CN1557604A - 高强度紫铜合金焊丝及其用途 - Google Patents

高强度紫铜合金焊丝及其用途 Download PDF

Info

Publication number
CN1557604A
CN1557604A CNA2004100210896A CN200410021089A CN1557604A CN 1557604 A CN1557604 A CN 1557604A CN A2004100210896 A CNA2004100210896 A CN A2004100210896A CN 200410021089 A CN200410021089 A CN 200410021089A CN 1557604 A CN1557604 A CN 1557604A
Authority
CN
China
Prior art keywords
welding
welding wire
high strength
copper alloy
red copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2004100210896A
Other languages
English (en)
Other versions
CN1268469C (zh
Inventor
解明远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200410021089 priority Critical patent/CN1268469C/zh
Publication of CN1557604A publication Critical patent/CN1557604A/zh
Application granted granted Critical
Publication of CN1268469C publication Critical patent/CN1268469C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种高强度紫铜合金焊丝，焊丝是由合金材料铝、锰、铁、镍、锌、镁、硼砂、铜按一定配比经电炉熔炼后，拉拔成丝而成，其制作过程是首先将各合金材料按上述配比，放入感应电炉进行熔炼，熔炼温度为1300－1400℃，达到终点温度时可以进行浇注，铸成圆棒深加工，再经多次拉拔成丝。优点是与目前广泛应用的铜合金焊丝H9201#相比，铜合金焊丝HS201#焊缝机械性能中拉力δb＝20－23Kg/mm2，而高强度特制紫铜合金焊丝，焊缝的机械性能中拉力δb＝35Kg/mm2左右，明显地提高了焊接强度。

Description

高强度紫铜合金焊丝及其用途
技术领域
本发明涉及一种高强度紫铜合金焊丝，属于焊接合金材料。可用于冶金、机械、电力、化工等领域的焊接和修复工作，特别对于应用氧枪喷头中紫铜与钢件的焊接及铜合金的氩弧焊、氧-乙炔气焊堆焊时，其效果更为明显。
背景技术
传统的氧枪喷头焊缝的焊接方式有采用直流焊接机反接法，所用焊条是铜107#电焊条。该方式存在有夹渣、气孔、微裂等缺陷；半自动氩弧焊机，用于紫铜与20#钢管的焊缝焊接，焊接材料采用紫铜焊丝：HS201#。解决了上述缺陷，但仍然满足不了焊接技术的需求。由于氧枪喷头制造工艺从锻造、铸造工艺发展到组合挤压工艺，使用寿命是铸造喷头的3-4倍，随着现代炼钢技术的提高，传统的焊接材料已满足不了实际的生产要求。
发明内容
本发明的目的是提供一种克服现有技术存在的夹渣、焊缝有气孔、微裂等缺点的高强度紫铜合金焊丝。
高强度紫铜合金焊丝，其特征在于：焊丝是由以下合金材料，经电炉熔炼后，拉拔成丝而成，各合金材料按下述重量份配比而成：铝10.7-7.1、锰0.7-0.3、铁1.1-0.9、镍0.8-0.2、锌0.6-0.01、镁0.2-0.01、硼砂0.03-0.01、铜60-110。
其制作过程为：首先将各合金材料按上述配比，放入感应电炉进行熔炼。其熔炼温度一般在1300-1400℃，达到终点温度时可以进行浇注，铸成圆棒深加工，再经多次拉拔成丝。
焊丝规格直径在Φ1.2-Φ6mm之间，为粗细两种规格。细丝直径为：Φ1.2-Φ3.2mm焊丝，可制成盘形焊丝，主要应用于自动氩弧焊，半自动氩弧焊焊接等。
粗焊丝直径为Φ3.2-Φ6mm，可制成圆形焊丝，主要应用于手把氩弧焊、气焊、修补。
本发明的高强度特制紫铜合金焊丝，主要应用于异性金属的焊接，如铜与钢件、铜与不锈钢、铜与灰口铸铁等异性金属的焊接或堆焊修补工作。其焊接机械性能有很大提高，与目前广泛应用的铜合金焊丝H9201#相比，铜合金焊丝：HS201#焊缝机械性能中拉力δb＝20-23Kg/mm2，而高强度特制紫铜合金焊丝，焊缝的机械性能中拉力δb＝35Kg/mm2左右，明显地提高了焊接强度。
本发明高强度特制紫铜合金焊丝，与目前现有技术相比具有如下优点：
1、焊丝机械性能好，耐高温，抗裂性强，装填量大，提高了氧枪喷头的使用寿命。
2、焊缝成型好，焊接时不发生飞溅，焊缝无气孔，夹渣，裂纹等缺陷。
3、生产成本低，制作方法简单。
4、采用弧方法堆焊时工作环境好，不产生烟气，焊缝牢固。
具体实施方式
实施例1：
高强度紫铜合金焊丝，焊丝是由以下合金材料，经电炉熔炼后，拉拔成丝而成，各合金材料按下述重量份配比而成：铝10.7-7.1、锰0.7-0.3、铁1.1-0.9、镍0.8-0.2、锌0.6-0.01、镁0.2-0.01、硼砂0.03-0.01、铜60-110。
其制作过程为：首先将各合金材料按上述配比，放入感应电炉进行熔炼。其熔炼温度一般在1300-1400℃，达到终点温度时可以进行浇注，铸成圆棒深加工，再经多次拉拔成丝。
焊丝规格直径在Φ1.2-Φ6mm之间，为粗细两种规格。细丝直径为：Φ1.2-Φ3.2mm焊丝，可制成盘形焊丝，主要应用于自动氩弧焊，半自动氩弧焊焊接等。
实施例2：
粗焊丝直径为Φ3.2-Φ6mm，可制成圆形焊丝，主要应用于手把氩弧焊、气焊、修补。其余同实施例1。

Claims (5)

1、高强度紫铜合金焊丝，其特征在于：焊丝是由以下合金材料，经电炉熔炼后，拉拔成丝而成，各合金材料按下述重量份配比而成：铝10.7-7.1、锰0.7-0.3、铁1.1-0.9、镍0.8-0.2、锌0.6-0.01、镁0.2-0.01、硼砂0.03-0.01，其余材料为铜；其制作过程是首先将各合金材料按上述配比，放入感应电炉进行熔炼，熔炼温度为1300-1400℃，达到终点温度时进行浇注，铸成圆棒深加工，再经多次拉拔成丝。
2、根据权利要求1所述的高强度紫铜合金焊丝，其特征在于：高强度紫铜合金焊丝的用途，主要应用于异性金属的焊接，如铜与钢件、铜与不锈钢、铜与灰口铸铁异性金属的焊接或堆焊修补工作。
3、根据权利要求1所述的高强度紫铜合金焊丝，其特征在于：焊丝规格直径在Ф1.2-Ф6mm之间，为粗细两种规格。
4、根据权利要求3所述的高强度紫铜合金焊丝，其特征在于：细丝直径为Ф1.2-Ф3.2mm的焊丝，制成盘形焊丝，主要应用于自动氩弧焊，半自动氩弧焊焊接。
5、根据权利要求3所述的高强度紫铜合金焊丝，其特征在于：粗焊丝直径为Ф3.2-Ф6mm，制成圆形焊丝，主要应用于手把氩弧焊、气焊、修补。
CN 200410021089 2004-01-19 2004-01-19 高强度紫铜合金焊丝及其用途 Expired - Fee Related CN1268469C (zh)