CN1480547A - 超细硬质合金的制备方法 - Google Patents

超细硬质合金的制备方法 Download PDF

Info

Publication number
CN1480547A
CN1480547A CNA031246729A CN03124672A CN1480547A CN 1480547 A CN1480547 A CN 1480547A CN A031246729 A CNA031246729 A CN A031246729A CN 03124672 A CN03124672 A CN 03124672A CN 1480547 A CN1480547 A CN 1480547A
Authority
CN
China
Prior art keywords
powder
hard alloy
batching
sintering
value
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031246729A
Other languages
English (en)
Other versions
CN1207418C (zh
Inventor
李来荣
刘知径
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhuzhou Cemented Carbide Group Co Ltd
Original Assignee
Zhuzhou Cemented Carbide Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuzhou Cemented Carbide Group Co Ltd filed Critical Zhuzhou Cemented Carbide Group Co Ltd
Priority to CN 03124672 priority Critical patent/CN1207418C/zh
Publication of CN1480547A publication Critical patent/CN1480547A/zh
Application granted granted Critical
Publication of CN1207418C publication Critical patent/CN1207418C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明涉及一种超细硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结等工序，在配料时选用HCP值为(26.5～28.5)KA/m的WC粉和(5.7～6.2)wt％的Co粉，并加入(0.18～0.22)wt％的VC，配料计算时，碳平衡值为(+0.18～+0.20)％。采用本发明的方法可使硬质合金的硬度达HV3：1800～1920，提高其耐磨性。并且可使用该种超细硬质合金制造的PCB微钻的钻径最小达0.5mm。

Description

超细硬质合金的制备方法
技术领域：
本发明涉及一种超细硬质合金的制备方法，特别是WC-Co超细硬质合金的制备方法。
背景技术：
硬质合金以其高硬度和高强度有着广泛的用途。目前国内在制造PCB微钻和有色金属切削刀片时所采用的材质一般为粒度0.8μm左右的WC粉和重量百分比为10％的Co粉，并添加重量百分比为0.5％的晶粒抑制剂Cr3C2粉，经湿磨、干燥、压制成型和烧结等工序制得。用该方法制得的硬质合金硬度较低，HV3：1550～1650，耐磨性较差。
发明内容：
本发明的目的是提供一种超细硬质合金的制备方法，使得用本方法制得的硬质合金耐磨性增加。
为达到上述目的，本发明的超细硬质合金的制备方法包括：配料、湿磨、干燥、压制成型和烧结等工序，在配料时选用HCP值为(26.5～28.5)KA/m的WC粉和(5.7～6.2)wt％的Co粉，并加入(0.18～0.22)wt％的VC，配料计算时，碳平衡值为(+0.18～+0.20)％。
由于选用了细WC粉以及采用适量的VC作晶粒抑制剂，可使得硬质合金中WC的平均晶粒度达(0.4～0.6)μm，在强度基本不变情况下，可使硬质合金的硬度达HV3：1800～1920，提高其耐磨性。并且可使用该种超细硬质合金制造的PCB微钻的钻径从过去最小1.0mm减小到最小0.5mm。
作为本发明的进一步改进，在配料时可加入(0.05～0.08)wt％的Cr3C2，这样可在不降低超细硬质合金使用性能情况下，提高其抗氧化性。
具体实施方式：
实施例1：配料时选用费氏粒度1.2μm的Co粉6.0wt％，1.2μmVC0.20wt％，HCP值为26.9KA/m的余量WC粉，控制碳平衡值+0.20％，以酒精作研磨介质，液固比420ml/Kg，球料比4.8∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1860，抗弯强度4230N/mm2，WC平均晶粒度为0.5μm。
实施例2：配料时选用费氏粒度0.5μm的Co粉5.7wt％，1.0μmVC0.22wt％，0.05wt％的Cr3C2，HCP值为28.5KA/m的余量WC粉，控制碳平衡值+0.20％，以酒精作研磨介质，液固比420ml/Kg，球料比4.8∶1，球磨80小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1920，抗弯强度3930N/mm2，WC平均晶粒度为0.45μm。
实施例3：配料时选用费氏粒度1.35μm的Co粉6.2wt％，1.2μmVC0.18wt％，0.08wt％的Cr3C2，HCP值为26.5KA/m的余量WC粉，控制碳平衡值+0.18％，以酒精作研磨介质，液固比420ml/Kg，球料比4.8∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1810，抗弯强度4350N/mm2，WC平均晶粒度为0.6μm。
实施例4：配料时选用费氏粒度1.15μm的Co粉6.0wt％，1.0μmVC0.20wt％，0.06wt％的Cr3C2，HCP值为27.8KA/m的余量WC粉，控制碳平衡值+0.20％，以酒精作研磨介质，液固比420ml/Kg，球料比4.8∶1，球磨80小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1900，抗弯强度4120N/mm2，WC平均晶粒度为0.5μm。
实施例5：配料时选用费氏粒度0.75μm的Co粉5.9wt％，1.2μmVC0.20wt％，HCP值为27.0KA/m的余量WC粉，控制碳平衡值+0.20％，以酒精作研磨介质，液固比420ml/Kg，球料比4.8∶1，球磨85小时，喷雾干燥制得混合料，经模压成型后，在气压烧结炉1410℃烧结，粗磨后的Φ3.25×38.5mm的棒材，其HV3：1850，抗弯强度4440N/mm2，WC平均晶粒度为0.5μm。

Claims (2)

1、一种超细硬质合金的制备方法，包括：配料、湿磨、干燥、压制成型和烧结等工序，其特征在于：在配料时选用HCP值为(26.5～28.5)KA/m的WC粉和(5.7～6.2)wt％的Co粉，并加入(0.18～0.22)wt％的VC，配料计算时，碳平衡值为(+0.18～+0.20)％。
2、根据权利要求1所述的超细硬质合金的制备方法，其特征在于：在配料时可加入(0.05～0.08)wt％的Cr3C2。
CN 03124672 2003-07-22 2003-07-22 超细硬质合金的制备方法 Expired - Lifetime CN1207418C (zh)