CN1634781A - Method for producing goblet by using glass tube - Google Patents
Method for producing goblet by using glass tube Download PDFInfo
- Publication number
- CN1634781A CN1634781A CN 200310121639 CN200310121639A CN1634781A CN 1634781 A CN1634781 A CN 1634781A CN 200310121639 CN200310121639 CN 200310121639 CN 200310121639 A CN200310121639 A CN 200310121639A CN 1634781 A CN1634781 A CN 1634781A
- Authority
- CN
- China
- Prior art keywords
- cup
- glass
- glass tubing
- neck
- making
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a method for making goblet by using glass tube, which comprises the following steps: A. blanking procedure: cutting a glass tube into glass tube sections; B. cup neck making procedure: air blowing and warming up the cup neck gradually until the glass tube is softened, then pressing the cup neck die on the cup neck position to make the glass tube contract and distort towards the inside, separating the cup neck pressing die and going on with air blowing and warming up until the glass is melted to a column shape, then doing annealing treatment; C. cup bottom making procedure: air blowing and warming up the cup bottom to make the glass tube contract and distort towards the inside until it is melted and cut off, the cup bottom forms a flat bottom; D. cup mouth making procedure: polishing the blank cup mouth and warming it up to form a circle. The invention has the advantages of simple production process, convenient operation, high yield, etc.
Description
One, technical field
The present invention relates to a kind of making method of glass cylinder, particularly a kind of method of making goblet of Glass tubing.
Two, background technology
The goblet of Xiao Shouing has two kinds of making methods in the market, and a kind of is to blow on mould with glass metal to form, and with the goblet that this method is made, luminance brightness is poor, complete processing complexity, scrap rate height; Another kind is cup and cup neck sectional making, and then bond together, this method increases than aforesaid method yield rate, luminance brightness is poor, the complete processing complicated problems but exist equally, the finished product cup has obvious interface in addition, influence the attractive in appearance of glass cylinder, interface ruptures easily, shortens the work-ing life of cup.
Three, summary of the invention
Make the above-mentioned disadvantage that goblet exists for overcoming, problem to be solved by this invention just provides the method with Glass tubing making goblet that a kind of complete processing is simple, easy and simple to handle, yield rate is high, luminance brightness good, the cup neck does not have interface.The technical solution adopted for the present invention to solve the technical problems, it may further comprise the steps:
A, blanking operation: the glass pipe is cut into and the corresponding glass pipeline section of goblet;
B, cup neck production process: at first the glass pipeline section is positioned at special use and fires on the equipment, and the glass pipeline section is rotated, aim at then a cup neck position progressively blow heat softening to Glass tubing, cup neck pressing mold is pressed in a glass neck position, make the inside shrinkage strain of Glass tubing to pore diameter less than 1 centimetre, separate cup neck pressing mold continue to be blown and to be heated to glass melting, make Glass tubing molten, carry out anneal again for column;
C, cup end production process: aim at position, cup bottom blow heat softening to Glass tubing, the cup undercutting is cut and is embossed in cup bottom position, makes the inside shrinkage strain of Glass tubing, continues to blow to heat to glass melting and cut off Glass tubing, the cup end, be fused into flat, carries out anneal then;
D: cup mouth making procedure: blank cup mouth is polished the round mouth of heating.
To blank cup annealing slaking, inspection after construction warehouse-in.Perhaps the blank cup is carried out the applique baking, the slaking of annealing again, inspection after construction warehouse-in.
After adopting the present invention, original making method has been carried out thorough improvement, directly made, can produce as long as there is special use to fire equipment of Glass tubing, production technique is simple, and is easy to operate, the yield rate height, the cup neck does not have interface, and the cup luminance brightness is good, elegant in appearance, and industrial scale is changeable according to investment.
Four, description of drawings
Fig. 1 is a process flow sheet of the present invention.
Five, embodiment
Shown in Figure 1, make the specific embodiments of the method for goblet for the present invention is a kind of with Glass tubing, it may further comprise the steps:
A, blanking operation 1: the glass pipe is cut into and the corresponding glass pipeline section of goblet, and the size of cup depends on the size of Glass tubing;
B, cup neck production process 2: at first the glass pipeline section is positioned at special use and fires on the equipment, and make the rotation of glass pipeline section; Progressively blow and heat to 1000 ℃-1400 ℃ in an aligning cup neck position then, makes Glass tubing softening; Cup neck pressing mold is pressed in a glass neck position, make the inside shrinkage strain of Glass tubing to pore diameter less than 1 centimetre; Separate cup neck pressing mold continues to blow and heats to 1400 ℃ of-1600 ℃ of glass meltings, and making Glass tubing molten is solid post, and cup end nature is recessed to the cup neck; Carry out anneal again;
C, cup end production process 3: blow and heat to 1000 ℃-1400 ℃ in position, aligning cup bottom, make Glass tubing softening, the cup undercutting is cut and is embossed in position, cup bottom, make the inside shrinkage strain of Glass tubing, the continuation air blowing is heated to 1400 ℃ of-1600 ℃ of glass meltings and is cut off Glass tubing, the cup end, be fused into flat naturally, carries out anneal then;
D: cup mouth making procedure 4: blank cup mouth is polished the round mouth of heating.
To blank cup annealing slaking 5, inspection after construction 8 warehouse-ins.
To requiring the cup of applique, to carry out applique, baking 6 at the blank cup earlier, the slaking 7 of annealing again, inspection after construction 8 warehouse-ins.
Show through testing repeatedly, making method technological design advantages of simple of the present invention, easy to operate, a people just can produce, yield rate can be up to 95%, and the cup neck does not have interface, and good looking appearance is generous, the cup luminance brightness is good, and it is comfortable to be smooth to the touch, and industrial scale is changeable according to investment.
Claims (3)
1, a kind of method of making goblet with Glass tubing, it is characterized in that: it may further comprise the steps:
A, blanking operation: the glass pipe is cut into and the corresponding glass pipeline section of goblet;
B, cup neck production process: at first the glass pipeline section is positioned at special use and fires on the equipment, and the glass pipeline section is rotated, aim at then a cup neck position progressively blow heat softening to Glass tubing, cup neck pressing mold is pressed in a glass neck position, make the inside shrinkage strain of Glass tubing to pore diameter less than 1 centimetre, separate cup neck pressing mold continue to be blown and to be heated to glass melting, make Glass tubing molten, carry out anneal again for column;
C, cup end production process: aim at position, cup bottom blow heat softening to Glass tubing, the cup undercutting is cut and is embossed in cup bottom position, makes the inside shrinkage strain of Glass tubing, continues to blow to heat to glass melting and cut off Glass tubing, the cup end, be fused into flat, carries out anneal then;
D: cup mouth making procedure: blank cup mouth is polished the round mouth of heating.
2, a kind of method of making goblet with Glass tubing according to claim 1 is characterized in that: to blank cup annealing slaking, inspection after construction warehouse-in.
3, a kind of method of making goblet with Glass tubing according to claim 1 is characterized in that: the blank cup is carried out the applique baking, the slaking of annealing again, inspection after construction warehouse-in.