CN1511184A - Paint, and method of producing same - Google Patents
Paint, and method of producing same Download PDFInfo
- Publication number
- CN1511184A CN1511184A CNA028078276A CN02807827A CN1511184A CN 1511184 A CN1511184 A CN 1511184A CN A028078276 A CNA028078276 A CN A028078276A CN 02807827 A CN02807827 A CN 02807827A CN 1511184 A CN1511184 A CN 1511184A
- Authority
- CN
- China
- Prior art keywords
- agent
- flame retardant
- retardant compositions
- film
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A paint has a film-forming binder component, a color-producing component, an d a fire-retardant component adapted to least substantially protect from fire a surface of which the paint is applied; and the paint is produced by a method including providing a film-forming binder component; providing a color- producing component; mixing the components with some of dried powder components missing; and adding a fire retardant component to replace the dry powder component.
Description
Invention field
The present invention relates generally to coating and preparation method thereof.
Background of invention
As everyone knows, coating can be applicable to industry, the other field of the family and the modern life.Known coating comprises the film-forming binder component usually, and this component can film forming, and adheres to the base material that scribbles coating, and described coating also comprises the colour developing component, such as pigment and other toners.
When known coating provides to a certain extent protection for the surface that scribbles coating, avoid atmospheric harmful effect, and when providing certain color for the surface that scribbles coating, coating can not prevent fully that substrate surface from meeting fire burns.Can think that it is desirable eliminating this shortcoming.
Summary of the invention
Therefore, the objective of the invention is to propose a kind of method that can avoid the coating of prior art defective and prepare this coating.
Consistent with these purposes of the present invention and other purposes that hereinafter will mention, one of the present invention is characterised in that, be set fourth as briefly, this coating comprises the film-forming binder component, colour developing component, and the flame retardant compositions that is suitable for fully preventing scribbling the surface combustion of coating at least.
By the coating of the present invention's design, except the normal attribute with coating, it can also fully prevent to scribble the substrate surface burning of coating at least, in many cases, can strengthen the working life of erosion resistance and prolongation coating.
According to another feature of the present invention, flame retardant compositions comprises at least a phosphoric acid salt or derivatives thereof, such as melamine polyphosphate, and ammonium polyphosphate.
According to another feature of the present invention, described flame retardant compositions comprises the trimeric cyanamide or derivatives thereof, as melamine cyanurate, melamine borate salt, melamine polyphosphate, trimeric cyanamide diphosphate, melamine pyrophosphate and melamine phosphate.
The present invention proposes to prepare the method for coating, and this method comprises the steps: to be prepared to the film adhesive component, prepares the colour developing component, said components and some is leaked fire (missing) dry powder component mix, and adds flame retardant compositions alternative dry powdery components.
Particularly in additional claims, illustrated its novel characteristic, this characteristic is decided to be feature of the present invention.Yet, among the present invention, no matter be its structure, or its working method, together with described other purposes and advantage, will give to explain fully in the specific below example.The explanation of preferred embodiment
Coating according to the present invention preparation comprises the film-forming binder component, and colour developing component and preventing at least substantially scribbles the flame retardant compositions of the surface combustion of coating.
Flame retardant compositions can comprise the phosphoric acid salt or derivatives thereof, such as melamine polyphosphate, and ammonium polyphosphate.
Equally, flame retardant compositions comprises the trimeric cyanamide or derivatives thereof, as melamine cyanurate, and melamine borate salt, melamine polyphosphate, trimeric cyanamide diphosphate, melamine pyrophosphate and melamine phosphate.
According to the present invention, in coating, flame retardant compositions may comprise carbonized agent, and as tetramethylolmethane, monopentaerythritol or dipentaerythritol, and comprise whipping agent are as trimeric cyanamide be selected from the additive that contains in the above reagent of enumerating.
Need to prove that film forming matter (matrix material and tenderizer) is one of main component of coating, can influence weather resistance, gloss, elasticity, bonding, snappiness and hardness, pigment is to be insoluble to binding agent and the colored powder that is dissolved in tinting material, to produce colour-change and padding ability, except that above-mentioned two class materials, coating also comprises volatile constituent, in most cases, volatile constituent and matrix material form solution or so-called basic varnish (varnish) together.The additive that also can comprise other in the coating, these additives help chemical substance to form the specified property of coating.
According to the present invention, coating can be prepared by the method that comprises the following steps: be prepared to the film adhesive component, prepare the colour developing component, said components and some are leaked fiery dry powder component mix, and add flame retardant compositions replacement dry powder component.
Particularly, filler as lime carbonate and titanium dioxide, is replaced by flame retardant compositions.Yet, also may replace a spot of film-forming components certainly.
By the following examples coating of the present invention will be described:
Embodiment 1
Two parts of formula epoxy coatings
A part
Functional materials weight %
Liquid-state epoxy resin Epotuf37-127 32.80 film-forming binder
Thinner phenylcarbinol 3.75 film-forming binder
Dispersant B YK P-104S 0.32 additive
Anti-depression agent BYK A-530 0.15 additive
Flowing additive BYK 501 0.16 additives
Primary coat pigment titanox 2,020 12.3 colour developing components
Supplement Microna7 18.99 dry powder components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
B part
Polymeric amide stiffening agent Epotuf37-801 13.32 film-forming binder
Thinner phenylcarbinol 3.21 film-forming binder
100.00
A part is 4/1 with the mixed volume ratio of B part.
Embodiment 2
The Synolac base paint
Functional materials weight %
Medium oil alkyd 80% Beckosol AA-203 31.48 film-forming binder
Solvent mineral turpentine 21.94 volatile constituents
Dispersion agent Soya Lecithin 0.13 additive
Thixotropic agent Thixatrol ST 0.32 thixotropic agent
Drop down Flow Control preparation Post 4 0.44 thixotropic agent
Cobalt siccative 12% cobalt naphthenate 0.08 additive
Calcium siccative 6% calcium naphthenate 0.78 additive
Anti Diacetylmonoxime (methyl ethyl ketoxine) 0.33 additive
Primary coat pigment Tipure 902 21.38 colour developing components
Replenish pigment Nicron 604 8.12 dry powder components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
Embodiment 3
Polyurethane paint
Functional materials weight
Urethane Spenkel F47-M-60 50.10 film-forming binder of oil modification
Dispersion agent Nuosperes 657 0.46 additives
Thixotropic agent Bentone SD-1 0.95 thixotropic agent
Solvent mineral turpentine 6.18 volatile constituents
Primary coat pigment Tronox CR-828 23.95 colour developing components
Cobalt siccative 12% cobalt naphthenate 0.38 additive
Calcium siccative 6% calcium naphthenate 1.26 additives
Zirconium siccative 24% zirconium naphthenate 1.61 additives
Anti Exkin#2 0.11 additive
Whipping agent trimeric cyanamide 5.25 fire retardants
Catalyzer melamine polyphosphate 4.50 fire retardants
Carbonized agent tetramethylolmethane 5.25 fire retardants
100.00
Embodiment 4
Strippable vinyl coating
Functional materials weight %
High molecular weight ethylene base resin Ucar YVNS 7.38 film-forming binder
Low-molecular-weight ethylenic base resin Ucar VYHD 3.69 film-forming binder
Plasticizer phthalic acid dioctyl ester 2.88 film-forming binder
White pigment TiPure 902 6.50 colour developing components
Thinner toluene 22.20 volatile constituents
Ketone solvent methyl iso-butyl ketone (MIBK) 20.95 volatile constituents
Acetic ester solvent acetic acid butyl ester 21.40 volatile constituents
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
Embodiment 5
Soluble cotton satin weave varnish
Functional materials weight %
Lower molecular weight soluble cotton soluble cotton 1/4sec 6.75 film-forming binder
High molecular soluble cotton soluble cotton 1/2sec 0.10 film-forming binder
Thinner toluene 13.75 volatile constituents
Horizontal solvent (lateral solvent) isopropyl acetone 2.70 volatile constituents
Rapid-curing cutback solvent acetic acid butyl ester 27.60 volatile constituents
Slow curing solvent PM acetic ester 2.70 volatile constituents
Coconut alcohol acid resin 70% Bookosol91-470 12.78 film-forming binder among the BA
Plasticizer phthalic acid dioctyl ester 1.34 film-forming binder
White pigment Tipure 902 9.80 colour developing components
Linking agent Cymel 303 6.95 film-forming binder
Crosslinking catalyst butyl acid phosphoric acid salt 0.53 additive
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
Embodiment 6
The egg-shell glaze latex paint
Functional materials weight %
Aqueous solvent 25.3 volatile constituents
Dispersion agent Potassium tripolyphosphate 0.22 additive
Tensio-active agent Igepal CO-630 0.84 additive
Defoamer Colloid 643 0.23 additives
Wet limit control agent (wet edge control) propylene glycol 2.77 additives
Biocide Nuosept 95 0.38 additives
White pigment TiPure 902 18.11 colour developing components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.5 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
Cellulose thickener Bernocol E411 FQ 0.32 thixotropic agent
Latex polymer 55% Rovace 9,100 34.88 film-forming binder
PH regulator agent 28% ammonium hydroxide 0.13 additive
Associative thickener acrylate water miscible liquid RM-5 1.82 thixotropic agent
100.00
The preparation method
Above-mentioned sample is prepared from by Cowles high speed dispersion device.The coating preparation technology of employing standard, in an amount of vehicle, vehicle comprises dispersion agent and wetting agent with the powder material high speed dispersion.
Finish after the dispersion, underspeed, the vehicle of equal amount with
All the other components in the prescription add together.
Embodiment 7
The acrylic acid or the like powder coating
Functional materials weight %
Vinylformic acid Racemic glycidol Fine-Clad A-207-SA 56.90 film-forming binder
Linking agent dodecanedioic acid 10.83 film-forming binder
Flowing additive Silwet L-7500 0.33 additive
White pigment Titanox 2,020 16.94 colour developing components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
Stoving temperature: 150 ℃, 20 minutes
The preparation method
Use W﹠amp; P ZSK-30 stirrer mixed powder
60/80 ℃ of bucket temperature
Speed of rotation: 250rpm
Classification: 100% by 200 orders
By above-mentioned listed examples as can be seen, the fire retardant of coating of the present invention part is made up of three kinds of flame retardant compositions, trimeric cyanamide just, melamine polyphosphate, and tetramethylolmethane.These three kinds of flame retardant compositions account for 15% of coating weight altogether altogether.
Should be understood that each above-mentioned composition, and two or more compositions together, be applied to be different from other materials and the method for the above-mentioned type.
With coating and working method thereof the present invention has been described, but the restriction of details shown in not being subjected to because under the situation that does not depart from spirit of the present invention, can be carried out various changes and structural changes.
Do not having under the situation about further analyzing, above-mentionedly everyly will fully disclose main points of the present invention, by using existing knowledge, other people can easily use it for different application, and do not lose feature.From the angle of prior art, these features have been formed the essential characteristic of the general or particular aspects of the present invention.
Limit by appended claims as new scope with requiring patent protection.
Claims (11)
1. the surface is painted the coating of predetermined color, described coating comprises:
The film-forming binder component is used for forming from the teeth outwards paint film;
The colour developing component is used for the color that provides predetermined from the teeth outwards;
Flame retardant compositions is suitable for preventing surface combustion,
Wherein, described flame retardant compositions comprises trimeric cyanamide, tetramethylolmethane, and melamine polyphosphate,
Remaining component comprises filler and additive.
2. coating as claimed in claim 1 is characterized in that, % counts by weight, and described flame retardant compositions comprises: 35% trimeric cyanamide, 35% tetramethylolmethane and 30% melamine polyphosphate.
3. coating as claimed in claim 1 is characterized in that, in the gross weight of coating, described flame retardant compositions comprises 5.25 weight % trimeric cyanamides, 5.25 weight % tetramethylolmethanes, 4.50 weight % melamine polyphosphates.
4. coating as claimed in claim 1 is characterized in that described flame retardant compositions is no more than 15% of coating gross weight.
5. coating as claimed in claim 1 is characterized in that, described coating comprises following component:
Two parts of formula epoxy coatings
A part
Functional materials weight %
Liquid-state epoxy resin Epotuf37-127 32.80 film-forming binder
Thinner phenylcarbinol 3.75 film-forming binder
Dispersant B YK P-104S 0.32 additive
Anti-depression agent BYK A-530 0.15 additive
Flowing additive BYK 501 0.16 additives
Primary coat pigment titanox 2,020 12.3 colour developing components
Supplement Microna7 18.99 dry powder components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
B part
Polymeric amide stiffening agent Epotuf37-801 13.32 film-forming binder
Thinner phenylcarbinol 3.21 film-forming binder
100.00
A part is 4/1 with the mixed volume ratio of B part.
6. coating as claimed in claim 1, described coating comprises following component:
The Synolac base paint
Functional materials weight %
Medium oil alkyd 80% Beckosol AA-203 31.48 film-forming binder
Solvent mineral turpentine 21.94 volatile constituents
Dispersion agent Soya Lecithin 0.13 additive
Thixotropic agent Thixatrol ST 0.32 thixotropic agent
Drop down Flow Control preparation Post 4 0.44 thixotropic agent
Cobalt siccative 12% cobalt naphthenate 0.08 additive
Calcium siccative 6% calcium naphthenate 0.78 additive
Anti Diacetylmonoxime 0.33 additive
Primary coat pigment Tipure902 21.38 colour developing components
Replenish pigment Nicron604 8.12 dry powder components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
7. coating as claimed in claim 1, described coating comprises following component:
Polyurethane paint
Functional materials weight
Urethane Spenkel F47-M-60 50.10 film-forming binder of oil modification
Dispersion agent Nuosperes 657 0.46 additives
Thixotropic agent Bentone SD-1 0.95 thixotropic agent
Solvent mineral turpentine 6.18 volatile constituents
Primary coat pigment Tronox CR-828 23.95 colour developing components
Cobalt siccative 12% cobalt naphthenate 0.38 additive
Calcium siccative 6% calcium naphthenate 1.26 additives
Zirconium siccative 24% zirconium naphthenate 1.61 additives
Anti Exkin#2 0.11 additive
Whipping agent trimeric cyanamide 5.25 fire retardants
Catalyzer melamine polyphosphate 4.50 fire retardants
Carbonized agent tetramethylolmethane 5.25 fire retardants
100.00
8. coating as claimed in claim 1, described coating comprises following component:
Strippable vinyl coating
Functional materials weight %
High molecular weight ethylene base resin Ucar YVNS 7.38 film-forming binder
Low-molecular-weight ethylenic base resin Ucar VYHD 3.69 film-forming binder
Plasticizer phthalic acid dioctyl ester 2.88 film-forming binder
White pigment TiPure 902 6.50 colour developing components
Thinner toluene 22.20 volatile constituents
Ketone solvent methyl iso-butyl ketone (MIBK) 20.95 volatile constituents
Acetic ester solvent acetic acid butyl ester 21.40 volatile constituents
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
9. coating as claimed in claim 1, described coating comprises following component:
Soluble cotton satin weave varnish
Functional materials weight %
Lower molecular weight soluble cotton soluble cotton 1/4sec 6.75 film-forming binder
High molecular soluble cotton soluble cotton 1/2sec 0.10 film-forming binder
Thinner toluene 13.75 volatile constituents
Horizontal solvent isopropyl acetone 2.70 volatile constituents
Rapid-curing cutback solvent acetic acid butyl ester 27.60 volatile constituents
Slow curing solvent PM acid esters 2.70 volatile constituents
Coconut alcohol acid resin 70% Bookosol 91-470 12.78 film-forming binder among the BA
Plasticizer phthalic acid dioctyl ester 1.34 film-forming binder
White pigment Tipure 902 9.80 colour developing components
Linking agent Cymel 303 6.95 film-forming binder
Crosslinking catalyst butyl acid phosphoric acid salt 0.53 additive
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
10. coating as claimed in claim 1, described coating comprises following component:
The egg-shell glaze latex paint
Functional materials weight %
Aqueous solvent 25.3 volatile constituents
Dispersion agent Potassium tripolyphosphate 0.22 additive
Tensio-active agent Igepal CO-630 0.84 additive
Defoamer Colloid 643 0.23 additives
Wet limit control agent propylene glycol 2.77 additives
Biocide Nuosept 95 0.38 additives
White pigment TiPure 902 18.11 colour developing components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.5 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
Cellulose thickener Bemocol E411 FQ 0.32 thixotropic agent
Latex polymer 55% Rovace 9,100 34.88 film-forming binder
PH regulator agent 28% ammonium hydroxide 0.13 additive
Associative thickener acrylate water miscible liquid RM-5 1.82 thixotropic agent
100.00
The preparation method
Above-mentioned sample is prepared from by Cowles high speed dispersion instrument.The coating complete processing of employing standard, in an amount of vehicle, vehicle comprises dispersion agent and wetting agent with the powder material high speed dispersion.
Finish after the dispersion, underspeed, the vehicle of equal amount all the other components in prescription add.
11. coating as claimed in claim 1, described coating comprises following component
The acrylic acid or the like powder coating
Functional materials weight %
Polyacrylic acid Racemic glycidol Fine-Clad A-207-SA 56.90 film-forming binder
Linking agent dodecanedioic acid 10.83 film-forming binder
Flowing additive Silwet L-7500 0.33 additive
White pigment Titanox 2,020 16.94 colour developing components
Whipping agent trimeric cyanamide 5.25 flame retardant compositions
Catalyzer melamine polyphosphate 4.50 flame retardant compositions
Carbonized agent tetramethylolmethane 5.25 flame retardant compositions
100.00
Stoving temperature: 150 ℃, 20 minutes
The preparation method
Use W﹠amp; P ZSK-30 stirrer mixed powder
60/80 ℃ of bucket temperature
Speed of rotation: 250rpm
Classification: 100% by 200 orders