CN1609122A - New method of preparing silk protein powder - Google Patents
New method of preparing silk protein powder Download PDFInfo
- Publication number
- CN1609122A CN1609122A CN 200310101985 CN200310101985A CN1609122A CN 1609122 A CN1609122 A CN 1609122A CN 200310101985 CN200310101985 CN 200310101985 CN 200310101985 A CN200310101985 A CN 200310101985A CN 1609122 A CN1609122 A CN 1609122A
- Authority
- CN
- China
- Prior art keywords
- silk fibroin
- silk protein
- water
- powder
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is new method of preparing insoluble silk protein powder and relates to biological high molecular material and cosmetics. Silk protein powder is prepared through regulating the molar ratio of calcium chloride, water and ethanol, controlling the damage degree of the bipolar structure in silk protein, reaction at 60-100 deg.c, dialyzing the mixture or diluting with water to obtain silk protein precipitate, and washing, drying and grinding the silk protein precipitate to obtain the silk protein powder. Thus prepared silk protein powder is water insoluble and excellent in wetting property, has active groups enriched in the surface, and is suitable for use as medical diagnosis and inspection material, ceramic material, enzyme immobilizing material, medicine slowly releasing material, etc. The said method has short process, simple operation, convenient control and other advantages.
Description
Technical field
The present invention is the novel method that preparation has the silk fibroin powder of good wettability, relates to biomaterial.
Background technology
Silk fibroin has excellent biocompatibility and favorable mechanical and physics, chemical property as natural biological albumen, is subjected to people's extensive concern.Wherein because fibroin to the human body nontoxicity, is easy to absorb, and surface active groups is more, is with a wide range of applications in technical field of biological material.And silk fibroin powder is in isolation technique, the medical diagnosis check, and pottery, the enzyme immobilization material, drug sustained release system and makeup aspect can widespread uses.
The preparation method of existing silk fibroin powder is a kind of to be that fibroin is dissolved in CaCl
2In/water/ethanol (mol ratio 1: 8: 2) ternary solution or other dense saline solution, prepare the aqueous solution of fibroin, prepare insoluble silk fibroin powder with spray-dired method then through dialysis or chromatographic separation.Another kind method reduces molecular weight with fibroin with strong acid, highly basic or enzymic hydrolysis, prepares low-molecular-weight silk fibroin powder.Can also prepare low-molecular-weight silk fibroin powder by the method for High Temperature High Pressure.Yet all there is the process complexity in prior preparation method, needs to use chemical reagent numerous, or has the highly energy-consuming reaction, and it is too high to be not suitable for large-scale production and cost.These have greatly limited the application of silk fibroin powder.
The present invention addresses the above problem the simple method that adopts, utilize solvent that the hydrogen bond action between silk fibroin molecular is partly decomposed, remove wherein inorganic salt and organic solvent through dialysis, precipitation obtains the fibroin solid, and is dry, can obtain water-fast silk fibroin powder after grinding.This method is simple to operate, and power consumption is few, the least possible use chemical reagent, and mild condition is easy to control, has great practical value.
Silk fibroin generally has two kinds of crystal forms, and wherein alpha-helix is soluble in water, and beta sheet is water-fast crystal form.Silk fibroin mainly exists with beta sheet under the state of nature, and water insoluble and other common solvent can be dissolved in CaCl by destroying the original beta sheet structure of silk fibroin
2In/water/ethanol (mol ratio 1: 8: 2) ternary solution or other dense saline solution.Ternary solution can be penetrated into fibroin inside, at first destroys the hydrogen bond in indefinite form district in the fibroin, destroys the beta sheet structure then, thereby silk fibroin is dissolved in the solution.Remove by dialysis again after the dissolving and desalt and ethanol, just obtain the pure water solution of silk fibroin.Because the beta sheet structure of silk fibroin is destroyed substantially, so silk fibroin can metastablely be present in the aqueous solution, use spraying drying at last, the silk fibroin solution drying is prepared powder or microballoon.Fibroin is subjected to the effect of power and is orientated in spray process, and therefore the powder of preparing is water-fast, and primary structure is the beta sheet conformation.Perhaps utilize concentrated acid or enzyme that silk fibroin is partly degraded, for preparing is generally water-soluble powder.And high-temperature high-voltage reaction is especially with fibroin structure completely destroy.
All aforesaid methods all are behind the original structure completely destroy with silk fibroin, prepare needed powder by various effects again.The reaction relative complex.Studies show that dense saline solution at first enters into the indefinite form district of fibroin when destroying the hydrogen bond structure of silk fibroin, just destroy the beta sheet crystalline texture of fibroin then.If so by rationally adjusting the proportioning of ternary solution, make the indefinite form district that solution can only the completely destroy fibroin, and can not the original beta sheet crystallizing field of completely destroy fibroin, dialysis treatment passed through, obtain the precipitation of silk fibroin, dry back grinding can obtain the water-fast powder of silk fibroin.
The objective of the invention is to simplify the preparation flow of silk fibroin powder, reduce energy expenditure, on the basis of not destroying the silk fibroin primary structure substantially, prepare silk fibroin powder with good wettability.
Summary of the invention
After the present invention is achieved in that silk come unstuck,,, obtain the liquid of approximate silk fibroin solution at a certain temperature with the hydrogen bond partial destruction of silk fibroin by regulating the proportioning of ternary solution.This solution is put into the dialysis band, in dialysis procedure, because the silk fibroin hydrogen bond is a partial destruction, also keep original beta sheet structure, silk fibroin precipitates from the aqueous solution separates out.Post precipitation appears in dialysis, puts into the loft drier drying after the fibroin precipitation is cleaned, and dried fibroin obtains silk fibroin powder after grinding.
Specific implementation of the present invention is: with silk at 0.5% Na
2CO
3100 ℃ are boiled 60min in the solution, repeatedly wash after drying with the sericin of removing the silk outside and the silk fibroin that will boil with distilled water, obtain pure silk fibroin.A certain amount of silk fibroin is joined CaCl
2In/water/ethanol ternary solution, the mol ratio of calcium chloride and water is 1: 8.1-1: between 15, calcium chloride and alcoholic acid mol ratio are 1: 2.1-1: between 5.Acquisition is similar to the mixture of solution, this mixture is dialysed in water to remove calcium chloride and ethanol with the dialysis band, silk fibroin is precipitated out in dialysis procedure, post precipitation appears in dialysis, it is dry in loft drier that silk fibroin is cleaned the back, and the exsiccant silk fibroin promptly obtains the silk fibroin powder after grinding.Dried silk fibroin can also utilize equipment such as ball mill further to grind, and can obtain the silk fibroin powder of diameter between 5nm-100nm, needs nano level powder art such as makeup medium thereby can be applied to.
The secondary structure that the present invention comes the partial destruction fibroin by the proportioning of regulating ternary solution first obtains the powder of needs, rather than the secondary structure completely destroy is passed through again the beta sheet crystal of mechanical effect recuperation section.Experiment flow is simplified greatly, prepares simpler.
The present invention prepares water-fast silk fibroin powder by the proportioning that changes ternary solution, mild condition, and flow process is simple, and gordian technique is:
1. rationally regulate calcium chloride, water and alcoholic acid molar ratio, calcium chloride, water and alcoholic acid molar ratio are controlled between 1: 8.1～1: 15, calcium chloride and alcoholic acid mol ratio are controlled at 1: 2.1-1: between 5, control obtains sizeable powder to the destructiveness of silk fibroin secondary structure.
2. the control ternary solvent is reacted in 60～100 ℃ of scopes, obtains being similar to the mixture of gel and solution intermediateness.
3. can obtain the silk fibroin precipitation with dialysis of dialysis band or distilled water diluting.
4. silk fibroin precipitates cleaning-drying again, grinds back acquisition silk fibroin powder.
For the preparation of silk fibroin powder, because distinctive secondary structure of silk fibroin and good intensity and toughness can't directly be handled the fibroin that comes unstuck by mechanical effect and obtain powder.Consider that the silk fibroin that nature exists is mainly the beta sheet structure, and contain indefinite form district with certain orientation, when ternary solution enters into silk fibroin inside, at first be to destroy the relatively poor indefinite form district of regularity, just destroy the hydrogen bond of beta sheet crystallizing field then, so by regulating the proportioning of ternary solution, can control the destructiveness of solution, obtain desired structure to the fibroin secondary structure.Proportioning to ternary solution, suitable ratio is that the mol ratio of calcium chloride and water is between 1: 8.1 to 1: 15, calcium chloride and alcoholic acid mol ratio are between 1: 2.1 to 1: 5, and the change of proportioning can determine the destructiveness to secondary structure, thereby further determine the diameter of silk fibroin powder.For operative temperature, temperature with original dissolving fibroin is a standard, is set between 60-100 ℃, and fibroin adds the back and interacts with solution, solution becomes similar intermediate structure for gel and solution, obtains the silk fibroin precipitation in three days with this mixture dilute with water or with the dialysis of dialysis band.Silk fibroin is deposited in the loft drier after the drying, and grinding can obtain the silk fibroin powder.
The silk fibroin powder infrared spectra of preparing, X-ray diffraction, and surperficial Electronic Speculum is measured the structure and the size of powder.The X-ray diffraction result shows that the main crystal form in the fibroin is a beta sheet, and infrared result shows that powder is β crystallization and undefined structure coexistence.This explanation solvent does not have completely destroy beta sheet district, thereby make the silk fibroin powder can be water insoluble, again because solution has destroyed the hydrogen bond in indefinite form district in the silk fibroin, at aqueous phase, for reducing the surface active energy, the indefinite form district all trends towards the surface of powder, thereby make silk fibroin powder have good wettability and biochemical reaction, this is applied to medical diagnosis check, pottery for silk fibroin powder, the enzyme immobilization material, drug sustained release system etc. provide favourable condition.
Advantage of the present invention is: do not need fibroin secondary structure completely destroy, do not need mechanical device to handle substantially, flow process is simple, is easy to control, and the preparation powder is even, has reduced the use of solvent as much as possible.The present invention provides further convenience to the silk fibroin powder in the use of association area, has great practical value.
Further specify the present invention with embodiment
Embodiment 1:
With silk at 0.5% Na
2CO
3100 ℃ are boiled 60min in the solution, carefully wash after drying with the sericin of removing the silk outside and the silk fibroin that will boil with distilled water, obtain pure silk fibroin.CaCl with 10 milliliters of 1 gram silk fibroin addings
2In/water/ethanol ternary solution, wherein the mol ratio of calcium chloride and water is 1: 8.1-1: 12, calcium chloride and alcoholic acid mol ratio are 1: 2.1-1: 3, mixture heating up is arrived 60-100 ℃, acquisition is similar to the mixture of gel and solution intermediateness, mixture with dialysis band dialysis three days, with grinding behind the silk fibroin cleaning-drying that is settled out in the dialysis procedure, is prepared the silk fibroin powder.
Embodiment 2
With silk at 0.5% Na
2CO
3100 ℃ are boiled 60min in the solution, carefully wash after drying with the sericin of removing the silk outside and the silk fibroin that will boil with distilled water, obtain pure silk fibroin.CaCl with 10 milliliters of 1 gram silk fibroin addings
2In/water/ethanol ternary solution, wherein the mol ratio of calcium chloride and water is 1: 9-1: 15, calcium chloride and alcoholic acid mol ratio are 1: 2.1-1: 5, mixture heating up is arrived 60-100 ℃, acquisition is similar to the mixture of gel and solution intermediateness, mixture with dialysis band dialysis three days, with grinding behind the silk fibroin cleaning-drying that is settled out in the dialysis procedure, is prepared the silk fibroin powder.
Embodiment 3
With silk at 0.5% Na
2CO
3100 ℃ are boiled 60min in the solution, carefully wash after drying with the sericin of removing the silk outside and the silk fibroin that will boil with distilled water, obtain pure silk fibroin.CaCl with 10 milliliters of 1 gram silk fibroin addings
2In/water/ethanol ternary solution, wherein the mol ratio of calcium chloride and water is 1: 8.1-1: 12, calcium chloride and alcoholic acid mol ratio are 1: 2.1-1: 3, mixture heating up is arrived 60-100 ℃, acquisition is similar to the mixture of gel and solution intermediateness, with the mixture dilute with water,, prepare the silk fibroin powder with grinding behind the silk fibroin cleaning-drying that is settled out in the dilution.
Embodiment 4
With silk at 0.5% Na
2CO
3100 ℃ are boiled 60min in the solution, carefully wash after drying with the sericin of removing the silk outside and the silk fibroin that will boil with distilled water, obtain pure silk fibroin.CaCl with 10 milliliters of 1 gram silk fibroin addings
2In/water/ethanol ternary solution, wherein the mol ratio of calcium chloride and water is 1: 9-1: 15, calcium chloride and alcoholic acid mol ratio are 1: 2.1-1: 5, mixture heating up is arrived 60-100 ℃, acquisition is similar to the mixture of gel and solution intermediateness, mixture with dialysis band dialysis three days, with grinding behind the silk fibroin cleaning-drying that is settled out in the dialysis procedure, is prepared the silk fibroin powder.
Claims (1)
1. the preparation method of an insoluble silk fibroin powder, it is characterized in that: regulate calcium chloride in the ternary solvent, water and alcoholic acid molar ratio, the mol ratio of calcium chloride and water is controlled at (1: 8.1-1: 15), calcium chloride and alcoholic acid mol ratio are controlled at (1: 2.1-1: 5), by the destructiveness of control to the silk fibroin secondary structure, obtain being similar to the mixture of gel and solution intermediateness, can obtain the silk fibroin precipitation with dialysis of dialysis band or distilled water diluting, cleaning-drying is after grinding obtains silk fibroin powder.