CN1539276A - Method for producing ring of guiding thread on fishing rod - Google Patents
Method for producing ring of guiding thread on fishing rod Download PDFInfo
- Publication number
- CN1539276A CN1539276A CNA2003101053667A CN200310105366A CN1539276A CN 1539276 A CN1539276 A CN 1539276A CN A2003101053667 A CNA2003101053667 A CN A2003101053667A CN 200310105366 A CN200310105366 A CN 200310105366A CN 1539276 A CN1539276 A CN 1539276A
- Authority
- CN
- China
- Prior art keywords
- conductor loop
- fishing pole
- pole conductor
- grams per
- density
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A fishing thread guiding ring for fishing rod is made up through segmenting, machining, removing oil, washing, chemical polishing, washing, anodizing, washing, neutralizing, washing, dyeing, washing, closing processing, washing and drying. Its advantages are beautiful appearance and light weight.
Description
Affiliated technical field
The present invention relates to angle the production method of fishing pole accessory, specifically a kind of fishing pole conductor loop and production method.
Background technology
As everyone knows, angling the fishing pole is the utensil of a kind of physical culture, leisure usefulness, the good fishing pole that angles is answered intensity height, good toughness, in light weight and outward appearance is beautiful, the existing conductor loop that angles Guide eye of fishing rod to use is ceramic conductor loop, and its production method is that clay is pulverized, again through moulding, glazing, fire and form, its weak point is that weight is big, appearance color is single, easily fragmentation etc. in assembling and use, in addition, the dimensional accuracy of this conductor loop is wayward, and the finished product rate of production is low.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of fishing pole conductor loop and production method are provided, the finished product rate height that the conductor loop that adopts this method to produce is in light weight, appearance color abundant, produce, in assembling and use, broken phenomenon do not occur.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of fishing pole conductor loop adopts aluminum material to make colored fishing pole conductor loop, and its production stage is:
1, metal tube is carried out segment processing and becomes fishing pole conductor loop blank,
2, fishing pole conductor loop blank is carried out mechanical process, fishing pole conductor loop blank two sides lathe car R arc, and adopt buffing,
3, carry out oil removal treatment again, the prescription of treatment fluid is as follows:
| Composition | Content (grams per liter) |
| Sodium carbonate | 40-50 |
| Tertiary sodium phosphate | 40-50 |
| Sodium silicate | 20-30 |
The treatment fluid temperature is controlled at 60 ℃-80 ℃,
4, clean again, generally adopt water to clean twice,
5, carry out chemical polishing again and handle, the prescription of treatment fluid is as follows:
| Composition | Content (mass percent) |
| Phosphoric acid (density 1,70) | 70-80 |
| Sulfuric acid (density 1,84) | 8-9 |
| Nitric acid (density 1,50) | 8-9 |
| Copper sulphate | 0、01-0、03 |
| Ammonium sulfate | 4-5 |
| Urea | 2-3 |
The treatment fluid temperature is controlled at 100 ℃-120 ℃, and the time is generally at 2 minutes to 3 minutes,
The present invention also can adopt electrochemical polishing treatment, adopt phosphoric acid (density 1,70) 85%-90%, chromic acid 10%-15%, water adjusts that solution density is 1,72-1,74, and temperature is controlled at 75 ℃-80 ℃, and Control of Voltage is at 14V-30V, anodic current density 7-12 peace/square decimeter, time, cathode material generally adopted lead or stainless steel generally at 3-5 minute
6, clean again, generally adopt water to clean twice,
7, carry out anodized again, can adopt the sulfuric acid dc anodizing to handle, also can adopt enamelled anodizing to handle,
When the sulfuric acid dc anodizing is handled, adopt sulfuric acid (density 1,84) 180 grams per liters-200 grams per liter, aluminium ion 5 grams per liters-20 grams per liter, temperature is controlled at 15 ℃-25 ℃, current density 0,8-1,5 peace/square decimeters, Control of Voltage are at 12V-22V, and the time is generally at 35-45 minute, cathode material generally adopts lead or stainless steel, and adopts air to stir
When enamelled anodizing is handled, adopt chromic acid 30 grams per liters-35 grams per liter, boric acid 1-3 grams per liter, temperature is controlled at 40 ℃-50 ℃, current density 2-4 peace/square decimeter, and Control of Voltage is at 40V-80V, time is generally at 40-60 minute, cathode material generally adopts lead or stainless steel, and adopts machinery to stir
8, clean again, generally adopt water to clean twice,
9, carry out neutralisation treatment again, adopt ammoniacal liquor 2-5 grams per liter, the time is 1-2 minute,
10, clean again, generally adopt water to clean twice,
11, the processing of dyeing again can be selected the plain reducing dye of acid dye, direct dyes, alizarin dyes, reactive dye and water-soluble seal ground section etc. for use,
12, clean again, generally adopt water to clean twice,
13, seal processing again, adopt sealer to seal, with constant color, increase corrosion resistance,
14, clean, be dried to fishing pole conductor loop again.
The invention has the beneficial effects as follows: 1, in light weight, fishing pole overall weight is alleviated a lot, the fishing pole is easy to carry, use flexibly 2, beautiful appearance, nearly all color can be painted by electrochemical oxidation, the full tone of light has improved the sight of fishing pole, 3, be difficult for broken owing to adopt metal material, therefore guaranteed with lead on eye bracket or the fishing pole not broken in the installation process, also guaranteed in transportation, not broken in the use, 4, the yield rate height, production cost is low, owing to adopt metal material to be made by machined, scale error is very little, yield rate is very high, install to be very easy to, and leads eye bracket and combines very firm.
Embodiment
Below in conjunction with accompanying drawing the present invention is further described:
A kind of fishing pole conductor loop adopts aluminum material to make colored fishing pole conductor loop, and its production stage is:
1, aluminium matter pipe is carried out segment processing and become fishing pole conductor loop blank, every segment length is greater than the thickness of fishing pole lead ring,
2, fishing pole conductor loop blank is carried out mechanical process, fishing pole conductor loop blank two sides lathe car R arc, and adopt buffing, can carry out turning processing respectively to the cylindrical and the interior circle of fishing pole conductor loop blank in case of necessity, to improve the dimensional accuracy of its inside and outside circle
3, carry out oil removal treatment again, the prescription of treatment fluid is as follows:
| Composition | Content (grams per liter) |
| Sodium carbonate | 40-50 |
| Tertiary sodium phosphate | 40-50 |
| Sodium silicate | 20-30 |
The treatment fluid temperature is controlled at 60 ℃-80 ℃,
4, clean again, generally adopt water to clean twice,
5, carry out chemical polishing again and handle, the prescription of treatment fluid is as follows:
The treatment fluid temperature is controlled at 100 ℃-120 ℃, and the time is generally at 2 minutes to 3 minutes,
| Composition | Content (mass percent) |
| Phosphoric acid (density 1,70) | 70-80 |
| Sulfuric acid (density 1,84) | 8-9 |
| Nitric acid (density 1,50) | 8-9 |
| Copper sulphate | 0、01-0、03 |
| Ammonium sulfate | 4-5 |
| Urea | 2-3 |
The present invention also can adopt electrochemical polishing treatment, adopt phosphoric acid (density 1,70) 85%-90%, chromic acid 10%-15%, water adjusts that solution density is 1,72-1,74, and temperature is controlled at 75 ℃-80 ℃, and Control of Voltage is at 14V-30V, anodic current density 7-12 peace/square decimeter, time, cathode material generally adopted lead or stainless steel generally at 3-5 minute
6, clean again, generally adopt water to clean twice,
7, carry out anodized again, can adopt the sulfuric acid dc anodizing to handle, also can adopt enamelled anodizing to handle,
When the sulfuric acid dc anodizing is handled, adopt sulfuric acid (density 1,84) 180 grams per liters-200 grams per liter, aluminium ion 5 grams per liters-20 grams per liter, temperature is controlled at 15 ℃-25 ℃, current density 0,8-1,5 peace/square decimeters, and Control of Voltage is at 12V-22V, time is generally at 35-45 minute, cathode material generally adopts lead or stainless steel, and adopts air to stir (injecting air in liquid)
When enamelled anodizing is handled, adopt chromic acid 30 grams per liters-35 grams per liter, boric acid 1-3 grams per liter, temperature is controlled at 40 ℃-50 ℃, current density 2-4 peace/square decimeter, and Control of Voltage is at 40V-80V, time is generally at 40-60 minute, cathode material generally adopts lead or stainless steel, and adopts machinery to stir
8, clean again, generally adopt water to clean twice,
9, carry out neutralisation treatment again, adopt ammoniacal liquor 2-5 grams per liter, the time is 1-2 minute,
10, clean again, generally adopt water to clean twice,
11, the processing of dyeing again can be selected the plain reducing dye of acid dye, direct dyes, alizarin dyes, reactive dye and water-soluble seal ground section etc. for use,
12, clean again, generally adopt water to clean twice,
13, seal processing again, adopt sealer to seal, with constant color, increase corrosion resistance,
14, clean, be dried to fishing pole conductor loop again.
Claims (8)
1, a kind of fishing pole conductor loop is characterized in that adopting aluminum material to make colored fishing pole conductor loop.
2, a kind of fishing pole conductor loop according to claim 1 is characterized in that production stage is:
(1), metal tube carried out segment processing become fishing pole conductor loop blank,
(2), fishing pole conductor loop blank is carried out machined, fishing pole conductor loop blank two sides are with lathe car R arc,
(3), again carry out oil removal treatment,
(4), clean again,
(5), again carry out chemical polishing and handle,
(6), clean again,
(7), again carry out anodized,
(8), clean again,
(9), again carry out neutralisation treatment,
(10), clean again,
(11), again the processing of dyeing,
(12), clean again,
(13), again seal processing,
(14), clean, be dried to fishing pole conductor loop again.
3, the production method of a kind of fishing pole conductor loop according to claim 2 is characterized in that the prescription of the treatment fluid that uses in the said oil removal treatment process is as follows:
Composition Content (grams per liter)
Sodium carbonate 40-50
Tertiary sodium phosphate 40-50
Sodium silicate 20-30
The treatment fluid temperature is controlled at 60 ℃-80 ℃.
4, the production method of a kind of fishing pole conductor loop according to claim 2, when it is characterized in that said chemical polishing is handled, the prescription of treatment fluid is as follows:
Composition Content (mass percent)
Phosphoric acid (density 1,70) 70-80
Sulfuric acid (density 1,84) 8-9
Nitric acid (density 1,50) 8-9
Copper sulphate 0、01-0、03
Ammonium sulfate 4-5
Urea 2-3
The treatment fluid temperature is controlled at 100 ℃-120 ℃, and the time is generally at 2 minutes to 3 minutes,
5, the production method of a kind of fishing pole conductor loop according to claim 2, it is characterized in that it is to adopt electrochemical treatments that said chemical polishing is handled, adopt phosphoric acid (density 1,70) 85%-90%, chromic acid 10%-15%, water adjust that solution density is 1,72-1,74, and temperature is controlled at 75 ℃-80 ℃, Control of Voltage is at 14V-30V, anodic current density 7-12 peace/square decimeter, the time, cathode material adopted lead or stainless steel at 3-5 minute.
6, the production method of a kind of fishing pole conductor loop according to claim 2, it is characterized in that said anodized adopts sulphuric acid anodizing to handle, adopt sulfuric acid (density 1,84) 180 grams per liters-200 grams per liter, aluminium ion 5 grams per liters-20 grams per liter, temperature are controlled at 15 ℃-25 ℃, current density 0,8-1,5 peace/square decimeters, Control of Voltage is at 12V-22V, time, cathode material adopted lead or stainless steel at 35-45 minute, and adopted air to stir.
7, the production method of a kind of fishing pole conductor loop according to claim 2, it is characterized in that said anodized adopts enamelled anodizing to handle, adopt chromic acid 30 grams per liters-35 grams per liter, boric acid 1-3 grams per liter, temperature are controlled at 40 ℃-50 ℃, current density 2-4 peace/square decimeter, Control of Voltage is at 40V-80V, time, cathode material adopted lead or stainless steel at 40-60 minute, and adopted machinery to stir.
8, the production method of a kind of fishing pole conductor loop according to claim 2 is characterized in that said N-process is to adopt ammoniacal liquor 2-5 grams per liter, and the time is 1-2 minute.