CN1559726A - Method of electromagnet continuoces casting of high spped steel composite roller - Google Patents
Method of electromagnet continuoces casting of high spped steel composite roller Download PDFInfo
- Publication number
- CN1559726A CN1559726A CNA2004100045028A CN200410004502A CN1559726A CN 1559726 A CN1559726 A CN 1559726A CN A2004100045028 A CNA2004100045028 A CN A2004100045028A CN 200410004502 A CN200410004502 A CN 200410004502A CN 1559726 A CN1559726 A CN 1559726A
- Authority
- CN
- China
- Prior art keywords
- casting
- high speed
- magnetic field
- electromagnetic
- speed steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method for electromagnetic conticasting of composite high-speed steel roller includes such steps as preheating the ball-ground cast iron particles in protective atmosphere, putting them in conticasting mould, externally applying an adjustable MF magnetic field, pouring the molten high-speed steel in the conticasting mould while electromagnetic stirring, and quick cooling.
Description
Technical field
The invention belongs to high-speed steel foundry engieering scope, particularly a kind of electromagnetic continuous-casting compound high speed steel roll method.
Background technology
At present in the production of compound high speed steel roll, adopt the continuous pouring method of forming, can utilize the advantage of ripe continuous manufacturing technology, have bigger potentiality, but because the alloying element content height has significant limitation by improving cooling velocity refinement cast sturcture.It is thick to be mainly as-cast structure, the segregation of alloying element and carbide, and interface bond strength is lower, and the surface quality of casting roll is relatively poor etc.Therefore developing new composite roll preparation method is present high-performance roll development and producer's urgent problem.
Summary of the invention
The purpose of this invention is to provide a kind of electromagnetic continuous-casting compound high speed steel roll method; it is characterized in that: described electromagnetic continuous casting method be with when casting need with the core nodular cast iron be preheating under the protective atmosphere between 300 ℃-600 ℃; put in the continuous casting mould; at this moment 1600 ℃ high speed molten steel is being cast in the cooling frame continuously; in casting; the intermediate frequency magnetic field 2 that adds 50-80Hz in continuous casting equipment 1 outside; its magnetic field intensity is 2000-6000 Gauss; magnetic field intensity is adjustable; being used in the Luo Lunzili liquid towards metal that produces under the effect of electromagnetic field retrains and stirs; fast after the cooling; prepare existing good roller surface quality, have the compound high speed steel roll of excellent properties again.
The invention has the beneficial effects as follows by adding electromagnetic field and prepare compound high speed steel roll, can utilize the effect of contraction and the stirring action of the Luo Lunzili liquid towards metal that under the effect of electromagnetic field, produces, the refinement microstructure, reduce the segregation of alloying element and the gross segregation of carbide, by control cooling velocity, electromagnetic field frequency and magnetic field intensity, improve the bond strength at interface, can reduce casting flaw, improve the surface quality of ingot casting.
Description of drawings
Fig. 1 is an electromagnetic continuous-casting compound high speed steel roll device schematic diagram.
Specific embodiments
The present invention is a kind of electromagnetic continuous-casting compound high speed steel roll method; with when casting need with the core nodular cast iron be preheating under the protective atmosphere between 300 ℃-600 ℃; put in the continuous casting mould; at this moment 1600 ℃ high speed molten steel is being cast in the cooling frame continuously; in casting; the intermediate frequency magnetic field 2 that adds 50-80Hz in continuous casting equipment 1 outside; its magnetic field intensity is 2000-6000 Gauss; magnetic field intensity is adjustable; being used in the Luo Lunzili liquid towards metal that produces under the effect of electromagnetic field retrains and stirs; after the cooling, prepare existing good roller surface quality fast, have the compound high speed steel roll of excellent properties again.
The Luo Lunzili liquid towards metal that produces under the effect of electromagnetic field retrains and stirs, can the refinement microstructure, reduce the segregation of alloying element and the gross segregation of carbide, by control cooling velocity, electromagnetic field frequency and magnetic field intensity.Improve the bond strength at interface, the frequency difference of electromagnetic field, electromagnetic field has different penetrating powers in liquid metal, and frequency is high more, and osmosis is more little, and frequency is low more, and electromagnetic field osmosis in liquid metal is strong more.Utilize the electromagnetic casting of different frequency, obtain the compound high speed steel roll that favorable surface quality combines with serviceability.Can reduce casting flaw, improve the surface quality of ingot casting.
Claims (1)
1. electromagnetic continuous-casting compound high speed steel roll method; it is characterized in that: described electromagnetic continuous casting method be with when casting need with the core nodular cast iron be preheating under the protective atmosphere between 300 ℃-600 ℃; put in the continuous casting mould; at this moment 1600 ℃ high speed molten steel is being cast in the cooling frame continuously; in casting; the intermediate frequency magnetic field (2) that adds 50-80Hz in continuous casting equipment (1) outside; its magnetic field intensity is 2000-6000 Gauss; frequency and magnetic field intensity are adjustable; being used in the Luo Lunzili liquid towards metal that produces under the effect of electromagnetic field retrains and stirs; fast after the cooling; prepare existing good roller surface quality, have the compound high speed steel roll of excellent properties again.