CN1594061A - Elevator counterweight object and its making method - Google Patents
Elevator counterweight object and its making method Download PDFInfo
- Publication number
- CN1594061A CN1594061A CN 200410020828 CN200410020828A CN1594061A CN 1594061 A CN1594061 A CN 1594061A CN 200410020828 CN200410020828 CN 200410020828 CN 200410020828 A CN200410020828 A CN 200410020828A CN 1594061 A CN1594061 A CN 1594061A
- Authority
- CN
- China
- Prior art keywords
- shell
- elevator counterweight
- cement
- water
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Elevator counterweight object comprises: housing. The elevator slide edges are set at both sides of the housing. The filler is set in the housing, produced by agitating scrap iron, cement, sand and stone, water and concreting. The elevator counterweight object is produced by following materials by weight percent: 3-7% of housing is produced by iron plate and the filler is produced by residual components, in which scrap iron of 50-60%, cement of 10-15%, sand and stone of 22-30%, water of 5-10%. The process comprises: agitating above components, putting into the housing, flatting the top, concreting, and moulding. According to the above proportion, the elevator counterweight object can be produced into different weights to satisfy the different matched elevators demand. The producing cost of the invention is just a half to the current elevator counterweight object, thus it has a good prospect.
Description
Technical field: the present invention relates to novel elevator balance weight body of a kind of alternative existing elevator counterweight iron and preparation method thereof.
Background technology: elevator counterweight iron is the important accessory of elevator.At present, the balance weight iron that elevator adopted is an ironcasting, because the price of ironcasting goes up constantly in recent years, so cause the raising of elevator productive costs, the reduction of enterprise profit.In addition, also be a kind of waste for limited iron resource.
Summary of the invention: the objective of the invention is at above-mentioned the deficiencies in the prior art, and a kind of rational in infrastructure, elevator counterweight body that cost is low and simple and practical method for making thereof are provided.For achieving the above object, the present invention adopts following technical proposals: the elevator counterweight body, comprise shell (1), and the both sides of shell (1) are shaped on elevator slideway ear (2), be provided with weighting material (3) in the shell (1), weighting material (3) is stirred and is solidified by scrap iron, cement, sandstone and water and forms.Concrete method for making: the elevator counterweight body is by following material and makes by weight percentage: shell 3-7% makes of iron plate, and other composition constitutes weighting material, wherein scrap iron 50-60%; Cement 10-15%; Sandstone 22-30%; Water 5-10%.Put into the shell that makes in advance after above-mentioned composition stirred, and with the top floating aftershaping that solidifies.Can according to the above ratio the elevator counterweight system be become various weight, to satisfy and the matching used demand of various elevators.
Characteristics of the present invention are the elevator counterweight iron of its alternative prior art, and it is rational in infrastructure, scientific formulation, material source is extensive, method for making is simple.The most important thing is that its cost of manufacture is about 50% of a present elevator counterweight iron, therefore have good application prospects.
Description of drawings:
Fig. 1 is a structural representation of the present invention.
Fig. 2 is the birds-eye view of Fig. 1.
The specific embodiment:
Embodiment 1
With reference to Fig. 1,2, the elevator counterweight body comprises shell 1, and the both sides of shell 1 are shaped on elevator slideway ear 2, are provided with weighting material 3 in the shell 1, and weighting material 3 is stirred and solidified by scrap iron, cement, sandstone and water and forms.
Above-mentioned elevator counterweight body is to be made by following material and method: shell is made of iron plate, its weight 2kg, and other composition is for being provided with filler in the enclosure, wherein scrap iron 24kg; Cement 6kg; Sandstone 13kg; Water 3kg.Put into the shell (shell will place on the plane) that makes in advance after above-mentioned composition stirred, and with top floating coagulation forming.During use, elevator slideway ear is placed in the slideway of elevator.
Embodiment 2
Make the method for elevator counterweight body as described in example 1 above, shell is made of iron plate, its weight 3kg, and other composition is for being provided with filler in the enclosure, wherein scrap iron 50kg; Cement 10kg; Sandstone 22kg; Water 5kg.After above-mentioned composition stirred, put into the shell (shell will place on the plane) that makes in advance, and with top floating coagulation forming.
Embodiment 3
Make the method for elevator counterweight body as described in example 1 above, shell is made of iron plate, its weight 7kg, and other composition is for being provided with filler in the enclosure, wherein scrap iron 60kg; Cement 15kg; Sandstone 30kg; Water 10kg.After above-mentioned composition stirred, put into the shell (shell will place on the plane) that makes in advance, and with top floating coagulation forming.
Embodiment 4
Make the method for elevator counterweight body as described in example 1 above, shell is made of iron plate, its weight 5kg, and other composition is for being provided with filler in the enclosure, wherein scrap iron 56kg; Cement 13kg; Sandstone 28kg; Water 7kg.After above-mentioned composition stirred, put into the shell (shell will place on the plane) that makes in advance, and with top floating coagulation forming.
Embodiment 5
Make the method for elevator counterweight body as described in example 1 above, shell is made of iron plate, its weight 6kg, and other composition is for being provided with filler in the enclosure, wherein scrap iron 58kg; Cement 14kg; Sandstone 28kg; Water 8kg.After above-mentioned composition stirred, put into the shell (shell will place on the plane) that makes in advance, and with top floating coagulation forming.
Claims (7)
1, a kind of elevator counterweight body is characterized in that: it comprises shell (1), and the both sides of shell (1) are shaped on elevator slideway ear (2), is provided with weighting material (3) in the shell (1).
2, make the method for elevator counterweight body as claimed in claim 1, it is characterized in that it is by following material and makes by weight percentage: shell 3-7% makes of iron plate, and other composition constitutes weighting material, wherein scrap iron 50-60%; Cement 10-15%; Sandstone 22-30%; Water 5-10% after above-mentioned composition stirred, puts into the shell that makes in advance, and with top floating coagulation forming.
3, the method for making elevator counterweight body according to claim 2, it is characterized in that it is by following material: shell is made of iron plate, its weight 2kg, other composition is for being provided with filler in the enclosure, wherein scrap iron 24kg; Cement 6kg; Sandstone 13kg; Water 3kg puts into the shell that makes in advance after above-mentioned composition stirred, and with top floating coagulation forming.
4, the method for making elevator counterweight body according to claim 2, it is characterized in that it is by following material: shell is made of iron plate, its weight 3kg, other composition is for being provided with filler in the enclosure, wherein scrap iron 50kg; Cement 10kg; Sandstone 22kg; Water 5kg puts into the shell that makes in advance after above-mentioned composition stirred, and with top floating coagulation forming.
5, the method for making elevator counterweight body according to claim 2, it is characterized in that it is by following material: shell is made of iron plate, its weight 7kg, other composition is for being provided with filler in the enclosure, wherein scrap iron 60kg; Cement 15kg; Sandstone 30kg; Water 10kg after above-mentioned composition stirred, puts into the shell that makes in advance, and with top floating coagulation forming.
6, the method for making elevator counterweight body according to claim 2, it is characterized in that it is by following material: shell is made of iron plate, its weight 5kg, other composition is for being provided with filler in the enclosure, wherein scrap iron 56kg; Cement 13kg; Sandstone 28kg; Water 7kg after above-mentioned composition stirred, puts into the shell that makes in advance, and with top floating coagulation forming.
7, the method for making elevator counterweight body according to claim 2, it is characterized in that it is by following material: shell is made of iron plate, its weight 6kg, other composition is for being provided with filler in the enclosure, wherein scrap iron 58kg; Cement 14kg; Sandstone 28kg; Water 8kg after above-mentioned composition stirred, puts into the shell that makes in advance, and with top floating coagulation forming.