CN1632058A - Melamine cyanuric acid microcapsule inorganic frame retardant and its preparation method - Google Patents
Melamine cyanuric acid microcapsule inorganic frame retardant and its preparation method Download PDFInfo
- Publication number
- CN1632058A CN1632058A CN 200410040990 CN200410040990A CN1632058A CN 1632058 A CN1632058 A CN 1632058A CN 200410040990 CN200410040990 CN 200410040990 CN 200410040990 A CN200410040990 A CN 200410040990A CN 1632058 A CN1632058 A CN 1632058A
- Authority
- CN
- China
- Prior art keywords
- combustion inhibitor
- retardant
- inorganic combustion
- melamine cyanurate
- cyanuric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Disclosed are melamine and its preparing method and application, with the characteristics that add 10-300 portions of inorganic flaming retardant, 100-1000portions of water into reactor with agitator and thermometer, make them to be dispersion in 50-130deg.C, the add into 0-300portions of antiflaming synergistic agent, 50-100 portions of melamine and 50-200 portions of cyanuric acid (emulsion or cream of ), which are stirred for 5 minutes to 2 hours in 50-150deg.C, in the course, can add into 100-1000 portions of water, generate the emulsion or cream of cyanuric acid covering inorganic flaming retardant which are filtered, are centrifugal separated, dried and scattered to be 0.01-500um cyanuric acid covering inorganic flaming retardant.
Description
One, technical field
The present invention relates to a kind of melamine cyanurate microcapsule inorganic combustion inhibitor and preparation method thereof, belong to the fire retardant preparation field.
Two, background technology
Inorganic combustion inhibitors such as magnesium hydroxide, aluminium hydroxide, phosphoric acid salt, borate, molybdate are to develop environment friendly flame retardant kind rapidly at present, and its consumption accounts for 80% of fire retardant aggregate consumption.Inorganic combustion inhibitor has Halogen, nontoxic, low cigarette, advantage such as inexpensive, is widely used in the polymer materials preparation field.The fire retardant mechanism of different inorganic combustion inhibitors is different, and metal hydroxides class inorganic combustion inhibitor (magnesium hydroxide, aluminium hydroxide) mainly is to discharge combination water by pyrolytic decomposition, plays the cooling fire retardation; Phosphoric acid salt and borate family (as ammonium polyphosphate, zinc borate etc.) then mainly are to form barrier layer at material surface, and the anoxybiotic thermal insulation suppresses burning.
The main drawback of inorganic combustion inhibitor is the surface polarity height, easily moisture absorption conglomeration, interface compatibility is poor when using as polymer flame retardant and between the resin, addition big (generally more than 50wt%), can cause after the filling the mobile variation of polymer processing with the mechanical property deterioration, so surface modification is such Study of Flame Retardant emphasis always.The surface modification of inorganic combustion inhibitor generally adopts coupling agent or tensio-active agent to handle at present, and surface treatment agent commonly used has silane series, titanic acid ester series, hard ester acid and its esters.Can reduce the inorganic combustion inhibitor surface polarity to a certain extent by coupling agent or tensio-active agent processing, the interface binding power between enhancing and the resin matrix increases material mechanical performance, but materials processing flowability and flame retardant properties are not had improvement substantially.
Melamine cyanurate is the triazine ring molecular complex with big plane hydrogen bond network that trimeric cyanamide and cyanuric acid are formed by hydrogen bonded, is a kind of good nitrogen flame retardant and lubricant.Its outward appearance is the white crystals powder with soapy feeling, and is nontoxic, tasteless, is insoluble in water and general organic solvent.It is stable below 300 ℃, and 400 ℃ begin distillation and are decomposed into trimeric cyanamide and cyanuric acid simultaneously.Characteristics such as that melamine cyanurate has is fire-retardant, lubricated, delustring can be used for that plastics are fire-retardant, power lubrication, Coating Matting and makeup and field of printing and dyeing.Melamine cyanurate has the advantage of nontoxic, low cigarette as fire retardant, its preparation is a raw material with trimeric cyanamide and cyanuric acid generally, water is dispersion medium, under 100-120 ℃ of temperature condition, react and make, have from thickening effect in the melamine cyanurate synthetic reaction process, reaction system viscosity continues to rise, and the material state changes no mobile paste into by the soup compound that can flow.
Three, summary of the invention
The objective of the invention is provides a kind of melamine cyanurate microcapsule inorganic combustion inhibitor and preparation method thereof at the deficiencies in the prior art.Be characterized in by realizing being scattered in inorganic combustion inhibitor particle or the coating of the inorganic combustion inhibitor of generation on the spot in the system in the melamine cyanurate building-up process from thickening effect, after resulting paste dehydrates, can be used as fire retardant after the pulverizing and use.
The present inventor finds that inorganic combustion inhibitor frictional coefficient after melamine cyanurate coats reduces, has good lubricity, and its flame-proofed polymer material can keep higher fluidity of molten; Can improve the interface compatibility of inorganic combustion inhibitor and polymer materials with melamine cyanurate as surface coating layer, improve material mechanical performance; Nitrogen flame retardant melamine cyanurate and inorganic combustion inhibitor have complementarity on fire retardant mechanism, give full play to its synergistic effect, and its composite flame retardant system has better flame retardant effect to some polymer materials than single inorganic combustion inhibitor.
The objective of the invention is to realize that by following technical measures wherein said raw material umber is parts by weight except that specified otherwise.
The recipe ingredient of melamine cyanurate microcapsule inorganic combustion inhibitor starting raw material is:
Powders 50-200 weight part
Trimeric cyanamide 50-100 weight part
Cyanuric acid 50-200 weight part
Water 200-2000 weight part
Retardant synergist 1-100 weight part
Wherein inorganic combustion inhibitor is at least a in magnesium hydroxide, aluminium hydroxide, phosphoric acid salt, poly-phosphate, borate, the molybdate.
Retardant synergist is at least a in phosphoric acid, ammonium sulfate, phospho-wolframic acid, silicotungstic acid, Dyhard RU 100, tetramethylolmethane, the dipentaerythrityl ether.
The preparation method of melamine cyanurate coated inorganic fire retardant:
Powders 10～300 weight parts, water 100-1000 weight part are added in the reactor of belt stirrer, thermometer, make it to disperse in temperature 50-130 ℃, add retardant synergist 1-100 weight part, trimeric cyanamide 50-100 weight part and cyanuric acid 50-200 weight part successively, in temperature 50-150 ℃ stirring reaction 5 minutes-2 hours, water 100-1000 weight part be can add in the reaction process, white or light cream or thickness paste obtained; With above-mentioned milk sap or thickness paste after filtration or obtain the melamine cyanurate coated inorganic fire retardant of 0.01-500 μ m after the centrifugation, drying, pulverizing.
The present invention has following advantage:
(1) technology is simple, and is easy to operate.
(2) melamine cyanurate form big plane hydrogen bond network process from the effective coated inorganic fire retardant of thickening effect.
(3) the melamine cyanurate water-intake rate is extremely low, can prevent inorganic combustion inhibitor moisture absorption caking.
(4) melamine cyanurate has excellent lubricating properties, and its coated inorganic fire retardant can reduce latter's frictional coefficient greatly, improves the fluidity of molten of its flame-proofed polymer material, improves its processing characteristics.
(5) melamine cyanurate coated inorganic fire retardant is a kind of novel organic-inorganic composite flame retardants with " nucleocapsid " structure, has complementarity on fire retardant mechanism, gives full play to synergistic effect, can improve the flame retardant properties of single inorganic combustion inhibitor.
(6) melamine cyanurate coated inorganic fire retardant can improve inorganic combustion inhibitor and polymer materials consistency, helps improving the material over-all properties.
Four, embodiment
Below by embodiment the present invention is specifically described.Be necessary to be pointed out that at this following examples only are used for the present invention is further specified; can not be interpreted as limiting the scope of the invention, the person skilled in the art in this field can make some nonessential improvement and adjustment to the present invention according to the invention described above content.
Embodiment:
1. in reactor, retardant synergist Dyhard RU 100 1kg is dissolved in the 200kg water, add magnesium hydrate powder 50kg, stirring makes its homodisperse, again with trimeric cyanamide 50kg and cyanuric acid 50kg, add in the reactor, in 95 ℃ of stirring reactions of temperature 1 hour, the thickness paste that obtains, this paste after filtration, dry, the powder-product that makes average particle size 3 μ m after pulverizing.
2. in reactor, retardant synergist phospho-wolframic acid 30kg is dissolved in the 1000kg water, add ammonium polyphosphate powder 100kg, stirring makes its homodisperse, add trimeric cyanamide 75kg and cyanuric acid 75kg more successively, 110 ℃ of stirring reactions of temperature 30 minutes, obtain the thickness paste, add water 3kg and continue reaction 20 minutes, the gained emulsion makes the powder-product that average particle size is 10 μ m after centrifugation, drying, pulverizing.
3. in reactor, retardant synergist Dyhard RU 100 15kg and tetramethylolmethane 15kg are dissolved in the 1800kg water, add zinc borate power 200kg, stirring makes its homodisperse, the cyanuric acid that adds trimeric cyanamide 100kg and 105kg again, in 100 ℃ of stirring reactions of temperature 10 minutes, obtain white milk sap, this milk sap makes the powder-product that average particle size is 50 μ m after the spraying equipment spraying drying.
4. in reactor, add 400kg water, be warming up to 100 ℃, add 60 kilograms in aluminium hydroxide, stirring makes its homodisperse, add phosphatase 11 kg, silicotungstic acid 1kg, trimeric cyanamide 60kg and cyanuric acid 65kg again and in mixing tank, be pre-mixed, in the middle then immigration reactor, stirring reaction 2 hours, the thickness paste that obtains, this paste after filtration, dry, make the powder-product that average particle size is 150 μ m after pulverizing.
Claims (4)
1. melamine cyanurate microcapsule inorganic combustion inhibitor fire retardant is characterized in that the recipe ingredient of starting raw material is by weight:
Powders 50-200 part
Trimeric cyanamide 50-100 part
Cyanuric acid 50-200 part
Water 200-2000 part
Retardant synergist 1-100 part
Melamine cyanurate microcapsule inorganic combustion inhibitor wherein is characterized in that inorganic combustion inhibitor is at least a in magnesium hydroxide, aluminium hydroxide, phosphoric acid salt, poly-phosphate, borate, the molybdate.
2. as according to melamine salt based flame retardant microcapsule inorganic combustion inhibitor as described in the claim 1, it is characterized in that retardant synergist is at least a in phosphoric acid, ammonium sulfate, phospho-wolframic acid, silicotungstic acid, Dyhard RU 100, tetramethylolmethane, the dipentaerythrityl ether.
3. as preparation method, it is characterized in that according to melamine salt based flame retardant microcapsule inorganic combustion inhibitor as described in the claim 1 or 2:
(1) powders 10～300 weight parts, water 100-1000 weight part are added in the reactor of belt stirrer, thermometer, make it to disperse in temperature 50-130 ℃, add retardant synergist 1-100 weight part, trimeric cyanamide 50-100 weight part and cyanuric acid 50-200 weight part then, in temperature 50-150 ℃ stirring reaction 5 minutes-2 hours, water 100-1000 weight part be can add in the reaction process, white or light cream or thickness paste obtained.
(2) above-mentioned milk sap or thickness paste after filtration or after the centrifugation, drying, pulverizing, are obtained the melamine cyanurate coated inorganic fire retardant of 0.01-500 μ m.
4. as the purposes of melamine cyanurate microcapsule inorganic combustion inhibitor as described in claims 1 or 2, it is characterized in that this product can be used as flame retardant of polymer or anti-flaming dope additive.