CN1554799A - Process for coating aluminium film and protective film for automobile reflector - Google Patents
Process for coating aluminium film and protective film for automobile reflector Download PDFInfo
- Publication number
- CN1554799A CN1554799A CNA2003101127533A CN200310112753A CN1554799A CN 1554799 A CN1554799 A CN 1554799A CN A2003101127533 A CNA2003101127533 A CN A2003101127533A CN 200310112753 A CN200310112753 A CN 200310112753A CN 1554799 A CN1554799 A CN 1554799A
- Authority
- CN
- China
- Prior art keywords
- film
- matrix
- protective film
- vacuum chamber
- film coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to automobile lamp film coating technology, and is the once completed process of aluminum film and protecting film under vacuum condition for the reflector and decorating ring with iron, BMC, ABS, PC and other base material. The technological process includes surface cleaning, stoving, spraying priming lacquer, stoving, vacuum evaporation to coating aluminum film and vacuum coating of protecting film. The once completion of aluminum film and protecting film can avoid oxidation of the aluminum film and raise film performance and lamp quality.
Description
Affiliated technical field
The present invention relates to the coating technique field, especially a kind ofly under vacuum condition, aluminize and the one step completed technology of protective film coating as the speculum and the case ring of plated film base material with materials such as ironware, BMC, ABS, PC.
Background technology
The wide range that protective film coating technology relates to all has a lot of application on automobile lamp industry and plastic surface metalation decorating film.The protective membrane of automobile lamp is after the vacuum evaporated aluminium film finishes at present; film surface manually sprays dope layer as protective membrane in atmosphere; aluminum membranous layer must be subjected to oxidation in atmosphere like this; reduced the performance of rete; and the chemistry painting industry chemical property instability of spray; often have send out color and under uviolizing xanthochromic wretched insufficiency, the stability of artificial spray is not high in addition, can cause defectives such as coating sagging.Be subjected to the restriction of environment purification, the protective membrane of spraying plating tends to cause particle, influences the attractive in appearance of light fixture.Existing automobile speculum aluminium plating film protective film coating technology can not adapt to growing more and more higher to the automobile lamp specification of quality of automobile industry.
Summary of the invention
In order to overcome the deficiency of existing protective film coating technology, the purpose of this invention is to provide and a kind ofly under vacuum condition, aluminize and the one step completed technology of protective film coating as the reflector and the case ring of plated film base material with materials such as ironware, BMC, ABS, PC.
The technical solution adopted for the present invention to solve the technical problems is: automobile speculum aluminium plating film protective film coating technology has following technical process: a. surface cleaning, in water purification and the scavenging solution and back is carried out surface cleaning with ultrasonic wave to matrix; B. oven dry is dried the matrix after cleaning with baking box; C. spray base carries out spray base to needing the plated film place on the matrix; D. oven dry is put into baking box with the matrix behind the spray base and is dried; E. the AM aluminum metallization film is put into vacuum chamber AM aluminum metallization film with the matrix that has sprayed after priming paint is dried; F. protective film coating; earlier with monomer material in airtight tank body; temperature is 26～30 ℃; pressure is 0.8～0.9 normal atmosphere, evaporates into gas, fills into vacuum chamber by certain flow then; pressure is 20～50Pa in the vacuum chamber; in the environment of ion glow discharge, the matrix aluminium film surface forms thin film, and the aluminium film surface that has plated is protected under vacuum condition.
Further: matrix must continue protective film coating under vacuum condition after the AM aluminum metallization film finishes in vacuum chamber, and the used monomer of protective film coating forms protective membrane under vacuum chamber glow discharge condition.
Further: the monomer material composition is hexamethyldisiloxane or claims hexamethyldisiloxane that molecular formula is:
The monomer boiling point is 101 ℃.
Automobile speculum aluminium plating film protective film coating technology of the present invention, matrix aluminium plating film and protective film coating are finished at vacuum condition next time, avoid the aluminium film to be subjected to oxidation in atmosphere, have improved the performance of rete; Spray monomer stable chemical performance, what overcome that the chemistry painting industry chemical property instability of original spray causes sends out color and xanthochromic deficiency under uviolizing; Effectively overcome the deficiency that artificial spray causes sagging easily; Plate the good looking appearance of back automobile lamp, improved the yield rate of automobile lamp.
Embodiment
With materials such as ironware, BMC, ABS, PC as automobile speculum aluminium plating film protective film coating technologies such as the reflector of plated film base material and case rings, have following technical process: a. surface cleaning, in water purification and the scavenging solution and back is carried out surface cleaning with ultrasonic wave to matrix; B. oven dry is dried the matrix after cleaning with baking box; C. spray base carries out spray base to needing the plated film place on the matrix; D. oven dry is put into baking box with the matrix behind the spray base and is dried; E. the AM aluminum metallization film is put into vacuum chamber AM aluminum metallization film with the matrix that has sprayed after priming paint is dried; F. protective film coating; earlier with monomer material in airtight tank body; temperature is 26～30 ℃; pressure is 0.8～0.9 normal atmosphere, evaporates into gas, fills into vacuum chamber by certain flow then; pressure is 20～50Pa in the vacuum chamber; in the environment of ion glow discharge, the matrix aluminium film surface forms thin film, and the aluminium film surface that has plated is protected under vacuum condition.
Matrix must continue protective film coating under vacuum condition after the AM aluminum metallization film finishes in vacuum chamber, and the used monomer of protective film coating forms protective membrane under vacuum chamber glow discharge condition.
The monomer material composition is hexamethyldisiloxane or claims hexamethyldisiloxane that molecular formula is:
The monomer boiling point is 101 ℃.
Automobile speculum aluminium plating film protective film coating technology of the present invention, matrix aluminium plating film and protective film coating are finished at vacuum condition next time, avoid the aluminium film to be subjected to oxidation in atmosphere, have improved the performance of rete; Spray monomer stable chemical performance, what overcome that the chemistry painting industry chemical property instability of original spray causes sends out color and xanthochromic deficiency under uviolizing; Effectively overcome the deficiency that artificial spray causes sagging easily; Plate the good looking appearance of back automobile lamp, improved the yield rate of automobile lamp.
Claims (3)
1. automobile speculum aluminium plating film protective film coating technology is characterized in that: have following technical process:
A. surface cleaning is carried out surface cleaning with ultrasonic wave to matrix with in water purification and the scavenging solution and back;
B. oven dry is dried the matrix after cleaning with baking box;
C. spray base carries out spray base to needing the plated film place on the matrix;
D. oven dry is put into baking box with the matrix behind the spray base and is dried;
E. the AM aluminum metallization film is put into vacuum chamber AM aluminum metallization film with the matrix that has sprayed after priming paint is dried;
F. protective film coating; earlier with monomer material in airtight tank body; temperature is 26～30 ℃; pressure is 0.8～0.9 normal atmosphere, evaporates into gas, fills into vacuum chamber by certain flow then; pressure is 20～50Pa in the vacuum chamber; in the environment of ion glow discharge, the matrix aluminium film surface forms thin film, and the aluminium film surface that has plated is protected under vacuum condition.
2, automobile speculum aluminium plating film protective film coating technology according to claim 1; it is characterized in that: matrix is after the AM aluminum metallization film finishes in vacuum chamber; must continue protective film coating under vacuum condition, the used monomer of protective film coating forms protective membrane under vacuum chamber glow discharge condition.
3, automobile speculum aluminium plating film protective film coating technology according to claim 1 is characterized in that: described monomer material composition is hexamethyldisiloxane or claims hexamethyldisiloxane that molecular formula is:
The monomer material boiling point is 101 ℃.