CN1640527A - Preparation method of filter membrane of palladium-based alloy/aperture gradient titanium-aluminum intermetallic compound homogeneous support body for hydrogen separation - Google Patents
Preparation method of filter membrane of palladium-based alloy/aperture gradient titanium-aluminum intermetallic compound homogeneous support body for hydrogen separation Download PDFInfo
- Publication number
- CN1640527A CN1640527A CN 200410003041 CN200410003041A CN1640527A CN 1640527 A CN1640527 A CN 1640527A CN 200410003041 CN200410003041 CN 200410003041 CN 200410003041 A CN200410003041 A CN 200410003041A CN 1640527 A CN1640527 A CN 1640527A
- Authority
- CN
- China
- Prior art keywords
- temperature
- palladium
- reaction
- intermetallic compound
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the production of semi-permeable membranes, a special preparation method of semi-permeable membranes for separation processes. The method comprises the steps of directly compounding Ti and Al element powder with Ti foil or Al foil to form a sheet-shaped or tubular blank through mould pressing or cold isostatic pressing, or firstly forming the Ti and Al element powder into a sheet-shaped or tubular blank through mould pressing or cold isostatic pressing, and then preparing the sheet-shaped or tubular blank into a composite formed blank through the surface melting and soaking of Al liquid; and then preparing a TiAl intermetallic compound pore-size gradient homogeneous support body by a two-stage vacuum sintering synthesis method of low-temperature pre-reaction and high-temperature short-time reaction, and then uniformly plating a layer of palladium-based alloy film with the thickness of 5-50 mu m on the surface of the TiAl intermetallic compound pore-size gradient homogeneous support body by adopting a chemical or physical vapor deposition (CVD or PVD) mode. The prepared membrane has good oxidation resistance, corrosion resistance and mechanical property, improves the permeation flux of the hydrogen separation membrane and prolongs the service life; the TiAl support body can also be directly used as a microfiltration membrane and a nanofiltration membrane with excellent performance. The preparation process of the invention does not need to add pore-forming agent, thus reducing energy consumption and almost having no pollution.
Description
Technical field:
The present invention relates to the production of semipermeable membrane, be used for the special preparation method of the pellicle of separating technology, preparation hydrogen separates the preparation method of the filter membrane of palladium-base alloy and bore diameter gradient TiAl intermetallic compound homogeneity supporter.
Background technology:
Membrane separation technique is the promotion by means of outside energy or chemical potential difference, gas or the liquid that two components or multicomponent are mixed separates, classification, purification and enrichment, most no phase change in the process, have efficient, energy-conservation, advantage such as technology is easy, small investment, pollution are little, be widely used in each production of national economy, research department and national defense construction field.In the gas film separation field, what be most widely used is the separation and the recovery of hydrogen.The inoranic membrane that is used for the hydrogen separation at present can be divided into non-support membrane and support membrane based on Metal Palladium, silver and alloy film thereof by structure.The introducing of supporter has realized the thinning of palladium film, has reduced the consumption of palladium, has reduced cost, has improved the saturating amount of film, and has kept characteristics such as the high temperature resistant and mechanical strength of metal film is big.
Hydrogen separation at present mainly contains with the supporter material therefor: ceramic body, and as aluminium oxide and glass, and metals such as copper, nickel and stainless steel.The preparation method who is adopted mainly contains: the solid particles sintering process prepares carrier and transition film; Sol-gel process prepares ultrafiltration, micro-filtration membrane; Split-phase method prepares glass-film; Adopt preparation microporous barriers such as chemical vapour deposition (CVD), electroless plating, these method complex process, cost is higher, and the filter membrane aperture is difficult to control; Exist the thermal coefficient of expansion of material and palladium film not match, the non-homogeneous activation of supporting body surface, the hydrogen embrittlement of metal, pottery crisp and be difficult for shortcoming such as weld assemblyization.
Summary of the invention:
The present invention is intended to improve antioxygenic property, corrosion resistance and the mechanical property of hydrogen separation membrane, improve the permeation flux of hydrogen separation membrane, prolong its service life, reduce cost, in a word, the present invention can prepare free from flaw, not come off, uniform fine and close composite membrane, and its preparation technology's simple flow, energy consumption is low, pollutes and reduces.
The present invention adopts following scheme:
In hydrogen separates with the palladium-base alloy film support, introduce the TiAl intermetallic compound of physical property and mechanical property excellence,, it is characterized in that with the method for preparation hydrogen separation with the filter membrane of palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter:
A. batch mixing:
With the Ti powder of particle diameter 200~10 μ m, the Al powder of particle diameter 200~5 μ m, according to 50~60at.%Ti, the composition proportion of 40~50at.%Al is evenly mixed.
B. combined shaping:
1. adopt the mode of die forming or cold isostatic compaction, with Ti, Al element powders directly and Ti paper tinsel or Al paper tinsel combined shaping, make sheet or tubulose base.Detailed process is: Ti paper tinsel or Al paper tinsel are placed the nose of punch of common moulding press, and directly contact with Ti, Al element mixed-powder, make laminar blank by die forming, mold pressing pressure is 50~600MPa; Perhaps adopt the cold isostatic compaction mode, pressure is 50~200MPa, and core bar becomes certain taper, and tapering is 0.1~2 °, Ti paper tinsel or Al paper tinsel are placed the core bar outside and closely contact with it, directly contact with Ti, Al element mixed-powder simultaneously, make the tubulose base by the cold isostatic compaction mode, the thickness of Ti paper tinsel or Al paper tinsel is 10~50 μ m, after the demoulding isostatic cool pressing base external diameter is carried out a small amount of machined, it is even to make external diameter, and internal diameter is tapering slightly, and thickness is the tubulose shaping base of 1~3mm.
2. or earlier be sheet or tubulose base with Ti, Al element powders die forming or cold isostatic compaction, make the combined shaping base by the mode of Al liquid surface infiltration then, Al liquid surface infiltration temperature is 670~900 ℃, and the infiltration time is 0.1~10min, and the infiltration layer thickness is 0.01~0.5mm.
C. reaction is synthetic:
By low temperature pre-reaction and high temperature, short time reaction two-stage vacuum-sintering synthetic method, preparation TiAl intermetallic compound bore diameter gradient homogeneity filtering membrane, when adopting vacuum non-pressure sintering, vacuum is 1 * 10
-1~1 * 10
-3Pa, the temperature in low temperature pre-reaction stage is 500~800 ℃, the time is 20~60 minutes; The temperature of the high temperature, short time stage of reaction is 1200~1400 ℃, and the time is 10~30 minutes; Cooling stage, the control cooling rate is 10~50 ℃/min.
Perhaps react synthetic by the low pressure high temperature insostatic pressing (HIP), pressure is 0.01~5MPa, and the temperature in low temperature pre-reaction stage is 500~800 ℃, and the time is 20~40 minutes; The temperature of the high temperature, short time stage of reaction is 1200~1300 ℃, and the time is 10~20 minutes; Cooling stage, the control cooling rate is 10~50 ℃/min.
Obtain bore diameter gradient TiAl intermetallic compound homogeneity supporter.
D.TiAl intermetallic compound homogeneity supporting body surface, adopt the method for chemistry or physical vapour deposition (PVD) (CVD or PVD), evenly plate one deck palladium base alloy films, thickness is 5~50 μ m, is combined into hydrogen and separates the filter membrane of using palladium-base alloy/bore diameter gradient TiAl intermetallic compound homogeneity supporter.
The present invention compared with prior art has the following advantages:
Since the TiAl intermetallic compound as the lightweight high-temperature structural material, has excellent mechanical property, acid-alkali-corrosive-resisting performance and antioxygenic property, its anti-oxidant limit can reach 800~950 ℃, adopt its preparation hydrogen to separate the palladium base alloy films supporter, improved antioxygenic property, corrosion resistance and the mechanical property of hydrogen separation membrane significantly, improved the permeation flux of hydrogen separation membrane, prolong service life, and reduced production cost.In addition, the thermal coefficient of expansion because of the TiAl intermetallic compound is 1.1~1.4 (10
-5/ K (0~600 ℃)), with the thermal coefficient of expansion 1.176 (10 of Metal Palladium
-5/ K) mate, help the compound of TiAl intermetallic compound bore diameter gradient homogeneous supporter and palladium base alloy films.
2. the present invention adopts the TiAl intermetallic compound to prepare the bore diameter gradient homogeneity filtering membrane, helps the pore-size distribution of controlling diaphragm.The pore-creating mechanism that adopts Ti, Al element powders to prepare filter membrane is that the inclined to one side diffusion of Al element causes the Kirkendall effect.Except powder metallurgical technique itself brings a certain amount of hole, the Kirkendall effect can cause the percent opening of TiAl alloy 20~30%, by the control process conditions: for example Ti, Al powder size proportioning and composition proportion, temperature that reaction is synthetic and temperature retention time etc. can access the accurately through hole of control of aperture.
3. Ti of the present invention, Al element powders combined shaping and reaction are synthetic, preparation hydrogen separates with palladium-base alloy TiAl intermetallic compound bore diameter gradient homogeneous supporter, owing to spreading institute partially, the Al element causes the Kirkendall effect, in supporter, can form the aperture by 1~10 μ m of non-compound end bore diameter gradient to 0.01~0.5 μ m of compound end, can control the bore diameter gradient situation of material by control complex condition and sintering process condition, therefore, TiAl intermetallic compound bore diameter gradient homogeneity filtering membrane, also can be directly as the micro-filtration membrane and the NF membrane of excellent performance.
4. Ti of the present invention, Al element powders combined shaping and reaction are synthetic, preparation hydrogen separates with in the palladium-base alloy TiAl intermetallic compound bore diameter gradient homogeneous supporter process, do not need to add pore creating material and can obtain 40~50% porosity, avoided removing the pore creating material link in the traditional handicraft, reduced energy consumption, and almost pollution-free.
5. the TiAl intermetallic compound of composition proportion of the present invention has high microscopic structure and grain size stabilized below 1300 ℃, has guaranteed the stability in use of TiAl inoranic membrane, and has effectively prevented the poisoning of palladium film; In addition, the weldability of TiAl intermetallic compound can also can solve the problem of pottery and glass difficult sealing under hot environment well.
The specific embodiment:
Embodiment 1
The employing granularity is that Ti powder and the granularity of 100~150 μ m is the Al powder of 50~100 μ m, carries out batch mixing by the composition proportion of Ti-46.5at.%Al; Die forming under the pressure of 200MPa subsequently places the Al paper tinsel nose of punch of common moulding press simultaneously, and making diameter is 50mm, the compound sheet base of thick 1~2mm; Adopt vacuum non-pressure sintering to react synthetic, vacuum degree control is 1 * 10
-2~1 * 10
-3Pa; Low temperature pre-reaction temperature is 600 ℃, and temperature retention time is 60min; The high temperature, short time reaction temperature is 1300 ℃, and temperature retention time is 20min; Cooling velocity was controlled at 40 ℃/min after reaction finished; Zhi Bei TiAl intermetallic compound bore diameter gradient homogeneous sheet supporter thus, porosity is 40~45%, percent opening is 30~35%, has good antioxygenic property and corrosion resistance simultaneously.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 10 μ m.
Embodiment 2
The employing granularity is that Ti powder and the granularity of 20~50 μ m is the Al powder of 50~100 μ m, carries out batch mixing by the composition proportion of Ti-48at.%Al; Adopt cold isostatic compaction tubulose base subsequently, the Al paper tinsel is close to the core bar outside, the core bar tapering is 0.5 °, and pressure is 150MPa; After a small amount of machined, making external diameter is 30mm, and internal diameter is 28~29mm, and height is the composite tube shaping base of 200mm; Sintering atmosphere is a vacuum, and vacuum degree control is 1 * 10
-2~1 * 10
-3Pa; Low temperature pre-reaction temperature is 620 ℃, and temperature retention time is 40min; The high temperature, short time reaction temperature is 1260 ℃, and temperature retention time is 30min; Cooling velocity was controlled at 30 ℃/min after reaction finished; Make the good TiAl intermetallic compound bore diameter gradient homogeneous tubular support of permeance property thus.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 15 μ m.
Embodiment 3
The employing granularity is that Ti powder and the granularity of 150~200 μ m is the Al powder of 20~50 μ m, carries out batch mixing by the composition proportion of Ti-48.5at.%Al; Die forming under the pressure of 200MPa, making diameter is 50mm, and the laminar blank of thick 1~2mm adopts the mode of Al liquid surface infiltration to make the combined shaping base subsequently, and the infiltration temperature is 700 ℃, and the infiltration time is 2min; Sintering adopts the low pressure high temperature insostatic pressing (HIP), and atmosphere Ar gas, pressure are 0.1MPa, and low temperature pre-reaction temperature is 620 ℃, and temperature retention time is 40min; The high temperature, short time reaction temperature is 1300 ℃, and temperature retention time is 10min.Cooling velocity was controlled at 20 ℃/min after reaction finished; Zhi Bei TiAl intermetallic compound bore diameter gradient homogeneous sheet supporter thus, porosity is 35~40%, percent opening is 25~35%, has good antioxygenic property and corrosion resistance simultaneously.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 25 μ m.
Embodiment 4
The employing granularity is that Ti powder and the granularity of 10~40 μ m is the Al powder of 10~40 μ m, carries out batch mixing by the composition proportion of Ti-47at.%Al; Adopt cold isostatic compaction tubulose base, the core bar tapering is 1 °, and pressure is 150MPa; After a small amount of machined, making external diameter is 40mm, and internal diameter is 37.5~38.5mm, and height is the tubulose shaping base of 220mm; Adopt the mode that tubulose base external diameter surface is carried out Al liquid infiltration to make the combined shaping base subsequently, the rotary speed of tubulose base is 0.25rpm, and the infiltration temperature is 720 ℃, and the infiltration time is 4min; Sintering atmosphere is a vacuum, and vacuum degree control is 1 * 10
-2~1 * 10
-3Pa; Low temperature pre-reaction temperature is 630 ℃, and temperature retention time is 30min; The high temperature, short time reaction temperature is 1300 ℃, and temperature retention time is 15min; Cooling velocity was controlled at 30 ℃/min after reaction finished; Make the good TiAl intermetallic compound bore diameter gradient homogeneous tubular support of permeance property thus.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 20 μ m.
Claims (5)
1. hydrogen separates the preparation method with the filter membrane of palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter, in separating with the palladium-base alloy film support, introduces hydrogen the TiAl intermetallic compound of physical property and mechanical property excellence, method so that preparation hydrogen separates the filter membrane of using palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter is characterized in that:
A. batch mixing:
With the Ti powder of particle diameter 200~10 μ m, the Al powder of particle diameter 200~5 μ m, according to 50~60at.%Ti, the composition proportion of 40~50at.%Al is evenly mixed;
B. combined shaping:
1. adopt the mode of die forming or cold isostatic compaction, with Ti, Al element powders directly and Ti paper tinsel or Al paper tinsel combined shaping, make sheet or tubulose base, detailed process is: the nose of punch that Ti paper tinsel or Al paper tinsel is placed common moulding press, and directly contact with Ti, Al element mixed-powder, make laminar blank by die forming, mold pressing pressure is 50~600MPa; Perhaps adopt the cold isostatic compaction mode, pressure is 50~200MPa, and core bar becomes certain taper, and tapering is 0.1~2 °, Ti paper tinsel or Al paper tinsel are placed the core bar outside and closely contact with it, directly contact with Ti, Al element mixed-powder simultaneously, make the tubulose base by the cold isostatic compaction mode, the thickness of Ti paper tinsel or Al paper tinsel is 10~50 μ m, after the demoulding isostatic cool pressing base external diameter is carried out a small amount of machined, it is even to make external diameter, and internal diameter is tapering slightly, and thickness is the tubulose shaping base of 1~3mm;
2. or earlier be sheet or tubulose base with Ti, Al element powders die forming or cold isostatic compaction, make the combined shaping base by the mode of Al liquid surface infiltration then, Al liquid surface infiltration temperature is 670~900 ℃, and the infiltration time is 0.1~10min, and the infiltration layer thickness is 0.01~0.5mm.
C. reaction is synthetic:
By low temperature pre-reaction and high temperature, short time reaction two-stage vacuum-sintering synthetic method, preparation TiAl intermetallic compound bore diameter gradient homogeneity filtering membrane, when adopting vacuum non-pressure sintering, vacuum is 1 * 10
-1~1 * 10
-3Pa, the temperature in low temperature pre-reaction stage is 500~800 ℃, the time is 20~60 minutes; The temperature of the high temperature, short time stage of reaction is 1200~1400 ℃, and the time is 10~30 minutes; Cooling stage, the control cooling rate is 10~50 ℃/min.
Perhaps react synthetic by the low pressure high temperature insostatic pressing (HIP), pressure is 0.01~5MPa, and the temperature in low temperature pre-reaction stage is 500~800 ℃, and the time is 20~40 minutes; The temperature of the high temperature, short time stage of reaction is 1200~1300 ℃, and the time is 10~20 minutes; Cooling stage, the control cooling rate is 10~50 ℃/min.
Obtain bore diameter gradient TiAl intermetallic compound homogeneity supporter;
D.TiAl intermetallic compound homogeneity supporting body surface, adopt the method for chemistry or physical vapour deposition (PVD) (CVD or PVD), evenly plate one deck palladium base alloy films, thickness is 5~50 μ m, and being combined into the hydrogen separation is the filter membrane of compound homogeneity supporter with palladium-base alloy/bore diameter gradient TiAl metal.
2. hydrogen according to claim 1 separates the preparation method with the filter membrane of palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter, it is characterized in that:
The employing granularity is that Ti powder and the granularity of 100~150 μ m is the Al powder of 50~100 μ m, carries out batch mixing by the composition proportion of Ti-46.5at.%Al; Die forming under the pressure of 200MPa subsequently places the Al paper tinsel nose of punch of common moulding press simultaneously, and making diameter is 50mm, the compound sheet base of thick 1~2mm; Its sintering atmosphere is a vacuum, and vacuum degree control is 1 * 10
-2~1 * 10
-3Pa; Low temperature pre-reaction temperature is 600 ℃, and temperature retention time is 60min; The high temperature, short time reaction temperature is 1300 ℃, and temperature retention time is 20min; Cooling velocity was controlled at 40 ℃/min after reaction finished; Zhi Bei TiAl intermetallic compound bore diameter gradient homogeneous sheet supporter thus, porosity is 40~45%, percent opening is 30~35%, has good antioxygenic property and corrosion resistance simultaneously.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 10 μ m.
3. hydrogen according to claim 1 separates the preparation method with the filter membrane of palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter, it is characterized in that:
The employing granularity is that Ti powder and the granularity of 20~50 μ m is the Al powder of 50~100 μ m, carries out batch mixing by the composition proportion of Ti-48at.%Al; Adopt cold isostatic compaction tubulose base subsequently, the Al paper tinsel is close to the core bar outside, the core bar tapering is 0.5 °, and pressure is 150MPa; After a small amount of machined, making external diameter is 30mm, and internal diameter is 28~29mm, and height is the composite tube shaping base of 200mm; Sintering atmosphere is a vacuum, and vacuum degree control is 1 * 10
-2~1 * 10
-3Pa; Low temperature pre-reaction temperature is 620 ℃, and temperature retention time is 40min; The high temperature, short time reaction temperature is 1260 ℃, and temperature retention time is 30min; Cooling velocity was controlled at 30 ℃/min after reaction finished; Make the good TiAl intermetallic compound bore diameter gradient homogeneous tubular support of permeance property thus.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 15 μ m.
4. hydrogen according to claim 1 separates the preparation method with the filter membrane of palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter, it is characterized in that:
The employing granularity is that Ti powder and the granularity of 150~200 μ m is the Al powder of 20~50 μ m, carries out batch mixing by the composition proportion of Ti-48.5at.%Al; Die forming under the pressure of 200MPa, making diameter is 50mm, and the laminar blank of thick 1~2mm adopts the mode of Al liquid surface infiltration to make the combined shaping base subsequently, and the infiltration temperature is 700 ℃, and the infiltration time is 2min; Sintering adopts the low pressure high temperature insostatic pressing (HIP), and atmosphere Ar gas, pressure are 0.1MPa, and low temperature pre-reaction temperature is 620 ℃, and temperature retention time is 40min; The high temperature, short time reaction temperature is 1300 ℃, and temperature retention time is 10min.Cooling velocity was controlled at 20 ℃/min after reaction finished; Zhi Bei TiAl intermetallic compound bore diameter gradient homogeneous sheet supporter thus, porosity is 35~40%, percent opening is 25~35%, has good antioxygenic property and corrosion resistance simultaneously.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 25 μ m.
5. hydrogen according to claim 1 separates the preparation method with the filter membrane of palladium-base alloy/bore diameter gradient Intermatallic Ti-Al compound homogeneous supporter, it is characterized in that:
The employing granularity is that Ti powder and the granularity of 10~40 μ m is the Al powder of 10~40 μ m, carries out batch mixing by the composition proportion of Ti-47at.%Al; Adopt cold isostatic compaction tubulose base, the core bar tapering is 1 °, and pressure is 150MPa; After a small amount of machined, making external diameter is 40mm, and internal diameter is 37.5~38.5mm, and height is the tubulose shaping base of 220mm; Adopt the mode that tubulose base external diameter surface is carried out Al liquid infiltration to make the combined shaping base subsequently, the rotary speed of tubulose base is 0.25rpm, and the infiltration temperature is 720 ℃, and the infiltration time is 4min; Sintering atmosphere is a vacuum, and vacuum degree control is 1 * 10
-2~1 * 10
-3Pa; Low temperature pre-reaction temperature is 630 ℃, and temperature retention time is 30min; The high temperature, short time reaction temperature is 1300 ℃, and temperature retention time is 15min; Cooling velocity was controlled at 30 ℃/min after reaction finished; Make the good TiAl intermetallic compound bore diameter gradient homogeneous tubular support of permeance property thus.Subsequently, in prepared TiAl intermetallic compound supporting body surface, adopt the mode of physical vapor deposition (PVD), evenly plate one deck palladium base alloy films, thickness is 20 μ m.