CN1533997A - 用作混凝土细掺料的钢渣微粉早强剂 - Google Patents
用作混凝土细掺料的钢渣微粉早强剂 Download PDFInfo
- Publication number
- CN1533997A CN1533997A CNA031211151A CN03121115A CN1533997A CN 1533997 A CN1533997 A CN 1533997A CN A031211151 A CNA031211151 A CN A031211151A CN 03121115 A CN03121115 A CN 03121115A CN 1533997 A CN1533997 A CN 1533997A
- Authority
- CN
- China
- Prior art keywords
- slag
- early strength
- micro powder
- concrete fine
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种用作混凝土细掺料的钢渣微粉早强剂，涉及工业废渣钢渣的综合利用，属于混凝土工程领域。本发明主要解决钢渣微粉用作混凝土细掺料必须面对的早期强度偏低问题，解决了钢渣微粉细掺料的早强问题，才能应用于混凝土工程。本发明的技术方案是制备出粉体状的早强剂，使之均匀地混合于钢渣微粉中，将含有早强剂的钢渣微粉作为细掺料直接供给商品混凝土搅拌站，使用于混凝土工程，该早强剂是由无机化工废渣，亚纳米级活性二氧化硅为主，辅以表面活性剂的粉体材料，它不含任何对钢筋有腐蚀作用的物质，因此可适用于素混凝土和钢筋混凝土工程。
Description
技术领域
工业废渣钢渣的综合利用，应用于混凝土工程领域。
背景技术
高性能混凝土，亦称二十一世纪混凝土，是指在传统混凝土中掺入用工业废渣制备的细掺料，等量替成部份水泥组份，制成强度高，耐久性好，并具有良好施工性能的混凝土。细掺料的工业废渣包括粉煤灰、高炉矿渣、钢渣等，目前钢渣细掺料尚处于试验和初步应用阶段。钢渣具有和水泥熟料相似的化学成份和矿物组成，但它缺少水化强度的主要物相硅酸三钙，也即其水化的胶凝性差，尤其早期强度偏低，从而限制了钢渣微粉作为混凝土细掺料的应用。
钢渣可利用的价值在于其活性激发技术，尤其作为混凝土细掺料的钢渣微粉，要求早期强度的发挥，目前钢渣微粉的开发应用处于起步阶段，尚未见到钢渣微粉早强剂的发明、研究、试验报导。
发明内容
本发明的早强剂是以无机化工废渣，亚纳米级活性二氧化硅为主，辅以表面活性剂，制备而成的粉体粉料，是一种复合型的早强剂，其具体配料比例为：工业硫酸铝渣20-30％；天然非金属矿制成的活性二氧化硅30-50％(其中颗粒度＜1微米，占40-50％)；水泥熟料20-30％；多元醇类表面活性剂0.03-0.06％。
本发明包含有两方面的机理，一方面采用硫酸盐类化工产品，利用三氧化硫激发钢渣成份中的铝酸三钙，水化初期快速形成水化硫铝酸钙，发挥早强作用；另一方面创新地采用亚纳米级活性二氧化硅，快速充分地分散充填到钢渣水化凝胶网络结构中，既发挥活性二氧化硅的胶凝性，又提高了凝胶网络的物理堆积密度，强化网络结构，提高早期强度。本早强剂不含对钢筋有腐蚀的物质，可适于素混凝土和钢筋混凝土工程。
具体实施方式
本发明的早强剂是制成粉体材料，其比表面积≥600m2/kg，在应用于钢渣微粉时，其配用量为3-6％(以钢渣微粉的重量为基准)，均匀混合于钢渣微粉之中即可。
本发明的早强剂经过数十组试验室试验，对比掺加早强剂与不掺早强剂的强度，其早期强度提高的比例均超过30％，符合“GB8075-87混凝土外加剂的分类，命名与定义”中对早强剂的相关规定。且本发明的早强剂价格低廉，用量较低，应用于钢渣微粉或钢渣矿渣复合微粉，平均每吨增加成本15～25元。技术经济效果明显，已开始在杭州地区试用推广。
Claims (2)
1.一种用作混凝土细掺料的钢渣微粉早强剂，其特征是，采用复合的方法从化学激发和物理堆积两方面提高钢渣微粉的早期强度，其配比为：工业硫酸铝渣20-30％；天然非金属矿制成的活性二氧化硅30-50％(其中颗粒度＜1微米，占40-50％)；水泥熟料20-30％；多元醇类表面活性剂0.03-0.06％。
2.根据权利要求1所述的用作混凝土细掺料的钢渣微粉早强剂，其特征是，制备成粉体材料，可方便地掺加到钢渣微粉之中，其用量为3％-6％。