CN1594201A - Composite microsphere containing hydroxyapatite and preparing method thereof - Google Patents
Composite microsphere containing hydroxyapatite and preparing method thereof Download PDFInfo
- Publication number
- CN1594201A CN1594201A CN 200410019979 CN200410019979A CN1594201A CN 1594201 A CN1594201 A CN 1594201A CN 200410019979 CN200410019979 CN 200410019979 CN 200410019979 A CN200410019979 A CN 200410019979A CN 1594201 A CN1594201 A CN 1594201A
- Authority
- CN
- China
- Prior art keywords
- hydroxyapatite
- microballoon
- complex microsphere
- sodium alginate
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a composite microsphere containing hydroxyapatite and preparing method thereof, wherein the weight percentage of its constituents include sodium alginate 20-50%, hydroxyapatite 40-70%, gelatin 0-13%, acacia gum 0-13%, the preparing process consists of formulating organic phase, charging the microsphere into the organic phase, agitating, charging calcium chloride solution, washing with water, immersing in water or 2.5% of calcium chloride solution for storage.
Description
Technical field
The invention belongs to materials science field, particularly a kind of complex microsphere that contains hydroxyapatite and preparation method thereof.
Background technology
Hydroxyapatite is one of maximum biological active materials of research at present, is widely used in various bone renovating materials and cell, pharmaceutical carrier, and application is also arranged aspect anticancer.But hydroxyapatite itself is very crisp, and easy-formation is not slightly soluble in water, at present the bibliographical information of relevant hydroxyapatite micro-sphere seldom, this has limited its application to a great extent.
Alginates is a class natural polysaccharide polymkeric substance, and is nontoxic and biodegradable, and sodium alginate attracts tremendous attention because of its gelification when polyvalent cation exists, and all obtained using widely at food, makeup, biomedicine field.Alginates micro-capsule, microballoon are widely used as carrier, are used for enzyme and proteinic fixing and controlled drug delivery system.The alginate calcium bead has excellent biological compatibility, has obtained in fields such as medicine sustained release using widely.The easy swelling of alginate microsphere that can be simple, physical strength is low, and matter is crisp, can not dryly use.Mostly report about alginate microsphere is alginate calcium or organic compound with gelatin, chitosan etc., does not still have report with the complex microsphere of inorganics.
Summary of the invention
The physical strength that the invention solves current material is low, and the crisp deficiency that waits of matter the invention provides complex microsphere that contains hydroxyapatite and preparation method thereof.
The component and the weight percentage of complex microsphere that contains hydroxyapatite is as follows:
Sodium alginate 20%～50%
Hydroxyapatite 40%～70%
Ethyl cellulose 10%～13%
Gelatin 0～13%
Gum arabic 0～13%
The preparation method of complex microsphere who contains hydroxyapatite is as follows:
1) presses the desired content of microballoon, take by weighing 10%～13% ethyl cellulose, be dissolved in volume ratio and be in the mixed solution of 2～1: 1 trichloromethane and normal hexane, as organic phase;
2) compound concentration is 2.5%～3% sodium alginate aqueous solution, sodium alginate content is the content of microballoon desired 20%～50%, take by weighing the hydroxyapatite of microballoon desired 40%～70%, after elder generation's water is moistening, join sodium alginate soln, the limit bevelling stirs and makes it be mixed into uniform white paste;
3) under the stirring velocity of 100～600r/min with step 2) in white paste pour organic phase in the step 1) into; Stir and formed uniform microballoon in 5～10 minutes; The adding mass percentage concentration is 2%～2.5% calcium chloride solution, keeps this speed to continue to stir 60～90min, outwells organism then, washes with water, soaks in the calcium chloride solution of water or 2.5% and preserves.
When pressing the desired content of microballoon if desired and adding gelatin or gum arabic, gelatin or gum arabic directly be dissolved in 2.5%～3% the sodium alginate aqueous solution.
Step 3) can also adopt following method: under the stirring velocity of 100～600r/min with step 2) in white paste pour organic phase in the step 1) into; Stir and formed uniform microballoon in 5～10 minutes; The adding mass percentage concentration is 2%～2.5% calcium chloride solution, keep this speed to continue to stir 60～90min, outwell organism then, directly carry out drying treatment after washing with water, the product that makes is used soaked in absolute ethyl alcohol 30～36h earlier, be placed on seasoning in the air then, constantly stir in case the microballoon adhesion, till complete drying.
The prepared complex microsphere size of the present invention is at 200～300 μ m, and we have synthesized the molecularly imprinted polymer that template is had specific recognition ability with its carrier as molecular imprinting.
With the compound physical strength that improves calcium alginate microsphere greatly of hydroxyapatite, and can regulate the swelling ratio of complex microsphere, density, physical strength etc. by the proportioning of adjusting them.Sodium alginate is by simple Ca
2+Crosslinking curing has advantages such as safe and simple, and the layered nano-structure with long-range order is incorporated in the carrier microballoons simultaneously.The complex microsphere of the present invention's preparation is expected to be used widely in fields such as cell cultures, pharmaceutical carrier, bone repair, molecular imprinting.
Description of drawings
Fig. 1: embodiment 1HA content is 50% microballoon;
Fig. 2: embodiment 2HA content is 70% microballoon;
Fig. 3: embodiment 3 contains the complex microsphere of 0.15g gelatin.
Embodiment
Embodiment 1. preparations contain the complex microsphere of HA50%
1) claims 0.1 gram ethyl cellulose (EC), be dissolved in the mixed solution of 30ml trichloromethane and 30ml normal hexane.
2) get 0.75 gram sodium alginate (Alg) and be dissolved in 25ml water, claim 0.75 gram hydroxyapatite (HA), moistening in grinding alms bowl with less water earlier, pour sodium alginate soln then into, the limit bevelling stirs and makes it be mixed into uniform white paste.
3) under the stirring velocity of 100～200r/min, will grind white paste in the alms bowl and be even thread shape and slowly pour in the organic solution, regulate the funnel state that agitator keeps liquid level.Stirred 5～15 minutes, and, added 25ml 2.5% calcium chloride solution if find to have formed microballoon uniformly.Keep this speed to continue to stir 90min, outwell organism then, water is given a baby a bath on the third day after its birth time, soaks in calcium chloride solution.Make the complex microsphere that contains HA50% as shown in Figure 1.
Embodiment 2. preparations contain the complex microsphere of HA70%
Claim 0.1 gram ethyl cellulose (EC), be dissolved in the mixed solution of 30ml trichloromethane and 30ml normal hexane.
Get 0.75 gram sodium alginate (Alg) and be dissolved in 25ml water, claim 1.75 gram hydroxyapatites (HA), moistening in grinding alms bowl with less water earlier, pour sodium alginate soln then into, the limit bevelling stirs and makes it be mixed into uniform white paste.
Under the stirring velocity of 100～200r/min, will grind white paste in the alms bowl and be even thread shape and slowly pour in the organic solution, regulate the funnel state that agitator keeps liquid level.Stirred 5～15 minutes, and, added the 25ml2.5% calcium chloride solution if find to have formed microballoon uniformly.Keep this speed to continue to stir 90min, outwell organism then, water is given a baby a bath on the third day after its birth time, soaks in calcium chloride solution.Make the complex microsphere that contains HA70% as shown in Figure 2.
Embodiment 3. preparations contain the hydroxyapatite/alginates complex microsphere of gelatin
Claim 0.1 gram ethyl cellulose (EC), be dissolved in the mixed solution of 30ml trichloromethane and 30ml normal hexane.
The gelatin of getting 0.75 gram sodium alginate (Alg) and 0.25 gram is dissolved in 25ml water, claims 1.75 gram hydroxyapatites (HA), and is moistening in grinding alms bowl with less water earlier, pours sodium alginate soln then into, and the limit bevelling stirs and makes it be mixed into uniform white paste.
Under agitation will grind white paste in the alms bowl and be even thread shape and slowly pour in the organic solution, regulate the funnel state that agitator keeps liquid level.Stir for some time,, add the 25ml2.5% calcium chloride solution if find to have formed microballoon uniformly.Keep this speed to continue to stir 90min, outwell organism then, water is given a baby a bath on the third day after its birth time, soaks in calcium chloride solution.Make the complex microsphere that contains the 0.15g gelatin as shown in Figure 3.
Embodiment 4. preparations contain the hydroxyapatite/alginates complex microsphere of gum arabic
1) claims 0.1 gram ethyl cellulose (EC), be dissolved in the mixed solution of 30ml trichloromethane and 30ml normal hexane.
2) get 0.75 gum arabic that restrains sodium alginate (Alg) and 0.25 gram and be dissolved in 25ml water, claim 1.75 gram hydroxyapatites (HA), use less water moistening in grinding alms bowl earlier, pour sodium alginate soln then into, the limit bevelling stirs and makes it be mixed into uniform white paste.
3) under the stirring velocity of 100～200r/min, will grind white paste in the alms bowl and be even thread shape and slowly pour in the organic solution, regulate the funnel state that agitator keeps liquid level.Stirred 5～15 minutes, and, added 25m 12.5% calcium chloride solution if find to have formed microballoon uniformly.Keep this speed to continue to stir 90min, outwell organism then, water is given a baby a bath on the third day after its birth time, soaks in calcium chloride solution.Make the hydroxyapatite/alginates complex microsphere that contains gum arabic.
Open and temperature sensitive title complex gel of injectable of proposing of the present invention and preparation method thereof, those skilled in the art can be by using for reference this paper content, and links such as appropriate change raw material, processing parameter, structure design realize.Product of the present invention and method are described by preferred embodiment, person skilled obviously can be in not breaking away from content of the present invention, spirit and scope to method as herein described with product is changed or suitably change and combination, realize the technology of the present invention.Special needs to be pointed out is, the replacement that all are similar and change apparent to those skilled in the artly, they are regarded as being included in spirit of the present invention, scope and the content.
Claims (5)
1. complex microsphere that contains hydroxyapatite, its component and weight percentage are as follows:
Sodium alginate 20%～50%
Hydroxyapatite 40%～70%
Ethyl cellulose 10%～13%
Gelatin 0～13%
Gum arabic 0～13%.
2. a kind of complex microsphere that contains hydroxyapatite as claimed in claim 1 is characterized in that described complex microsphere particle diameter is at 200～300 μ m.
3. a kind of preparation method who contains the complex microsphere of hydroxyapatite as claimed in claim 1 may further comprise the steps:
1) presses the desired content of microballoon, take by weighing 10%～13% ethyl cellulose, be dissolved in volume ratio and be in the mixed solution of 2～1: 1 trichloromethane and normal hexane, as organic phase;
2) compound concentration is 2.5%～3% sodium alginate aqueous solution, sodium alginate content is the content of microballoon desired 20%～50%, take by weighing the hydroxyapatite of microballoon desired 40%～70%, after elder generation's water is moistening, join sodium alginate soln, the limit bevelling stirs and makes it be mixed into uniform white paste;
3) under the stirring velocity of 100～600r/min with step 2) in white paste pour organic phase in the step 1) into; Stir and formed uniform microballoon in 5～10 minutes; The adding mass percentage concentration is 2%～2.5% calcium chloride solution, keeps this speed to continue to stir 60～90min, outwells organism then, washes with water, soaks in the calcium chloride solution of water or 2.5% and preserves.
4. a kind of preparation method who contains the complex microsphere of hydroxyapatite as claimed in claim 3, it is characterized in that described step 2) in, when pressing the desired content of microballoon and adding gelatin or gum arabic, gelatin or gum arabic directly be dissolved in 2.5%～3% the sodium alginate aqueous solution.
5. as claim 3 or 4 described a kind of preparation methods that contain the complex microsphere of hydroxyapatite, it is characterized in that described step 3) is: under the stirring velocity of 100～600r/min with step 2) in white paste pour step into
1) organic phase in; Stir and formed uniform microballoon in 5～10 minutes; The adding mass percentage concentration is 2%～2.5% calcium chloride solution, keep this speed to continue to stir 60～90min, outwell organism then, directly carry out drying treatment after washing with water, the product that makes is used soaked in absolute ethyl alcohol 30～36h earlier, be placed on seasoning in the air then, constantly stir in case the microballoon adhesion, till complete drying.