CN1546181A - Degradable material capable of guiding the regeneration and renovation process of hard tissue and its preparation - Google Patents
Degradable material capable of guiding the regeneration and renovation process of hard tissue and its preparation Download PDFInfo
- Publication number
- CN1546181A CN1546181A CNA2003101173832A CN200310117383A CN1546181A CN 1546181 A CN1546181 A CN 1546181A CN A2003101173832 A CNA2003101173832 A CN A2003101173832A CN 200310117383 A CN200310117383 A CN 200310117383A CN 1546181 A CN1546181 A CN 1546181A
- Authority
- CN
- China
- Prior art keywords
- solution
- chitosan
- acid
- collagen
- concentration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a degradable material for conducting hard tissue regeneration and renovation, and its preparation method which comprises, using degradable biomaterial collagen, chitosan or hydroxyl chitosan, tertiary calcium phosphate or hydroxyapatite as principal raw material, preparing acid solution and suspending liquid, mixing to prepare hard tissue filler, wherein the prepared biological material has good compatibility with the wound tissue.
Description
Technical field
The present invention relates to a kind of biological engineering material and preparation method thereof, relate in particular to the regenerated degradation material of a kind of hard tissue repair, belong to the biological engineering material technical field.
Background technology
Sclerous tissues's (bone, tooth) repairs in the past few decades, although proposed many kind reparation approach, comprises and utilizes tissue engineering product [Langer R, et al.Science, 1993; 260:920-926], gene therapy [Mulligan RC, et al.Science, 1993; 260-932] etc.But 70% bone alternate material still uses from body bone or allograph bone clinically, makes patient face high operation syndrome and infection rate.And various metals, pottery or polymethyl methacrylate bone cement etc. biocompatibility, biological activity, biodegradability and and the aspects such as mechanics matching of host bone separately shortcoming is all arranged.
In recent years, the applied research of hard tissue engineering suddenly launches at a plurality of fields paulins such as orthopedics, oral surgery and cranio-facial surgeries.The research relevant with hard tissue engineering mainly concentrates on three aspects: the basic research of signaling molecule (as skeletal growth factor, bone-inducing factor), various bone alternate materials are the research of carrier, relate to the clinical trial of bone morphogenetic protein(BMP) (BMP).Wherein manufacturing and designing novel bone alternate material is current key.Collagen is the main component of sclerous tissues's organic matter, and high temperature can cause its degeneration.Hydroxyapatite is the main component of sclerous tissues's inanimate matter, these two kinds of materials have been widely used in the reparation of sclerous tissues, referring to [LIUS.New mineralized collagen membrane useful for guided tissue regeneration e.g.for covering bonedefects, for soft tissue flaps over bone grafts, for skin wound healing and for skin sealingWO200115711-A1] and patent " preparation method of nanometer phase calcium-phosphorus salt/collagen/polylactic acid bone composite material " (publication number CN1272383).But the preparation method complexity of above-mentioned material costs an arm and a leg, and is difficult for being received by masses.At present, the annual volume of whole world hard tissue repair and substitution material is about 2,100,000,000 dollars of [Suchanek W, et al.Processing and propertiesof hydroxyapatite-based biomaterials for use as hard tissue replacement implants.J Mater Res, 1998; 13:94-117].Estimate that according to the U.S. relate to the metathetical surgical intervention of bone its domestic every year and surpass 1,000,000 person-times, and the treatment of symptoms such as osteoporosis is only limited to take medicines such as calcium tablet, vitamin, hormone, therapeutic effect is very poor.Therefore exploitation novel or improved hard tissue repairing material is remained an urgent demand of great market.
Chitosan is a series of products behind the chitin deacetylase, is to be only second to cellulosic second largest class polysaccharide on the earth.This alkaline mucopolysaccharide has distinctive molecular structure feature, chemical property and biological function.As excellent biological compatibility and biodegradability, catabolite is N-acetylglucosamine and the glucosamine nontoxic to human body, the intermediate product that produces in the degradation process does not accumulate in vivo, no immunogenicity [Jiang Xuesong, Wang Bosheng etc. biomedical engineering's magazine, 1996:13 (4): 353.], antibiotic, antiinflammatory, hemostasis, promotion wound healing etc.In recent years, along with going deep into extensive of research, chitosan has been widely used in biomedical sector, as dialyzer, absorbable suture, drug release carrier, fixed enzyme vector etc.Some project has had productive value and Practical significance.And carboxymethyl chitosan, phosphonized chitosan are the derivant of chitosan, and the phosphorylation chitin is the derivant of chitin.These several derivants all have very strong chelating ability to calcium ion, have unique effect aspect induced osteogenesis.
Summary of the invention
The objective of the invention is with degradable biological material collagen, chitosan, calcium phosphate (or hydroxyapatite) is primary raw material, prepare a kind of guiding hard tissue repair or regenerated bulk, tubulose, bar-shaped, membranaceous or gel-like material, this material not only preparation technology is simple, cost is low, and the compatibility of prepared biomaterial and wound tissue is good, have excellent anti-bacterium capability and induced osteogenesis activity, and easy to use, be easy to be extended and applied.
Technical scheme of the present invention is as follows: a kind of degradation material that guides hard tissue regeneration to repair is characterized in that this material can prepare by following step:
(1) collagen and chitosan or carboxymethyl chitosan are dissolved in respectively in the acid solution, are made into concentration and are 1～5% solution; Calcium phosphate, calcium hydrogen phosphate, dalcium biphosphate, calcium deficiency apatite or hydroxyapatite powder are added in the acid solution, make concentration and be 10～200% suspension;
(2) suspension is joined in the mixed solution of collagen and chitosan solution or collagen and carboxymethyl chitosan by 1～10% volume ratio, uniform mixing makes gelatinous mixture; Wherein collagen and chitosan solution or collagen are 1～100: 100～1 with the mixed volume ratio of carboxymethyl chitosan sugar juice;
(3) above-mentioned gelatinous mixture is regulated pH value to 5～8 with sodium bicarbonate, the sterilization back is standby; Or pour gelatinous mixture in the container airing or lyophilizing, make block, bar-shaped, tubulose or film material, put into cross-linking agent 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride buffer then, or handle as solidification liquid with ammonia, ammonia/ethanol, ammonia/acetone, ammonia hydroxide/methanol mixed liquor, after water dashes, airing or lyophilizing again, the sterilization back is standby.
It is that 0.5～10% hyaluronate sodium, concentration are that 0.5～10% bone morphogenetic protein(BMP) water or normal saline suspension or concentration are 0.5～10% parathyroid hormone normal saline suspension that the present invention also can be in the gelatinous mixture in the described step (2) adds concentration by 1～10% volume ratio, and wherein the pH value of the solution of hyaluronate sodium can be adjusted in 1～4 scope with hydrochloric acid.
On the basis of such scheme, the present invention also can be in above-mentioned steps (3) compound phosphoric acid chitin or phosphonized chitosan again in the sample before secondary airing or the lyophilizing, its method is that phosphorylation chitin or phosphonized chitosan are dissolved in distilled water or the acid solution, make concentration and be 0.1～10% aqueous solution or acid solution, sample after water dashed is put into wherein, adsorbed airing or lyophilizing then 2 minutes to 2 hours.
Acid solution described in the present invention adopts any in dilute hydrochloric acid, acetic acid, formic acid, propanoic acid, lactic acid or the maleic acid.
The thickness of the membrane material of the present invention's preparation is 0.1～5 millimeter; The diameter of club-shaped material is 0.1～10 centimetre; The internal diameter of tubular material is 0.1～5 centimetre, 0.2～10 centimetre of external diameter.
A kind of preparation method that guides the degradation material of hard tissue regeneration reparation provided by the present invention, this method is carried out as follows:
(1) collagen and chitosan or carboxymethyl chitosan are dissolved in respectively in the acid solution, are made into concentration and are 1～5% solution; Calcium phosphate, calcium hydrogen phosphate, dalcium biphosphate, calcium deficiency apatite or hydroxyapatite powder are added in the acid solution, make concentration and be 10～200% suspension;
(2) suspension is joined in the mixed solution of collagen and chitosan solution or collagen and carboxymethyl chitosan by 1～10% volume ratio, uniform mixing makes gelatinous mixture; Wherein collagen and chitosan solution or collagen are 1～100: 100～1 with the mixed volume ratio of carboxymethyl chitosan sugar juice;
(3) above-mentioned gelatinous mixture is regulated pH value to 5～8 with sodium bicarbonate, the sterilization back is standby; Or pour gelatinous mixture in the container airing or lyophilizing, make block, bar-shaped, tubulose or film material, put into cross-linking agent 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride buffer then, or handle as solidification liquid with ammonia, ammonia/ethanol, ammonia/acetone, ammonia hydroxide/methanol mixed liquor, after water dashes, airing or lyophilizing again, the sterilization back is standby.
In the preparation method of invention, adding concentration by 1～10% volume ratio in the gelatinous mixture in the described step (2) is that 0.5～10% hyaluronate sodium, concentration are that 0.5～10% bone morphogenetic protein(BMP) water or normal saline suspension or concentration are 0.5～10% parathyroid hormone normal saline suspension, and wherein the pH value of the solution of hyaluronate sodium can be adjusted in 1～4 scope with hydrochloric acid.
In above-mentioned preparation method, the present invention also compound phosphoric acid chitin or phosphonized chitosan again in the sample before secondary airing or the lyophilizing in described step (3), its method is that phosphorylation chitin or phosphonized chitosan are dissolved in distilled water or the acid solution, make concentration and be 0.1～10% aqueous solution or acid solution, sample after water dashed is put into wherein, adsorbed 2 minutes to 2 hours, then airing or freeze in.
The present invention compared with prior art, have the following advantages and the salience effect: it is base stock that the present invention adopts the good degradable biomaterial collagen of histocompatibility, chitosan, calcium phosphate (or hydroxyapatite) or hyaluronate sodium, also can add somatomedin such as bone morphogenetic protein(BMP).Preparation technology is simple, and cost is low; Prepared sclerous tissues repaiies material and not only can be used as gel state and be injected directly into pathological changes or defect, also can make membranaceous, block, tubulose, shape such as bar-shaped promotes hard tissue repair as implant or guiding film.Show through cell experiment and zoopery: this material can (comprise dentistry, bone surgery etc.) in vivo generally to be used, be a kind of multifunctional material hard tissue repair, antimicrobial, degradation in vivo adjustable-speed that promotes and induce, in surgical operation, be with a wide range of applications.
The specific embodiment
Employed calcium phosphate among the present invention (comprising α type, β type or indefinite form), calcium hydrogen phosphate, dalcium biphosphate, calcium deficiency apatite or its particle diameter of hydroxyapatite by nanometer to micron order.Wherein hydroxyapatite and calcium phosphate can be formed by high temperature sintering, also can be got by normal-temperature reaction.
The following examples will the present invention will be further described.
Embodiment 1:
With collagen and deacetylation be 70%, molecular weight is that 200000 daltonian chitosans are dissolved in respectively in 2% the glacial acetic acid solution, makes concentration and be 1% collagen, chitosan solution, discontinuous degassing, both are even by 1: 1 mixed.Calcium phosphate powder is added in 2% the glacial acetic acid solution, makes concentration and be 10% suspension; By 1% volume ratio the calcium phosphate suspension is joined in the collagen/chitosan mixed liquor mix homogeneously then.This gel state mixture can be used sodium bicarbonate (NaHCO
3) adjusting pH value to 5, Co
60The sterilization back is standby.This gel-like material can be injected directly into the position that needs reparation with needle tubing.
Embodiment 2:
With collagen and deacetylation be 80%, molecular weight is that 100000 daltonian carboxymethyl chitosans are dissolved in the lactic acid solution respectively, make concentration and be 2% collagen, carboxymethyl chitosan sugar juice, discontinuous degassing, collagen and carboxymethyl chitosan sugar juice are pressed 100: 1 volume ratio mix homogeneously.Hydroxyapatite powder is added in the lactic acid solution, makes concentration and be 100% suspension; By 10% volume ratio the hydroxyapatite suspension is joined in collagen/carboxymethyl chitosan mixed liquor mix homogeneously then.Adding concentration by 1% volume ratio again is 0.5% hyaluronate sodium acid solution.Wherein sodium hyaluronate solution is 1 with hydrochloric acid adjusting pH value, so that fully mix with collagen/carboxymethyl chitosan sugar juice.Use sodium bicarbonate (NaHCO then
3) regulate pH value to 8, with ozonization, standby.
Embodiment 3
With collagen and deacetylation be 80%, molecular weight is that 100000 daltonian chitosans are dissolved in the lactic acid solution respectively, make concentration and be 2% collagen, chitosan solution, discontinuous degassing, collagen and chitosan solution are pressed 100: 1 volume ratio mix homogeneously.The calcium hydrogen phosphate powder is soluble in water, make concentration and be 200% suspension; By 10% volume ratio the calcium hydrogen phosphate suspension is joined in the collagen/chitosan mixed liquor mix homogeneously then.Add the suspension that concentration is 1% bone morphogenetic protein(BMP) water by 1% volume ratio again.Use sodium bicarbonate (NaHCO then
3) adjusting pH value to 6, gamma-radiation sterilization, standby.
Embodiment 4:
Chitosan with 5% (deacetylation is 98%) formic acid solution and 5% collagen formic acid solution are added to hydroxyapatite in the formic acid solution by powder in 1: 100 ratio mixing, make concentration and be 10% suspension; By 1% volume ratio 10% hydroxyapatite suspension is joined in the collagen/chitosan mixed liquor mix homogeneously then.Chitosan/collagen/hydroxyapatite the mixture of preparation is sloughed bubble be divided in lyophilizing film forming in the container, the thickness of film is 0.1 millimeter.Ammonia with 25% soaked after 5 minutes, and distilled water flushing is clean, lyophilizing again, Co
60Sterilization, standby.
Embodiment 5:
With collagen, deacetylation be 50%, molecular weight is that 300000 daltonian chitosans are dissolved in respectively in the hydrochloric acid solution of 0.5M, make 1% solution, and press 2: 1 volume ratio mix homogeneously, the hydrochloric acid of the hyaluronate sodium with 0.5% (0.5M) solution joins in the mixed solution of above-mentioned collagen and chitosan with 1% volume ratio; Add volume ratio again and be 1% nanocrystalline hydroxyapatite concentration and be 100% suspension, mix homogeneously is packed in the concentric annular mould, freezingly rapidly freezes, lyophilizing, and making internal diameter is 0.1 centimetre, 0.2 centimetre of tubular material of external diameter.After 20 minutes, distilled water flushing is clean, lyophilizing again, Co with ammonia/acetone (9: 1) immersion
60Sterilization, standby.
Embodiment 6:
With collagen, deacetylation is 90%, molecular weight is for being 80000 daltonian chitosans, hyaluronate sodium is dissolved in respectively in the acetum of 0.1M, make 5% the collagen and the sodium hyaluronate solution of chitosan solution and 10%, the volume ratio of pressing 1: 20 is with collagen and chitosan solution mix homogeneously, the sodium hyaluronate solution that adds volume ratio 10% again, add volume ratio then and be 10% concentration and be 200% calcium hydrogen phosphate suspension, in the concentric annular of packing into behind the mix homogeneously mould, freezing rapidly freezing, lyophilizing, making internal diameter is 0.2 centimetre, 10 centimetres of tubular materials of external diameter.After 20 minutes, distilled water flushing is clean with ammonia/ethanol (10: 1) immersion.The phosphorylation chitin is dissolved in distilled water, makes concentration and be 0.1 aqueous solution, the sample after above water dashes is put into wherein, adsorbs lyophilizing again, Co 30 minutes
60Sterilization, standby.
Embodiment 7:
With collagen, deacetylation be 80%, molecular weight is that 150000 daltonian chitosans are dissolved in respectively in the maleic acid solution of 0.5M, make 3% solution, and by 2: 1 mix homogeneously, add 1% scarce epiglaubite suspension again, pour that airing becomes bar-shaped in the mould into.The diameter of rod be the diameter of club-shaped material be 0.1 centimetre soak 2 hours minutes with 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride/carboxyl butanimide/2-morpholine ethylsulfonic acid buffer after, distilled water flushing is clean, again airing, Co
60Sterilization, standby.
Attached, the preparation of 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride/carboxyl butanimide/2-morpholine ethylsulfonic acid buffer: get the 0.533 single hydration 2-morpholine-ethylsulfonic acid of gram (MEC) and be dissolved in 50 ml deionized water, add 0.4 gram 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride (EDC) and 0.096 gram N-Hydroxysuccinimide, mix homogeneously.
Embodiment 8:
With collagen, deacetylation be 80%, molecular weight is that 150000 daltonian chitosans are dissolved in respectively in the maleic acid solution of 0.5M, make 4% solution, and by 1: 2 mix homogeneously, add 10% scarce epiglaubite suspension again, pour that airing becomes bar-shaped in the mould into.The diameter of club-shaped material is 10 centimetres.After soaking 2 minutes with 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride/carboxyl butanimide/2-morpholine ethylsulfonic acid buffer, distilled water flushing is clean, it is 1% phosphonized chitosan aqueous solution that sample after above water dashed is put into concentration, adsorbs lyophilizing again, Co 4 hours
60Sterilization, standby.
Embodiment 9:
With collagen, deacetylation be 85%, molecular weight is for being that 200000 daltonian chitosans are dissolved in the lactic acid respectively, make 5% solution, and by 1: 100 mix homogeneously, add volume ratio again and be 5% nanometer hydroxyapatite suspension and 1% bone morphogenetic protein(BMP) suspension, pack into behind the mix homogeneously freezingly rapidly in the mould freeze, lyophilizing, make bulk sample.Ammonia with 30% soaked after 5 minutes, and distilled water flushing is clean.Phosphonized chitosan is dissolved in 1% acetum, and making concentration is 10% acid solution, and the sample after above water is dashed is put into wherein, adsorbs lyophilizing again, Co 30 minutes
60Sterilization, standby.
Embodiment 10:
Collagen and carboxymethyl chitosan are dissolved in respectively in the lactic acid solution, make concentration and be 2% collagen, chitosan solution, discontinuous degassing, both are even by 1: 100 mixed.The biphosphate calcium powder is added in the lactic acid solution, makes concentration and be 10% suspension; By 10% volume ratio the dalcium biphosphate suspension is joined in the collagen/chitosan mixed liquor mix homogeneously then.10% add the bone morphogenetic protein(BMP) suspension that concentration is 0.5% hyaluronate sodium and 0.5% respectively by volume again.Wherein the solution pH value acceptable salts acid of hyaluronate sodium is adjusted in 1, so that mix with collagen/chitosan solution.Use sodium bicarbonate (NaHCO then
3) regulate pH value to 7.4, with ozonization, standby.
Embodiment 11:
With collagen, deacetylation be 85%, molecular weight is that 200000 daltonian chitosans are dissolved in the lactic acid respectively, make 1% solution, and by 100: 1 mix homogeneously, the normal saline solution that adds the parathyroid hormone of 5% nanometer hydroxyapatite suspension and 0.5% more freezingly rapidly behind the mix homogeneously freezes, lyophilizing.Ammonia with 30% soaked after 5 minutes, and distilled water flushing is clean, lyophilizing again, Co
60Sterilization, standby.
Embodiment 12:
With collagen, deacetylation be 85%, molecular weight is that 200000 daltonian chitosans are dissolved in the lactic acid respectively, make 2% solution, and by 1: 1 mix homogeneously, the normal saline solution that adds the parathyroid hormone of 5% nanometer hydroxyapatite suspension and 10% more freezingly rapidly behind the mix homogeneously freezes, lyophilizing.After soaking 5 minutes with 30% ammonia, distilled water flushing is clean, and the phosphorylation chitin is dissolved in distilled water, makes concentration and be 10% aqueous solution, and the sample after above water dashes is put into wherein, adsorbs lyophilizing again, Co 2 hours
60Sterilization, standby.
Embodiment 13:
Carboxymethyl chitosan with 2% (deacetylation is 98%, and molecular weight is 100000) formic acid solution and 3% collagen formic acid solution are added to hydroxyapatite in the formic acid solution by powder in 1: 2 ratio mixing, make concentration and be 10% suspension; By 1% volume ratio the hydroxyapatite suspension is joined in the collagen/chitosan mixed liquor mix homogeneously then.Adding concentration by 10% volume ratio again is 10% bone morphogenetic protein(BMP) normal saline suspension.Chitosan/collagen/hydroxyapatite the mixture of preparation is sloughed bubble be divided in lyophilizing film forming in the container, the thickness of film is 5 millimeters.Ammonia with 25% soaked after 5 minutes, and distilled water flushing is clean, lyophilizing again, Co
60Sterilization, standby.
Claims (9)
1. degradation material that guides hard tissue regeneration to repair is characterized in that this material can prepare by following step:
(1) collagen and chitosan or carboxymethyl chitosan are dissolved in respectively in the acid solution, are made into concentration and are 1～5% solution; Calcium phosphate, calcium hydrogen phosphate, dalcium biphosphate, calcium deficiency apatite or hydroxyapatite powder are added in the acid solution, make concentration and be 10～200% suspension;
(2) suspension is joined in the mixed solution of collagen and chitosan solution or collagen and carboxymethyl chitosan by 1～10% volume ratio, uniform mixing makes gelatinous mixture; Wherein collagen and chitosan solution or collagen are 1～100: 100～1 with the mixed volume ratio of carboxymethyl chitosan sugar juice;
(3) above-mentioned gelatinous mixture is regulated pH value to 5～8 with sodium bicarbonate, the sterilization back is standby; Or pour gelatinous mixture in the container airing or lyophilizing, make block, bar-shaped, tubulose or film material, put into cross-linking agent 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride buffer then, or handle as solidification liquid with ammonia, ammonia/ethanol, ammonia/acetone, ammonia hydroxide/methanol mixed liquor, after water dashes, airing or lyophilizing again, the sterilization back is standby.
2. according to the described material of claim 1, it is characterized in that: adding concentration by 1～10% volume ratio in the gelatinous mixture in described step (2) is that 0.5～10% hyaluronate sodium, concentration are that 0.5～10% bone morphogenetic protein(BMP) water or normal saline suspension or concentration are 0.5～10% parathyroid hormone normal saline suspension, and wherein the pH value of the solution of hyaluronate sodium can be adjusted in 1～4 scope with hydrochloric acid.
3. according to claim 1 or 2 described materials, it is characterized in that: also compound phosphoric acid chitin or phosphonized chitosan again in the sample in the step (3) before secondary airing or the lyophilizing, its method is that phosphorylation chitin or phosphonized chitosan are dissolved in distilled water or the acid solution, make concentration and be 0.1～10% aqueous solution or acid solution, sample after water dashed is put into wherein, adsorbed airing or lyophilizing then 2 minutes to 2 hours.
4. according to the described material of the arbitrary claim of claim 3, it is characterized in that: described acid solution adopts any in dilute hydrochloric acid, acetic acid, formic acid, propanoic acid, lactic acid or the maleic acid.
5. according to the described material of the arbitrary claim of claim 3, it is characterized in that: the thickness of described membrane material is 0.1～5 millimeter; The diameter of club-shaped material is 0.1～10 centimetre; The internal diameter of tubular material is 0.1～5 centimetre, 0.2～10 centimetre of external diameter.
6. preparation method that guides the degradation material that hard tissue regeneration repairs is characterized in that this method undertaken by following step:
(1) collagen and chitosan or carboxymethyl chitosan are dissolved in respectively in the acid solution, are made into concentration and are 1～5% solution; Calcium phosphate, calcium hydrogen phosphate, dalcium biphosphate, calcium deficiency apatite or hydroxyapatite powder are added in the acid solution, make concentration and be 10～200% suspension;
(2) suspension is joined in the mixed solution of collagen and chitosan solution or collagen and carboxymethyl chitosan by 1～10% volume ratio, uniform mixing makes gelatinous mixture; Wherein collagen and chitosan solution or collagen are 1～100: 100～1 with the mixed volume ratio of carboxymethyl chitosan sugar juice;
(3) above-mentioned gelatinous mixture is regulated pH value to 5～8 with sodium bicarbonate, the sterilization back is standby; Or pour gelatinous mixture in the container airing or lyophilizing, make block, bar-shaped, tubulose or film material, put into cross-linking agent 1-ethyl-(dimethyl aminopropyl)-carbodiimide hydrochloride buffer then, or handle as solidification liquid with ammonia, ammonia/ethanol, ammonia/acetone, ammonia hydroxide/methanol mixed liquor, after water dashes, airing or lyophilizing again, the sterilization back is standby.
7. according to the described material of claim 6, it is characterized in that: adding concentration by 1～10% volume ratio in the gelatinous mixture in described step (2) is that 0.5～10% hyaluronate sodium, concentration are that 0.5～10% bone morphogenetic protein(BMP) water or normal saline suspension or concentration are 0.5～10% parathyroid hormone normal saline suspension, and wherein the pH value of the solution of hyaluronate sodium can be adjusted in 1～4 scope with hydrochloric acid.
8. according to claim 6 or 7 described materials, it is characterized in that: also compound phosphoric acid chitin or phosphonized chitosan again in the sample in the step (3) before secondary airing or the lyophilizing, its method is that phosphorylation chitin or phosphonized chitosan are dissolved in distilled water or the acid solution, make concentration and be 0.1～10% aqueous solution or acid solution, sample after water dashed is put into wherein, adsorbed airing or lyophilizing then 2 minutes to 2 hours.
9. according to the described material of the arbitrary claim of claim 8, it is characterized in that: described acid solution adopts any in dilute hydrochloric acid, acetic acid, formic acid, propanoic acid, lactic acid or the maleic acid.