CN1484486A - Method for preparing electromagnetic shielding compound material - Google Patents
Method for preparing electromagnetic shielding compound material Download PDFInfo
- Publication number
- CN1484486A CN1484486A CNA031418007A CN03141800A CN1484486A CN 1484486 A CN1484486 A CN 1484486A CN A031418007 A CNA031418007 A CN A031418007A CN 03141800 A CN03141800 A CN 03141800A CN 1484486 A CN1484486 A CN 1484486A
- Authority
- CN
- China
- Prior art keywords
- electromagnetic shielding
- composite material
- preparation
- wood materials
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A preparation method for an electromagnetic shielding compound material includes 1) selecting a wood material to be immersed for 1-24h in magnetic metal salt solution, then to be dried 2) further controlling its size and shape, fully mixing it with modified resin and forming it into formation under certain temperature and pressure controlling its pore space rate and distribution 3) high temperature processing it under 250-1500deg.C and bright inert atmosphere, temperature rising speed: 1-20deg.C/m for 1-6h 4) coating process with organic material controlling the thickness and solidifying at room temperature.
Description
Technical field
The present invention relates to a kind of preparation method of composite material, particularly a kind of light-duty, high preparation method who absorbs the high-efficiency electromagnetic shielding composite material of low reflection electromagnetic wave ability belongs to field of compound material.
Background technology
Development along with science and technology and electronics industry, the application of various electronic equipments is also increasing, none is not radiating the electromagnetic radiation of various energy these electronic equipments, so electromagnetic interference is more and more outstanding, become the major obstacle that can many equipment, system normally play a role, electromagnetic wave becomes a serious social concern to the pollution of human work and living environment thereupon simultaneously, threatening human beings'health, and because the leakage of electromagenetic wave radiation usually causes some national defence or military information-leakage.
Find that by literature search the preparation method around electromagnetic shielding composite material has many bibliographical informations.As United States Patent (USP) 6,136,429, name is called: " Electromagnetic Shielding and Wave Absorption Sheetand The Production of the Same " (electromagnetic shielding and suction wave plate material and preparation method thereof).The technical characterstic of this patent is to become soft magnetic alloy powder/insulator/soft magnetic powder sandwich style by two surface preparation that the soft magnetic metal alloy powder are coated on the insulator sheet material, perhaps simultaneously soft magnetic alloy powder is dispersed in the insulator sheet material, further is prepared into soft magnetic alloy powder/(insulator+powder)/soft magnetic alloy powder sandwich style sheet material again.This technology is complex process on the one hand, soft magnetic alloy powder skewness usually on the other hand, thus influence effectiveness.Chinese patent 02124139.2 for another example, and name is called: " a kind of preparation method who is used for the graphite-base composite material of electromagnetic shielding ".Its characteristics are expansible graphite and the method for the additive that can produce magnetic particle by mechanical-physical or solution dissolving are mixed, and then higher temperature heating down, and compression molding.Because with graphite is raw material, cost is higher relatively.
Summary of the invention
The present invention is directed to the deficiencies in the prior art and defective, a kind of lightweight, the high preparation method who absorbs the high-efficiency electromagnetic shielding composite material of low reflection electromagnetic wave ability are provided, make the electromagnetic shielding composite material of preparation with low cost, technology is simple relatively, have the high characteristics of low, in light weight, the super wide frequency range inner shield of density effect, and solved in the past electromagnetic shielding material effectively with the electromagnetic master of being reflected into, only in the effective drawback of some frequency range inner shield.
The present invention is achieved by the following technical solutions, the present invention adopts, and a large amount of wood materials with low cost, wide material sources are raw material, burn till processing through impregnation process, forming processes and non-oxidation high temperature, and further the material that burns till processing is carried out coating and handle, promptly obtain a kind of electromagnetic shielding composite material of superior performance.
Below the inventive method is further described, method step is as follows:
1) selects wood materials, and wood materials flood preliminary treatment 1-24 hour in the aqueous solution of magnetic metal salt after, take out drying;
2) wood materials that further will handle again carries out the size processing, controls its size and dimension, and fully mixes with modified resin, carries out forming processes under uniform temperature and certain pressure, and controls its porosity and distribution of pores;
3) further carrying out high-temperature process under the non-oxygen inert atmosphere and in 250-1500 ℃ of temperature range again, programming rate 1-20 ℃/minute, temperature retention time 1-6 hour;
4) material with high-temperature process carries out the coating processing with organic substance, controls certain thickness, and cold curing promptly obtains lightweight, the high high-efficiency electromagnetic shielding composite material that absorbs low reflection electromagnetic wave ability later on.
In the step 1), improve magnetic metal salt impregnation rate can by earlier with wood materials under the non-oxygen inert conditions and in 250 ℃ of-650 ℃ of temperature ranges, handled 1-8 hour with 1-20 ℃/minute programming rate; Described this wood materials refers to straw shell, straw, cavings, jowar shell, timber etc. especially.
Magnetic metal salt in the step 1) refers to nickelous carbonate (Ni especially
2CO
3), bicarbonate nickel (Ni (HCO
3)
2), nickel nitrate (Ni
2NO
3), nickelous sulfate (Ni
2SO
4), nickel acetate (Ni
2(COOH)
2), hydrochloric acid nickel (NiCl
2), ferric carbonate (Fe
2CO
3), bicarbonate iron (Fe (HCO
3)
2), ferric nitrate (Fe
2NO
3), ferrous sulfate (Fe
2SO
4), ferric acetate (Fe (COOH)
2), iron chloride (FeCl
3), frerrous chloride (FeCl
2) in one or several.
Step 2) modified resin refers to a kind of in phenolic resins, furfural resin, pollopas, the furane resins especially in; The condition of molding of the wood materials of modified resin and size processing is: forming temperature 100-350 ℃, briquetting pressure is 10-50Mpa.
Certain organic substance in the step 4) refers to a kind of in organic silicone, acrylic acid, ABS resin, polyurethane, the epoxy resin, and step 4) floating coat thickness range is 50-1000um simultaneously.
The present invention has substantive distinguishing features and marked improvement, the electromagnetic shielding composite material that the present invention makes is with low cost, technology is simple relatively, have the high characteristics of low, in light weight, the super wide frequency range inner shield of density effect, the electromagnetic shielding composite material of the preparation of the present invention simultaneously also has the effect of high absorption in the super wide frequency range, low reflected electromagnetic shielding, solved in the past electromagnetic shielding material effectively with the electromagnetic master of being reflected into, only in the effective drawback of some frequency range inner shield.The electromagnetic shielding material of the present invention's preparation can be applied to the broadband electromagnetical shielding material in anti-electromagnetic interference, electromagnetic pollution, communication and the field of information security technology, in fields such as electronics, electric, communication, national defence good prospects for application is arranged, as can be applicable to each electron-like and electric product, in TV, sound equipment, VCD level, computer, game machine, microwave oven, mobile phone, can make electromagnetic-wave leakage drop to the national health safety limit, guarantee health, simultaneously can also prevent Electromagnetic Interference effectively and the electronics that produces and the misoperation of power equipment; Be applied to high power radar, microwave medicine equipment, microwave pulverizer, can protect operating personnel to avoid the harm of electromagnetic radiation; Simultaneously, the electromagnetic shielding material of the present invention preparation is used to eliminate the communication that building reflection electromagnetic wave tall and big in the city causes and the electromagnetic interference ghost image of navigation system.
Embodiment
Provide following three embodiment in conjunction with content of the present invention:
Embodiment one
Choosing dry wood materials-straw shell is raw material, and the programming rate with 1 ℃/minute under non-oxygen condition was handled 1 hour at 250 ℃, and dipping took out dry after 1 hour in the aqueous solution of magnetic metal salt-nickelous carbonate then.To handle and dried straw shell powder and modified resin-phenolic resins fully mix afterwards compression moulding under 100 ℃, 10MPA pressure, and further under non-oxygen inert atmosphere, be warming up to 250 ℃ with 1 ℃/minute speed, be incubated 1 hour and carry out the non-oxidation processing.Shoot out ABS resin on the sample after the high-temperature process, thickness is 50um, prepares the electromagnetic shielding composite material of the above shield effectiveness of 50dB in the 150MHZ-1.5GHZ scope after the cold curing.
Embodiment two
Choosing dry wood materials-cavings is raw material, and the programming rate with 20 ℃/minute under non-oxygen condition was handled 8 hours at 650 ℃, and dipping took out dry after 24 hours in the aqueous solution of magnetic metal salt-iron chloride then.To handle and dried cavings material powder and modified resin-furane resins fully mix afterwards compression moulding under 350 ℃, 50MPA pressure, and further under non-oxygen inert atmosphere, be warming up to 1500 ℃ with 20 ℃/minute speed, be incubated 6 hours and carry out the non-oxidation processing.Spray acrylic resin on the sample after the high-temperature process, thickness is 1000um, prepares the electromagnetic shielding composite material of the above shield effectiveness of 65dB in the 150MHZ-1.5GHZ scope after the cold curing.
Embodiment three
Choosing dry wood materials-jowar shell is raw material, and the programming rate with 1 ℃/minute under non-oxygen condition was handled 3 hours at 450 ℃, and dipping took out dry after 12 hours in the aqueous solution of magnetic metal salt-nickel nitrate then.To handle and dried jowar shell material powder and modified resin-furfural resin fully mix afterwards compression moulding under 250 ℃, 30MPA pressure, and further under non-oxygen inert atmosphere, be warming up to 875 ℃ with 10 ℃/minute speed, be incubated 4 hours and carry out the non-oxidation processing.The organic silicone resin of spraying on the sample after the high-temperature process, thickness is 500um, prepares the electromagnetic shielding composite material of the above shield effectiveness of 60dB in the 150MHZ-1.5GHZ scope after the cold curing.
Claims (8)
1. the preparation method of an electromagnetic shielding material composite material is characterized in that, method step is specific as follows:
1) selects wood materials, and wood materials flood preliminary treatment 1-24 hour in the aqueous solution of magnetic metal salt after, take out drying;
2) wood materials that further will handle again carries out the size processing, controls its size and dimension, and fully mixes with modified resin, carries out forming processes under uniform temperature and pressure, and controls its porosity and distribution of pores;
3) further carrying out high-temperature process under the non-oxygen inert atmosphere and in 250-1500 ℃ of temperature range again, programming rate 1-20 ℃/minute, temperature retention time 1-6 hour;
4) material with high-temperature process carries out the coating processing with organic substance, the control coating layer thickness, and cold curing promptly obtains lightweight later on, the high high-efficiency electromagnetic that absorbs low reflection electromagnetic wave ability shields composite material.
2. the preparation method of kind of electromagnetic shielding composite material according to claim 1, it is characterized in that, in the step 1), improve magnetic metal salt impregnation rate and adopt following method: elder generation under the non-oxygen inert conditions and in 250 ℃ of-650 ℃ of temperature ranges, handles wood materials 1-8 hour with 1-20 ℃/minute programming rate.
3. the preparation method of electromagnetic shielding composite material according to claim 1 and 2 is characterized in that, described wood materials refers to straw shell, straw, cavings, jowar shell, timber especially.
4. the preparation method of electromagnetic shielding composite material according to claim 1, it is characterized in that, in the step 1), described magnetic metal salt refers in nickelous carbonate, bicarbonate nickel, nickel nitrate, nickelous sulfate, nickel acetate, hydrochloric acid nickel, ferric carbonate, bicarbonate iron, ferric nitrate, ferrous sulfate, ferric acetate, iron chloride, the frerrous chloride one or several especially.
5. the preparation method of electromagnetic shielding composite material according to claim 1 is characterized in that step 2) in, described modified resin refers to a kind of in phenolic resins, furfural resin, pollopas, the furane resins especially.
6. the preparation method of electromagnetic shielding composite material according to claim 1 or 5, it is characterized in that the condition of molding of the wood materials of modified resin and size processing is: forming temperature 100-350 ℃, briquetting pressure is 10-50Mpa.
7. the preparation method of electromagnetic shielding composite material according to claim 1 is characterized in that, in the step 4), described organic substance refers to a kind of in organic silicone, acrylic acid, ABS resin, polyurethane, the epoxy resin.
8. the preparation method of electromagnetic shielding composite material according to claim 1 is characterized in that, in the step 4), described control coating layer thickness scope is 50-1000um.