CN1508091A - 一种直流电弧炉炉底耐火材料 - Google Patents
一种直流电弧炉炉底耐火材料 Download PDFInfo
- Publication number
- CN1508091A CN1508091A CNA021576149A CN02157614A CN1508091A CN 1508091 A CN1508091 A CN 1508091A CN A021576149 A CNA021576149 A CN A021576149A CN 02157614 A CN02157614 A CN 02157614A CN 1508091 A CN1508091 A CN 1508091A
- Authority
- CN
- China
- Prior art keywords
- arc furnace
- gross weight
- percentage composition
- aluminium
- total weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种直流电弧炉炉底耐火材料，由氧化镁、碳、铁、钛、铝、铝镁合金组成，所述的氧化镁在总重量中的百分含量在60－80％之间，所述的碳在总重量中的百分含量在8－20％之间，所述的铁在总重量中的百分含量在3－9％之间，所述的钛在总重量中的百分含量在0.5－2％之间，所述的铝在总重量中的百分含量在1－3％之间，所述的铝镁合金在总重量中的百分含量在1－4％之间。所述的导电耐火材料具有电阻率低，价格低的优点，开炉工序简单，在电炉操作中可任意修补，能大幅度提高电炉的使用寿命，降低电极消耗。
Description
技术领域
本发明涉及一种工程材料，特别涉及一种耐火材料，具体来说是一种直流电弧炉炉底耐火材料。
背景技术
目前，现有的直流电弧炉底阳极是直流电弧炉的特有设备，也是直流电弧炉的技术核心。炼钢用直流电弧炉底阳极有两大类，第一是通过在直流电弧炉炉底耐火材料中埋入金属元件做阳极的方式，第二是直流电弧炉炉底用导电耐火材料作为底阳极的方式，其炉床采用可以导电的耐火砖砌筑，使炉床本身构成导电阳极。因为石墨耐火砖散发的热量较多，为驱散炉底的高温，采用轴流式风机对炉底进行强制冷却，使工艺复杂。另外在铜板上直接铺砌导电耐火砖，一般来说，炉底导电耐火砖的碳含量要达到15％以上才能保证足够的导电性，但从侵蚀性能看，含碳10％的沥青粘结镁砂砖最好。然而这种沥青粘结砖只有经过高温预处理后才有足够的导电性能，成本较高，这种散状导电材料的电阻率较高，开炉工序复杂。
发明内容：
为了解决现有导电耐火材料中存在的以上所述的缺点，本发明的目的是提供一种直流电弧炉炉底耐火材料，具体的，所述的导电耐火材料是由氧化镁、碳、铁、钛、铝、铝镁合金组成，所述的氧化镁在总重量中的百分含量在60-80％之间，所述的碳在总重量中的百分含量在8-20％之间，所述的铁在总重量中的百分含量在3-9％之间，所述的钛在总重量中的百分含量在0.5-2％之间，所述的铝在总重量中的百分含量在1-3％之间，所述的铝镁合金在总重量中的百分含量在1-4％之间，进一步的，所述的导电耐火材料用作直流电弧炉炉底材料。
本发明所述导电耐火材料的有益效果是：本发明提出这种新型的导电耐火材料，与现有直流电弧炉底阳极相比，电阻率低，适用范围广，可适用于各种类型直流电弧炉底阳极，在操作中可任意修补，价格低，开炉工序简单。
具体实施方式：
一种直流电弧炉炉底耐火材料，具体的，所述的导电耐火材料是由氧化镁、碳、铁、钛、铝、铝镁合金组成，所述的氧化镁在总重量中的百分含量在60-80％之间，所述的碳在总重量中的百分含量在8-20％之间，所述的铁在总重量中的百分含量在3-9％之间，所述的钛在总重量中的百分含量在0.5-2％之间，所述的铝在总重量中的百分含量在1-3％之间，所述的铝镁合金在总重量中的百分含量在1-4％之间，进一步的，所述的导电耐火材料用作直流电弧炉炉底材料。
Claims (2)
1.一种直流电弧炉炉底耐火材料，其特征在于：所述的导电耐火材料是由氧化镁、碳、铁、钛、铝、铝镁合金组成，所述的氧化镁在总重量中的百分含量在60-80％之间，所述的碳在总重量中的百分含量在8-20％之间，所述的铁在总重量中的百分含量在3-9％之间，所述的钛在总重量中的百分含量在0.5-2％之间，所述的铝在总重量中的百分含量在1-3％之间，所述的铝镁合金在总重量中的百分含量在1-4％之间。
2.根据权利要求1所述的直流电弧炉炉底耐火材料，其特征在于：所述的直流电弧炉炉底耐火材料导电。