CN1562890A - Pulp in use for ceramics powder in water based flow-casting technique - Google Patents
Pulp in use for ceramics powder in water based flow-casting technique Download PDFInfo
- Publication number
- CN1562890A CN1562890A CN 200410017748 CN200410017748A CN1562890A CN 1562890 A CN1562890 A CN 1562890A CN 200410017748 CN200410017748 CN 200410017748 CN 200410017748 A CN200410017748 A CN 200410017748A CN 1562890 A CN1562890 A CN 1562890A
- Authority
- CN
- China
- Prior art keywords
- slurry
- propylene glycol
- casting technique
- polyvinyl alcohol
- based flow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The characteristics of this size material are: water is used as dissolvant, poval is used as binder, propylene glycol is used as plastic agent, the quantity ratio of propylene glycol and poval is 1:2-2:1, degree of polymerization of poval is 1200-2000, alcoholysis degree is 55-99 percent, used poval is one of 1,3-poval and 1,2-poval or the both mixed according to any ratio. In the size material, volume content of binder and plastic agent is 5.5-7.5 percent when volume quantity of ceramics particle is 30 percent, surface tension of the size material can be reduced by water-base curtain coating technology provided by the invention.
Description
Technical field
The present invention relates to the slurry that a kind of ceramic powder water-based flow casting technique is used, relate to or rather and adopt water, by selecting suitable binding agent and plastic agent, the surface tension of control casting slurry as solvent, the wettability of raising on the casting films band belongs to the preparation technology field of ceramic membrane.
Background technology
Curtain coating (doctor-blade process) is one of technology of preparation thin-film material, aspect the structure design of material and the functional development important application is being arranged also, and casting technique comprises water base and two kinds of non-aqueous tape-castings.Non-aqueous tape-casting technology is comparative maturity at present, (1.USP 4587068 Method ofmaking ceramic tapes, May 6,1986 Borase, et al.2.USP 4353958 Greenceramic tapes and method of producing them, Oct.12,1982, Kita et al.3.USP4329271 Flexible ceramic tape and method of making same, Oct.12,1982, Kemret al.4.USP 5904892 Tape casting carbide dummy wafer, May18,1999, Holmes.), the diaphragm structure of preparation is even, the intensity height, and snappiness is good, be convenient to cutting and processing, in industrial production, use for many years.But the non-aqueous tape-casting process need use a large amount of deleterious organism as solvent, and the production cost height causes environmental pollution after the discharging, harmful HUMAN HEALTH.In contrast to this, water-based tape casting then adopts water as solvent, and the organism consumption is few, and cost is low, pollutes for a short time, and Environmental compatibility is good, and is harmless to HUMAN HEALTH, is convenient to scale operation, and therefore, in recent years, people have carried out many researchs to water-based flow casting technique.But; present business-like casting apparatus generally adopts Mylar (Mai La, polyester polymer trade(brand)name) as the casting films band; this film band mainly designs at non-aqueous tape-casting; surface tension is usually about 20 dyne, and the slurry of water-based tape casting, surface tension is than higher; therefore; the wettability of existing slurry on the casting films band is very poor, and cast film had usually very significantly and shrinks before drying.
Summary of the invention
The object of the present invention is to provide and a kind ofly can be applied to flow casting molding, prescription with the good aqueous casting slurry of casting films band Mylar wettability, mainly be to select suitable binding agent and plastic agent, dual function by binding agent and plastic agent, reduce the surface tension of casting slurry, make the surface tension of itself and Mylar approaching, reach the purpose of good wet.
The present invention adopts water as solvent unique in the casting technique.Adopt polyvinyl alcohol (PVA) as binding agent, the polymerization degree of PVA is between 1200-2000, and alcoholysis degree is between 50%-99%.Selecting propylene glycol for use is plastic agent;
Below the present invention is elaborated.The binding agent that the present invention uses is polyvinyl alcohol.Plastic agent is a propylene glycol.
Polyvinyl alcohol mainly contains following two kinds of structures:
1,3-ethylene glycol structure 1 structure
The x span is 500-1000 in the formula.Above-mentioned two kinds of structures are represented the polyvinyl alcohol of complete alcoholysis.Because PVA obtains from the alcoholysis of poly carboxylic acid methyl esters, the alcoholysis degree difference, the number of remaining carboxylate methyl ester is also variant among the then last PVA.For the polyvinyl alcohol of alcoholysis degree 50%, then there is half carboxyl still to be carboxylate methyl ester in the said structure.
Can there be four kinds usually as polyvinyl alcohol alcoholysis degree of the present invention, promptly 50%, 78%, 88%, 99%, the PVA that the present invention adopts can be the PVA of single a kind of alcoholysis degree, also can be the mixture of arbitrary proportion of the PVA of two kinds or more of different alcoholysis degrees, and wherein the alcoholysis degree scope is between 50%-99%.。The polymerization degree that is used for polyvinyl alcohol of the present invention is between 1000-2000.The preferred polymerization degree is between 1200-1700.Polyvinyl alcohol is very wide in industrial application, such as at papermaking, weaving, printing and medicine industry, its production technique is very ripe, and the product of different polymerization degree and alcoholysis degree can have been bought, cheap, its preparation method is also well-known in the polyvinyl alcohol technical field.
The structure of plastic agent is as follows:
1, ammediol 1,2-propylene glycol
Plastic agent adopts 1, ammediol and 1, a kind of in the 2-propylene glycol or two kinds in the mixture of any ratio as plastic agent.The mass ratio of propylene glycol and PVA is 1: 2-2: 1.Preferred mass ratio is 1: 1-3: 2.Improve the consumption of plastic agent and can avoid the surface of film that small pit is arranged, but too much plastic agent then can reduce film strength.The preparation method of propylene glycol is at industrial also comparative maturity.
Binding agent and the plastic agent content in slurry, different and variant with the volume content of the ceramic particle in the slurry.In slurry, when the volume content of ceramic particle was 30%, the volume content of binding agent in slurry was between 5.5-7.5%, and mass content is between 6.9-7.2%.
Adopt his plasticity such as PEG, glycerine etc., also can obtain complete casting films.But the slurry of preparation can not wetting Mylar.The invention provides a kind of pervasive ceramic size that can good wet Mylar film band, and this wettability prescription does not appear in the newspapers as yet in other patents and document.
The casting technique that the present invention proposes is easy to realize that technological process also is easy to control.The ceramic size that the water-based tape casting that provides is used is not only applicable to Al
2O
3Be the oxide compound of representative, and be applicable to SiC, Si
3N
4, the casting method moulding of non-oxide ceramic materials such as TiC.(seeing embodiment for details)
Embodiment
The following stated embodiment sets forth in detail substantive distinguishing features of the present invention and obvious improvement.
Embodiment 1
With 64 gram meta particle diameters is that 2 microns SiC joins 20ml and contains in the water of dispersion agent ball milling 24h.The PVA solution that adds 12wt%.Wherein, the total mass of PVA is 6.17 grams, and alcoholysis degree is 99%.Add propylene glycol, wherein, the quality of propylene glycol is identical with PVA, 1, the quality of ammediol be propylene glycol total mass 30%, continuation ball milling 24 hours.The slurry viscosity that obtains is between 350-600mPa.s.With the slurries filtration that obtains, vacuum outgas, curtain coating then, seasoning 4 hours.
Embodiment 2
With 64 gram meta particle diameters 0.6 micron Si
3N
4, join 20ml and contain in the water of dispersion agent ball milling 24h.The PVA solution that adds 12wt%.Wherein, the total mass of PVA is 6.17 grams, and alcoholysis degree is 88%.Add propylene glycol, the quality of propylene glycol is identical with PVA, 1, the quality of ammediol be propylene glycol total mass 50%, continuation ball milling 20 hours.The slurry viscosity that obtains is between 350-600mPa.s.With the slurries filtration that obtains, vacuum outgas, curtain coating then, seasoning 6 hours.
Embodiment 3
With 140 gram meta particle diameters is that 3 microns TiC joins 20ml and contains in the water of dispersion agent ball milling 24h.The PVA solution that adds 12wt%.Wherein, the total mass of PVA is 8.74 grams, and alcoholysis degree is 78%.Add propylene glycol, wherein, the quality of propylene glycol is identical with PVA, 1, the quality of ammediol be propylene glycol total mass 80%, continuation ball milling 18 hours.The slurry viscosity that obtains is between 300-600mPa.s.With the slurries filtration that obtains, vacuum outgas, curtain coating then, seasoning 7 hours.
Embodiment 4
With 80 gram meta particle diameters 0.4 micron Al
2O
3Join 20ml and contain in the water of dispersion agent ball milling 24h.The PVA solution that adds 12wt%.Wherein, the total mass of PVA is 6.20 grams, and alcoholysis degree is 50%.Add 1, ammediol, the quality of propylene glycol is identical with PVA, continues ball milling 24 hours.The slurry viscosity that obtains is between 250-600mPa.s.All the other are with embodiment 1.
Embodiment 5
64 gram SiC are joined 20ml contain in the water of dispersion agent ball milling 24h.The PVA solution that adds 13wt%.The alcoholysis degree of PVA is 50% and 78% two kind.Wherein the total mass of PVA is 4.58 grams, and alcoholysis degree is that the quality of 50% PVA is 60% of a PVA total mass, adds propylene glycol, and quality and the PVA of propylene glycol are suitable, 1, the quality of 2-propylene glycol be propylene glycol total mass 50%, continuation ball milling 18 hours.The slurry viscosity that obtains is between 250-500mPa.s.All the other are with embodiment 1.
Embodiment 6
With 64 gram Si
3N
4Join 20ml and contain in the water of dispersion agent ball milling 24h.The PVA solution that adds 13wt%.The alcoholysis degree of PVA is 50% and 88% two kind.Wherein the total mass of PVA is 4.58 grams, and alcoholysis degree is that the quality of 50% PVA is 80% of a PVA total mass, adds propylene glycol, and quality and the PVA of propylene glycol are suitable, 1, the quality of 2-propylene glycol be propylene glycol total mass 80%, continuation ball milling 16 hours.The slurry viscosity that obtains is between 250-450mPa.s.All the other are with embodiment 2.
Embodiment 7
With 140 gram meta particle diameters is that 3 microns TiC joins 20ml and contains in the water of dispersion agent ball milling 24h.The PVA solution that adds 13wt%.The alcoholysis degree of PVA is 50% and 99% two kind, and wherein the total mass of PVA is 4.58 grams, and alcoholysis degree is that the quality of 50% PVA is 50% of a binding agent total mass.Add 1, the 2-propylene glycol, the quality and the PVA of propylene glycol are suitable.Stirred 6 hours.The slurry viscosity that obtains is between 250-400mPa.s.All the other are with embodiment 4.
Claims (8)
1. slurry that the ceramic powder water-based flow casting technique is used is characterized in that:
(1) with water is solvent; Polyvinyl alcohol is a binding agent; Propylene glycol is a plastic agent;
(2) mass ratio of propylene glycol and polyvinyl alcohol is 1: 2-2: 1.
2. the slurry of using by the described water-based flow casting technique of claim 1, the polymerization degree that it is characterized in that described polyvinyl alcohol is between 1200-2000, and alcoholysis degree is between 50-99%.
3. the slurry of using by the described water-based flow casting technique of claim 1, the polymerization degree that it is characterized in that described polyvinyl alcohol is between 1200-1700.
4. the slurry of using by claim 1 or 2 described water-based flow casting techniques is characterized in that selecting for use a kind of polyvinyl alcohol of alcoholysis degree or the mixture of the arbitrary proportion of the polyvinyl alcohol of two or more different alcoholysis degrees; Select for use alcoholysis degree to be respectively 50%, 78%, 88% or 99% polyvinyl alcohol.
5. the slurry of using by the described water-based flow casting technique of claim 1, the mass ratio that it is characterized in that described propylene glycol and polyvinyl alcohol is 1: 1-3: 2.
6. the slurry of using by the described water-based flow casting technique of claim 1 is characterized in that propylene glycol adopts 1, ammediol and 1, a kind of or two kinds of mixtures of pressing arbitrary proportion in the 2-propylene glycol.
7. the slurry of using by the described water-based flow casting technique of claim 1, the volume content that it is characterized in that ceramic particle in the slurry is 30% o'clock, the volume content of binding agent in slurry is between 5.5-7.5%.
8. the slurry of using by the described water-based flow casting technique of claim 1 is applicable to Al
2O
3SiC, Si
3N
4Or the stupalith casting technique of TiC.