CN1600468A - Method and equipment for producing directional vertical taper pipe in motorcycle through cold extrusion - Google Patents
Method and equipment for producing directional vertical taper pipe in motorcycle through cold extrusion Download PDFInfo
- Publication number
- CN1600468A CN1600468A CN 200410040546 CN200410040546A CN1600468A CN 1600468 A CN1600468 A CN 1600468A CN 200410040546 CN200410040546 CN 200410040546 CN 200410040546 A CN200410040546 A CN 200410040546A CN 1600468 A CN1600468 A CN 1600468A
- Authority
- CN
- China
- Prior art keywords
- steel pipe
- conical riser
- demoulding
- riser
- shaping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A cold extrusion technology for machining the vertical conic stearing tube of motorcycle includes reducing hoop, hole enlargnig and plumply shaping to obtain the target product with conic internal hole, cylindrical upper segment, and stepped cylindrical lower segment. The extrusion apparatus for reducing hoop and enlarging hole is composed of lower and upper demoulding buffer cylinders and shaping cylinder. The extrusion apparatus for plumply shaping consists of demoulding cylinder and extruding cylinder.
Description
(1), affiliated technical field
The present invention relates to a kind of production method and device thereof of conical riser, particularly a kind of method and device of producing the motorcycle direction conical riser in the cold extrusion mode.
(2), technical background
As shown in Figure 1, the motorcycle direction conical riser is that the descending and face shaping of diameter is successively by diameter maximum linear section (AB section), taper section (BC section), the less straightway of diameter (CD section), minimum straightway four steel pipes that part seamlessly transits such as (DE sections) of diameter.Existing motorcycle direction conical riser is to make with straight steel pipe, traditional processing method is: at first steel pipe is carried out heat temperature raising, then steel pipe is forged into taper, after cooling, it is processed, it is rough turn together promptly will to forge into the whole outer surface of steel pipe of taper with lathe, and finish turning together again.This processing method exists following deficiency:
1. waste material: to process a maximum gauge is that 34 millimeters, length are that 288.5 millimeters conical riser is an example, and before processing, must select diameter for use is that 35.5 millimeters, thickness are 5.5 millimeters steel pipe, and each steel pipe weight is 1.2 kilograms.Think annual 2500000 the standpipes calculating of producing, will consume 3000 tons of steel.
2. consume coal-fired: think annual 2500000 the above-mentioned conical risers calculating of producing, will consume coal-fired 833 tons every year.
3. material is selected single: be example to produce above-mentioned conical riser still, the diameter of steel tube of selecting for use can not be too big, because waste material too, can not be too little, because production and processing does not reach the specification requirement of product, the general diameter of just can only selecting for use is that 35.5 millimeters, thickness are 5.5 millimeters steel pipe, and therefore, the selection of its material is single.
4. standpipe is coarse: because steel pipe has been carried out heat temperature raising, and forge, conical riser all produces the oxidation shell from inside to outside, and flexural deformation, and is low with axial ratio, wall unevenness.The oxidation shell that is produced is unfavorable to cutting, and the lathe tool wearing and tearing are big.Though with lathe its outer surface is processed, fineness still difficulty reaches product requirement, and endoporus is irregular, many, the wall unevenness of oxidation shell.
5. workload is big: must all process the outer surface of conical riser, amount of machining is big.
6. percent defective height: generally use the conical riser of produced in conventional processes, percent defective is up to 3%～4%.
Based on above-mentioned deficiency, relevant technologies personnel attempt to change the processing method of producing the motorcycle direction conical riser, want to process with the cold-stamped mode, carried out years of researches work, wherein, most of technical staff are seeing that be " after the punching press handbook by China Machine Press in the title of the 2nd edition the 15th printing June in 2002, particularly see the 403rd page of this book go up have " avoiding taper " to describe in the basic demand to cold-extruded part after, stopped research work, therefore, the method of producing the motorcycle direction conical riser with the cold extrusion mode does not have breakthrough so far, and its main cause is, just as " " during the extruding taper; will produce a harmful horizontal component; bring difficulty to extruding, and should strengthen surplus to this part, the extruding back obtains with machining " described in the punching press handbook.
(3), summary of the invention
One of purpose of the present invention just provides the method that a kind of technology is simple, with low cost, saving is produced the motorcycle direction conical riser with material and the low cold extrusion of percent defective.
Another object of the present invention just provides a kind of method of the present invention of utilizing, and steel pipe is contracted bind round the device of reaming.
A further object of the present invention just provides a kind of method of the present invention of utilizing, the device that the conical riser of preliminarily forming is carried out full shaping.
First purpose of the present invention is to realize that by such technical scheme its step is as follows:
(1) the hoop reaming of contracting: under the cold extrusion effect of hydraulic test, the liquid pressure scope is 10MPa～35Mpa, the internal diameter upper end is little, the lower end is big, and the middle part is taper, it is cylindric that the bottom is, the upper end is two sections columned hoop moulds that contract that diameter is different, be placed on the steel pipe from the isodiametric steel pipe upper end that scribbles releasing agent, simultaneously, the upper end is taper, the cylindrical reaming mould in bottom inserts in the steel pipe from the steel pipe lower end, making steel pipe is benchmark with the middle part, preliminarily forming is that top dwindles, the bottom enlarges and the even level and smooth preliminarily forming conical riser of profile, utilizes hydraulic test to carry out the demoulding again;
(2) full shaping: under the pressure effect of hydraulic test, the liquid pressure scope is 10MPa～35Mpa, the full finishing die that internal diameter size is met product standard is placed on the above-mentioned preliminarily forming conical riser, simultaneously, cold extrusion is carried out at two ends up and down to the preliminarily forming conical riser, makes that the preliminarily forming conical riser is full to form in the full finishing die, to overcome the irregular deformation that previous step occurs in rapid, after utilizing hydraulic test to carry out the demoulding again, promptly become the conical riser of standard.
Before this, the those skilled in the art generally believes: be not suitable for the production Tapered Cup in the cold extrusion mode.The present invention has overcome this technology prejudice just, utilizes existing cold extrusion equipment, and common steel pipe is produced conical riser in the cold-stamped mode.In the present invention, to contract the hoop die sleeve on steel pipe, under the common cold extrusion effect to steel pipe in contract hoop mould and reaming mould, make steel pipe be its standard with the middle part, one half contract the hoop tapered and cylindric, it is tapered and cylindric that another half expands hoop, and the outline of the taper of two halves is evenly level and smooth, constitutes a complete bullet.The effect of binding round mould of contracting is that the constriction steel pipe makes it to be configured as the less bullet of diameter and cylindric, and overcomes the harmful horizontal component that is produced in the reaming mould mechanism, guarantees the axiality of conical riser simultaneously.
Second purpose of the present invention is to realize by such technical scheme; it is to utilize described cold extrusion to produce the method for motorcycle direction conical riser; to steel pipe contract the hoop reaming pressurizing unit; this device includes the bottom knockout cushion cylinder that is subjected to hydraulic pump control; last demoulding cushion cylinder and shaping oil cylinder; bottom knockout cushion cylinder and shaping oil cylinder are arranged at the bottom and the top of frame respectively accordingly; the upper end is tapered; the cylindrical reaming mould in bottom vertically is fixed in the case top of bottom knockout cushion cylinder; the pressure head of shaping oil cylinder and last demoulding cushion cylinder; the internal diameter upper end is little; the lower end is big; and the middle part be taper contract that mould is affixed successively is integral for hoop from top to bottom; the pressure head of last demoulding cushion cylinder is corresponding with the endoporus top of the hoop mould that contracts, and the pressure head of bottom knockout cushion cylinder is affixed with the buffering bracketing plate that is placed on the reaming mould versatilely.
The above-mentioned hoop reaming pressurizing unit that contracts is work like this: the top that the steel pipe lower end is placed in the reaming mould; the steel pipe lower end is cushioned the bracketing plate and is supported; the pressure head of hydraulic pump control shaping oil cylinder moves down; and demoulding cushion cylinder is gone up in promotion and the hoop mould that contracts moves down together; make the hoop mould that contracts be placed on the steel pipe fully; the bander that tentatively contracts who finishes steel pipe does; the shaping oil cylinder continues to exert pressure; promotion contract the hoop mould move down; buffering bracketing plate buffering is supporting steel pipe; and with the moving down and move down of the hoop mould that contracts, until the bottom of reaming mould, in this process; finish following work simultaneously; in the hoop mould that contracts, making steel pipe is benchmark with the middle part, and preliminarily forming is that top dwindles; the bottom enlarges and the even level and smooth preliminarily forming conical riser of profile.Then; move on the pressure head of hydraulic pump control shaping oil cylinder; and drive to go up demoulding cushion cylinder and the hoop mould that contracts moves on together; meanwhile; the pressure head of hydraulic pump control bottom knockout cushion cylinder upwards ejects; bottom by buffering bracketing plate promotion preliminarily forming conical riser; make between preliminarily forming conical riser and the reaming mould and be separated; the pressure head that hydraulic pump is also controlled demoulding cushion cylinder ejects downwards; promote the top of preliminarily forming conical riser; make the preliminarily forming conical riser and contract to be separated between the hoop mould, thus the purpose of the realization conical riser demoulding.
The 3rd purpose of the present invention is to realize by such technical scheme, it is to utilize described cold extrusion to produce the method for motorcycle direction conical riser, conical riser is carried out the pressurizing unit of full shaping, this device includes demoulding oil jar and the extrusion oil cylinder that is subjected to hydraulic pump control, extrusion oil cylinder and demoulding oil jar are provided with the top and the bottom of frame respectively accordingly, full finishing die is fixed in the top of demoulding oil jar housing, the pressure head of demoulding oil jar is corresponding with the endoporus bottom of full finishing die, and the pressure head of extrusion oil cylinder is corresponding with the endoporus top of full finishing die.
Above-mentioned full shaping pressurizing unit is work like this: little big mode below the preliminarily forming conical riser vertically is put in the full finishing die, the pressure head of hydraulic pump control extrusion oil cylinder, top to preliminary conical riser is pushed from the top down, makes preliminarily forming conical riser full conical riser that is shaped as standard in full finishing die.Then, move on the pressure head of hydraulic pump control extrusion oil cylinder, the pressure head of controlling demoulding oil jar simultaneously upwards ejects from the bottom of the conical riser of standard, the conical riser of standard and full finishing die is separated, the purpose of the conical riser demoulding of realization standard.
Owing to adopted technique scheme, the present invention to have following advantage:
1. method is simple, operation is few, saves material: be that 34 millimeters, length are that 288.5 millimeters conical riser is an example to process a maximum gauge still, before processing, can select diameter for use is that 28 millimeters, thickness are 4 millimeters steel pipe, and each steel pipe weight is 0.8 kilogram.Think annual 2500000 the standpipes calculating of producing, need to consume 2000 tons of steel, compare, save with 1000 tons of materials with traditional diamond-making technique.
2. the present invention need not steel pipe is heated, and has saved the fire coal that consumes because of the heating steel pipe in the traditional diamond-making technique.
3. the material range of choice is wide: with method processing of the present invention, less demanding to type of material, general steel pipe can carry out, still be that 34 millimeters, length are that 288.5 millimeters conical riser is an example to process a maximum gauge, the scope of diameter of steel tube is: 28 millimeters～30 millimeters, the scope of steel pipe thickness is: 4 millimeters～5 millimeters, the weight range of whenever wanting steel pipe is 0.8kg～0.95kg, therefore, the material range of choice is wide.
4. the inside and outside smooth rule of the conical riser of producing with method of the present invention, with the axial ratio height, wall thickness is even.
5. the conical riser of producing with method of the present invention only needs its sub-fraction processing, and processing capacity is minimum.
6. percent defective is low: with the conical riser that method of the present invention is produced, percent defective is lower than 1 ‰.
(4), description of drawings
Description of drawings of the present invention is as follows:
Fig. 1 is the conical riser of standard;
Fig. 2 is the first kind of deformation process figure that is become the conical riser of standard by steel pipe;
Fig. 3 is the second kind of deformation process figure that is become the conical riser of standard by steel pipe;
Fig. 4 be among the present invention to the contract structural representation of pressurizing unit of hoop reaming of steel pipe;
Fig. 5 carries out the structural representation of the pressurizing unit of full shaping to conical riser among the present invention;
Fig. 6 is the structural representation of the full finishing die among Fig. 5;
Fig. 7 contracts to bind round the cold extrusion process chart of reaming pressurizing unit;
Fig. 8 is the cold extrusion process chart of full shaping pressurizing unit.
Among the figure: 1. bottom knockout cushion cylinder; 2. go up demoulding cushion cylinder; 3. shaping oil cylinder; 4. frame; 5. reaming mould; 6. the hoop mould contracts; 7. cushion the bracketing plate; 8. demoulding oil jar; 9. extrusion oil cylinder; 10. frame; 11. full finishing die; 12. fixed die; 13. movable mold; 14. housing; 15. free gap; 16. preliminarily forming conical riser; 17. transition shaping conical riser; 18. the conical riser of standard; 19. steel pipe.
(5), the specific embodiment
The invention will be further described below in conjunction with drawings and Examples:
As shown in Figure 2, step of the present invention is as follows:
(1) the hoop reaming of contracting: under the cold extrusion effect of hydraulic test, the liquid pressure scope is 10MPa～35Mpa, the internal diameter upper end is little, the lower end is big, and the middle part is taper, it is cylindric that the bottom is, the upper end is two sections columned hoop moulds that contract that diameter is different, be placed on the steel pipe from isodiametric steel pipe 19 upper ends that scribble releasing agent, simultaneously, the upper end is taper, the cylindrical reaming mould in bottom inserts in the steel pipe 19 from the steel pipe lower end, making steel pipe 19 is benchmark with the middle part, preliminarily forming is that top dwindles, the bottom enlarges and the even level and smooth preliminarily forming conical riser 16 of profile, utilizes hydraulic test to carry out the demoulding again; Among Fig. 2-(b), the AB section is the cylindric of diameter maximum, and the BC section is a taper, and the CD section is less cylindric of diameter, and the DC section is the cylindric of diameter minimum.
(2) full shaping: under the pressure effect of hydraulic test, the liquid pressure scope is 10MPa～35Mpa, the full finishing die that internal diameter size is met product standard is placed on the above-mentioned preliminarily forming conical riser 16, simultaneously, cold extrusion is carried out at two ends up and down to preliminarily forming conical riser 16, makes preliminarily forming conical riser 16 full forming in the full finishing die, to overcome the rapid middle irregular deformation that occurs of previous step, after utilizing hydraulic test to carry out the demoulding again, promptly become the conical riser 18 of standard.Among Fig. 2-(c), the AB section is the cylindric of diameter maximum, and the BC section is a taper, and the CD section is less cylindric of diameter, and the DC section is the cylindric of diameter minimum, and with Fig. 2-(b) compare, the conical riser of standard that different is is pressed to have lacked some.
Before this, the those skilled in the art generally believes: be not suitable for the production Tapered Cup in the cold extrusion mode.The present invention has overcome this technology prejudice just, utilizes existing cold extrusion equipment, and common steel pipe is produced conical riser in the cold-stamped mode.In the present invention, to contract the hoop die sleeve on steel pipe, under the common cold extrusion effect to steel pipe in contract hoop mould and reaming mould, make steel pipe be its standard with the middle part, one half contract the hoop tapered and cylindric, it is tapered and cylindric that another half expands hoop, and the outline of the taper of two halves is evenly level and smooth, constitutes a complete bullet.The effect of binding round mould of contracting is that the constriction steel pipe makes it to be configured as the less bullet of diameter and cylindric, and overcomes the harmful horizontal component that is produced in the reaming mould mechanism, guarantees the axiality of conical riser simultaneously.
In described this step of hoop reaming that contracts, with the buffering bracketing mechanism bottom of supporting steel pipe all the time, this buffering support mechanism descends along with the decline of steel pipe, makes steel pipe under steady, constant speed, finish simultaneously dwindle, expansion process, finally form the preliminarily forming conical riser.
As shown in Figure 3, in order to reduce the difficulty of the manufacturing, be convenient in the hydraulic test condition also can produce conical riser than under the low environment, the step of the described hoop reaming of contracting can be undertaken by following two steps:
(1) under the cold extrusion effect of hydraulic test, the internal diameter upper end is little, the lower end is big, and the middle part is taper, it is cylindric that the bottom is, the upper end is one section columned hoop mould that contracts, be placed on the steel pipe 19 from isodiametric steel pipe 19 upper ends that scribble releasing agent, simultaneously, the upper end is taper, the cylindrical reaming mould in bottom inserts in the steel pipe 19 from steel pipe 19 lower ends, making steel pipe 19 is benchmark with the middle part, preliminarily forming is that top dwindles, the bottom enlarges and the even level and smooth transition shaping conical riser 17 of profile, utilize hydraulic test to carry out the demoulding again, the upper end of the conical riser that the demoulding is come out has only one section to be cylindric; Shown in Fig. 3-(b), the AB section is the cylindric of diameter maximum, and the BC section is a taper, and the CE section is less cylindric of diameter.
(2) internal diameter one end is little, the other end is big, and the middle part is taper, the end end that an end end is cylindric, internal diameter is less that internal diameter is bigger is two sections columned hoop moulds that contract that diameter is different, be placed in fully on the transition shaping conical riser 17 of previous step in rapid, under the cold extrusion effect of hydraulic test to the two ends of transition shaping conical riser 17, make the different cylindrical preliminarily forming conical riser 16 of two sections diameters of end formed one-tenth of the less end of the diameter of this transition shaping conical riser 17, utilize hydraulic test to carry out the demoulding again.Among Fig. 3-(c), the AB section is the cylindric of diameter maximum, and the BC section is a taper, and the CD section is less cylindric of diameter, and the DE section is the cylindric of diameter minimum.
As shown in Figure 4; of the present invention steel pipe is contracted bound round the pressurizing unit of reaming; it is characterized in that: include the bottom knockout cushion cylinder 1 that is subjected to hydraulic pump control; last demoulding cushion cylinder 2 and shaping oil cylinder 3; bottom knockout cushion cylinder 1 and shaping oil cylinder 3 are arranged at the bottom and the top of frame 4 respectively accordingly; the upper end is tapered; the cylindrical reaming mould 5 in bottom vertically is fixed in the case top of bottom knockout cushion cylinder 1; the pressure head of shaping oil cylinder 3 and last demoulding cushion cylinder 2; the internal diameter upper end is little; the lower end is big; and the middle part be taper contract that mould 6 is affixed successively is integral for hoop from top to bottom; the pressure head of last demoulding cushion cylinder 2 is corresponding with the endoporus top of the hoop mould 6 that contracts, and the pressure head of bottom knockout cushion cylinder 1 is affixed with the buffering bracketing plate 7 that is placed on the reaming mould versatilely.
As shown in Figure 7; the above-mentioned hoop reaming pressurizing unit that contracts is work like this: shown in Fig. 7-(a); the steel pipe lower end is placed in the top of reaming mould 5; the steel pipe lower end is cushioned bracketing plate 7 and is supported; shown in Fig. 7-(b); the pressure head of hydraulic pump control shaping oil cylinder 3 moves down, and demoulding cushion cylinder 2 is gone up in promotion and the hoop mould 6 that contracts moves down together, makes the hoop mould 6 that contracts be placed on the steel pipe fully; the bander that tentatively contracts who finishes steel pipe does; shown in Fig. 7-(c), shaping oil cylinder 3 continues to exert pressure, and the hoop mould 6 that promotes to contract moves down; buffering bracketing plate 7 bufferings are supporting steel pipe; and with the moving down and move down of the hoop mould 6 that contracts, until the bottom of reaming mould 5, in this process; finish following work simultaneously; in the hoop mould 6 that contracts, making steel pipe is benchmark with the middle part, and preliminarily forming is that top dwindles; the bottom enlarges and the even level and smooth preliminarily forming conical riser 16 of profile.Then; shown in Fig. 7-(d); move on the pressure head of hydraulic pump control shaping oil cylinder 3; and drive to go up demoulding cushion cylinder 2 and the hoop mould 6 that contracts moves on together; meanwhile; the pressure head of hydraulic pump control bottom knockout cushion cylinder 1 upwards ejects; bottom by buffering bracketing plate 7 promotion preliminarily forming conical risers 16; make between preliminarily forming conical riser 16 and the reaming mould 5 and be separated; the pressure head that hydraulic pump is also controlled demoulding cushion cylinder 2 ejects downwards; promote the top of preliminarily forming conical riser 16, make preliminarily forming conical riser 16 and contract to be separated between the hoop mould 6, thus the purpose of the realization conical riser demoulding.
As shown in Figure 5, the pressurizing unit that conical riser is carried out full shaping of the present invention, it is characterized in that: include the demoulding oil jar 8 and the extrusion oil cylinder 9 that are subjected to hydraulic pump control, extrusion oil cylinder 9 and demoulding oil jar 8 are provided with the top and the bottom of frame 10 respectively accordingly, full finishing die 11 is fixed in the top of demoulding oil jar 8 housings, the pressure head of demoulding oil jar 8 is corresponding with the endoporus bottom of full finishing die 11, and the pressure head of extrusion oil cylinder 9 is corresponding with the endoporus top of full finishing die 11.
As shown in Figure 8, above-mentioned full shaping pressurizing unit is like this work: shown in Fig. 8-(a), little big mode below the preliminarily forming conical riser vertically is put in the full finishing die, shown in Fig. 8-(b), the pressure head of hydraulic pump control extrusion oil cylinder 9, top to preliminary conical riser 16 is pushed from the top down, makes preliminarily forming conical riser 16 full conical riser 18 that is shaped as standard in full finishing die.Then, shown in Fig. 8-(c), Fig. 7-(d), move on the pressure head of hydraulic pump control extrusion oil cylinder 9, the pressure head of controlling demoulding oil jar 8 simultaneously upwards ejects from the bottom of the conical riser 18 of standard, the conical riser 18 of standard is separated with full finishing die 11, realizes the purpose of conical riser 18 demouldings of standard.
As shown in Figure 6, full finishing die 11 can include fixed die 12 and movable mold 13 constitutes, fixed die 12 is fixedly installed in the housing 14, surround an activity space together by housing 14, fixed die 12 end faces and duplicate, movable mold 13 is positioned at activity space versatilely, and spacing leaving longitudinally-moving gap 15, the bottom surface internal diameter of movable mold 13 is corresponding with the internal diameter of fixed die 12 end faces.The effect of this full finishing die is: make conical riser 18 demouldings of standard be divided into two steps, the pressure head of hydraulic pump control demoulding oil jar 8 is when the bottom of the conical riser 18 of standard upwards ejects, shown in Fig. 8-(c), at first, make between the conical riser 18 of standard and the fixed die 12 and break away from, movable mold 13 does not stress because of free gap 15 is arranged, the pressure head that breaks away from oil cylinder 8 only need overcome the conical riser 18 of standard and the contact resistance between the fixed die 12, in case the conical riser 18 and the fixed die 12 of standard are separated, movable mold 13 is butted on the housing by the pressure head of demoulding oil jar 8, under the pressure head effect of demoulding oil jar 8, the movable mold 13 and the conical riser 18 of standard are separated, shown in Fig. 8-(d).The disengaging mode of this segmentation can more easily realize conical riser 18 demouldings of standard, can also reduce the specification requirement to hydraulic test simultaneously.
Claims (6)
1. the method for motorcycle direction conical riser is produced in a cold extrusion, and its step is as follows:
(1) the hoop reaming of contracting: under the cold extrusion effect of hydraulic test, the liquid pressure scope is 10MPa～35Mpa, the internal diameter upper end is little, the lower end is big, and the middle part is taper, it is cylindric that the bottom is, the upper end is two sections columned hoop moulds that contract that diameter is different, be placed on the steel pipe from the isodiametric steel pipe upper end that scribbles releasing agent, simultaneously, the upper end is taper, the cylindrical reaming mould in bottom inserts in the steel pipe from the steel pipe lower end, making steel pipe is benchmark with the middle part, preliminarily forming is that top dwindles, the bottom enlarges and the even level and smooth preliminarily forming conical riser of profile, utilizes hydraulic test to carry out the demoulding again;
(2) full shaping: under the pressure effect of hydraulic test, the liquid pressure scope is 10MPa～35Mpa, the full finishing die that internal diameter size is met product standard is placed on the above-mentioned preliminarily forming conical riser, simultaneously, cold extrusion is carried out at two ends up and down to the preliminarily forming conical riser, makes that the preliminarily forming conical riser is full to form in the full finishing die, to overcome the irregular deformation that previous step occurs in rapid, after utilizing hydraulic test to carry out the demoulding again, promptly become the conical riser of standard.
2. the method for motorcycle direction conical riser is produced in cold extrusion as claimed in claim 1, it is characterized in that in described this step of hoop reaming that contracts, cushion the bracketing mechanism bottom of supporting steel pipe all the time with one, this buffering support mechanism descends along with the decline of steel pipe, make steel pipe under steady, constant speed, finish simultaneously dwindle, expansion process, finally form the preliminarily forming conical riser.
3. the method for motorcycle direction conical riser is produced in cold extrusion as claimed in claim 1 or 2, it is characterized in that the step of the described hoop reaming of contracting was undertaken by following two steps:
(1) under the cold extrusion effect of hydraulic test, the internal diameter upper end is little, the lower end is big, and the middle part is taper, it is cylindric that the bottom is, the upper end is one section columned hoop mould that contracts, be placed on the steel pipe from the isodiametric steel pipe upper end that scribbles releasing agent, simultaneously, the upper end is taper, the cylindrical reaming mould in bottom inserts in the steel pipe from the steel pipe lower end, making steel pipe is benchmark with the middle part, preliminarily forming is that top dwindles, the bottom enlarges and the even level and smooth transition shaping conical riser of profile, utilize hydraulic test to carry out the demoulding again, the upper end of the conical riser that the demoulding is come out has only one section to be cylindric;
(2) internal diameter one end is little, the other end is big, and the middle part is taper, the end end that an end end is cylindric, internal diameter is less that internal diameter is bigger is two sections columned hoop moulds that contract that diameter is different, be placed in fully on the transition shaping conical riser of previous step in rapid, under the cold extrusion effect of hydraulic test to the two ends of transition shaping conical riser, make the different cylindrical preliminarily forming conical riser of two sections diameters of end formed one-tenth of the less end of the diameter of this transition shaping conical riser, utilize hydraulic test to carry out the demoulding again.
4. one kind as claim 1; the method of 2 described cold extrusions production motorcycle direction conical risers contracts to steel pipe and binds round the pressurizing unit of reaming; it is characterized in that: include the bottom knockout cushion cylinder (1) that is subjected to hydraulic pump control; last demoulding cushion cylinder (2) and shaping oil cylinder (3); bottom knockout cushion cylinder (1) and shaping oil cylinder (3) are arranged at the bottom and the top of frame (4) respectively accordingly; the upper end is tapered; the cylindrical reaming mould in bottom (5) vertically is fixed in the case top of bottom knockout cushion cylinder (1); the pressure head of shaping oil cylinder (3) and last demoulding cushion cylinder (2); the internal diameter upper end is little; the lower end is big; and the middle part is affixed successively being integral of hoop mould (6) of contracting of taper from top to bottom; the pressure head of last demoulding cushion cylinder (2) is corresponding with the endoporus top of the hoop mould (6) that contracts, and the pressure head of bottom knockout cushion cylinder (1) is affixed with the buffering bracketing plate (7) that is placed on the reaming mould versatilely.
5. one kind as claim 1, the method of 2 described cold extrusions production motorcycle direction conical risers is carried out full shaping to conical riser pressurizing unit, it is characterized in that: include the demoulding oil jar (8) and the extrusion oil cylinder (9) that are subjected to hydraulic pump control, extrusion oil cylinder (9) and demoulding oil jar (8) are provided with the top and the bottom of frame (10) respectively accordingly, full finishing die (11) is fixed in the top of demoulding oil jar (8) housing, the pressure head of demoulding oil jar (8) is corresponding with the endoporus bottom of full finishing die (11), and the pressure head of extrusion oil cylinder (9) is corresponding with the endoporus top of full finishing die (11).
6. the method for cold extrusion production motorcycle direction conical riser as claimed in claim 5 is carried out full shaping to conical riser pressurizing unit, it is characterized in that: full finishing die (11) includes fixed die (12) and movable mold (13) constitutes, fixed die (12) is fixedly installed in the housing (14), by housing (14), fixed die (12) end face and duplicate surround an activity space together, movable mold (13) is positioned at activity space versatilely, and spacing leaving longitudinally-moving gap (15), the bottom surface internal diameter of movable mold (13) is corresponding with the internal diameter of fixed die (12) end face.