CN1621463A - Composite fire-proof paint - Google Patents
Composite fire-proof paint Download PDFInfo
- Publication number
- CN1621463A CN1621463A CN 200310115803 CN200310115803A CN1621463A CN 1621463 A CN1621463 A CN 1621463A CN 200310115803 CN200310115803 CN 200310115803 CN 200310115803 A CN200310115803 A CN 200310115803A CN 1621463 A CN1621463 A CN 1621463A
- Authority
- CN
- China
- Prior art keywords
- agent
- formaldehyde resin
- coating
- account
- carbonized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is one kind of water soluble fireproof composite inorganic/organic polymer filming paint. The present invention has excellent fireproof performance, can bear the effect of flame, and has fireproof foamed layer with high heat isolating performance, high mechanical strength, less chap and falling out, good decoration property, low cost and other advantages.
Description
Technical field:
The present invention relates to a kind of NEW TYPE OF COMPOSITE frie retardant coating, belong to the composite coating of inorganic polymer and organic polymer film forming material.
Background technology:
At present, frie retardant coating has two big classes in the world: a class is the frie retardant coating of non-expansion type, though very strong fire-resistant and water resistance is arranged, thermal insulation is bad, and fire resistance is not high.Another kind of is intumescent coating, especially when meeting fire, can form the thermofin of honeycomb microbubble structure, heat-proof quality is good, this class coating normally with organic polymer as film forming material, this class coating excellent in heat insulating performance, fire resistance is good, but the foam insulation physical strength is low, easily drops, and causes fire resistance to reduce or inefficacy, cost is higher in addition, and is ornamental also not ideal enough.
Summary of the invention:
The objective of the invention is to overcome above-mentioned deficiency, a kind of NEW TYPE OF COMPOSITE frie retardant coating is provided.
The present invention is achieved in that by following component and forms:
Binding agent: urea-formaldehyde resin and terpolycyantoamino-formaldehyde resin are also compound with silicon sol.
Whipping agent: ammonium polyphosphate, monoammonium phosphate diammonium phosphate are also used.
Carbonized agent: starch, tetramethylolmethane.
Pigment or filler: titanium white silica flour, aluminium hydroxide aluminum oxide.
Subsidiary material: carbohydrate alcohols, urea water etc.
Its set of dispense is such as following: (by weight)
Urea-formaldehyde resin 35～75
Terpolycyantoamino-formaldehyde resin 5～35
Silicon sol 10～40
Ammonium polyphosphate 4～40
Monoammonium phosphate 4～40
Diammonium phosphate 4～40
Starch (carbonized agent) 20～25
Tetramethylolmethane (carbonized agent) 0～5
Titanium white 8～16
Silica flour 8～16
Aluminum oxide and aluminium hydroxide 4～8
Subsidiary material: sucrose, methyl alcohol, ethanol, propylene glycol, urea, water etc. about 30.
Coating machine intensity of the present invention is big, be difficult for the be full of cracks difficult drop-off at flame impingement repeatedly and the cold and hot thermofin that produces closely knit honeycomb microbubble structure that acted on repeatedly, the heat-proof quality excellence can be in 45 ℃ on weathering resistance, under 100% humidity and the carbon dioxide atmosphere effect, coating was perfect in 48 hours.Tackiness agent in the coating and can make finishing paint usefulness in addition, coating have the gloss of enamel and do not have the fragility of porcelain.This paint adhesion is strong, has moisture resistance, also has certain acid-fast alkali-proof because it is solvent or diluent with water, and construction is also convenient, safe comprehensive cost is low.This coating is mainly used in the timber wood-based plate, can be widely used in aspects such as the various warehouses of various building national defense construction, oil, electric power, subway boats and ships vehicle, the storage of historical relic's protection treasure.This coating is indoor timber structure fire prevention and the good coating of decorating.
Embodiment:
Binding agent: urea-formaldehyde resin and terpolycyantoamino-formaldehyde resin are also compound with silicon sol.
Whipping agent: ammonium polyphosphate, monoammonium phosphate diammonium phosphate are also used.
Carbonized agent: starch, tetramethylolmethane.
Pigment or filler: titanium white silica flour, aluminium hydroxide aluminum oxide.
Subsidiary material: carbohydrate alcohols, urea water etc.
Its set of dispense is such as following: (by weight)
Urea-formaldehyde resin 35～75
Terpolycyantoamino-formaldehyde resin 5～35
Silicon sol 10～40
Ammonium polyphosphate 4～40
Monoammonium phosphate 4～40
Diammonium phosphate 4～40
Starch (carbonized agent) 20～25
Tetramethylolmethane (carbonized agent) 0～5
Titanium white 8～16
Silica flour 8～16
Aluminum oxide and aluminium hydroxide 4～8
Subsidiary material: sucrose, methyl alcohol, ethanol, propylene glycol, urea, water etc. about 30.
Claims (2)
1, a kind of NEW TYPE OF COMPOSITE frie retardant coating, by tackiness agent: terpolycyantoamino-formaldehyde resin, carbonized agent: tetramethylolmethane, the expansion type ammonium phosphate salt, pigment and filler: titanium white, the oxide compound of aluminium and silicon and subsidiary material are formed, it is characterized in that with adding urea-formaldehyde resin again in the silicon sol compound tackiness agent, account for 35～75% of binder wt per-cent, add starch in the carbonized agent and account for carbonized agent 80～100%, with ammonium polyphosphate, monoammonium phosphate, diammonium phosphate and usefulness account for 12～40% of coating weight per-cent in the whipping agent;
2, NEW TYPE OF COMPOSITE frie retardant coating as claimed in claim 1, but it is characterized in that this tackiness agent is a finishing paint of being made making coatings by urea-formaldehyde resin melamine formaldehyde resin, silicon sol.