CN1594599A - Method for making high-grade cabretta soft leather with defective sheepskin blue plate - Google Patents
Method for making high-grade cabretta soft leather with defective sheepskin blue plate Download PDFInfo
- Publication number
- CN1594599A CN1594599A CN 200410012350 CN200410012350A CN1594599A CN 1594599 A CN1594599 A CN 1594599A CN 200410012350 CN200410012350 CN 200410012350 CN 200410012350 A CN200410012350 A CN 200410012350A CN 1594599 A CN1594599 A CN 1594599A
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- soft
- wax
- small molecules
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for making high-grade sheep skin soft upper leather from inferior sheep skin, which comprises: dying, polishing leather, spraying sarcenet oil, mending, smoothing, grounding using grounding agent, brushing and scraping using multi-membrane agent several times, plucking skin, beating soft, scraping skin, Spraying surface slurry, spraying fixation agent, spraying hand feeling agent, ironing etc. Grounding agent is formulated by cation compound resin, non-ionic wax, cation color cream and water. Multi-membrane agent is formulated by non-ionic caseose-free color cream, compound resin, small molecule acroleic acid, swelling resin etc. Surface slurry is formulated by color cream, non-ionic wax, compound resin, silicon casein, flexible acroleic acid, paint slurry etc. fixation agent is formulated by water and aqueous gloss oil. Grounding agent is used mechanically and manually in the invention. Multi-membrane agent ,surface slurry and fixation agent have low cost , little pollution and can make high-grade sheep skin soft upper leather from inferior sheep skin.
Description
Technical field
The present invention relates to leather processing technology.
Background technology
High-grade cabretta soft leathers such as existing clothing leather, luggage leather, sofa artificial leather, upper leather can only process with fine sheepskin backboard.A large amount of inferior sheepskin backboards can't be processed into high-grade cabretta soft leather as residual plate, tinea plate, bur plate etc. with existing technology at all, can only handle at a low price as inferior sheep.Both uneconomical economically, also cause the waste of resource.
Summary of the invention
The present invention just provides and a kind of inferior sheepskin backboard is made the method for high-grade cabretta soft leather, and this method comprises following operation:
A, with the dyeing of inferior sheepskin backboard;
B, buffing, spray lining oil;
C, split cream and repair dry and cracked, bur with mending, emery cloth is tied;
D, play back cover with primer;
E, usefulness filming agent brushing one time, oven dry, mechanical pier light;
F, with filming agent brushing one time, oven dry, toggling, mechanical press polish again;
G, repeat to choose skin behind the e, f operation three times;
That h, machinery fall is soft, choose skin, manual shovel skin;
I, spray plane slurry 2 times;
J, spray fixing agent;
K, spray hand feeling agent;
L, machinery fall soft, press skin, and the limit is cut in arrangement;
M, graduation, finished product warehouse-in,
The primer prescription, by weight:
Water 10 positively charged ion compound resin 8-12 nonionic wax 3-5
Cationic wax 3-5 positively charged ion color 3-5 weak cation oil 2-3
The filming agent prescription, by weight:
Nonionic does not have junket color 10-12 nonionic wax 3-5 compound resin 5-7
Positively charged ion Chinese wax 2-4 small molecules vinylformic acid 6-10 solvent impregnated resin 6-7
Small molecules urethane 10-13 matting agent 3-4 non-ionic oil 1-2
Extruded resin 3-5 thickening material 1-2 flow agent 2-3
Soft acrylic resin 5-7 organosilicon surface slip agent 1-2
The starch adhesive prescription, by weight:
Color 10-13 nonionic wax 3-5 compound resin 2-4
Positively charged ion Chinese wax 1-2 small molecules vinylformic acid 10-13 silicic acid casein 2-3
Soft vinylformic acid 10-12 small molecules urethane 10-13 pigment pulp-water 2-3
Water 18
The fixing agent prescription, by weight:
Water 1 water-based gloss oil 1-1.3.
Optimum formulas such as primer of the present invention, by weight:
Water 10 sun are from compound resin 10 nonionic waxes 4
Cationic wax 3 positively charged ion colors 5 weak cation oil 2
Best filming agent prescription, by weight:
Nonionic does not have junket color 10 nonionic waxes 3 compound resins 5
Positively charged ion Chinese wax 2 small molecules vinylformic acid 8 solvent impregnated resins 6
Small molecules urethane 10 matting agents 4 non-ionic oils 1
Extruded resin 3 thickening materials 2 flow agents 2
Soft acrylic resin 6 organosilicon surface slip agents 1
Best starch adhesive prescription, by weight:
Color 10 nonionic waxes 3 compound resins 2 positively charged ion Chinese wax 1
Small molecules vinylformic acid 10 silicic acid caseins 2 soft vinylformic acid 10
Small molecules urethane 10 pigment pulp-waters 2 water 18
The optimal fixation agent prescription, by weight:
Water 1 water-based gloss oil 1.
The present invention adopts machinery and the manual method that combines, and use to implementing the custom-designed primer of this method, filming agent, starch adhesive and fixing agent, cost is low, pollution is light, the inferior sheepskin backboards such as residual plate, alkali plate, tinea plate, leather thorn plate that can at all can't be processed at present high-grade leather are processed into qualified of all kinds high-grade cabretta soft leather, have very high economic worth and practicality, also avoided the waste of resource.
Embodiment
Inferior sheepskin backboard is coloured to waste plate of all kinds; Use the buffing machine buffing, spray lining oil; Split dry and cracked, the bur of the manual repairing of cream with benefit, emery cloth is tied; On surface, play back cover with primer; With filming agent brushing one time, oven dry, mechanical pier light, choose do not mend dry and cracked, the bur skin mends, emery cloth is tied; Use the filming agent brushing again one time, oven dry, toggling, machine printed; Use overlay film such as preceding brushing twice again, that machinery falls is soft, choose skin, manual shovel skin; Twice in spray plane slurry; The spray fixing agent; The spray hand feeling agent; Fall soft, press whole qualified high-grade cabretta soft leather.
Press following formulation primer:
10 kilograms in water, positively charged ion compound resin 8-12 kilogram, nonionic wax 3-5 kilogram, cationic wax 3-5 kilogram, positively charged ion color 3-5 kilogram, weak cation oil 2-3 kilogram.
Press following formulation filming agent:
Nonionic does not have junket color 10-12 kilogram, nonionic wax 3-5 kilogram, compound resin 5-7 kilogram, positively charged ion Chinese wax 2-4 kilogram, small molecules vinylformic acid 6-10 kilogram, solvent impregnated resin 6-7 kilogram, small molecules urethane 10-13 kilogram, matting agent 3-4 kilogram, non-ionic oil 1-2 kilogram, extruded resin 3-5 kilogram, thickening material 1-2 kilogram, flow agent 2-3 kilogram, soft acrylic resin 5-7 kilogram, organosilicon surface slip agent 1-2 kilogram.
Press following formulation starch adhesive:
Color 10-13 kilogram, nonionic wax 3-5 kilogram, compound resin 2-4 kilogram, positively charged ion Chinese wax 1-2 kilogram, small molecules vinylformic acid 10-13 kilogram, silicic acid casein 2-3, soft vinylformic acid 10-12 kilogram, small molecules urethane 10-13 kilogram, pigment pulp-water 2-3 kilogram, 18 kilograms in water.
Press following formulation fixing agent:
10 kilograms in water, water-based gloss oil 10-13 kilogram.
Or prepare primer by optimum formula:
10 kilograms in water, 10 kilograms of positively charged ion compound resins (MT-900), 4 kilograms in nonionic wax (KM1), (6074) 3 kilograms of cationic waxes, 5 kilograms of positively charged ion colors (BLATRS), 2 kilograms of weak cation oil (BASF).
Or join coating agent by optimum formula:
Nonionic does not have 10 kilograms of junket colors, 3 kilograms in nonionic wax (KM1), 5 kilograms of compound resins (CRF-20), (362) 2 kilograms of positively charged ion Chinese wax, 8 kilograms in small molecules vinylformic acid (AR1), (660) 6 kilograms of solvent impregnated resins, 10 kilograms of small molecules urethane (RPU), 4 kilograms of matting agents, 1 kilogram of non-ionic oil, 3 kilograms of extruded resins, 2 kilograms of thickening materials, 2 kilograms of flow agents, 6 kilograms of soft acrylic resins, 1 kilogram of organosilicon surface slip agent.
Or prepare starch adhesive by optimum formula:
10 kilograms of colors, 3 kilograms in nonionic wax (KM1), 2 kilograms of compound resins (CRF-20), (362) 1 kilograms of positively charged ion Chinese wax, 2 kilograms of 10 kilograms of silicic acid caseins of small molecules vinylformic acid (AR1) (CW), 10 kilograms in acid vinylformic acid (AR8), 10 kilograms of small molecules Polyurethanes (RPU), 2 kilograms of pigment pulp-waters, 18 kilograms in water.
Or prepare fixing agent by optimum formula:
10 kilograms in water, 10 kilograms of water-based gloss oils (FN/W).
Claims (2)
1, inferior sheepskin backboard is made the method for high-grade cabretta soft leather, is comprised following operation:
A, with the dyeing of inferior sheepskin backboard;
B, buffing, spray lining oil;
C, split cream and repair dry and cracked, bur with mending, emery cloth is tied;
D, play back cover with primer;
E, usefulness filming agent brushing one time, oven dry, mechanical pier light;
F, with filming agent brushing one time, oven dry, toggling, mechanical press polish again;
G, repeat to choose skin behind the e, f operation three times;
That h, machinery fall is soft, choose skin, manual shovel skin;
I, spray plane slurry 2 times;
J, spray fixing agent;
K, spray hand feeling agent;
L, machinery fall soft, press skin, and the limit is cut in arrangement;
M, graduation, finished product warehouse-in,
The primer prescription, by weight:
Water 10 positively charged ion compound resin 8-12 nonionic wax 3-5
Cationic wax 3-5 positively charged ion color 3-5 weak cation oil 2-3
The filming agent prescription, by weight:
Nonionic does not have junket color 10-12 nonionic wax 3-5 compound resin 5-7
Positively charged ion Chinese wax 2-4 small molecules vinylformic acid 6-10 solvent impregnated resin 6-7
Small molecules urethane 10-13 matting agent 3-4 non-ionic oil 1-2
Extruded resin 3-5 thickening material 1-2 flow agent 2-3
Soft acrylic resin 5-7 organosilicon surface slip agent 1-2
The starch adhesive prescription, by weight:
Color 10-13 nonionic wax 3-5 compound resin 2-4
Positively charged ion Chinese wax 1-2 small molecules vinylformic acid 10-13 silicic acid casein 2-3
Soft vinylformic acid 10-12 small molecules urethane 10-13 pigment pulp-water 2-3
Water 18
The fixing agent prescription, by weight:
Water 1 water-based gloss oil 1-1.3.
2, according to claim 1 inferior sheepskin backboard is made the method for high-grade cabretta soft leather, it is characterized in that:
Said primer prescription, by weight:
Water 10 sun are from compound resin 10 nonionic waxes 4
Cationic wax 3 positively charged ion colors 5 weak cation oil 2
Said filming agent prescription, by weight:
Nonionic does not have junket color 10 nonionic waxes 3 compound resins 5
Positively charged ion Chinese wax 2 small molecules vinylformic acid 8 solvent impregnated resins 6
Small molecules urethane 10 matting agents 4 non-ionic oils 1
Extruded resin 3 thickening materials 2 flow agents 2
Soft acrylic resin 6 organosilicon surface slip agents 1
Said starch adhesive prescription, by weight:
Color 10 nonionic waxes 3 compound resins 2 positively charged ion Chinese wax 1
Small molecules vinylformic acid 10 silicic acid caseins 2 soft vinylformic acid 10
Small molecules urethane 10 pigment pulp-waters 2 water 18
Said fixing agent prescription, by weight:
Water 1 water-based gloss oil 1.