CN1480495A - Fluorine-carbon lacquer for sectional plastic-steel material and its preparing method - Google Patents
Fluorine-carbon lacquer for sectional plastic-steel material and its preparing method Download PDFInfo
- Publication number
- CN1480495A CN1480495A CNA031531504A CN03153150A CN1480495A CN 1480495 A CN1480495 A CN 1480495A CN A031531504 A CNA031531504 A CN A031531504A CN 03153150 A CN03153150 A CN 03153150A CN 1480495 A CN1480495 A CN 1480495A
- Authority
- CN
- China
- Prior art keywords
- resin
- fluoro
- component
- fluorine
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A F-C paint for plastic-steel section is composed of the individually packed component A and B. Said component A contains fluoric resin, promoter resin, pigment, filler, assistant, drying agent and solvent mixture. Said component B is cross-linking agent. Its advantages are high adhesion and high resistance to aging and salt fog.
Description
Technical field
The present invention relates to coating industry, specifically, relate to plastic-steel section bar and coat with lacquer and preparation method thereof with fluorine carbon.
Background technology
There is more than 3300 of plastic-steel door and window production line in China at present, can produce 6,000 ten thousand square metres of door and windows every year, is that 300,000,000 square metres building is supporting.Because plastic-steel door and window has easy processing, price is low than aluminum alloy doors and windows, and advantages such as good seal performance are being to occupy leading sash stuff behind wooden door and window on the door and window market.Building the plastic-steel door and window of being installed now most is the single white door and window of tone, can not satisfy human consumer's needs, and the developed regions top-grade building strengthens day by day to colored door and window demand.Because of door and window directly is subjected to solar radiation, ultraviolet ray can be quickened the aging of plastic-steel section bar, shorten door and window work-ing life, the effective means that overcomes above defective is exactly the durable in use and various coating of color of external coating one deck at section bar, can make plastic-steel door and window have characteristics such as attractive in appearance, corrosion-resistant, super-weathering resistance and self-cleaning property.
The best coating of weathering resistance is fluorocarbon coating at present, and about the fluorocarbon coating aspect, our company once applied for patent in nineteen ninety-five, and name is called " fluoro-containing coating method for making and application thereof ", and the patent No. is 95111961.3.Though it is good that this series products has sticking power, paint film mechanical property excellence, characteristics such as salt fog resistance and ageing resistance are good, but after it must coat supporting priming paint earlier, be coated with fluorine carbon lacquer again, the operating procedure more complicated, production efficiency is low, can not satisfy in enormous quantities, and high efficiency construction needs.Therefore, be badly in need of solving the bottom surface unification property problem of fluorine carbon lacquer, guarantee that the sticking power of fluorine carbon finishing paint is good, characteristics such as mechanical property excellence do not change, and have become the task of top priority.
Summary of the invention
The objective of the invention is to remedy prior art and have weak point, and provide a kind of construction operation simple, the mechanical property excellence, ageing resistance, two component plastic-steel section bars that the salt fog performance is good coat with lacquer and preparation method thereof with fluorine carbon.Technical scheme of the present invention is as follows:
Plastic-steel section bar proposed by the invention coats with lacquer with fluorine carbon, contains the component A and the component B of independent packing; Wherein component A has: fluoro-resin, promotor resin, color stuffing, auxiliary agent, siccative and mixed solvent; Component B has: linking agent; Each component weight ratio: fluoro-resin: promotor portions of resin color stuffing: auxiliary agent: siccative: mixed solvent: linking agent=1: 0.07~0.15: 0.30~0.40: 0.02~0.10: 0.0010~0.0035: 0.01~0.20: 0.10~0.16; Fluoro-resin is by trifluorochloroethylene, vinyl fatty ester, hydroxyl vinyl ether and the aliphatics olefin(e) acid is quarternary copolymerized forms, its hydroxyl value 40~60mgKOH/g, and carboxylic value 3~8mgKOH/g, solid content 40~70%, and fluorine content is 15~45%; The promotor resin is the compound that is made of special polyester resin, as the LTW-B resin of Degussa company; Color stuffing comprises Rutile type Titanium Dioxide, phthalocyanine blue, red iron oxide, permanent yellow, carbon black, talcum powder etc.; Linking agent is a hexamethylene vulcabond dimer, as the DESMODEYN75 of German BAYER company; Auxiliary agent is the mixture of following three kinds of auxiliary agents, and auxiliary agent is as follows:
(1) flow agent, composition are organically-modified siloxanes or fluorine-carbon modified polyacrylic acid, as 3033,3777 of Dutch EFKA company (EFKA), and as 358 of German Bi Ke chemical company (BYK), preferred BYK-358, consumption is 0.001~0.005 times of fluoro-resin;
(2) defoamer, composition are polysiloxane solution, and as 066 of German Bi Ke chemical company (BYK), consumption is 0.001~0.005 times of fluoro-resin;
(3) dispersion agent, composition are the high molecular weight block copolymer solution that contains affine pigment group, and as 161 of German Bi Ke chemical company (BYK), consumption is 0.01~0.09 times of fluoro-resin;
Solvent is dimethylbenzene, n-butyl acetate by 1: 1~2 mixture;
The preparation method that plastic-steel section bar of the present invention coats with lacquer with fluorine carbon: the A component is pressed formulation weight than the dispersion agent of fluoro-resin, promotor resin and the specified amount of adding part in container, mixed solvent partly, the various color stuffings of back adding stir, give dispersion, grind, after reaching the regulation fineness, add residual fluorine resin, siccative and various auxiliary agent again by formula ratio, and with remaining mixed solvent adjusting viscosity, after-filtration stirs, sampling is made lacquer according to a certain ratio with component B, through every technical indicator metering packing after the assay was approved;
The drying conditions that plastic-steel section bar of the present invention coats with lacquer with fluorine carbon: normal temperature self-drying or low-temperature bake: storing temperature: 60 ℃~70 ℃, storing time: 50~60 minutes;
Plastic-steel section bar is with containing a spot of UV light absorber in the fluorine carbon lacquer, and as 5060 of Ciba company (CIBA), consumption is 0~0.02 times of fluoro-resin; Can also contain a spot of anti-stain resistant agent, as 3700 of German Bi Ke company (BYK), consumption is 0~0.02 times of fluoro-resin.
Raw material is described below:
1, fluoro-resin: be product by our company's development and production, product index: hydroxyl value 40~60mgKOH/g, carboxylic value 3~8mgKOH/g, solid content 40~70%, and fluorine content is 15~45%; The fluoro-resin that other company produces as long as performance index are qualified, also can adopt.
2, promotor resin LTW-B: be Degussa company product.
3, linking agent DESMODEYN75: be German BAYER company product.
4, color stuffing comprises Rutile type Titanium Dioxide, phthalocyanine blue, red iron oxide, permanent yellow, carbon black, talcum powder etc., and commercially available or import all can be used.
5, auxiliary agent B YK-358, BYK-066, BYK-161; Be German Bi Ke chemical company product.
6, siccative: dibutyl tin laurate, commercially available or import all can be used.
The present invention has following advantage compared to existing technology:
1. plastic-steel section bar of the present invention can be brushed or spray with fluorine carbon lacquer, is fit to normal temperature self-drying or low-temperature bake, and the plastic-steel section bar coating process is simple, can satisfy streamline operration, and province's energy saves time;
2. repeat to cover with paint, lacquer, colour wash, etc. and repair easily;
3. coating surface can be low, and pollution resistance is good, easy cleaning;
4. not be used in to give on the plastic-steel section bar and prime;
5. paint film mechanical property excellence;
6. the salt fog resistance of paint film and ageing resistance excellence.
Embodiment:
Exemplify five embodiment below and four comparative examples are further specified the present invention, but be not limited only to these embodiment.
Embodiment 1
In the beaker of 500ml, add fluoro-resin (53%) 35g, promotor resin 5g, dispersant B YK-161 1.5g, mixed solvent 3.0g, back adding titanium dioxide 20.0g stirs, talcum powder 2.0g gives dispersion, grinds, when reaching regulation fineness 20 μ m, press formula ratio and add residual fluorine resin 30g and flow agent BYK-358 0.2g, defoamer BYK-066 0.1g, siccative 0.2g and mixed solvent 3.0g, viscosity is regulated in the back that stirs, filter, sampling is coated with lacquer by 0.10~0.16 proportioning system with component B, detects through every technical indicator, after the assay was approved metering packing.
Embodiment 2~5
Operation steps and reaction conditions are with embodiment 1, and concrete consumption of raw material such as table 1 make plastic-steel section bar and coat with lacquer performance such as table 2 with fluorine carbon.
Table 1. embodiment 1~5 proportioning raw materials wt/wt
Material name | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
Fluoro-resin (53%) g | ????65 | ????65 | ????65 | ????65 | ????65 |
Promotor resin g | ????5.0 | ????5.0 | ????5.0 | ????5.0 | ????5.0 |
Titanium dioxide g | ????20.0 | ????5.0 | ????17.0 | ????5.0 | ????18.0 |
Red iron oxide g | ????----- | ????15.0 | ????----- | ????----- | ????----- |
The blue g of phthalein cyanogen | ????----- | ????----- | ????3.0 | ????----- | ????----- |
Permanent yellow g | ????----- | ????----- | ????----- | ????15.0 | ????----- |
Carbon black g | ????----- | ????----- | ????----- | ????----- | ????2.0 |
Talcum powder g | ????2.0 | ????2.0 | ????2.0 | ????2.0 | ????2.0 |
????BYK-358g | ????0.2 | ????0.2 | ????0.2 | ????0.2 | ????0.2 |
????BYK-066g | ????0.1 | ????0.1 | ????0.1 | ????0.1 | ????0.1 |
????BYK-161g | ????1.5 | ????5.3 | ????3.76 | ????5.3 | ????3.5 |
Siccative g | ????0.2 | ????0.2 | ????0.2 | ????0.2 | ????0.2 |
Mixed solvent g | ????6.0 | ????2.2 | ????3.74 | ????2.2 | ????4.0 |
Linking agent g | ????10.0 | ????10.0 | ????10.0 | ????10.0 | ????10.0 |
Table 2. film performance test data
Comparative example 1~4
Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 |
60 ℃ of gloss | ????85 | ????86 | ????84 | ????86 | ????84 |
Pencil hardness | ????2H | ????2H | ????2H | ????2H | ????2H |
Sticking power (cross-hatching) 100/100 | Qualified | Qualified | Qualified | Qualified | Qualified |
Snappiness/flawless | Qualified | Qualified | Qualified | Qualified | Qualified |
??? Shock resistance 50kgcm | By | By | By | By | By |
Recoatability | Well | Well | Well | Well | Well |
Acid resistance 10%H 2SO 4, 7 days no changes of normal temperature | Qualified | Qualified | Qualified | Qualified | Qualified |
Alkali resistance 10%NaOH, 7 days no changes of normal temperature | Qualified | Qualified | Qualified | Qualified | Qualified |
Resistance to salt water 3%NACL, 7 days no changes of normal temperature | Qualified | Qualified | Qualified | Qualified | Qualified |
Anti-10% ammoniacal liquor, 7 days no changes of normal temperature | Qualified | Qualified | Qualified | Qualified | Qualified |
Salt fog resistance 3000 hours, no change | Qualified | Qualified | Qualified | Qualified | Qualified |
Ageing resistance, 2000 hours | Paint film does not have efflorescence, does not have be full of cracks, does not have and bubbles, and nothing comes off, and allows light discolouration and loss of gloss | ||||
Temperature tolerance-30 ℃~100 ℃ | No change | ||||
Anti-3% washing composition (40 ℃) 〉=72h | There is not influence | ||||
Water tolerance 288h | Do not have and bubble, nothing comes off, and does not have obvious loss of gloss and changes | ||||
Abrasion resistance 12000 times | Paint film does not have breakage | ||||
Freeze-thaw resistance circulation 20 times | Paint film does not have foaming, and nothing comes off | ||||
Stain resistance | The reflection rate of descent is not more than 2.3 |
Operation steps and reaction conditions are with embodiment 1, and raw material consumption such as table 3 make plastic-steel section bar and compare as table 4 with fluorine carbon lacquer performance.
Table 3. comparative example 1~4 proportioning raw materials wt/wt
Material name | Comparative example 1 | Comparative example 2 | Comparative example 3 | Comparative example 4 |
Fluoro-resin (53%) g | ????65 | ????65 | ????----- | ????65 |
Acrylic resin (53%) g | ????----- | ????----- | ????65 | ????----- |
Adhesion promoter g | ????----- | ????5.0 | ????5.0 | ????----- |
Titanium dioxide g | ????20.0 | ????20.0 | ????20.0 | ????17.0 |
Red iron oxide g | ????----- | ????----- | ????----- | ????----- |
The blue g of phthalein cyanogen | ????----- | ????----- | ????----- | ????5.7 |
Permanent yellow g | ????----- | ????----- | ????----- | ????----- |
Carbon black g | ????----- | ????----- | ????----- | ????----- |
Talcum powder g | ????2.0 | ????2.0 | ????2.0 | ????2.0 |
????BYK-358g | ????0.2 | ????0.2 | ????0.2 | ????0.2 |
????BYK-066g | ????0.1 | ????0.1 | ????0.1 | ????0.1 |
????BYK-161g | ????1.5 | ????1.5 | ????1.5 | ????3.76 |
Siccative g | ????0.2 | ????----- | ????0.2 | ????0.2 |
Mixed solvent g | ????6.0 | ????6.0 | ????6.0 | ????1.04 |
Linking agent g | ????9.5 | ????9.98 | ????10.0 | ????9.5 |
Table 4. film performance test data
Above result shows:
Test event | Embodiment 1 | Comparative example 1 | Comparative example 2 | Comparative example 3 | Comparative example 4 |
60 ℃ of gloss | ????85 | ????85 | ????85 | ????85 | ????86 |
Surface drying (min) is done solid work (h) | ????20 ????24 | ????20 ????24 | ????30 ????48 | ????20 ????24 | ????20 ????24 |
Pencil hardness | ????2H | ????2H | ????2H | ????H | ????2H |
Sticking power (cross-hatching) 100/100 | Qualified | Defective | Qualified | Defective | Defective |
Snappiness/mm flawless | Qualified | Qualified | Qualified | Qualified | Qualified |
Shock resistance 50kg.cm | By | By | By | By | By |
Acid resistance 10%H 2SO 4. 7 days no changes of normal temperature | Qualified | Qualified | Qualified | Defective | Qualified |
7 days no changes of alkali resistance 10%NaOH. normal temperature | Qualified | Qualified | Qualified | Defective | Qualified |
7 days no changes of resistance to salt water 3%NACL. normal temperature | Qualified | Qualified | Qualified | Defective | Qualified |
Anti-10% ammoniacal liquor. 7 days no changes of normal temperature | Qualified | Qualified | Qualified | Defective | Qualified |
Salt fog resistance 3000 hours, no change | Qualified | Qualified | Qualified | Defective | Qualified |
Anti-2000 hours agings, paint film does not have efflorescence, does not have be full of cracks, does not have and bubbles, and nothing comes off, and allows variable color and loss of gloss | Qualified | Qualified | Qualified | Defective | Qualified |
1. add in the fluoro-resin with the promotor resin, compatibility is relatively good, can improve paint film adhesion well;
By fluoro-resin as the main body filmogen, the hardness of paint film, salt fog resistance and ageing resistance, anti-ammoniacal liquor, resistance to salt water, alkali resistance, acid resistance improve 2~3 times than acrylic coating;
3. add a spot of siccative, can improve the drying property of filming well;
4. different pigment, dispersant dosage is different.
Product of the present invention is fit to the covering with paint and the protection on plastic-steel section bar surface.
Claims (4)
1, plastic-steel section bar is with fluorine carbon lacquer, it is characterized in that it contains the component A and the component B of independent packing; Wherein component A has fluoro-resin, promotor resin, color stuffing, auxiliary agent, siccative and mixed solvent; Component B has linking agent; Each component weight ratio fluoro-resin: promotor portions of resin color stuffing: auxiliary agent: siccative: mixed solvent: linking agent=1: 0.07~0.15: 0.30~0.40: 0.02~0.10: 0.0010~0.0035: 0.01~0.20: 0.10~0.16.
2, fluorine carbon lacquer according to claim 1, it is characterized in that fluoro-resin is by trifluorochloroethylene, vinyl fatty ester, hydroxyl vinyl ether and the aliphatics olefin(e) acid is quarternary copolymerized forms, its hydroxyl value 40~60mgKOH/g, carboxylic value 3~8mgKOH/g, solid content 40~70%, and fluorine content is 15~45%; The promotor resin is the compound that is made of special polyester resin, as the LTW-B resin of Degussa company; Color stuffing comprises Rutile type Titanium Dioxide, phthalocyanine blue, red iron oxide, permanent yellow, carbon black, talcum powder etc., and homemade import all can be used; Linking agent is a hexamethylene vulcabond dimer, as the DESMODEYN75 of German BAYER company; Be the mixture of three kinds of auxiliary agents below the auxiliary agent, auxiliary agent is as follows:
(1) flow agent, composition are organically-modified siloxanes or fluorine-carbon modified polyacrylic acid, and as EFKA-3033, the EFKA-3777 of Dutch EFKA company, as the BYK-358 of German Bi Ke chemical company, consumption is 0.001~0.005 times of fluoro-resin;
(2) defoamer, composition are polysiloxane solution, and as the BYK-066 of German Bi Ke chemical company, consumption is 0.001~0.005 times of fluoro-resin;
(3) dispersion agent, composition are the high molecular weight block copolymer solution that contains affine pigment group, and as the BYK-161 of German Bi Ke chemical company, consumption is 0.01~0.09 times of fluoro-resin; Solvent is dimethylbenzene, n-butyl acetate by 1: 1~2 mixture.
3, plastic-steel section bar is with the preparation method of fluorine carbon lacquer: it is characterized in that the A component by formulation weight than the dispersion agent that in container, adds fluoro-resin, promotor resin and specified amount partly, partly mixed solvent, back adding color stuffing stirs, give dispersion, grind, after reaching the regulation fineness, add residual fluorine resin, siccative and various auxiliary agent again by formula ratio, and with remaining mixed solvent adjusting viscosity, after-filtration stirs, sampling is made lacquer according to a certain ratio with component B, through every technical indicator metering packing after the assay was approved.
4, according to the preparation method of the described plastic-steel section bar of claim 3, it is characterized in that drying conditions is: normal temperature self-drying or low-temperature bake, storing temperature: 60 ℃~70 ℃ with fluorine carbon lacquer; Storing time: 50~60 minutes.