CN101342645B - 高等级管线钢用高强度高韧性高焊速埋弧焊丝 - Google Patents

高等级管线钢用高强度高韧性高焊速埋弧焊丝 Download PDF

Info

Publication number
CN101342645B
CN101342645B CN 200810005040 CN200810005040A CN101342645B CN 101342645 B CN101342645 B CN 101342645B CN 200810005040 CN200810005040 CN 200810005040 CN 200810005040 A CN200810005040 A CN 200810005040A CN 101342645 B CN101342645 B CN 101342645B
Authority
CN
China
Prior art keywords
percent
welding
welding wire
submerged arc
arc welding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 200810005040
Other languages
English (en)
Other versions
CN101342645A (zh
Inventor
陈延清
杨忠文
王全礼
毕宗岳
张飞虎
牛辉
邱利
张锦刚
董现春
张峰
陈涛
谈树美
张永强
贾培新
郭占山
张晓峰
鞠建斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Group Co Ltd
Baoji Petroleum Steel Pipe Co Ltd
Original Assignee
Shougang Corp
Baoji Petroleum Steel Pipe Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Corp, Baoji Petroleum Steel Pipe Co Ltd filed Critical Shougang Corp
Priority to CN 200810005040 priority Critical patent/CN101342645B/zh
Publication of CN101342645A publication Critical patent/CN101342645A/zh
Application granted granted Critical
Publication of CN101342645B publication Critical patent/CN101342645B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高等级管线钢用高强度高韧性高焊速埋弧焊丝，由下述Wt％的成份组成：C 0.03-0.09，Si 0.208-0.30，Mn 1.70-2.30，P＜0.010，S＜0.008，Ti 0.04-0.09，Mo 0.368-0.70，B 0.0031-0.009，Zr 0.001-0.003，余量为Fe。本发明通过调整焊丝中的碳、锰含量，并添加Mo、Ti、B、稀土其它微量元素，达到了焊接X80钢级焊缝所需的高焊速、高强度、高韧性的需要。本发明与F80焊剂匹配能保证焊缝金属具有高强度的同时具有高韧性及良好的工艺性能。

Description

高等级管线钢用高强度高韧性高焊速埋弧焊丝
技术领域
本发明涉及一种高等级管线钢用高强度高韧性高焊速埋弧焊丝。
背景技术
由于X80级管线钢的碳含量较低，材料金相组织占绝大部份的是针状铁素体，为了使焊缝的性能与母材的性能相匹配，必须在保证焊缝强度的同时保证焊缝的韧性。但是随着母材和焊丝碳含量的降低便会引起焊缝的强度下降。因此，必需添加固熔强化元素以达到强化焊缝的作用，同时又不影响焊缝的韧性。
发明内容
本发明提供一种高等级管线钢用高强度高韧性高焊速埋弧焊丝，适用于高速度焊接大壁厚X80级管线钢产品。通过调整焊丝中的碳、锰含量，并添Mo、Ti、B、Zr等微量元素，达到了焊接X80钢级焊缝所需的高焊速、高强度、高韧性的需要。
本发明在降低碳含量的同时增加Mn、Mo等固溶强化的元素，保证焊缝金属具有高强度；同时添加Ti元素形成TiN，细化晶粒，提高韧性；加入B元素以升高先共析铁素体形核能量，消除晶粒边界铁素体和铁素体侧板条的形成，在焊缝区获得更多的针状体素体，使焊缝的韧性得到保证。加入Zr元素以升高先析铁素体形核能量，细化晶粒，消除晶粒边界铁素体和侧板条铁素体的形成。添加Si元素的主要作用是增加焊缝金属流动性。
本发明由下述Wt％的成份组成：C 0.03-0.09，Si 0.208-0.30，Mn1.70-2.30，P＜0.010，S＜0.008，Ti 0.04-0.09，Mo 0.368-0.70，B0.0031-0.009，Zr 0.001-0.003，余量为Fe。
本发明与F80焊剂、SJ101焊剂及其它高等级管线钢焊接专用焊剂匹配均能保证焊缝金属具有高强度的同时具有高韧性及良好的工艺性能。
本发明具有的优点和效果：
1、本发明(H80焊丝)与本申请人生产的F80焊剂匹配用于国产X80级管线钢焊接得到的焊缝性能如下(详见附件一：H80埋弧焊焊丝试验总结报告)：
①焊缝的抗拉强度σb≥700Mpa；CVN-10℃(平均值)≥100J。
②焊缝的组织为少量F+AF+少量P，其中大量为针状铁素体组织。
2、本发明与F80焊剂匹配，焊缝有较好的机械性能。熔敷金属的屈服强度σs＝550-660MPa，并具有较高的低温韧性。
3、本发明与F80焊剂匹配，具有良好的工艺性能。在X80钢高钢级、15mm以上大壁厚钢管焊接中，焊速可达1.5-2.0m/min，焊缝表面光滑、脱渣性好。
4、本发明适应性强，可用于国内各钢厂X80卷板焊接，焊缝性能稳定。
具体实施方式：
本发明实施例一。
1、焊丝成分(余量为Fe)：
  成分   C   Si   Mn   Mo   Ti   B   Zr   S   P
  含量(Wt％)   0.04   0.268   1.75   0.368   0.072   0.0031   0.0012   0.005   0.009
2、冶炼工艺：采用脱硫铁水，控制入炉铁水硫含量，选用S、P含量低的原材料，采用转炉炼钢和顶底复合吹炼工艺，将冶炼终点的C、S、P控制在较低的水平，经脱氧合金化后，采用LF炉等炉外精炼工艺，添加Mn、Si、Mo、Ti、B、Zr等微量元素，冶炼出成分符合要求的钢水，钢水经品种铸机全保护浇铸成连铸坯，连铸坯经高速无扭轧机轧制成Φ5.5mm的盘条。盘条经剥壳-酸洗-涂硼砂-拔丝-镀铜制成Φ4mm或Φ3.2mm成品焊丝。
3、焊丝熔敷金属试验力学性能(详见附件二：H80焊丝+F80焊剂熔敷金属试验报告)：
Figure GSB00000069445500031
本发明实施例二。
1、焊丝成分(余量为Fe)：
  成分   C   Si   Mn   Mo   Ti   Zr   B   S   P
  含量(Wt％)   0.05   0.218   1.79   0.48   0.062   0.002   0.004   0.004   0.008
2、冶炼工艺与实施例一相同。
3、焊丝熔敷金属试验力学性能：
Figure GSB00000069445500032
本发明实施例三。
1、焊丝成分(余量为Fe)：
  成分   C   Si   Mn   Mo   Ti   Zr   B   S   P
  含量(Wt％)   0.056   0.208   1.82   0.41   0.082   0.003   0.0035   0.005   0.009
2、冶炼工艺与实施例一相同。
3、焊丝熔敷金属试验力学性能：
Figure GSB00000069445500033

Claims (1)

1.一种高等级管线钢用高强度高韧性高焊速埋弧焊丝，其特征是所述焊丝由下述Wt％的成份组成：C 0.03-0.09，Si 0.208-0.30，Mn 1.70-2.30，P＜0.010，S＜0.008，Ti 0.04-0.09，Mo 0.368-0.70，B 0.0031-0.009，Zr0.001-0.003，余量为Fe。
CN 200810005040 2008-01-08 2008-02-01 高等级管线钢用高强度高韧性高焊速埋弧焊丝 Active CN101342645B (zh)