of color homogeneous, its production technique:
(1) selects materials: select suitable parent glass composition and material side;
(2) operation system: the working portion temperature is improved 10-40 ℃, material pipeline joint temperature is reached more than 1270 ℃, improve the temperature of material melting area, road, stirring area, feed basin simultaneously;
(3) flame atmosphere: produce the powder brick and adopt neutrality, green brick adopts week reduction, and brown and blue brick adopts oxidizing atmosphere;
(4) heat up, stir, throw toner, stirring, pressure brick.