CN1482196A - Manufacturing method for aluminum foil adhesive tape - Google Patents
Manufacturing method for aluminum foil adhesive tape Download PDFInfo
- Publication number
- CN1482196A CN1482196A CNA031317561A CN03131756A CN1482196A CN 1482196 A CN1482196 A CN 1482196A CN A031317561 A CNA031317561 A CN A031317561A CN 03131756 A CN03131756 A CN 03131756A CN 1482196 A CN1482196 A CN 1482196A
- Authority
- CN
- China
- Prior art keywords
- aluminum foil
- working method
- foil tape
- drying
- tape according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The adhesive aluminum foil tape is used to connect the condensation pipe to the outer wall of inner container of refrigerator. It consists of the following steps: preparing aluminum foil as substrate; painting one side of the aluminum foil with compound adhesive while stoving at 50-80 deg.c in a stoving channel; coating film of PE, PET or BOPP to the surface of compound adhesive while being taken out from the stoving channel and winding; coating back processing agent to the other side of the film; stoving at 50-100 deg.c for 48 hr before being set at normal temperature for 48-52 hr; painting the other side of the aluminum foil with pressure-sensitive adhesive while stoving at 150-150 deg.c in a stoving channel; winding and cutting. The adhesive aluminum foil tape may be stripped and head-to-end connected effectively, and has high binding rate to foamed polyurethane material and relatively high tensile strength.
Description
Technical field
The invention discloses a kind of working method of aluminum foil tape, more particularly is a kind of being used for the prolong of refrigerator and the refrigerator body inner bladder outer wall working method of the aluminum foil tape of cementation mutually.
Background technology
At present, be used for the prolong of refrigerator and refrigerator body inner bag mutually the sealing tape of cementation mainly contain following two kinds: a kind of is the aluminum foil tape of band separate-type paper, and another kind is that no-off paper claims aluminum foil tape linerless and that play high-temperature insulation again.With regard to preceding a kind of with regard to, it is to be base material with the aluminium foil, is the pressure sensitive adhesive of acrylic acid or the like at a side surface of this base material coating raw material, in the compound one deck separate-type paper of a side surface that is coated with pressure sensitive adhesive, this separate-type paper claims separate paper again then.When using this sealing tape, need on one side separate-type paper is removed, on one side aluminum foil tape is sticked to prolong and refrigerator body inner bladder outer wall.Bring two problems like this, the one, release trimming adhesive gel adhesive tape is thrown off on the limit can increase great inconvenience to the operative employee.The 2nd, in the operation place of this sealing tape of all uses, the separate-type paper after removing and discarding is dispersed throughout ground, bows one's head promptly to see, has both decreased and has looked forward to, and hinders workshop condition again.With regard to the back is a kind of, the separate-type paper that a kind of sealing tape will use before though it had saved, substantially overcome aforementioned deficiency, but because it is to adopt organic silicone oil to smear processing, promptly carry out release processing, thereby bring following defective by smearing organic silicone oil, the one, in use, the one section sealing tape in back be difficult to the last period sealing tape realize that in joint separately head and the tail are bonding mutually sliding property is bigger because silicone oil is handled the back.The 2nd, in the treating processes that foams between outcase of refrigerator and inner bag, because sealing tape has been done the release processing of silicone oil, the clinging power rapid drawdown can't be glued it well mutually with the polyurethane foam material affinity, directly influence the quality of refrigerator.All technical indicator of this sealing tape is: with the combination rate of polyurethane foam material be about 85%; Hold 3000 hours viscosity time; Tensile strength is 10N/cm.For this reason, no matter be on the internet, still on relevant technical magazine, often be seen in the content of collection " linerless aluminum foil tape " production technology, issued on the internet as Lianshui County, Jiangsu Province sunlight plastic cement company limited and to have advertiseed for linerless aluminum foil tape technology sincerely, and required the sealing tape back side can reach 95% with the whipping agent combination rate.
Summary of the invention
The object of the present invention is to provide a kind of working method of aluminum foil tape, head and the tail strong bond problem between back one section belt and the last end belt can not only be solved with the sealing tape of this method processing, and the good combination between itself and the polyurethane foam material can be guaranteed.
The objective of the invention is to reach like this, a kind of working method of aluminum foil tape, it may further comprise the steps:
1, choosing aluminium foil is base material;
2, to the side surface coating composite adhesive of aluminium foil base material, make drying while applying via 50 ℃～80 ℃ drying tunnel and handle;
3, go out drying tunnel and rolling, the one side with any one film among PE or PET or the BOPP etc. during rolling is compounded in aforesaid composite adhesive surface;
4, the another side to film applies back side treatment agent;
5, drying took out after 48 hours in 50 ℃～100 ℃ drying room, placed at normal temperatures 48～52 hours;
6, to the opposite side surface applied pressure sensitive adhesive of base material, make the substrate passed 100 ℃～150 ℃ drying tunnel drying while applying;
7, rolling, cut.
The working method of aluminum foil tape of the present invention, described composite adhesive are two component composite adhesives.
The working method of aluminum foil tape of the present invention, described pressure sensitive adhesive are any one in acrylate pressure sensitive adhesive or the rubber pressure-sensitive adhesive.
The working method of aluminum foil tape of the present invention, described back side treatment agent is respectively with weight part ratio: 1 part of tween, 1 part of silicone oil, 2 parts of pimelinketone, 2 parts of catalyzer, 2 parts in resol, add 100 parts of dissolution with solvents, stir down evenly and prepare through normal temperature and pressure.
The working method of aluminum foil tape of the present invention, described tween are any one in tween 30 or the tween 80.
The working method of aluminum foil tape of the present invention, described catalyzer are two bay catalyzer.
The working method of aluminum foil tape of the present invention, described resol are pure phenolic resin.
The working method of aluminum foil tape of the present invention, described solvent are any one in toluene or the dimethylbenzene.
The inventive method has strengthened the head and the tail connectivity bonding strength between the sealing tape effectively owing to having adopted the side surface to aluminium foil release with the realization of coating composite adhesive; And, because to the another side of film coating back side treatment agent, can improve the combination rate of itself and polyurethane foam material effectively; In addition, the tensile strength of aluminum foil tape also has corresponding improvement.
Accompanying drawing and drawing explanation
The sealing tape product figure of accompanying drawing for adopting the inventive method to obtain.
Among the figure: 1, aluminium foil base material; 2, compound glue layer; 3, pressure-sensitive adhesive layer; 4, adhesive layer; 5, back side treatment agent layer.
Embodiment
Embodiment 1:
1, chooses fine aluminium foil base material 1;
2, coating is 108 (II type) first, component B composite adhesive by the model that chemical plant, the southeast, Wujin, city, Wujin, Jiangsu Province produces to a side surface of aluminium foil base material 1 by coating machine, side surface at aluminium foil base material 1 forms composite adhesive layer 2, make its coating machine drying tunnel through 55 ℃ while being coated with, carry out drying and handle;
3, go out drying tunnel and rolling, in the time of rolling a face of PE film 4 is compounded in the surface of composite adhesive layer 2;
4, when a face with PE film 4 is compound on the composite adhesive layer 2, the another side coating back side treatment agent to PE film 4 forms back side treatment agent layer 5 on this surface of PE film 4.Wherein: the used tween of preparation back side treatment agent is a tween 80; Silicone oil is 107 silicone oil of being produced by Shanghai resin institute; Catalyzer is two commercially available bay catalyzer; Resol is 2402 commercially available pure phenolic resins.
5, drying 48 hours in 60 ℃ drying room was placed after the taking-up 49 hours at normal temperatures;
6, the opposite side surface to aluminium foil base material 1 applies acrylate pressure sensitive adhesive by coating machine, makes it to form varistor layer 3 at this side surface of aluminium foil base tree 1, and the coating machine drying tunnel drying while being coated with through 110 ℃ is handled;
7, rolling, cut, thus obtain bonding strength good, with the sealing tape of polyurethane foam material combination degree height, tensile strength excellence.All technical indicator test of sealing tape through the inventive method is obtained: and the combination rate between the polyurethane foam material reaches 100%; Hold the viscosity time more than or equal to 10,000 hours; Tensile strength is 80-120N/cm.
Embodiment 2:
1, chooses fine aluminium foil base material 1;
2, coating is 108 (II type) first, component B composite adhesive by the model that chemical plant, the southeast, Wujin, city, Wujin, Jiangsu Province produces to a side surface of aluminium foil base material 1 by coating machine, side surface at aluminium foil base material 1 forms composite adhesive layer 2, make its coating machine drying tunnel through 65 ℃ while being coated with, carry out drying and handle;
3, go out drying tunnel and rolling, in the time of rolling a face of PET film 4 is compounded in the surface of composite adhesive layer 2;
4, when a face with PET film 4 is compound on the composite adhesive layer 2, the another side coating back side treatment agent to PET film 4 forms back side treatment agent layer 5 on this surface of PET film 4.Wherein: the used tween of preparation back side treatment agent is a tween 30.
5, drying 48 hours in 75 ℃ drying room was placed after the taking-up 50 hours at normal temperatures;
6, the opposite side surface to aluminium foil base material 1 applies rubber pressure-sensitive adhesive by coating machine, makes it to form varistor layer 3 at this side surface of aluminium foil base material 1, and the coating machine drying tunnel drying while being coated with through 125 ℃ is handled;
7, rolling, cut, obtain aluminum foil tape as all performances as described in the embodiment 1.Embodiment 8:
1, chooses fine aluminium foil base material 1;
2, coating is 108 (II type) first, component B composite adhesive by the model that chemical plant, the southeast, Wujin, city, Wujin, Jiangsu Province produces to a side surface of aluminium foil base material 1 by coating machine, side surface at aluminium foil base material 1 forms composite adhesive layer 2, make its coating machine drying tunnel through 65 ℃ while being coated with, carry out drying and handle;
3, go out drying tunnel and rolling, in the time of rolling a face of BOPP film 4 is compounded in the surface of composite adhesive layer 2;
4, when a face with BOPP film 4 is compound on the composite adhesive layer 2, the another side coating back side treatment agent to BOPP film 4 forms back side treatment agent layer 5 on this surface of BOPP film 4.The preparation back side used material of treatment agent is selected with embodiment 1.
5, drying 48 hours in 90 ℃ drying room was placed after the taking-up 50 hours at normal temperatures;
6, the opposite side surface to aluminium foil base material 1 applies rubber pressure-sensitive adhesive by coating machine, makes it to form varistor layer 3 at this side surface of aluminium foil base material 1, and the coating machine drying tunnel drying while being coated with through 125 ℃ is handled;
7, rolling, cut, obtain aluminum foil tape as all performances as described in the embodiment 1.
Claims (8)
1, a kind of working method of aluminum foil tape is characterized in that it may further comprise the steps:
1, choosing aluminium foil is base material;
2, to the side surface coating composite adhesive of aluminium foil base material, make drying while applying via 50 ℃～80 ℃ drying tunnel and handle;
3, go out drying tunnel and rolling, the one side with any one film among PE or PET or the BOPP etc. during rolling is compounded in aforesaid composite adhesive surface;
4, the another side to film applies back side treatment agent;
5, drying took out after 48 hours in 50 ℃～100 ℃ drying room, placed at normal temperatures 48～52 hours;
6, to the opposite side surface applied pressure sensitive adhesive of base material, make the substrate passed 100 ℃～150 ℃ drying tunnel drying while applying;
7, rolling, cut.
2, the working method of a kind of aluminum foil tape according to claim 1 is characterized in that described composite adhesive is two component composite adhesives.
3, the working method of a kind of aluminum foil tape according to claim 1 is characterized in that described pressure sensitive adhesive is any one in acrylate pressure sensitive adhesive or the rubber pressure-sensitive adhesive.
4, the working method of a kind of aluminum foil tape according to claim 1, it is characterized in that described back side treatment agent is respectively with weight part ratio: 1 part of tween, 1 part of silicone oil, 2 parts of pimelinketone, 2 parts of catalyzer, 2 parts in resol, add 100 parts of dissolution with solvents, stir down evenly and prepare through normal temperature and pressure.
5, the working method of a kind of aluminum foil tape according to claim 4 is characterized in that described tween is any one in tween 30 or the tween 80.
6, the working method of a kind of aluminum foil tape according to claim 4 is characterized in that described catalyzer is two bay catalyzer.
7, the working method of a kind of aluminum foil tape according to claim 4 is characterized in that described resol is pure phenolic resin.
8, the working method of a kind of aluminum foil tape according to claim 4 is characterized in that described solvent is any one in toluene or the dimethylbenzene.