CN1541966A - Photochromic glass and production method thereof - Google Patents
Photochromic glass and production method thereof Download PDFInfo
- Publication number
- CN1541966A CN1541966A CNA2003101062473A CN200310106247A CN1541966A CN 1541966 A CN1541966 A CN 1541966A CN A2003101062473 A CNA2003101062473 A CN A2003101062473A CN 200310106247 A CN200310106247 A CN 200310106247A CN 1541966 A CN1541966 A CN 1541966A
- Authority
- CN
- China
- Prior art keywords
- photochromic glass
- weight percent
- photochromic
- sio
- tio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The photochromatic glass consists of oxide SiO2, B2O3 and Al2O3 and photochromatic material Ag, CuO, Cl and Br, as well as 3-6 kinds of characterized alkali oxide. Its preparation process includes melting with the standard material mixture inside platinum crucibles at 1420-1480 deg.c, clarifying, stirring at 1150 deg.c, mechanically pressing into lens blank, and finally reheating at 600 deg.c for about 40 min. The photochromatic glass has fast photochromatic rate, ultraviolet resistance and high refractivity.
Description
Affiliated technical field:
The present invention relates to the glass mirror in a kind of optical technology, is a kind of photochromic glass lens blank and production technology thereof.
Background technology:
The photochromic glass eyeglass is well received eyeglass materials, and existing photochromic glass lens blank is to adopt the production method of porcelain platinum continuous smelting to make, and contains oxide S iO usually
2, B
2O
3, Al
2O
3Reach photochromic agent Ag, CuO, compositions such as Cl, Br.Because the problem on raw material constitutes, its change is faded slowly, and specific refractory power is low, and barrier propterty is also poor.
Summary of the invention:
The purpose of this invention is to provide a kind of change and fade soon, specific refractory power height, photochromic glass that barrier propterty is good and production method thereof.
Technical solution of the present invention is:
A kind of photochromic glass comprises oxide S iO
2, B
2O
3, Al
2O
3Reach photochromic agent Ag, CuO, Cl, Br, it is characterized in that: also comprise 3-6 kind basic oxide, wherein the weight percent content of each composition is:
SiO
250-60
B
2O
318-25
Al
2O
35-10
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
All the other are basic oxide.
Basic oxide described in the present invention are K
2O, Na
2O, Li
2O and BaO, ZrO
2, TiO
2In at least 3 kinds.
Basic oxide K2O, Na2O, Li2O and BaO described in the present invention, the shared weight percent of ZrO2, TiO2 are respectively:
K
2O5-10
Na
2O2-5
Li
2O1-5
BaO1-3
ZrO
22-5
TiO
21-3
Can comprise following weight percent composition at least among the present invention:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O
5-10
Na
2O2-5
Li
2O1-5
ZrO
22-5
TiO
21-3
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
Can comprise following weight percent composition at least among the present invention:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Li
2O1-5
BaO1-3
TiO
20-1
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
Also comprise following weight percent composition among the present invention at least:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Na
2O2-5
Li
2O1-5
BaO1-3
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3。
The method of the described photochromic glass of a kind of production claim 1, it is characterized in that: the standard raw materials mixture is put into the many crucibles of full platinum, under 1420-1480 ℃ temperature, found, clarify, then under about 1150 ℃ temperature, stir, mechanical compaction becomes the blank eyeglass again, at last under about 600 ℃ temperature, carry out reheating about 40 minutes, can obtain to can be used for making the blank with photochromic effect of eyeglass.
Beneficial effect of the present invention is: becomes and fades soon, and the specific refractory power height, barrier propterty is good, and especially preventing ultraviolet effect is good.
The present invention is described in further detail below in conjunction with embodiment:
Embodiment:
Embodiment one:
To descend standard raw materials (weight percent) mixture to put into the many crucible continuous production of full platinum:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Na
2O2-5
Li
2O1-5
ZrO
22-5
TiO
21-3
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3。
The above-mentioned raw materials mixture is founded, clarified under 1420-1480 ℃ temperature, then under about 1150 ℃ temperature, stir, mechanical compaction becomes the blank eyeglass again, at last under about 600 ℃ temperature, carry out reheating about 40 minutes, can obtain to can be used for making the blank with photochromic effect of eyeglass.
Embodiment two:
To descend standard raw materials (weight percent) mixture to put into the many crucible continuous production of full platinum:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Li
2O1-5
BaO1-3
TiO
20-1
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3。
The above-mentioned raw materials mixture is founded, clarified under 1420-1480 ℃ temperature, then under about 1150 ℃ temperature, stir, mechanical compaction becomes the blank eyeglass again, at last under about 600 ℃ temperature, carry out reheating about 40 minutes, can obtain to can be used for making the blank with photochromic effect of eyeglass.
Embodiment three:
To descend standard raw materials (weight percent) mixture to put into the many crucible continuous production of full platinum:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Na
2O2-5
Li
2O1-5
BaO1-3
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3。
The above-mentioned raw materials mixture is founded, clarified under 1420-1480 ℃ temperature, then under about 1150 ℃ temperature, stir, mechanical compaction becomes the blank eyeglass again, at last under about 600 ℃ temperature, carry out reheating about 40 minutes, can obtain to can be used for making the blank with photochromic effect of eyeglass.
Claims (7)
1, a kind of photochromic glass comprises oxide S iO
2, B
2O
3, Al
2O
3Reach photochromic agent Ag, CuO, Cl, Br, it is characterized in that: also comprise 3-6 kind basic oxide, wherein the weight percent content of each composition is:
SiO
250-60
B
2O
318-25
Al
2O
35-10
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
All the other are basic oxide.
2, photochromic glass according to claim 1 is characterized in that: basic oxide are K
2O, Na
2O, Li
2O and BaO, ZrO
2, TiO
2In at least 3 kinds.
3, photochromic glass according to claim 2 is characterized in that: basic oxide K2O, Na2O, Li2O, BaO, the shared weight percent of ZrO2, TiO2 are respectively:
K
2O5-10
Na
2O2-5
Li
2O1-5
BaO1-3
ZrO
22-5
TiO
21-3
4, photochromic glass according to claim 3 is characterized in that: comprise following weight percent composition at least:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Na
2O2-5
Li
2O1-5
ZrO
22-5
TiO
21-3
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
5, photochromic glass according to claim 3 is characterized in that: comprise following weight percent composition at least:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Li
2O1-5
BaO1-3
TiO
20-1
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
6, photochromic glass according to claim 3 is characterized in that: comprise following weight percent composition at least:
SiO
250-60
B
2O
318-25
Al
2O
35-10
K
2O5-10
Na
2O2-5
Li
2O1-5
BaO1-3
Ag0.08-0.3
CuO0.002-0.015
Cl0.2-0.6
Br0.05-0.3
7, the method for the described photochromic glass of a kind of production claim 1, it is characterized in that: the standard raw materials mixture is put into the many crucibles of full platinum, under 1420-1480 ℃ temperature, found, clarify, then under about 1150 ℃ temperature, stir, mechanical compaction becomes the blank eyeglass again, at last under about 600 ℃ temperature, carry out reheating about 40 minutes, can obtain to can be used for making the blank with photochromic effect of eyeglass.