CN1586917A - Composite film with reflecting holographic and angular color change information double property - Google Patents
Composite film with reflecting holographic and angular color change information double property Download PDFInfo
- Publication number
- CN1586917A CN1586917A CN 200410066617 CN200410066617A CN1586917A CN 1586917 A CN1586917 A CN 1586917A CN 200410066617 CN200410066617 CN 200410066617 CN 200410066617 A CN200410066617 A CN 200410066617A CN 1586917 A CN1586917 A CN 1586917A
- Authority
- CN
- China
- Prior art keywords
- layer
- angular color
- color change
- angular
- laminated film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The composite film with reflecting hologram and angular color changing diagram consists of reflecting holographic layer and angular color changing information diagram layer connected via connecting layer. The reflecting holographic layer consists of surface covering layer, protecting layer, optical polymer information record layer and reinforcing layer compounded successively. The angular color changing information diagram layer consists of isolating layer, light changing function layer of angular color changing material, isolating layer, coloring layer and adhering layer compounded successively. The preparation process of the composite film includes the following steps: preparing reflecting holographic layer and the angular color changing layer separately, laminating or hot compounding the two, and optical copying. The present invention has raised anti-fake effect and may be used in anti-fake widely.
Description
Technical field
The invention belongs to false-proof film material technology field, be specifically related to a kind of laminated film with reflection holography and angular color change dual nature.
Background of invention
In the prior art, reflection hologram (seeing Chinese patent 021374732) with the making of superpolymer photosensitive material, have very high reflection efficiency, good field angle and stereoeffect, can be used as anti-fake material and ornament materials, be different from embossed holographic and seek for the uniqueness of material and the uniqueness of vision, improved false proof grade to a certain extent.Specific pattern or the literal made of angular photochromic material have angular color change performance (seeing Chinese patent 021369747), and the material variable color is obvious, and difficulty is forged in identification easily, thereby reach effectively false proof effect.But, above-mentioned two kinds of technology are combined, prepare the false-proof film that has reflection hologram and angular color change pattern function concurrently, to improve anti-counterfeiting power, be not reported so far.
Summary of the invention
The objective of the invention is to propose a kind of false-proof film that has reflection hologram and angular color change information pattern dual nature concurrently and preparation method thereof.
The false-proof film that the present invention proposes is made of through articulamentum is compound two functional layers, wherein, one is to have high brightness, transparent reflection holography layer with great visual angle, another is that angular color change pattern or literal are arranged on the surface, and the color after changing viewing angle presents the angular color change patterned layer of different color.
Among the present invention, the reflection holography functional layer 3 that described reflection holography layer 10 is made up of coverlay 1, protective seam 2, superpolymer hologram recording material and enhancement layer 4 is compound successively constitutes, as shown in Figure 1; The light that described angular color change layer 20 is made up of separation layer 22, angular photochromic material becomes pattern functional layer 23, separation layer 24, tack coat 26 is compound successively constitutes, as shown in Figure 2; Reflection holography layer 10 connects to form the composite anti-fake film with angular color change layer 20 by articulamentum 5, sees shown in Figure 3.
Among the present invention, in the described angular color change layer 20, as required, between separation layer 24 and tack coat 26, also dyed layer 25 can be set.
Among the present invention, before reflection holography layer 10 and angular color change layer 20 were compound, the former downside also was provided with a release layer 6, so that articulamentum 5 is protected, the latter's upside also is provided with a protective seam 21, so that separation layer 22 is protected.
Among the present invention, articulamentum 5 can adopt adhesivess such as polyacrylic or Polyurethane rubber.
Described overlayer 1 can adopt membraneous materials such as polyethylene terephthalate (PET) film, Biaxially oriented polypropylene (BOPP) film or tygon (PE) film.
Described protective seam 2 can adopt the material or the photopolymer binder of esters of acrylic acid.
Described enhancement layer 4 is used to strengthen the brightness and the visual field of reflection hologram.
Described separation layer 22,24 is used for the defencive function layer; its material can adopt prepolymer and trimethylolpropane tris acrylic acid ester monomer or aliphatic urethane diacrylate, the epoxy acrylate etc. of amino acrylates class; coat the surface of functional layer, to prevent penetrating of functional layer.
Described dyed layer 25 can add as required.
Described tack coat 26 can adopt pressure sensitive adhesive, also can adopt hot melt adhesive.
Among the present invention, described reflection hologram functional layer 3 is made of compositions such as photographic layer, monomer, light-initiated systems.Wherein, photographic layer is a refractive index film forming matter within the specific limits.Described angular color change functional layer 23 is that a kind of components such as photoinitiator, cellulose derivative and polymerisable monomer that contain are by being polymerized.See Chinese patent 021374732 and 021369747.
The preparation method of false proof laminated film of the present invention is as follows: prepare hologram layer 10 and angular color change layer 20 respectively earlier, carry out compound then.Prepare hologram pattern 3 in the photographic layer inside of method in hologram layer 10 by reflection record on the composite bed at last.Wherein, hologram layer 10 is made up of refractive index film forming matter within the specific limits; preparation can be adopted the method for patent 021374732: compositions such as monomer, light-initiated system are joined in the solvent under red light; be mixed to dissolving with magnetic agitation; coat (as PET, PE, OPP etc.) on the plastic foil; in temperature is that drying makes in 65~75 ℃ the drying box, goes up enhancement layer then again, and protective seam and overlayer get final product.The preparation of angular color change layer 20 can be adopted the method in the patent 021369747.With photoinitiator (as: isobutyl benzoin ether, 2,4,6-trimethylbenzene formyl hexichol phosphine oxide, 1-hydroxy cyclohexyl phenylketone, 2,2-dimethyl-2-phenyl acetophenone etc.) be mixed in the solution of cellulose derivative and polymerisable monomer and dissolve, after decompression is taken out and is desolvated, obtain jelly, jelly is coated on the base material, pass through the magnetic field of 0.5~5.0T under the room temperature, then under the radiation of ultraviolet light, solidify, obtain having angular color change pattern 23, separation layer 22 and 24 is gone up promptly more again in its both sides.20 on reflection holography layer 10 and angular color change layer compound can be finished also and can be finished by the compound technology of heat by laminating technology by articulamentum 5.
To have the reflection hologram template is fixed on the optical table, the directional light of identical incident angle (becoming 30 ° of-80 ° of angles with the dry plate normal) is a reference light during with logging template H2 with coherent light, the recording sheet that reflection holography recording layer and angular color change patterned layer is compound contacts with template by the dimethylbenzene matching fluid, form evenly about 2-6 μ dimethylbenzene optically coupled layers, under the irradiation of reference light, in thin layer, write down reflection holography Fig. 3.The photopolymer film obtains a reflection holography Fig. 3 who contains the angular color change pattern through photocuring and hot enhancement process.
The composite anti-fake film that the present invention proposes can seen two kinds of patterns by translation-angle under the light source usually, and one is to observe holographic three-dimensional pattern under the light of certain angle; Another tool is that the angular color change pattern or the literal on surface transfers green to by golden red behind rotational angle.Therefore, the present invention proposes anti-counterfeiting power, this film can be used as false proof Jianzhen's sign, driving license, identity document, credit card, reaches the covering of all kinds of documents etc.
Description of drawings
Fig. 1 is the structural diagrams of reflection holography layer.
Fig. 2 is the structural diagrams of angular color change layer.
Fig. 3 is the structural diagrams of composite membrane of the present invention.
Fig. 4 is the structure of composite membrane diagram of embodiment 1.
Fig. 5 is the structure of composite membrane diagram of embodiment 2.
Fig. 6 is the structure of composite membrane diagram of embodiment 3.
Fig. 7 is the structure of composite membrane diagram of embodiment 4.
Number in the figure: 1 is overlayer, and 2 is protective seam, and 3 is reflection hologram; 4 is enhancement layer, and 5 is articulamentum, and 6 is release layer; 10 is the reflection holography layer, and 20 is the angular color change layer, and 21 is protective seam; 22 is separation layer; 23 is angular color change figure, and 24 is separation layer, and 25 is dyed layer; 26 is adhesive linkage, and 27 is release layer.
Embodiment
The invention is further illustrated by the following examples.
Have the transparent membrane with dual nature that reflection hologram and information pattern change with the viewing angle turn colors, structure as shown in Figure 4.Wherein the preparation of reflection holography layer is coated the PET film that has organic protection layer 2 with reference to method as described above with photographic layer material, monomer, light trigger etc., and coating thickness is 15 υ m, and dry back is diaphragm again.
The preparation of angular color change pattern functional layer is equally referring to method as described above, the optic angle that angular color change effect material is made with pattern or literal become Figure 23 and isolated protective layer 22,24 compound, become the angular color change layer.Peel off the release layer 6 of reflection holography recording layer, peel off the protective seam 21 of angular color change functional layer, about 110 ℃, reflection holography layer 10 and angular color change layer 20 are combined with each other with the acrylic acid heat-sensitive glue.
Adopt the method for reflection holography record to carry out optical reproduction, to have the reflection hologram template is fixed on the optical table, the directional light of identical incident angle when writing down with template H2 with coherent light (becoming 30 ° of-80 ° of angles with the dry plate normal) is a reference light, the recording sheet that reflection holography layer and angular color change patterned layer is compound contacts with template by the dimethylbenzene matching fluid, form uniformly about 2-6 μ dimethylbenzene optically coupled layers, under the irradiation of reference light, in thin layer, write down reflection hologram.The photopolymer film obtains a reflection hologram that contains the angular color change pattern through photocuring and hot enhancement process.
The reflection holography layer includes PET diaphragm 1, organic protection layer 2, and hologram 3, and isolate enhancement layer 4.Then, coating one deck adhesive sticker 26 is compound with PET release film 27 under the angular color change layer, with the protection non-drying glue layer.
This film can be seen lifelike space pattern a specific angle, and when visible another angular color change pattern or literal behind rotational angle, pattern or literal color behind rotational angle transfers green to by golden red.
This clear films can be used for the safety anti-fake label, and the protection commodity are in case false Jianzhen.Also can be used for the covering of all kinds of documents, prevent to duplicate or distort.
Have reflection hologram and information pattern and have a dual nature film with what the viewing angle turn colors changed, its structure as shown in Figure 5.Wherein the material of reflection holography layer employing is coated PET with embodiment 1, and coating thickness is 12 μ m, and dry back is diaphragm again.Reflection holography layer 10 includes PET coverlay 1, protective seam 2, and light polymers information recording layer 3, and isolate enhancement layer 4.
The preparation of angular color change pattern functional layer 23 is with embodiment 1.Peel off the release layer 6 of reflection holography recording layer and the protective seam 21 of angular color change patterned layer respectively, about 110 ℃, reflection holography layer 10 and angular color change layer 20 are combined with each other with acrylic acid heat sensitive adhesive layer 5.Adopt the method for reflection holography record to carry out optical reproduction, to have the reflection hologram template is fixed on the optical table, the directional light of identical incident angle when writing down with template H2 with coherent light (becoming 30 ° of-80 ° of angles with the dry plate normal) is a reference light, the recording sheet that reflection holography layer and angular color change patterned layer is compound contacts with template by the dimethylbenzene matching fluid, form uniformly about 2-6 μ dimethylbenzene optically coupled layers, under the irradiation of reference light, in thin layer, write down reflection hologram., finish holographic recording after, the material that has write down is cured the enhancing photographic fixing under UV light, obtain a reflection hologram that contains the angular color change pattern.And on the film bottom is multiple dyed layer 25, this dyed layer can be the polymkeric substance of polyvinyl acetate or polyacrylate and the potpourri of required mill base, is that with the difference of embodiment 1 this film is an opaque coating.Coat adhesive linkage 26 again.
This film can be seen lifelike space pattern a specific angle, when behind rotational angle on its surface, as seen another angular color change pattern or literal, pattern or literal color behind rotational angle transfers green to by golden red.The pattern contrast of background color obviously improves.
This film can be directly used in the safety anti-fake label, label, and the protection commodity are in case false Jianzhen.
Have the anti-film of taking off of above-mentioned dual nature, the anti-function of taking off is made realization by rupture diaphragm.Its structure as shown in Figure 6.
The preparation of each function film such as embodiment 1; fragile base material adopts the polyurethane-type photopolymer film (as the product of sky minister company of Fudan University; model is PA5003J); add enhancement layer 4 and separation layer 24 respectively; be composited with functional membrane then; coat dyed layer 25 and non-drying glue layer 26 again, go up release diaphragm 27 again.
When the sign that this method is made, take off from separator paper layer 27, be pasted on base material after, when base material is opened, the sign corollary failure, thereby guaranteed that sign can not utilized once more.
Have the anti-film of taking off of above-mentioned dual nature, prevent that taking off function is realized by the hollow out manufacture craft.Its structure as shown in Figure 7.
Each function film is made as embodiment 2, and dyed layer adopts the hollow out substrate layer.When the sign that this method is made, take off from separator paper layer 27, be pasted on base material after, when base material was opened, sign demonstrated hollow out information and the corollary failure (see figure 7) immediately, thereby has guaranteed that sign can not utilized once more.
Claims (6)
1, a kind of laminated film with reflection holography layer and angular color change information dual nature is characterized in that by reflection holography layer (10) and the compound formation of angular color change information figure layer (20); Wherein, reflection holography functional layer (3) and the compound successively formation of enhancement layer (4) that described reflection holography layer (10) is made up of coverlay (1), protective seam (2), superpolymer hologram recording material; the light that described angular color change layer (20) is made up of separation layer (22), angular photochromic material becomes pattern functional layer (23), separation layer (24), the compound successively formation of tack coat (26), and reflection holography layer (10) is connected by articulamentum (5) with angular color change layer (20).
2, laminated film according to claim 1 is characterized in that being provided with dyed layer (25) between separation layer (24) and tack coat (26)).
3, laminated film according to claim 1 is characterized in that the downside of described tack coat (26) is provided with a release layer (27).
4, laminated film according to claim 1 is characterized in that described articulamentum (5) adopts polyacrylic or Polyurethane rubber.
5, laminated film according to claim 1 is characterized in that adding has fragile base material in described enhancement layer (4) and the separation layer (24).
6, laminated film according to claim 2 is characterized in that described dyed layer (25) adopts the hollow out substrate layer.