CN1594503A - Method for producing form coke from Jurassic steam coal - Google Patents
Method for producing form coke from Jurassic steam coal Download PDFInfo
- Publication number
- CN1594503A CN1594503A CN 200410026299 CN200410026299A CN1594503A CN 1594503 A CN1594503 A CN 1594503A CN 200410026299 CN200410026299 CN 200410026299 CN 200410026299 A CN200410026299 A CN 200410026299A CN 1594503 A CN1594503 A CN 1594503A
- Authority
- CN
- China
- Prior art keywords
- coal
- binding agent
- tar
- coke
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Method for producing form coke from Jurassic steam coal comprising the steps of, coal disintegrating, washing, drying, dry distillation so as to obtain high temperature coal tar and half-tar or refined gluing coal, disintegrating to below 0.4mm, obtaining powdered coal binding agent, distilling into pitch binding agent, preparing shaped coal by mixing 8-15% of pitch binding agent, 15-25% of powdered coal binding agent, charring the molded coal to obtain molded coke.
Description
Technical field
The invention belongs to a kind of production method technical field of coke, be specifically related to the method for jurassic period steam coal production formed coke.
Background technology
Need more than 100,000,000 ton of metallurgical coke China's year, and only more than 3,000 ten thousand tons of one-level (ash content 12%) metallurgical coke annual production, half outlet back remaining half use for domestic metallurgical industry, present domestic first-class metallurgical coke is short supply seriously.The reason of high grade coke famine is that common coal-coking process adopts coking coal to produce coke, according to statistics in 1987, China's coking coal reserves account for 28% of national coal reserves, coking coal is few, and ash content is higher, be again the coal of difficult washing, low ash, doctor negative to wash the burnt feed coal of refining few, is difficult to the mass production high grade coke.And the reserves of whole world coking coal account for 10% of world's coal reserves, and coke market, the world lacks high grade coke at present.
Publication number is that CN1153810A, denomination of invention are the Chinese patent of " method that hard coal is produced formed coke ", the employing high-quality anthracite is a raw material, add petroleum coke powder, to reduce the formed coke ash content, because it is higher that the most refinery coke of China contains sulphur content, can not heavy addition, limit it and reduced the effect of formed coke ash content, sulphur content, cause the superfine casting formed coke of high-quality that this patent can not industrial mass production ash content 4～5%, refinery coke price height, per tonly reach 1,000 yuan, increased the cost of superfine casting formed coke.
The patent No. is 99126265.4, denomination of invention is the Chinese patent of " method that the high volatilization of low ash long-flame coal is produced formed coke ", the feed coal that uses is the long flame coal cinder below the 100mm, to this lump coal washing, external ash content in the coal cinder can not be removed, even add the coal washing operation, because the washing rate of ash content 1～4% clean fine coal is low, be difficult to the superfine casting formed coke of high-quality of suitability for industrialized production ash content 4～5%.To the granularity of caking coal pulverizing and to the broken granularity of semi-coke powder all is below the 1mm, and such grain size category cooperates improper.Use in the coal tar that 500～700 ℃ of destructive distillation obtain the light oil composition more, the tar-bitumen composition is less, and coal tar is as the liquid-containing binder of making formed coke, and its effective constituent is the tar-bitumen composition in the coal tar.This patent is not carried out the distillatory pre-treatment to coal tar, does not remove the compositions such as ammoniacal liquor in the coal tar, has influence on the consumption of coal tar.
Jurassic period, steam coal was distributed widely in ground such as Shaanxi, Inner Mongol, Ningxia, Gansu, Xinjiang, its reserves account for 40～50% of national coal reserves, jurassic period, steam coal compared with hard coal, lean coal, coking coal, rich coal, bottle coal etc., its contain ash content minimum, contain low, the easy washing of sulphur content, the coal tar productive rate is the highest, be preparation high-quality formed coke ideal raw material coal, use the method for jurassic period steam coal production formed coke to need urgent some technical problems that solve.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of method of jurassic period steam coal production formed coke.
Solving the problems of the technologies described above the technical scheme that is adopted is that it comprises the steps:
(1) with jurassic period steam coal to be crushed to granularity with pulverizer be 0～5mm, through washing, oven dry, make and wash smart feed coal.
(2) will wash smart feed coal and pack charring furnace into 950～1150 ℃ of high temperature carbonizations 4～10 hours, and obtain coal-tar heavy oil and semicoke, it is to make jurassic period steam coal semi-coke powder below the 0.8mm that semicoke is crushed to granularity with pulverizer.
(3) coking coal or rich coal being crushed to granularity is 0～5mm, and washing, oven dry must be washed smart caking coal, and being crushed to granularity with pulverizer is below the 0.4mm, makes coking coal powder binding agent or rich coal powder binding agent.
(4) coal tar is made the tar-bitumen binding agent after 250～300 ℃ of distillations.
(5) with weight ratio be tar-bitumen binding agent 8～15%, coking coal powder binding agent 15～25% or rich coal powder binding agent 11～20%, all the other for jurassic period the steam coal semi-coke powder be mixed into compound.
(6) compound adds 60MPa pressure at normal temperatures and makes moulded coal.
(7) moulded coal is packed into made formed coke in 5～1 hours 950～1150 ℃ of following charings in the charring furnace.
The preferred weight proportioning that the present invention prepares each raw material of moulded coal compound is: tar-bitumen binding agent 10～14%, coking coal powder binding agent 17～22% or rich coal powder binding agent 14～18%, all the other for jurassic period the steam coal semi-coke powder.
The optimum weight proportioning that the present invention prepares each raw material of moulded coal compound is: tar-bitumen binding agent 12%, coking coal powder binding agent 20% or rich coal powder binding agent 16%, all the other for jurassic period the steam coal semi-coke powder.
The present invention is in preparation tar-bitumen binding agent processing step, and coal tar is made the tar-bitumen binding agent after 250～270 ℃ of preferred temperature distillations.
The present invention to jurassic period steam coal carry out washing, reduce jurassic period steam coal ash content and sulphur content with the washing method, thereby can produce the superfine casting formed coke of high-quality of ash content 4～5%.It is 0～5mm smalls that the feed coal that uses is surmised, and is the washing of 0～5mm smalls to granularity, can remove the external ash content in the feed coal effectively, the washing rate height of ash content 1～4% clean fine coal, thereby the superfine casting formed coke of high-quality that can mass production ash content 4～5%.The granularity that caking coal is pulverized is less, below 0.4mm, jurassic period the grinding particle size of steam coal semi-coke powder bigger, below 0.8mm, such grain size category cooperates, and can improve formed coke intensity or reduce the consumption of coal dust binding agent.Use 950～1150 ℃ of high temperature carbonizations to obtain coal-tar heavy oil, it is many to contain the tar-bitumen composition in the coal-tar heavy oil.Coal tar is carried out 250～300 ℃ of distillatory handle, removed oxious components such as the ammoniacal liquor in the coal tar, waste water, reduce the consumption of tar-bitumen.Advantages such as that the present invention has is reasonable in design, environmental pollution is little, production cost of products is low, formed coke intensity height, the quality of being produced are good, can produce in the formed coke at the jurassic period steam coal and be applicable.
Embodiment
The present invention is described in more detail below in conjunction with embodiment, but the invention is not restricted to these embodiment.
Embodiment 1
(1) with jurassic period steam coal to be crushed to granularity with pulverizer be 0～5mm, through flotation machine system and the washing oven dry of jig system, make and wash smart feed coal.
(2) will wash smart feed coal and pack external combustion internally heated upright carbonization furnace into 950 ℃ of high temperature carbonizations 10 hours, and obtain coal-tar heavy oil and semicoke, it is to make jurassic period steam coal semi-coke powder below the 0.8mm that semicoke is crushed to granularity with pulverizer.
(3) coking coal being crushed to granularity is 0～5mm, through flotation machine system and the washing oven dry of dense medium wet washer system, must wash smart caking coal, being crushed to granularity with pulverizer is below the 0.4mm, make the coking coal powder binding agent, rich coal is adopted to use the same method make rich coal powder binding agent.
(4) coal tar is made the tar-bitumen binding agent after 250～300 ℃ of distillations in distiller, and the preferred distillation temperature of coal tar is 250～270 ℃, and the best distillation temperature of coal tar is 260 ℃, and the distillation temperature of present embodiment coal tar adopts 260 ℃.
(5) make compound by following weight ratio mixing with the stirrer stirring:
Tar-bitumen binding agent 12%
Coking coal powder binding agent 20%
Jurassic period, the steam coal semi-coke powder added to 100%.
(6) compound that (5) are prepared adopts hydraulic molding machine to add 60MPa pressure at normal temperatures and makes moulded coal.
(7) moulded coal is packed into made formed coke in 12 hours 950 ℃ of following charings in the external combustion internally heated upright carbonization furnace.
Embodiment 2
In the present embodiment, in the step of preparation process of jurassic period steam coal semi-coke powder, will wash smart feed coal and pack external combustion internally heated upright carbonization furnace into, obtain coal-tar heavy oil and semicoke 1150 ℃ of high temperature carbonizations 4 hours.
In the step of preparation process of moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 8%
Coking coal (caking index G is 110) powder binding agent 15%
Jurassic period, the steam coal semi-coke powder added to 100%
Moulded coal packed into made formed coke in 5 hours 1150 ℃ of following charings in the external combustion internally heated upright carbonization furnace.Other step of formed coke preparation method is identical with embodiment 1.
Embodiment 3
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 15%
Coking coal powder binding agent 25%
Jurassic period the steam coal semi-coke powder to add to other step of 100% formed coke preparation method identical with embodiment 1.
Embodiment 4
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 8%
Coking coal powder binding agent 25%
Jurassic period the steam coal semi-coke powder to add to other step of 100% formed coke preparation method identical with embodiment 1.
Embodiment 5
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 15%
Coking coal (caking index G is 110) powder binding agent 15%
Jurassic period the steam coal semi-coke powder to add to other step of 100% formed coke preparation method identical with embodiment 1.
Embodiment 6
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 12%
Rich coal powder binding agent 16%
Jurassic period the steam coal semi-coke powder to add to other step of 100% formed coke preparation method identical with embodiment 1.
Embodiment 7
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 8%
Rich coal (caking index G is 110) powder binding agent 11%
Jurassic period, the steam coal semi-coke powder added to 100%
Other step of formed coke preparation method is identical with embodiment 1.
Embodiment 8
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 15%
Rich coal powder binding agent 20%
Jurassic period, the steam coal semi-coke powder added to 100%
Other step of formed coke preparation method is identical with embodiment 1.
Embodiment 9
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 8%
Rich coal powder binding agent 20%
Jurassic period, the steam coal semi-coke powder added to 100%
Other step of formed coke preparation method is identical with embodiment 1.
Embodiment 10
In the processing step of present embodiment moulded coal, the weight proportion of used compound raw material is as follows:
Tar-bitumen binding agent 15%
Rich coal (caking index G is 110) powder binding agent 11%
Jurassic period, the steam coal semi-coke powder added to 100%
Other step of formed coke preparation method is identical with embodiment 1.
In order further to verify the feasibility of processing step of the present invention, the applicant adopted the embodiment of the invention 1 preparation method in 2002, carried out the commerical test of 3 tons of output with the jurassic period steam coal production of Shaanxi Shenfu coalfield superfine casting formed coke, according to by standard GB 8729-88 superfine casting formed coke being detected, detected result is as follows:
The profile of formed coke is cylindrical and conical, and columniform geometrical dimension is that diameter is 106mm, the high 45mm of being, conical geometrical dimension is that the bottom surface diameter is 125mm, high 55mm.Ash content is low to reach 4.2%, and sulphur content is 0.41%, and dropping strength is 95%, has all reached superfine casting formed coke index.
The applicant adopted the embodiment of the invention 1 method, had carried out annual output ton industrialization trial production in 2003, used the jurassic period steam coal in the refreshing coalfield of Shaanxi elm to produce superfine casting formed coke in batches.(GB8729-88) checks by national standard, and detected result is as follows:
The profile of formed coke is cylindrical and conical, and columniform geometrical dimension is that diameter is 106mm, the high 45mm of being, conical geometrical dimension is that the bottom surface diameter is 125mm, high 55mm, ash content is low to reach 5.22%, sulphur content is 0.43%, and dropping strength is 94%, has all reached superfine casting formed coke index.
Claims (4)
1, a kind of method of jurassic period steam coal production formed coke is characterized in that it comprises the steps:
(1) with jurassic period steam coal to be crushed to granularity with pulverizer be 0～5mm, through washing, oven dry, make and wash smart feed coal;
(2) will wash smart feed coal and pack charring furnace into 950～1150 ℃ of high temperature carbonizations 4～10 hours, and obtain coal-tar heavy oil and semicoke, it is to make jurassic period steam coal semi-coke powder below the 0.8mm that semicoke is crushed to granularity with pulverizer;
(3) coking coal or rich coal being crushed to granularity is 0～5mm, and washing, oven dry must be washed smart caking coal, and being crushed to granularity with pulverizer is below the 0.4mm, makes coking coal powder binding agent or rich coal powder binding agent;
(4) coal tar is made the tar-bitumen binding agent after 250～300 ℃ of distillations;
(5) with weight ratio be tar-bitumen binding agent 8～15%, coking coal powder binding agent 15～25% or rich coal powder binding agent 11～20%, all the other for jurassic period the steam coal semi-coke powder be mixed into compound;
(6) compound adds 60MPa pressure at normal temperatures and makes moulded coal;
(7) moulded coal is packed into made formed coke in 5～12 hours 950～1150 ℃ of following charings in the charring furnace.
2, produce the method for formed coke according to claim 1 steam coal of described jurassic period, it is characterized in that the weight proportion that wherein prepares each raw material of moulded coal compound is: tar-bitumen binding agent 10～14%, coking coal powder binding agent 17～22% or rich coal powder binding agent 14～1 8%, all the other are jurassic period steam coal semi-coke powder.
3, produce the method for formed coke according to claim 1 steam coal of described jurassic period, it is characterized in that the weight proportion that wherein prepares each raw material of moulded coal compound is: tar-bitumen binding agent 12%, coking coal powder binding agent 20% or rich coal powder binding agent 16%, all the other are jurassic period steam coal semi-coke powder.
4, produce the method for formed coke according to claim 1 steam coal of described jurassic period, it is characterized in that: (4) processing step wherein coal tar after 250～270 ℃ of distillations, make the tar-bitumen binding agent.