CN1563163A - Color plastic mud in use for hand kneading and preparation method - Google Patents
Color plastic mud in use for hand kneading and preparation method Download PDFInfo
- Publication number
- CN1563163A CN1563163A CN 200410031129 CN200410031129A CN1563163A CN 1563163 A CN1563163 A CN 1563163A CN 200410031129 CN200410031129 CN 200410031129 CN 200410031129 A CN200410031129 A CN 200410031129A CN 1563163 A CN1563163 A CN 1563163A
- Authority
- CN
- China
- Prior art keywords
- plasticine
- tinting material
- rubber
- mixture
- prescription
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A colour hand plasticine is prepared from natural rubber, butadiene rubber, low-pressure polyethylene, vaseline, white oil, pottery clay, calcium carbonate, antiager, colouring pigment and DOP. The preparing process includes proportioning materials, alloying, blending, parking, soaking, extruding and packing.
Description
Technical field
The present invention relates to a kind of hand plasticine, particularly a kind of colored hand plasticine and preparation method thereof.
Background technology
Existing colored hand plasticine is all boiled out by various oil and paraffin, and its main defective is a contaminate environment in the production process, and product has irritating smell, and is harmful, fades easily, the too high levels that the product heavy metal content that has is particularly plumbous.
Summary of the invention
The objective of the invention is to overcome prior art defective, improve a kind of colored hand plasticine and preparation method thereof.
The present invention adopts following technical scheme.
The colored hand plasticine of the present invention is made by following materials of weight proportions:
In natural rubber, cis-1,4-polybutadiene rubber and the low pressure polyethylene any one, two or three arbitrarily than mixture 80-120, Vaseline 24-36, white oil 8-12, potter's clay 160-240, lime carbonate 320-480, anti-aging agent 0.16-0.24, tinting material 0.08-0.12, DOP 8-12.
Raw material role division is as follows in the prescription:
Rubber and polyethylene are as the base mateiral of the colored hand plasticine of the present invention;
Vaseline and white oil are as the tenderizer of the colored hand plasticine of the present invention;
Potter's clay, lime carbonate are as the weighting agent of the colored hand plasticine of the present invention;
DOP is as the softening agent of the colored hand plasticine of the present invention.
In the prescription, natural rubber, cis-1,4-polybutadiene rubber and low pressure polyethylene can be wherein any one, also can be any the two or three's mixtures, and ratio is not limit;
Lime carbonate can adopt GL ground limestone, more than preferred 400 orders.
Anti-aging agent adopts the mixture of Sorbic Acid and paraffin, and the ratio of the two can be arbitrarily.
Colored hand plasticine of the present invention and technology thereof have following effect:
1, product is nonpoisonous and tasteless, meets European Community's hygienic standard after testing;
2, orthostatic is good, and is soft, tack-free, do not do and do not split;
3, owing to product does not have can reclaim through over cure, free from environmental pollution;
4, product color is bright-coloured, pure, does not fade;
5, production process is pollution-free, nuisanceless, to the not injury of operator's person.
Further specify the present invention below by specific embodiment.
[embodiment 1]
Adopt following materials of weight proportions:
Natural rubber, cis-1,4-polybutadiene rubber and low pressure polyethylene mixture 100, Vaseline 30 white oils 10, potter's clay 200, lime carbonate 400, anti-aging agent 0.2, tinting material 0.1, DOP 10.
In the prescription, natural rubber, cis-1,4-polybutadiene rubber and low pressure polyethylene three ratio are 40: 40: 20; The ratio of Sorbic Acid and paraffin is 1: 1 in the anti-aging agent; Tinting material adopts red pigment.
The colored hand plasticine of the present invention adopts following method preparation:
1, batching:, carry out weigh batching according to scheduling of production.
2, blend: adopt mill, rubber and low pressure polyethylene in the prescription are plasticated.
3, mixing: as to adopt mill, behind the mixture mixing after plasticating, tinting material, Sorbic Acid, paraffin, weighting agent, tenderizer in the prescription are successively added mixing.
4, park: rubber unvulcanizate was parked 24 hours.
5, heat refining, extrusion moulding, packing.
[embodiment 2]
Adopt following materials of weight proportions:
Natural rubber and cis-1,4-polybutadiene rubber mixture 120, Vaseline 36, white oil 12, potter's clay 240, lime carbonate 480, anti-aging agent 0.24, tinting material 0.12, DOP 12.
In the prescription, the ratio of the two is 100: 20 in natural rubber and the low pressure polyethylene mixture; The ratio of Sorbic Acid and paraffin is 5: 1 in the anti-aging agent; Tinting material adopts yellow ultramarine.
Make the colored hand plasticine of the present invention according to the method for embodiment 1.
[embodiment 3]
Adopt following materials of weight proportions:
Natural rubber and cis-1,4-polybutadiene rubber mixture 80, Vaseline 24, white oil 8, potter's clay 160, lime carbonate 320, anti-aging agent 0.16, tinting material 0.08, DOP8.
In the prescription, the ratio of the two is 10: 70 in natural rubber and the cis-1,4-polybutadiene rubber mixture; The ratio of Sorbic Acid and paraffin is 1: 5 in the anti-aging agent; Tinting material adopts blue pigments.
Make the colored hand plasticine of the present invention according to the method for embodiment 1.
[embodiment 4]
Adopt following materials of weight proportions:
Cis-1,4-polybutadiene rubber and low pressure polyethylene mixture 100, Vaseline 30, white oil 10, potter's clay 200, lime carbonate 400, anti-aging agent 0.2, tinting material 0.1, DOP 10.
In the prescription, the ratio of the two is 90: 10 in cis-1,4-polybutadiene rubber and the low pressure polyethylene mixture; The ratio of Sorbic Acid and paraffin is 1: 10 in the anti-aging agent; Tinting material adopts red pigment.
Make the colored hand plasticine of the present invention according to the method for embodiment 1.
[embodiment 5]
Adopt following materials of weight proportions:
Natural rubber and low pressure polyethylene mixture 120, Vaseline 36, white oil 12, potter's clay 240, lime carbonate 480, anti-aging agent 0.24, white factice 120, tinting material 0.12, DOP 12.
In the prescription, the ratio of the two is 100: 20 in natural rubber and the low pressure polyethylene mixture; The ratio of Sorbic Acid and paraffin is 10: 1 in the anti-aging agent; Tinting material adopts yellow ultramarine.
Make the colored hand plasticine of the present invention according to the method for embodiment 1.
[embodiment 6]
Adopt following materials of weight proportions:
Natural rubber and cis-1,4-polybutadiene rubber mixture 80, Vaseline 24, white oil 8, potter's clay 160, lime carbonate 320, anti-aging agent 0.16, tinting material 0.08, DOP 8.
In the prescription, the ratio of the two is 10: 70 in natural rubber and the cis-1,4-polybutadiene rubber mixture; The ratio of Sorbic Acid and paraffin is 10: 1 in the anti-aging agent; Tinting material adopts blue pigments.
Make the colored hand plasticine of the present invention according to the method for embodiment 1.
[embodiment 7]
Adopt following materials of weight proportions:
Cis-1,4-polybutadiene rubber and low pressure polyethylene mixture 100, Vaseline 30, white oil 10, potter's clay 200, lime carbonate 400, anti-aging agent 0.2, tinting material 0.1, DOP 10.
In the prescription, the ratio of the two is 90: 10 in cis-1,4-polybutadiene rubber and the low pressure polyethylene mixture; The ratio of Sorbic Acid and paraffin is 10: 1 in the anti-aging agent; Tinting material adopts red pigment.
Make the colored hand plasticine of the present invention according to the method for embodiment 1.
[embodiment 8]
Adopt following materials of weight proportions:
Cis-1,4-polybutadiene rubber 100, Vaseline 30, white oil 10, potter's clay 200, lime carbonate 400, anti-aging agent 0.2, tinting material 0.1, DOP 10.
Other are identical with embodiment 7.
[embodiment 9]
Adopt following materials of weight proportions:
Low pressure polyethylene 100, Vaseline 30, white oil 10, potter's clay 200, lime carbonate 400, anti-aging agent 0.2, tinting material 0.1, DOP 10.
Other are identical with embodiment 7.
[embodiment 10]
Adopt following materials of weight proportions:
Natural rubber 100, Vaseline 30, white oil 10, potter's clay 200, lime carbonate 400, anti-aging agent 0.2, tinting material 0.1, DOP 10.
Other are identical with embodiment 7.
Claims (3)
1, a kind of colored hand plasticine, make by following materials of weight proportions:
In natural rubber, cis-1,4-polybutadiene rubber and the low pressure polyethylene any one, two or three arbitrarily than mixture 80-120, Vaseline 24-36, white oil 8-12, potter's clay 160-240, lime carbonate 320-480, anti-aging agent 0.16-0.2, tinting material 0.08-0.12, DOP8-12
Wherein, described anti-aging agent adopts the mixture of Sorbic Acid and paraffin, and the ratio of the two is arbitrarily; Tinting material is various pigment.
2, colored hand plasticine according to claim 1 is characterized in that described lime carbonate is GL ground limestone.
3, the preparation method of the described colored hand plasticine of claim 1 comprises the steps:
(1) batching: carry out weigh batching according to described prescription;
(2) blend: adopt mill, rubber and low pressure polyethylene in the prescription are plasticated;
(3) mixing: as to adopt mill, behind the mixture mixing after plasticating, tinting material, Sorbic Acid, paraffin, weighting agent, tenderizer in the prescription are successively added mixing;
(4) park: rubber unvulcanizate was parked 24 hours;
(5) heat refining, extrusion moulding, packing.