CN1504437A - Surface treatment technology for glaze-free Colored pottery - Google Patents
Surface treatment technology for glaze-free Colored pottery Download PDFInfo
- Publication number
- CN1504437A CN1504437A CNA021279403A CN02127940A CN1504437A CN 1504437 A CN1504437 A CN 1504437A CN A021279403 A CNA021279403 A CN A021279403A CN 02127940 A CN02127940 A CN 02127940A CN 1504437 A CN1504437 A CN 1504437A
- Authority
- CN
- China
- Prior art keywords
- greenwave
- baking
- glaze
- moulding
- tinting material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for making chromatic color on crockery and pottery surface with no glaze luster, including the steps of, high temperature burning hand finishing greenware, polishing the blank surface, first roasting the greenware coated by coloring agent, applying multicolor pattern onto the greenware, second forming by baking, spraying a layer of heatproof coloring agent onto the greenware, after baking, coating the impression-transfer glue brush onto the transfer paper and plastering it onto the greenware with coloring agent, placing it into the hot transfer press baking oven for baking, tearing the transfer paper for formation.
Description
Affiliated technical field:
The present invention relates to the pottery process of surface treatment, particularly a kind of have a treatment process that is no glaze glossy colour tint on the pottery surface.
Background technology:
At present, the technology of carrying out painted processing for the pottery surface is a lot, but the method that generally all adopts secondary to fire, this method makes the bonding force on color and pottery surface undesirable, easily decolouring.Chinese patent discloses a kind of denomination of invention and has been " surface treatment method of advanced ceramics technology ", its number of patent application: 99108073.4.The described method of this patent application technology comprises: greenwave enters factory, washing polishing, barbecue, upper surface treatment agent, burns till, goes up pattern decorative for the first time, fires for the second time, quality inspection, dispatch from the factory.This method is not fired after needing earlier to have glaze and handle treatment agent on the pottery surface again, because firing temperature is low, the firing time is long, and not only coloring effect is stablized inadequately, and, also influencing the quality of pottery itself, technical process is long, and efficient is low.
Summary of the invention:
The purpose of this invention is to provide that a kind of technical process is short, efficient is high, coloring stabilized and do not influence the surface treatment technology for glaze-free Colored pottery of the quality of pottery own.This technology is in the greenwave surface colour after smoking for the first time, in computer is controlled at, down baking of low temperature, make the beautiful in colour of greenwave surface, no glaze gloss but color stable, simple and tasteful, colour-fast, do not come off, thereby make Tao Chanpinji view and admire, decorate and be concealed in one.
Concrete technical scheme of the present invention is as follows:
The present invention includes greenwave, the billet surface polishing of high-temperature firing manual assembly, greenwave, greenwave surface that baking for the first time the is sprayed with tinting material pattern of enameling, the secondary baking moulding is characterized in that:
A: manual to behind pottery mud engraving and the pattern forming, depress at standard atmosphere, high-temperature firing greenwave moulding through 900 ℃-1100 ℃, at 160 ℃ of-220 ℃ of tinting materials of bright and clean pure moulding greenwave surface spray one deck heatproof, depress through the computer controlled temperature 150 ℃ of-195 ℃ of bakings at standard atmosphere for the first time;
B: transfer printing glue is brushed above the greenwave that is sprayed with tinting material that also tightly is fitted on transfer paper after baking, and being placed on and tearing transfer paper after the baking in the heat transfer machine baking box is moulding, and its storing temperature is 162 ℃-192 ℃, and storing time is 90-120 minute.
When there is tinting material on greenwave of the present invention surface, be sprayed with the chromatic colorant agent earlier, on through the greenwave behind 900 ℃-1100 ℃ the high-temperature firing, in 150 ℃ of-195 ℃ of following heat transfer machine baking boxs, cooperate the baking of tinting material color again.
Transfer printing glue of the present invention and water ratio are: 1: 3.
Technical process of the present invention is short, efficient is high, coloring stabilized and do not influence the quality of pottery own, in the greenwave surface colour after smoking for the first time, in computer is controlled at, down baking of low temperature, make the beautiful in colour of greenwave surface, no glaze gloss but color stable, simple and tasteful, colour-fast, do not come off, thereby make Tao Chanpinji view and admire, decorate and be concealed in one.
Specific embodiments:
Embodiment 1:
The present invention includes greenwave, the billet surface polishing of high-temperature firing manual assembly, greenwave, greenwave surface that baking for the first time the is sprayed with tinting material pattern of enameling, the secondary baking moulding is characterized in that:
A: to behind pottery mud engraving and the pattern forming, depress by hand, behind 900 ℃ high-temperature firing greenwave, in 160 ℃ of tinting materials of bright and clean pure greenwave surface spray one deck heatproof, greenwave moulding after drying at standard atmosphere;
B: transfer printing glue is brushed above the greenwave that is sprayed with tinting material that also tightly is fitted on transfer paper after baking, and being placed on and tearing transfer paper after the baking in the heat transfer machine baking box is moulding, and its storing temperature is 162 ℃, and storing time is 90 minutes.
When there is background color on greenwave of the present invention surface, be sprayed with the chromatic colorant agent earlier, on through the greenwave behind 900 ℃ ℃ the high-temperature firing, in 160 ℃ of following heat transfer machine baking boxs, cooperate the baking of tinting material color again.
Transfer printing glue of the present invention and water ratio are: 1: 3.
Embodiment 2:
The present invention includes greenwave, the billet surface polishing of high-temperature firing manual assembly, greenwave, greenwave surface that baking for the first time the is sprayed with tinting material pattern of enameling, the secondary baking moulding is characterized in that:
A: to behind pottery mud engraving and the pattern forming, depress by hand, through 950 ℃ high-temperature firing greenwave, in 180 ℃ of tinting materials of bright and clean pure greenwave surface spray one deck heatproof, greenwave moulding after drying at standard atmosphere;
B: transfer printing glue is brushed above the greenwave that is sprayed with tinting material that also tightly is fitted on transfer paper after baking, and being placed on and tearing transfer paper after the baking in the heat transfer machine baking box is moulding, and its storing temperature is 182 ℃, and storing time is 100 minutes.
When there was background color on greenwave of the present invention surface, the spray tinting material was cooperating the baking of tinting material color again in 195 ℃ of following heat transfer machine baking boxs on the greenwave behind 950 ℃ the high-temperature firing earlier.
Transfer printing glue of the present invention and water ratio are: 1: 3.
Embodiment 3:
The present invention includes greenwave, the billet surface polishing of high-temperature firing manual assembly, greenwave, greenwave surface that baking for the first time the is sprayed with tinting material pattern of enameling, the secondary baking moulding is characterized in that:
A: to behind pottery mud engraving and the pattern forming, depress by hand, become greenwave, in 220 ℃ of tinting materials of bright and clean pure greenwave surface spray one deck heatproof, greenwave moulding after drying through 1100 ℃ high-temperature firings at standard atmosphere;
B: transfer printing glue is brushed above the greenwave that is sprayed with tinting material that also tightly is fitted on transfer paper after baking, and being placed on and tearing transfer paper after the baking in the heat transfer machine baking box is moulding, and its storing temperature is 192 ℃, and storing time is 120 minutes.
When there was background color on greenwave of the present invention surface, spray tinting material (priming paint) was cooperating the baking of tinting material color again in 175 ℃ of following heat transfer machine baking boxs on the greenwave behind 1100 ℃ the high-temperature firing earlier.
Transfer printing glue of the present invention and water ratio are: 1: 3.
Technical process of the present invention is short, efficient is high, coloring stabilized and do not influence the quality of pottery own, in the greenwave surface colour after smoking for the first time, in computer is controlled at, down baking of low temperature, make the beautiful in colour of greenwave surface, no glaze gloss but color stable, simple and tasteful, colour-fast, do not come off, thereby make Tao Chanpinji view and admire, decorate and be concealed in one.
Claims (3)
1, surface treatment technology for glaze-free Colored pottery comprises greenwave, the billet surface polishing of high-temperature firing manual assembly, greenwave, greenwave surface that baking for the first time the is sprayed with tinting material pattern of enameling, and the secondary baking moulding is characterized in that:
A: manual to behind pottery mud engraving and the pattern forming, depress at standard atmosphere, high-temperature firing greenwave moulding through 900 ℃-1100 ℃, at 160 ℃ of-220 ℃ of tinting materials of bright and clean pure moulding greenwave surface spray one deck heatproof, depress through the computer controlled temperature 150 ℃ of-195 ℃ of bakings at standard atmosphere for the first time;
B: transfer printing glue is brushed above the greenwave that is sprayed with tinting material that also tightly is fitted on transfer paper after baking, and being placed on and tearing transfer paper after the baking in the heat transfer machine baking box is moulding, and its storing temperature is 162 ℃-192 ℃, and storing time is 90-120 minute.
2, surface treatment technology for glaze-free Colored pottery according to claim 1, it is characterized in that: when there is tinting material on described greenwave surface, be sprayed with the chromatic colorant agent earlier, on through the greenwave behind 900 ℃-1100 ℃ the high-temperature firing, in 150 ℃ of-195 ℃ of following heat transfer machine baking boxs, cooperate the baking of tinting material color again.
3, surface treatment technology for glaze-free Colored pottery according to claim 1 is characterized in that: described transfer printing glue and water ratio are: 1: 3.