CN1488499A - Method for preparing wear-resistant decorating composite board of special material and board material thereof - Google Patents
Method for preparing wear-resistant decorating composite board of special material and board material thereof Download PDFInfo
- Publication number
- CN1488499A CN1488499A CNA021554277A CN02155427A CN1488499A CN 1488499 A CN1488499 A CN 1488499A CN A021554277 A CNA021554277 A CN A021554277A CN 02155427 A CN02155427 A CN 02155427A CN 1488499 A CN1488499 A CN 1488499A
- Authority
- CN
- China
- Prior art keywords
- paper
- composite plate
- wear
- preparation
- ply
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention refers to a manufacturing method for heteroxeny material wear-resisting decoration composite board. It includes material-preparation, cutting and cleaning steps to wear paper, grained paper, balance paper, high molecular film. It includes following steps: a. weighs the wear paper, grained paper, and balance paper, high molecular film; b. squeezes out polythene board; c. all the materials in a and b steps are stacked together and put into the combining line; d. produces the product by putting the material to heating and pressing device.
Description
Technical field
The present invention relates to the preparation method and composite plate sheet material, the especially preparation method of the wear-resisting decoration composite plate of xenogenesis material and the sheet material thereof realized of method thus thereof of the nonmetal composite plate in a kind of building, decoration gadget field.
Background technology
Produce plastic-aluminum or mould aluminum composite plate or the sheet forming of composite plate has accumulated many valuable experience and new creation under theory instructs and in the production practices according to the preparation method of present composite plate.Excellent works occurs yet but do not see more on the wear-resisting decoration composite plate production method that solves the xenogenesis material so far, and its product also aquatic foods is rare.Certainly, this is not have the composite plate of foreign material combination not to be present in existing building materials market; Such as on the one or both sides of glued board or plastic plate or metallic plate, pasting one or more layers woodgrained paper or polyethylene veneer etc., thereby constituted the composite plate of some kinds of styles.But, in using practice with as technical indicators such as its intensity of composite plate of the method production, toughness, service life, environmental requirement all can not make the people satisfied fully, trace it to its cause, key is still to exist many problems on the preparation method of above-mentioned composite plate or manufacture craft or the material selection.
Summary of the invention
Technical problem to be solved by this invention provides a kind of preparation method and sheet material thereof of wear-resisting decoration composite plate of xenogenesis material.Specifically provide the preparation method who the composite plate that is made of unlike material is carried out Combined Processing, method instructs the shaped component of different composite plate of processing different shape or composite plate thus again.Take this, the technical scheme that the present invention addresses the above problem is: a kind of preparation method of wear-resisting decoration composite plate of xenogenesis material, comprise respectively the getting the raw materials ready of abrasion-proof paper, woodgrained paper, balance paper, polymeric membrane, cut out, purifying step, it is characterized in that, comprise the steps: that also a. carries out weighing with described abrasion-proof paper, woodgrained paper, balance paper, polymeric membrane respectively, b. use injection machine polyethylene extrusion sheet material, c. constitutes folded the dropping on of the abrasion-proof paper in described a., the b. step, woodgrained paper, balance paper, polymeric membrane, polyethylene board together flitch and goes into recombination line; D. the flitch of going into described recombination line in the c step is sent in the execution workshop section that has at least one pressue device of heating and be prepared into composite plate sheet material.
Again, the composite plate sheet material that the preparation method produced according to above-mentioned composite plate can be a kind of wear-resisting decoration composite plate of xenogenesis material, it has wear-resisting ply of paper, the wood grain ply of paper, polyethylene (PE) layer, macromolecule membranous layer, the balance ply of paper, wherein, has one deck adhesive linkage at least between mill ply of paper one aspect and the described wood grain ply of paper in described, mutually bonding with described polyethylene (PE) layer at the another side of described wood grain ply of paper, the another side of described polyethylene (PE) layer becomes flitch and through hot pressing composite plate in aggregates by adhesive linkage and described balance ply of paper are mutually bonding.
Self-evident, the quite immediate technical scheme and the document of public publish, owing in the method that the present invention relates to, be provided with the committed step of the wear-resisting decoration composite plate of production and processing xenogenesis material, be above-mentioned a, b, c, the d step, and produced corresponding sheet material with described step, make that substantive distinguishing features that the present invention had and significant technological progress are conspicuous: the one, described preparation method can be used as a kind of wear-resisting decoration composite plate and other building materials of current manufacturing xenogenesis material, the preparation method of decorated molded member, why " to pass through " be because this method has the governed characteristics of rule, as long as grasp when entering recombination line blanking to flitch, procedure of processing just can satisfy and reproduce the preparation requirement of this method; The 2nd, relating to composite plate sheet material in this method is because the implementation process of the ladder step of this method causes it to become shaping finished product spare; Thereby can not ftracture owing in process, make affinity between the composite bed strengthen the composite bed (the especially limit of shaping finished product spare) that has guaranteed this product, also prolong the service life of product thereupon and its product on do not have (burr, press cut etc.) flaw, promptly can under the prerequisite that does not increase unnecessary rolling step, just can produce the composite plate of instructing or the finished parts of composite plate by this method.
Description of drawings
Fig. 1 is the preparation flow figure of method involved in the present invention;
Fig. 2 is a kind of section structure schematic diagram of the composite plate that the present invention relates to;
Fig. 3 is the structural representation of the composite ceiling that the present invention relates to;
Fig. 4 is another section structure schematic diagram of the composite plate that the present invention relates to.
Among the figure: 1-abrasion-proof paper (layer), 2-woodgrained paper (layer), 3-polyethylene board (PE) layer, 4-polymeric membrane (layer) (adhesive linkage), 5-balance paper (layer), 501-diaphragm (layer), the 502-monolithic composite panel, 6-installs connector (hole).
The specific embodiment
The present invention relates to a kind of preparation method of wear-resisting decoration composite plate of xenogenesis material, comprise respectively the getting the raw materials ready of abrasion-proof paper 1, woodgrained paper 2, balance paper 5, polymeric membrane (adhesive linkage) 4, cut out, purifying step, wherein, comprise the steps: that also a. carries out weighing with described abrasion-proof paper 1, woodgrained paper 2, balance paper 5, polymeric membrane 4 respectively, b. use injection machine polyethylene extrusion sheet material 3, c. constitutes folded the dropping on of the abrasion-proof paper 1 in described a., the b. step, woodgrained paper 2, balance paper 5, polymeric membrane 4, polyethylene board 3 together flitch and goes into recombination line; D. the flitch of going into described recombination line in the c step is sent in the execution workshop section that has at least one pressue device of heating and be prepared into composite plate sheet material 502.Here, the weighing in the described a step is meant respectively: abrasion-proof paper 33-62g/m
2, woodgrained paper 70-80g/m
2, balance paper 90-130g/m
2And the described pressue device of heating can be respectively that a kind of hot pressing cylinder roller press that has thermal source control or a kind of hot pressing cylinder cold press that has thermal source control and its control temperature circle of heating are between 50 ℃ of-260 ℃ of degree.In addition, described recombination line can be respectively the recombination line that is made of at least one group of hot pressing cylinder roller press that has thermal source control, or the recombination line that is made of at least one group of hot pressing cylinder cold press that has thermal source control.
Again, with opinion of the present invention, the composite plate sheet material of being produced can be a kind of wear-resisting decoration composite plate of xenogenesis material, it has wear-resisting ply of paper 1, wood grain ply of paper 2, polyethylene (PE) layer 3, macromolecule membranous layer 4, balance ply of paper 5, wherein, has at least one floor height molecule rete (adhesive linkage) 4 between described wear-resisting ply of paper 1 one aspect and the described wood grain ply of paper 2, mutually bonding with described polyethylene (PE) layer 3 at the another side of described wood grain ply of paper 2, the another side of described polyethylene (PE) layer 3 becomes flitch and through hot pressing composite plate 502 in aggregates by macromolecule layer (adhesive linkage) 4 and described balance ply of paper 5 are mutually bonding.And, can also establish on its extexine of described composite plate and have layer protecting film layer 501; On the one marginal position of described composite plate, can also be provided with connector 6 is installed.In addition, if being carried out hot-working once more, above-mentioned composite plate make it become ceiling, then can be undertaken: earlier composite plate is got the raw materials ready by following step, shear, the operation of clean film, then. is the blank part with composite plate embryo spare by the shape bar stock cutting by punching that has a corner at least, put again the blank part in heater by predetermined temperature, the time preheating, it is molding that blank part that again will be after this places the forcing press medium-pressure type, again molding is placed that beading is a beading spare on the punch press, then beading spare is placed side cut, punching, cut edge on the shock wave machine, punching, shock wave is a shaping finished product spare, at last the finished parts of gained is checked, packing, warehouse-in.Here said heater can be a kind of device in a kind of drying baker or the foregoing recombination line that has electric heating, hydro-thermal, steam heat thermal source.Such as, use above-mentioned device can produce the composite ceiling of unlike material.One of its example is that the composite plate that will make with above-mentioned material earlier is by four subangle punching presses or cut out blanking and become the ceiling blank part that has an acute angle between four hem widths and limit and the limit, then → go into drying baker to preheat, temperature adjusting between 67 ℃-89 ℃, be decided to be 7 minutes preheating time, afterwards, with blank part → go into above-mentioned recombination line to make composite ceiling.Two of its example is by six subangle punching presses or cut out blanking to become the angle between hexagon wide and limit and the limit all be the blank part of acute angle with described composite plate, simultaneously, make the hot pressing cylinder roller head machine preheating in the recombination line keep it temperature-resistant after 5 minutes, again the blank part is inserted the hot pressing cylinder roller head machine, produce the composite ceiling of moulding at last.Certainly, for easy for installation also can on described composite plate or composite plate finished parts (as ceiling), the setting connector or default installing hole are installed.
Only for supporting special case of the present invention not limit the scope of enforcement of the present invention, all relating to the preparation method of above-mentioned composite plate or with described method, instruct composite plate or the composite plate shaping finished product spare manufactured out all to belong to the claimed scope of the present invention to above-mentioned the cited case.
Claims (8)
1. the preparation method of the wear-resisting decoration composite plate of an xenogenesis material, comprise respectively the getting the raw materials ready of abrasion-proof paper, woodgrained paper, balance paper, polymeric membrane, cut out, purifying step, it is characterized in that, comprise the steps: that also a. carries out weighing with described abrasion-proof paper, woodgrained paper, balance paper, polymeric membrane respectively, b. use injection machine polyethylene extrusion sheet material, c. constitutes folded the dropping on of the abrasion-proof paper in described a., the b. step, woodgrained paper, balance paper, polymeric membrane, polyethylene board together flitch and goes into recombination line; D. the flitch of going into described recombination line in the c step is sent in the execution workshop section that has at least one pressue device of heating and be prepared into composite plate sheet material.
2. the preparation method of the wear-resisting decoration composite plate of xenogenesis material according to claim 1 is characterized in that, the weighing in the described a step is meant respectively: abrasion-proof paper 33-62g/m
2, woodgrained paper 70-80g/m
2, balance paper 90-130g/m
2
3. the preparation method of the wear-resisting decoration composite plate of xenogenesis material according to claim 1, it is characterized in that the described pressue device of heating can be respectively a kind of hot pressing cylinder roller press or a kind of hot pressing cylinder cold press that has thermal source control that has thermal source control.
4. the preparation method of the wear-resisting decoration composite plate of xenogenesis material according to claim 1, it is characterized in that, described recombination line can be respectively the recombination line that is made of at least one group of hot pressing cylinder roller press that has thermal source control, or the recombination line that constitutes by at least one group of hot pressing cylinder cold press that has thermal source control
5. according to the preparation method of the wear-resisting decoration composite plate of claim 1 or 3 described xenogenesis materials, it is characterized in that, the described pressue device of heating, its control temperature circle of heating is between 50 ℃ of-260 ℃ of degree.
6. the related sheet material of the preparation method of the wear-resisting decoration composite plate of xenogenesis material according to claim 1 is a kind of wear-resisting decoration composite plate of xenogenesis material, it has wear-resisting ply of paper, the wood grain ply of paper, polyethylene (PE) layer, macromolecule membranous layer, the balance ply of paper, it is characterized in that, has one deck adhesive linkage at least between mill ply of paper one aspect and the described wood grain ply of paper in described, mutually bonding with described polyethylene (PE) layer at the another side of described wood grain ply of paper, the another side of described polyethylene (PE) layer becomes flitch and through hot pressing composite plate in aggregates by adhesive linkage and described balance ply of paper are mutually bonding.
7. the sheet material that the preparation method of the wear-resisting decoration composite plate of xenogenesis material according to claim 6 is related is characterized in that, can also establish on its extexine of described composite plate to have the layer protecting film layer.
8. the sheet material that the preparation method of the wear-resisting decoration composite plate of xenogenesis material according to claim 6 is related is characterized in that, can also be provided with the installation connector on the one marginal position of described composite plate.