CN1594128A - PDMDAAC homopolymer inorganic and organic composite flocculant and preparation process thereof - Google Patents
PDMDAAC homopolymer inorganic and organic composite flocculant and preparation process thereof Download PDFInfo
- Publication number
- CN1594128A CN1594128A CN 200410024480 CN200410024480A CN1594128A CN 1594128 A CN1594128 A CN 1594128A CN 200410024480 CN200410024480 CN 200410024480 CN 200410024480 A CN200410024480 A CN 200410024480A CN 1594128 A CN1594128 A CN 1594128A
- Authority
- CN
- China
- Prior art keywords
- pdmdaac
- pac
- ammonium chloride
- dimethyl diallyl
- diallyl ammonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a PDMDAAC homopolymer inorganic and organic composite flocculant and preparation process thereof, wherein AlCl#-[3] * 6H#-[2]O, PDMDAAC are used as raw materials, and is introduced into the PAC solution. The flocculating agent has strong adsorption and bridging capacity for colloidal matter.
Description
(1) technical field
The present invention relates to polymeric aluminum-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent (PAC-PDMDAAC) and preparation technology thereof, belong to technical field of chemistry.
(2) background technology
Developing rapidly of industrial or agricultural, population increase, the water resources that the mankind depend on for existence is poor day by day.The problem of water resources crisis more and more becomes the important factor of restriction China Economic development.At present, China's water resources has been subjected to pollution in various degree, and increasing trend is arranged.For the conserve water resource, improve the utilization ratio of water, alleviate the waste water pollution on the environment, keep the Sustainable development situation of China's economic society, must strengthen improvement to trade effluent and sanitary sewage.In water technology, coagulating sedimentation is to use the most general, the most extensive and lower-cost key technique, it is determining operation condition, final outflow water water quality and the running cost of follow-up flow process, thereby becomes one of research contents important in the field of environment engineering.The quality of coagulating treatment effect depends on the quality of coagulating agent to a great extent.So development and efficient, nontoxic, the inexpensive high-molecular coagulant adopting of development of new become a urgent task in the water treatment field, are of great immediate significance.
At present, polymerize aluminum chloride (PAC) and Poly Dimethyl Diallyl Ammonium Chloride (PDMDAAC) are both at home and abroad at the inorganic and organic polymer coargulator to widespread use in water treatment, wastewater treatment and the sludge dewatering treatment.The advantage of PAC is reflected in that it is more excellent than traditional aluminum salt flocculant (as Tai-Ace S 150, aluminum chloride etc.) usefulness, and is more cheap than the organic polymer coargulator.But, aspect form, the polymerization degree and corresponding cohesion-flocculating effect, PAC still is between traditional aluminum salt flocculant and the organic polymer coargulator, its molecular weight and far short of what is expected to the adsorption bridging energy force rate organic polymer coargulator of colloidalmaterial, but also existence is to the instability problem of further hydrolysis reaction.In addition, PAC exists shortcomings such as sludge quantity than organic polymer coargulator dosage height, generation is big in application.The advantage of PDMDAAC flocculation agent is that it has that molecular weight height, product stability are good, strong to the adsorption bridging ability of colloidalmaterial, flocculating effect good, sludge quantity applied widely, that produce is few etc. than inorganic polymer flocculant, and shortcoming is that price height, best dispensing narrow range, cost of water treatment are high.The inorganic shortcoming that exists separately with organic polymer coargulator impels flocculation agent to develop to the composite flocculation agent direction, so that overcome shortcoming separately, enhanced flocculation usefulness improves purifying water effect, reduces cost of water treatment.So developing more, the inorganic organic polymer composite flocculant of high effect nontoxic becomes one of main task of water treatment field.
About research reports such as the aluminium base inorganic organic composite coagulators of polymerization, of heap of stone referring to thanking, Hu Yong has etc. the research that distributes of polymerize aluminum chloride and organic polymer composite flocculant form, environmental science and technology, 2003,00 (3), 15-16. soup heart tiger, Huang Xiuwei etc. inorganic/organic composite coagulator is to the research of decolorizing printing and dyeing waste water, 2001,27 (5), 267-270. but with AlCl
36H
2O, PDMDAAC homopolymer are that main raw material prepares PAC-PDMDAAC homopolymer inorganic organic composite coagulator, the present domestic bibliographical information of not seeing.In the bibliographic data base, do not see the pertinent literature report at present abroad.
(3) summary of the invention
The present invention is directed to the deficiency of existing flocculation agent, a kind of polymeric aluminum-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent and preparation technology thereof is provided, prepare the flocculation agent that not only has good storage stability but also have good flocculating effect.
Polymeric aluminum of the present invention-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent, outward appearance is light yellow or colourless liquid, contains Al
2O
3Weight percent 9.2%～11.6%, solid content is the weight percent 5.0%～11.0% of 39%～41% Poly Dimethyl Diallyl Ammonium Chloride, density (20 ℃) 1.1～1.2, basicity 30%～55%, pH are 3.1～3.5.
The preparation technology of polymeric aluminum of the present invention-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent is with AlCl
36H
2O is a raw material, is dissolved in the distilled water adding Na by weight 68～73: 100
2CO
3Regulate basicity 30%～55%, normal temperature down reaction and adding distil water stir water white liquid, be evaporated to crystallization at 40 ℃～60 ℃ then to separate out, polymeric aluminum; With the dimethyl diallyl ammonium chloride is raw material, and it is 55%～57% that adding distil water is diluted to concentration expressed in percentage by weight, logical N
220 minutes～40 minutes, the initiator of adding 2%～4% weight percent, 40～50 ℃ of constant temperature polymerizations got dimethyl diallyl ammonium chloride in 4 hours～6 hours; With weight ratio is to get above-mentioned polymeric aluminum and dimethyl diallyl ammonium chloride in 19: 1～9: 1,30 ℃～50 ℃ reactions 50 minutes～70 minutes, obtains polymeric aluminum-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent.
Polymeric aluminum of the present invention-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent is hereinafter to be referred as the PAC-PDMDAAC inorganic organic composite coagulator.
Preparation method to PAC-PDMDAAC inorganic organic composite coagulator of the present invention is described in detail as follows as follows below:
(1) gets 68～73gAlCl
36H
2The O solid adds 100ml distilled water in beaker, stir to add Na down
2CO
3Powder is to predetermined basicity (30%～55%), normal temperature is reaction down, add in the reaction process 20ml distilled water stir water white liquid, be evaporated to crystallization at 40 ℃～60 ℃ then and separate out, measure concrete concentration and the basicity of PAC with PAC product analysis measuring method.This step is prepared Al
2O
3Weight percentage is 10%～11% PAC.
(2) dimethyl diallyl ammonium chloride (DMDAAC) of getting 55～57g places three mouthfuls of round-bottomed flasks of 150ml, and it is 55～57% that adding distil water is diluted to concentration expressed in percentage by weight, logical 20～40 minutes N
2, add the initiator of 2～4% weight percents then, place water bath with thermostatic control, stir polymerization and stop after 4～6 hours.Preparing characteristic concentration (representing with viscosities il) is 1.0～1.1mlg
-1, solid content is 39～41% PDMDAAC.
Above-mentioned initiator is selected from Potassium Persulphate or ammonium persulphate.
(3) be to get PAC and the PDMDAAC that method for preparing goes out about 19: 1～9: 1 with weight ratio respectively, 30～50 ℃ of reactions 50～70 minutes, to prepare the PAC/PDMDAAC mass ratio is PAC-PDMDAAC product about 19: 1～9: 1, and the effective concentration of product is with Al
2O
3The weight percent 9.0%～11.0% of meter.
The PAC-PDMDAAC inorganic organic composite coagulator that the present invention prepares can be widely used in feedwater, wastewater treatment, fields such as oil production, papermaking, mining, textile printing and dyeing, daily-use chemical industry as a kind of new and effective water treatment agent.
PAC-PDMDAAC inorganic organic composite coagulator of the present invention compared with prior art has following excellent results:
The present invention-PAC-PDMDAAC inorganic organic composite coagulator belongs to novel high polymer flocculation agent in the water treatment field.This flocculation agent is the inorganic organic polymer coargulator of NEW TYPE OF COMPOSITE that grows up on the basis of traditional aluminum salt flocculant, is with AlCl
36H
2O, PDMDAAC are raw material, adopt the method that PDMDAAC is incorporated in the PAC solution to be prepared from.This flocculation agent combines advantages such as PDMDAAC molecular weight height, product stability are good, strong to the adsorption bridging ability of colloidalmaterial, flocculating effect good, sludge quantity applied widely, that produce is few, and advantage such as the best dispensing of aluminium salt wide ranges, cost of water treatment be low.The present invention is with AlCl
36H
2O, PDMDAAC are main production raw material, have prepared the PAC-PDMDAAC inorganic organic composite coagulator, have characteristics such as production technique is simple and direct, economic, suitable.This flocculation agent can be widely used in feedwater, wastewater treatment, fields such as oil production, papermaking, mining, textile printing and dyeing, daily-use chemical industry, and good water treatment effect is arranged.
(4) embodiment
Embodiment 1:
Get a certain amount of AlCl
36H
2O solid wiring solution-forming stirs adding Na down
2CO
3Powder is to predetermined basicity 38%, and the effective concentration of preparing PAC is (with Al
2O
3Meter) be 10.75%.Be 19: 1 by weight, get PAC and PDMDAAC respectively, prepare the PAC-PDMDAAC inorganic organic composite coagulator.Product is represented with No.1, lists in the table 1.The preparation method is as follows:
(1) gets 70.0gAlCl
36H
2The O solid adds 100ml distilled water in beaker, stir to add Na down
2CO
3Powder is to predetermined basicity 38%, and normal temperature is reaction down, add in the reaction process 20ml distilled water stir water white liquid, be evaporated to crystallization at 50 ℃ then to separate out, measure concrete concentration and the basicity of PAC with PAC product analysis measuring method.This step is prepared Al
2O
3Weight percentage is 10.22% PAC.
(2) dimethyl diallyl ammonium chloride (DMDAAC) of getting 55g places three mouthfuls of round-bottomed flasks of 150ml, and it is 55% that adding distil water is diluted to concentration, logical N
2Add 3% initiator potassium persulfate half an hour then, places 45 ℃ of waters bath with thermostatic control, stirs polymerization and stop after 5 hours.Prepare characteristic concentration (representing) and be 1.08mlg with viscosities il
-1, solid content is 40.6% PDMDAAC product.
(3) get PAC95g and the PDMDAAC5g that method for preparing goes out respectively, 19: 1 PAC-PDMDAAC is prepared the PAC/PDMDAAC weight ratio and is in 40 ℃ of reactions 1 hour.The effective concentration of product is with Al
2O
3The weight percent 9.70% of meter.
The PAC-PDMDAAC inorganic organic composite coagulator, outward appearance is a light yellow liquid, contains Al
2O
3Weight percent 9.70%, contain the weight percent 5.06% of PDMDAAC (solid content is 40.6%), density (20 ℃) 1.15, basicity 38%, pH are 3.3.
Embodiment 2:
Get a certain amount of AlCl
36H
2O solid wiring solution-forming stirs adding Na down
2CO
3Powder is to predetermined basicity 35%, and the effective concentration of preparing PAC is (with Al
2O
3Meter) be 10.17%.Be 9: 1 by weight, get PAC and PDMDAAC respectively, prepare the PAC-PDMDAAC inorganic organic composite coagulator, the product of this preparation is represented with No.2, lists among the table 1.
Preparation method such as embodiment 1, but different is: get AlCl
36H
2O solid 68g prepares PAC, and PAC effective concentration is (with Al
2O
3Meter) be 10.17% weight percent.The dimethyl diallyl ammonium chloride (DMDAAC) of getting 56g places three mouthfuls of round-bottomed flasks of 150ml, and it is 56% weight percent that adding distil water is diluted to concentration, logical N
2Add the initiator ammonium persulfate of weight percent 4% half an hour then, places 42 ℃ of waters bath with thermostatic control, stirs polymerization and stop after 6 hours.Get the PAC of 90g and the PDMDAAC of 10g, preparation PAC-PDMDAAC.
The PAC-PDMDAAC inorganic organic composite coagulator, outward appearance is a light yellow liquid, contains Al
2O
3Weight percent 9.15%, contain the weight percent 10.05% of PDMDAAC (solid content is 40.8%), density (20 ℃) 1.17, basicity 35%, pH are 3.5.
Embodiment 3:
Get a certain amount of AlCl
36H
2O solid wiring solution-forming stirs adding Na down
2CO
3Powder is to predetermined basicity 45%, and the effective concentration of preparing PAC is (with Al
2O
3Meter) be 10.19%.Get a certain amount of PAC and PDMDAAC product respectively, its mass ratio is 17: 1, prepares the PAC-PDMDAAC inorganic organic composite coagulator, and the product of this preparation is represented with No.3, lists among the table 1.Preparation method such as embodiment 1, but different is to get AlCl
36H
2O solid 69g, the effective concentration of preparing PAC is (with Al
2O
3Meter) is 10.19%, during preparation PAC-PDMDAAC, gets the PAC of 94g and the PDMDAAC of 6g.
The PAC-PDMDAAC inorganic organic composite coagulator, outward appearance is a light yellow liquid, contains Al
2O
3Weight percent 9.62%, contain the weight percent 5.56% of PDMDAAC (solid content is 40.6%), density (20 ℃) 1.15, basicity 45%, pH are 3.1.
Embodiment 4:
Get a certain amount of AlCl
36H
2O solid wiring solution-forming stirs adding Na down
2CO
3Powder is to predetermined basicity (48%), and the effective concentration of preparing PAC is (with Al
2O
3Meter) be 10.26%.Get a certain amount of PAC and PDMDAAC product respectively, its mass ratio is 11: 1, prepares the PAC-PDMDAAC inorganic organic composite coagulator, and the product of this preparation is represented with No.4, lists among the table 1.Preparation method such as embodiment 1, but different is to get AlCl
36H
2O solid 71g, the effective concentration of preparing PAC is (with Al
2O
3Meter) is 10.26%, during preparation PAC-PDMDAAC, gets the PAC of 91g and the PDMDAAC of 9g.
The PAC-PDMDAAC inorganic organic composite coagulator, outward appearance is a light yellow liquid, contains Al
2O
3Weight percent 9.41%, contain the weight percent 8.33% of PDMDAAC (solid content is 40.6%), density (20 ℃) 1.16, basicity 48%, pH are 3.4.
PAC-PDMDAAC of the present invention is applicable to feedwater, wastewater treatment, fields such as oil production, papermaking, mining, textile printing and dyeing, daily-use chemical industry.
One of application example
The No.1,2,3 of above embodiment 1,2,3,4 preparations, the coagulation turbidity removal that 4PAC-PDMDAAC inorganic organic composite coagulator product is used for Huanghe water are handled, contrasted with PAC, PDMDAAC simultaneously.Raw water turbidity is 692.5NTU, pH value 8.64, and SS is 1300mg/L, belongs to the ultra.Result is listed in table 1.
Table 1 PAC-PDMDAAC inorganic organic composite coagulator is handled the effect of Huanghe water
| ????No. | Under the different dosages (in mg/L), handle the residual turbidity (NTU) of back water | ||||
| ????10 | ????20 | ????30 | ????40 | ????50 | |
| ????1 | ????3.9 | ????2.1 | ????1.2 | ????0.4 | ????0.4 |
| ????2 | ????3.5 | ????2.0 | ????1.3 | ????0.6 | ????0.4 |
| ????3 | ????3.0 | ????1.9 | ????1.5 | ????0.4 | ????0.4 |
| ????4 | ????2.9 | ????1.8 | ????1.2 | ????0.5 | ????0.4 |
| ???PAC | ????36.0 | ????19.7 | ????8.2 | ????7.3 | ????5.4 |
| ?PDMDAAC | ????25.5 | ????18.1 | ????15.2 | ????10.3 | ????7.5 |
From above result as seen, the coagulation turbidity removal effect of PAC-PDMDAAC inorganic organic composite coagulator processing ultra sample obviously is better than PAC flocculation agent and PDMDAAC flocculation agent.
Two of application example
No.1,2,3, the 4PAC-PDMDAAC inorganic organic composite coagulator product of above embodiment 1,2,3,4 preparations is used for the crouch coagulating treatment of Tiger Mountain reservoir of Jinan, contrasts with PAC, PDMDAAC simultaneously.The raw water quality situation is as follows: pH value 7.71, turbidity are 22.3NTU, UV
254Be 0.062, permanganate index (COD
Mn) be 5.02mg/L, belong to medium turbidity water.Result is listed in table 2.
Table 2 PAC-PDMDAAC inorganic organic composite coagulator is handled
The effect (dosage is 15mg/L) of the Tiger Mountain reservoir water that crouches
| ????No. | Residual turbidity (NTU) | ??????????????COD Mn(mg/L) | ??????????????????UV 254 | ||||
| Before the processing | After the processing | Clearance (%) | Before the processing | After the processing | Clearance (%) | ||
| ????1 | ????1.8 | ??5.02 | ??2.14 | ??57.4 | ??0.062 | ??0.026 | ??58.1 |
| ????2 | ????1.6 | ??5.02 | ??2.11 | ??58.0 | ??0.062 | ??0.024 | ??61.3 |
| ????3 | ????1.6 | ??5.02 | ??2.04 | ??59.4 | ??0.062 | ??0.023 | ??62.9 |
| ????4 | ????1.5 | ??5.02 | ??2.00 | ??60.2 | ??0.062 | ??0.021 | ??66.1 |
| ???PAC | ????4.6 | ??5.02 | ??2.99 | ??40.4 | ??0.062 | ??0.033 | ??48.4 |
| ?PDMDAAC | ????3.8 | ??5.02 | ??2.59 | ??48.4 | ??0.062 | ??0.028 | ??54.8 |
From above result as seen, the coagulation turbidity removal effect that the PAC-PDMDAAC inorganic organic composite coagulator is handled medium turbidity water sample obviously is better than PAC flocculation agent and PDMDAAC flocculation agent, and COD
MnClearance improve 20% than PAC, improve 12% than PDMDAAC, UV
254Clearance improve 18% than PAC, improve 12% than PDMDAAC.
Three of application example
No.1,2,3, the 4PAC-PDMDAAC inorganic organic composite coagulator product of above embodiment 1,2,3,4 preparations are used to contain the coagulating treatment of disperseing gorgeous yellow dye waste water, contrast with PAC simultaneously.The raw water quality situation is as follows: pH value 6.98, and disperseing gorgeous yellow dye content is 100mg/L, absorbancy is 1.034.Result is listed in table 3.
Table 3 PAC-PDMDAAC inorganic organic composite coagulator decolorizing effect
| ????No. | Under the different dosages (in mg/L), the percent of decolourization of water sample (%) | ||||
| ????20 | ????40 | ????80 | ????120 | ????160 | |
| ????1 | ????10.05 | ????78.63 | ????95.32 | ????94.23 | ????91.21 |
| ????2 | ????13.73 | ????98.36 | ????97.58 | ????97.67 | ????97.19 |
| ????3 | ????65.37 | ????97.74 | ????98.22 | ????97.54 | ????95.36 |
| ????4 | ????86.07 | ????98.74 | ????98.65 | ????97.97 | ????96.42 |
| ???PAC | ????7.0 | ????7.4 | ????10.64 | ????88.39 | ????92.94 |
| ?PDMDAAC | ????78.05 | ????94.29 | ????89.16 | ????54.35 | ????34.62 |
From above result as seen, the PAC-PDMDAAC inorganic organic composite coagulator is compared with PAC, and when reaching equal percent of decolourization, dosage only is 1/2 of PAC, though be more or less the same with decolorizing effect under the equal dosage of PDMDAAC, the price of PAC-PDMDAAC only is about 1/4 of PDMDAAC.
Four of application example
No.1,2,3, the 4PAC-PDMDAAC inorganic organic composite coagulator product of above embodiment 1,2,3,4 preparations are used for the Shengli Oil Field coagulating treatment of the oily(waste)water of oil recovery factory, river now, contrast with PAC, PDMDAAC simultaneously.The raw water quality situation is as follows: pH value 7.6, COD
CrBe 486mg/L, water temperature is 45 ℃.Result is listed in table 4.
Table 4 PAC-PDMDAAC inorganic organic composite coagulator is handled the effect of oily(waste)water
| ????No. | Under the different dosages (in mg/L), handle the COD of back water sample Cr(mg/L) | ||||
| ????20 | ????40 | ????60 | ????80 | ????100 | |
| ????1 | ????186 | ????156 | ????112 | ????94 | ????131 |
| ????2 | ????174 | ????145 | ????106 | ????85 | ????124 |
| ????3 | ????171 | ????147 | ????103 | ????89 | ????125 |
| ????4 | ????162 | ????142 | ????101 | ????81 | ????123 |
| ???PAC | ????365 | ????284 | ????243 | ????226 | ????182 |
| ?PDMDAAC | ????213 | ????202 | ????192 | ????183 | ????172 |
From above result as seen, the flocculating effect that the PAC-PDMDAAC inorganic organic composite coagulator is handled oily(waste)water obviously is better than the PAC flocculation agent and reaches the PDMDAAC flocculation agent, and COD
CrClearance improve 21% than PAC, improve 19% than PDMDAAC.
Five of application example
The No.1,2,3 of above embodiment 1,2,3,4 preparations, the coagulating waste water that 4PAC-PDMDAAC inorganic organic composite coagulator product is used for different pH values are handled, contrasted with PAC simultaneously.The raw water quality situation is as follows: kaolin content is 100mg/L, and turbidity is 113NTU.Result is listed in table 5.
Table 5 PAC-PDMDAAC inorganic organic composite coagulator
Turbidity removal effect (dosage is 33mg/L)
| ????No. | Under the different pH, handle the residual turbidity (NTU) of back water sample | ||||
| ????5 | ????6 | ????7 | ????8 | ????9 | |
| ????1 | ????17.2 | ????7.1 | ????1.4 | ????1.7 | ????2.3 |
| ????2 | ????16.4 | ????6.4 | ????1.2 | ????1.4 | ????2.1 |
| ????3 | ????16.2 | ????6.3 | ????1.2 | ????1.4 | ????2.1 |
| ????4 | ????15.6 | ????5.5 | ????0.98 | ????1.1 | ????2.0 |
| ????PAC | ????34.0 | ????32 | ????1.7 | ????2.6 | ????2.8 |
From above result as seen, the suitable pH value scope of PAC-PDMDAAC inorganic organic composite coagulator obviously is wider than the PAC flocculation agent.
Six of application example
After the No.1,2,3 of above embodiment 1,2,3,4 preparations, coagulating waste water that 4PAC-PDMDAAC inorganic organic composite coagulator product is used for different pH values handled, get supernatant liquor and survey its remaining aluminium, the while contrasts with PAC.The raw water quality situation is as follows: kaolin content is 100mg/L, and turbidity is 116NTU.Result is listed in table 6.
Table 6 PAC-PDMDAAC inorganic organic composite coagulator
Remaining aluminium (dosage is 33mg/L)
| ????No. | Under the different pH, handle the remaining aluminium (mg/L) of back water sample | ||||
| ????5 | ????6 | ????7 | ????8 | ????9 | |
| ????1 | ????2.41 | ????0.90 | ????0.43 | ????0.88 | ????1.11 |
| ????2 | ????2.36 | ????0.85 | ????0.44 | ????0.75 | ????1.22 |
| ????3 | ????2.31 | ????0.88 | ????0.39 | ????0.76 | ????1.10 |
| ????4 | ????2.26 | ????0.78 | ????0.36 | ????0.74 | ????1.06 |
| ????PAC | ????2.55 | ????1.31 | ????0.69 | ????1.10 | ????1.64 |
From above result as seen, the remaining aluminium of PAC-PDMDAAC homopolymer inorganic organic composite coagulator is starkly lower than the PAC flocculation agent, only is 1/2～2/3 of PAC.
Claims (4)
1, a kind of polymeric aluminum-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent is characterized in that outward appearance is light yellow or colourless liquid, contains Al
2O
3Weight percent 9.2%～11.6%, solid content is the weight percent 5.0%～11.0% of 39%～41% Poly Dimethyl Diallyl Ammonium Chloride, 20 ℃ 1.1～1.2 of density, basicity 30%～55%, pH are 3.1～3.5.
2, the preparation method of the described polymeric aluminum of a kind of claim 1-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent is characterized in that, with AlCl
36H
2O is a raw material, is dissolved in the distilled water adding Na by weight 68～73: 100
2CO
3Regulate basicity 30%～55%, normal temperature down reaction and adding distil water stir water white liquid, be evaporated to crystallization at 40 ℃～60 ℃ then to separate out, polymeric aluminum; With the dimethyl diallyl ammonium chloride is raw material, and it is 55%～57% that adding distil water is diluted to concentration expressed in percentage by weight, logical N
220 minutes～40 minutes, the initiator of adding 2%～4% weight percent, 40 ℃～50 ℃ constant temperature polymerizations got dimethyl diallyl ammonium chloride in 4～6 hours; With weight ratio is to get above-mentioned polymeric aluminum and dimethyl diallyl ammonium chloride in 19: 1～9: 1,30 ℃～50 ℃ reactions 50 minutes～70 minutes, obtains polymeric aluminum-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent.
3, the preparation method of polymeric aluminum as claimed in claim 2-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent is characterized in that, described initiator is selected from Potassium Persulphate or ammonium persulphate.
4, the application of the polymeric aluminum of claim 1-dimethyl diallyl ammonium chloride homopolymer inorganic organic composited flocculation agent is characterized in that being used for feedwater, wastewater treatment, the water treatment agent of oil production, papermaking, mining, textile printing and dyeing, daily-use chemical industry.