CN1458242A - 淋浴自动调温阀用蜡质感温介质 - Google Patents

淋浴自动调温阀用蜡质感温介质 Download PDF

Info

Publication number
CN1458242A
CN1458242A CN02109670A CN02109670A CN1458242A CN 1458242 A CN1458242 A CN 1458242A CN 02109670 A CN02109670 A CN 02109670A CN 02109670 A CN02109670 A CN 02109670A CN 1458242 A CN1458242 A CN 1458242A
Authority
CN
China
Prior art keywords
wax
temperature
sensing medium
temperature sensing
regulating valve
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN02109670A
Other languages
English (en)
Other versions
CN1183230C (zh
Inventor
孙剑锋
高蒿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Petroleum and Chemical Corp
Sinopec Fushun Research Institute of Petroleum and Petrochemicals
Original Assignee
China Petroleum and Chemical Corp
Sinopec Fushun Research Institute of Petroleum and Petrochemicals
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Petroleum and Chemical Corp, Sinopec Fushun Research Institute of Petroleum and Petrochemicals filed Critical China Petroleum and Chemical Corp
Priority to CNB021096708A priority Critical patent/CN1183230C/zh
Publication of CN1458242A publication Critical patent/CN1458242A/zh
Application granted granted Critical
Publication of CN1183230C publication Critical patent/CN1183230C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本发明涉及一种淋浴自动调温阀用蜡质感温介质的制备方法。本发明的制备方法是以含有C18～C23的石油蜡类物质为原料，经发汗或多次发汗－精制工艺制得目的产物。本发明制备过程简单，原料价格低，精制费用低，有效降低了产品的成本。用本发明方法制备的产物制成的调温阀用于淋浴装置，可达到自动调节水温的作用，克服了现有调温阀调温慢、浪费水的情况。

Description

淋浴自动调温阀用蜡质感温介质
1、技术领域
本发明属于特种蜡技术领域，特别是涉及一种自动调温阀用蜡质感温介质，具体地说是淋浴自动调温阀用蜡质感温介质及其制备方法。
2、背景技术
用蜡类物质作感温介质的温控阀是一神自力式的开关，其原理是利用蜡类介质相变过程中体积变化控制阀门开度从而达到控制物流流量的目的。这种蜡质温控阀同时具有感应环境温度变化和输出动作的双重作用。因为蜡质温控开关具有温度特性不随系统压力而明显变化、机械强度高、化学稳定性好、容易批量生产以及安装、成本低、温控稳定可靠等优点，所以在内燃机冷却系统、各神发动机冷却等系统上得以广泛应用。
现有技术中介绍的制备蜡质感温介质的方法均以溶剂萃取方法为主，例如：DD 241,829、DD 241,830等专利是以溶剂萃取的方法制备80～90℃的蜡质感温介质；而DD 247,572、SU 1,084,289、RU 2,009,171、US 5,223,122等专利介绍的制备方式，也是以溶剂萃取为主。这些专利介绍的制备方式不仅对环境有污染，而且产物适用范围一般为10～15℃左右，不适于淋浴自动调温。
目前淋浴器一般配有两个阀门，分别控制冷热水的流量。这神淋浴器使用时需不断手动调节这两个阀门以使出口处水温达到35～42℃的人体适宜的温度。这样不仅费时费力，而且调节水温的过程还浪费大量的水资源。自动控制淋浴水温的相关技术需使用自动控制系统或其它一些控温元件等。如97204892.8公开了一神采用温度传感器和压力检测传感器共同作用的淋浴水温控制方法，但该种方法较为复杂，不适用于各个淋浴头的水温控制；91230691.2公开了一神采用金属温控弹簧控制淋浴水温的自动控温装置，但该装置需使用特殊的温控弹簧，其使用稳定性差，并且成本高、寿命短。
感温蜡已在一些领域广泛应用，但在控制淋浴水温方面还没有技术公开，主要原因在于没有性能适宜的感温蜡材料，另外感温蜡的生产成本太高也是限制这类产品应用的重要原因。
3、发明内容
本发明的目的在于提供一种适用于淋浴水温自动控制用的感温蜡，具体地说是可在35～42℃范围内自动调节水温的感温蜡，本发明同时提供一神方法简便、成本低廉的感温蜡制备方法。
本发明的淋浴自动调温阀用蜡质感温介质，是利用含有C18～C23的石油蜡类物质为原料，经1～3次发汗并通过精制工艺制得，这神产物的熔点为35～42℃，是具有分子量分布窄、正构烷烃含量高等特点的蜡类物质。用于淋浴自动调温阀时，可以在35～42℃范围内自动调节水温。
本发明蜡质感温介质的具体生产过程为：
将含有C18～C23石油蜡类物质原料进行1～3次发汗制取熔点为35～42℃的蜡组分。所述的C18～C23石油蜡类物质原料为蜡膏或皂蜡，蜡膏是减一线、减二线馏分油经脱蜡所得的含油小于20m％的蜡膏等；可选的皂蜡为熔点在40～45℃的含油小于5m％的商品皂蜡。所述的发汗过程及条件为：发汗终点温度为35～44℃，每次发汗制取熔点在35～42℃的组分作为产物或下次发汗的原料。发汗按照本领域通常的过程进行，即熔融的原料先缓慢降温至熔点以下，然后缓慢升温至终点温度，在升温过程中可分段截取蜡下，分别记作一蜡下、二蜡下、三蜡下等，通过一个发汗过程可得到熔点不同的蜡上及若干蜡下组分。
将上述过程制备的蜡组分经白土精制即得目的产品。白土精制条件为添加3％～5％白土，在120～130℃下处理0.5～1小时。
本发明的优点是：通过选择适宜的原料，采用一定的精制方法，制备出可以用于淋浴自动控制水温的感温蜡。本发明制备方法的原料价格便宜，制备过程简单，精制费用低，可以有效降低最终产品的成本，使产品获得广泛的应用。本发明感温蜡的物理、化学性质稳定，用于制备淋浴自动控温阀时，可以获得良好的使用效果，并可具有较长的使用寿命。
4、附图说明
图1、2是本发明实施例1、实施例2制备的淋浴调温阀蜡质感温介质的膨胀性能曲线，图中横座标为温度，纵座标为相对行程量。
5、具体实施方式
利用蜡质温控阀具有感应温度变化并作出相应调整的特性，可将其应用于淋浴器的自动调温，其原理是通过其感应淋浴喷头处水温的变化控制热水的流量，从而达到自动调节淋浴水温的目的。
利用本发明制备的蜡质感温介质制成的蜡质温控阀可根据淋浴器出口水温的变化迅速调节热水的流量，从而达到自动调节淋浴水温的目的。通过选用适宜原料，并采用一定的精制过程，获得成本低廉、性能优良的感温蜡产品。
以下通过实施例说明本发明的蜡质感温介质的制备方法及膨胀性能。
实施例1：
取熔点为42.5℃、油含量为3％的商品皂蜡，以42.0℃为终点温度进行发汗，取其三蜡下(熔点为40.8℃)为产物。
将上述发汗产物在120℃下加入5％白土，混合0.5小时后过滤即得目的产物。由此产物制成淋浴调温阀的膨胀性能曲线如图1所示。
实施例2：
取熔点为42.2℃的减二线蜡膏(油含量为15m％)，以43.5℃为终点温度进行发汗，取其二蜡下(熔点为38.7℃)为产物；用上述产物以42.0℃为终点温度进行发汗，取其二蜡下(熔点为35.8℃)为产物；用上述产物以36.0℃为终点温度进行发汗，取其蜡上(熔点为36.8℃)为产物。
将上述经三次发汗制得的产物在130℃下加入3％白土，混合1小时后过滤即得目的产物。由此产物制成淋浴调温阀的膨胀性能曲线如图2所示。

Claims (7)

1、一神淋浴自动调温阀用蜡质感温介质，其特征在于其熔点为35～42℃，以含有C18～C23的石油蜡类物质为原料，经1～3次发汗并精制制得。
2、按照权利要求1所述的蜡质感温介质，其特征在于所述的石油蜡类物质原料是蜡膏或皂蜡。
3、按照权利要求1所述的蜡质感温介质，其特征在于所述的发汗终点温度为35～44℃。
4、按照权利要求1的蜡质感温介质，其特征在于所述的精制是加入3％～5％活性白土进行的。
5、按照权利要求4所述的蜡质感温介质，其特征在于所述的精制为在120～130℃下进行的，时间为0.5～1小时。
6、按照权利要求2所述的蜡质感温介质，其特征在于所述的蜡膏是减一线、减二线馏分油经脱蜡所得的含油小于20％的蜡膏。
7、按照权利要求2所述的蜡质感温介质，其特征在于所述的皂蜡是熔点40～45℃含油小于5％的商品皂蜡。
CNB021096708A 2002-05-15 2002-05-15 淋浴自动调温阀用蜡质感温介质 Expired - Lifetime CN1183230C (zh)