CN1510093A - Organic nanometer adhesion agent and producing method thereof - Google Patents
Organic nanometer adhesion agent and producing method thereof Download PDFInfo
- Publication number
- CN1510093A CN1510093A CNA021573352A CN02157335A CN1510093A CN 1510093 A CN1510093 A CN 1510093A CN A021573352 A CNA021573352 A CN A021573352A CN 02157335 A CN02157335 A CN 02157335A CN 1510093 A CN1510093 A CN 1510093A
- Authority
- CN
- China
- Prior art keywords
- reactor
- parts
- foam plastic
- polystyrene foam
- adhesion agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A nano-class organic adhesive is prepared from used foam polystyrene plastics, rosin resin, industrial acetone, lead-free gasoline, SiO2 nanoparticles, and Al, Ag or Cu powder through proportional mixing. Its advantages are high adhesion and shielding effect and low cost.
Description
Technical field
The present invention relates to a kind of nanometer organic adhesion agent and production method thereof, described nanometer organic adhesion agent uses nano material, can improve the quality of products and hides performance.
Technical background
Chinese patent 01116090.X discloses a kind of organic adhesion agent, and this organic adhesion agent waste polystyrene foam plastic, Gum Rosin, acetone, gasoline, Resins, epoxy, solidifying agent, the agent of connection idol are formulated.This tackiness agent can reduce white pollution, reduce cost, but its covering power is not ideal, and is shorter when envrionment temperature staging life greater than more than 25 ℃ the time, and apt to deteriorate.Therefore, need to propose a kind of nanometer organic adhesion agent and production method thereof.
Summary of the invention
The object of the present invention is to provide a kind of nanometer organic adhesion agent and production method thereof, this tackiness agent does not contain harmful materials such as formaldehyde, and has higher cementability and opacifying property, and cost is lower.
The objective of the invention is to realize by following technical proposals: a kind of nanometer organic adhesion agent, form by following feedstock production, the weight ratio of described raw material is:
Waste polystyrene foam plastic 10
Gum Rosin 6
Industrial acetone 12
No. 93 white gasolinees 72
Nano silicon 0.5
Aluminium silver powder or copper powder 10-25.
The production method of above-mentioned nanometer organic adhesion agent is: with waste polystyrene foam plastic, Gum Rosin, industrial acetone, white gasoline, nano silicon, aluminium silver powder or copper powder is that raw material carries out hybrid reaction, and the blended step is:
A, waste polystyrene foam plastic cleaned dry, get wherein 5 parts, get 6 parts of Gum Rosins again, in the reactor of packing into, add 12 parts of acetone and 72 parts of No. 93 white gasolinees then in reactor, sealing was stirred 4-6 minute;
B, again 5 parts useless polystyrene porous plastics is divided 5-10 time, each 1 minute at interval, evenly add in the reactor, keep stirrer work when feeding intake;
C, after the waste polystyrene foam plastic in the described reactor dissolves fully, again 0.5 part of nano silica powder is added in the reactor, stirred 20~30 minutes;
D, stop to stir, 10-25 part aluminium silver powder or copper powder are added in the described reactor again, sealing was stirred 20~30 minutes, discharged can at last while stirring, promptly made the present invention.
The present invention compared with prior art has following advantage:
1, because raw material of the present invention does not contain harmful materials such as benzene,toluene,xylene, formaldehyde, thus harmless, safe in utilization, belong to the environment-friendly health type tackiness agent.
2, because the present invention has adopted the nanometer titanium dioxide silicon materials, good, the strong covering power of the tackiness agent sticking power of making, and have characteristics such as anticorrosion, antirust, heat-resisting, reflective, rapid-curing cutback.
3, owing to use waste polystyrene foam plastic in the material of the present invention, reduced production cost.
4, tackiness agent of the present invention can be deposited 18 months during greater than 30 ℃ in envrionment temperature and never degenerate.
Embodiment
Embodiment one:
A kind of nanometer organic adhesion agent is formed by following feedstock production, and the weight ratio of described raw material is:
Waste polystyrene foam plastic 10
Gum Rosin 6
Industrial acetone 12
No. 93 white gasolinees 72
Nano silicon 0.5
Aluminium silver powder 10-20.
Wherein, nano silicon is nano level pulvis.
The tackiness agent made from above-mentioned raw materials also can be called silver paint.
Embodiment of preparation method of the present invention is:
A, waste polystyrene foam plastic cleaned dry, get wherein 5 parts, get 6 parts of Gum Rosins again, in the reactor of packing into, add 12 parts of acetone and 72 parts of No. 93 white gasolinees then in reactor, sealing was stirred 4-6 minute;
B, again 5 parts useless polystyrene porous plastics is divided 5-10 time, each 1 minute at interval, evenly add in the reactor, keep stirrer work when feeding intake;
C, after the waste polystyrene foam plastic in the described reactor dissolves fully, again 0.5 part of nano silica powder is added in the reactor, stirred 20~30 minutes;
D, stop to stir, 10-20 part aluminium silver powder is added in the described reactor again, sealing was stirred 20~30 minutes, discharged can at last while stirring, and the packing jar of the 1 liter of capacity of packing into promptly makes the present invention.
The present invention after reactor adds material, should guarantee that reactor stirs, and avoids solvent evaporates at every turn under sealed state in preparation process.
Product of the present invention is widely used in the decoration of various materials such as metal, plastics, timber, concrete, stone material, and particularly metallic surface is decorated and be anticorrosion.Surface daub on a wall as vehicle, boats and ships, oil tank, iron tower, radiator, stair, guardrail, door and window, pipeline, engine, iron skill decoration etc.
Product of the present invention need not increase any material in use again.Opening jar stirs and can directly brush or spray.Substrate surface will be handled totally before covering with paint, lacquer, colour wash, etc., with after the paint can lid is built.Note during use ventilating.
Embodiment two:
A kind of nanometer organic adhesion agent is formed by following feedstock production, and the weight ratio of described raw material is:
Waste polystyrene foam plastic 10
Gum Rosin 6
Industrial acetone 12
No. 93 white gasolinees 72
Nano silicon 0.5
Copper powder 10-25.
Wherein, nano silicon is nano level pulvis.
The tackiness agent made from above-mentioned raw materials also can be called gold paint.
The preparation technology's flow process and the embodiment one of present embodiment are basic identical, do not describe one by one at this.
Claims (3)
1, a kind of nanometer organic adhesion agent is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
Waste polystyrene foam plastic 10
Gum Rosin 6
Industrial acetone 12
No. 93 white gasolinees 72
Nano silicon 0.5
Aluminium silver powder or copper powder 10-25.
2, nanometer organic adhesion agent according to claim 1 is characterized in that: formed by following feedstock production, the weight ratio of described raw material is:
Waste polystyrene foam plastic 10
Gum Rosin 6
Industrial acetone 12
No. 93 white gasolinees 72
Nano silicon 0.5
Copper powder 10-25.
3, a kind of production method of nanometer organic adhesion agent is characterized in that: with waste polystyrene foam plastic, Gum Rosin, industrial acetone, white gasoline, nano silicon, aluminium silver powder or copper powder is that raw material carries out hybrid reaction, and the blended step is:
A, waste polystyrene foam plastic cleaned dry, get wherein 5 parts, get 6 parts of Gum Rosins again, in the reactor of packing into, add 12 parts of acetone and 72 parts of No. 93 white gasolinees then in reactor, sealing was stirred 4-6 minute;
B, again 5 parts useless polystyrene porous plastics is divided 5-10 time, each 1 minute at interval, evenly add in the reactor, keep stirrer work when feeding intake;
C, after the waste polystyrene foam plastic in the described reactor dissolves fully, again 0.5 part of nano silica powder is added in the reactor, stirred 20~30 minutes;
D, stop to stir, 10-25 part aluminium silver powder or copper powder are added in the described reactor again, sealing was stirred 20~30 minutes, discharged can at last while stirring, promptly made the present invention.