CN1454944A - Antibacterial water-based coating composition - Google Patents
Antibacterial water-based coating composition Download PDFInfo
- Publication number
- CN1454944A CN1454944A CN 02117093 CN02117093A CN1454944A CN 1454944 A CN1454944 A CN 1454944A CN 02117093 CN02117093 CN 02117093 CN 02117093 A CN02117093 A CN 02117093A CN 1454944 A CN1454944 A CN 1454944A
- Authority
- CN
- China
- Prior art keywords
- weight
- titanium dioxide
- water paint
- paint composition
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a safe, non-toxic and long-acting broad-spectrum antibacterial water coating composite capable of degrading organic dyed material. Its composition comprises coating emulsion, water and conventional additive and nano titanium dioxide photocatalyst which are dispersed in said emulsion and water, in which the content of said nano titanium dioxide photocatalyst in said antibacterial water coating composite is 0.1-5.0% of total weight of said composite, and the grain size distribution of most of nano titanium dioxide photocatalyst is less than 100 nm, and its antibacterial efficiency is up to 99%.
Description
Invention field
The present invention relates to the long-acting broad-spectrum antibacterial water-based paint compositions of a kind of safety non-toxic and energy degradable organic pollutant.More particularly, the present invention relates to mix and with the antibiotic water paint composition of the nano titanium dioxide photocatalyst of conjugated system organism surface modification a kind of comprising with semiconductor material.
Prior art
Along with the raising of global environmental consciousness, people are urgent further to the demand of functional environment-friendly coating.By adopting the water-based and the powder coating of low volatility, wherein add the nano functional filler of safety non-toxic, be the effective means that reduces source of pollution, coating is extended more forward in the mankind's effect.Coating must be considered its usefulness and toxicity problem with sterilant, and security is an important factor of considering use value.At present, the sterilant that coating adopts mainly contains the substituted arene class, heterogeneous ring compound, organic bactericide such as aminated compounds and organometallic compound, the antimicrobial nano filler is compared with organic antibacterial agent has high security, slow-releasing is good, preferable weather resistance is arranged, broad spectrum antibacterial is arranged, be difficult for developing immunity to drugs, good heat resistance, easy to process, the most important coating that is to use this nano functional filler to make not only can be with new building materials, the formaldehyde that caking agent etc. produce, the acetaldehyde that smoking produces, organic foreign odors such as thiomethyl alcohol of generations such as family's dust decompose under UV-irradiation and eliminate, and can decompose oil content and organically surface contamination, can effectively improve the quality of human health life.
Summary of the invention
In view of above-mentioned prior art situation, the present inventor has carried out research extensively and profoundly in the Application Areas of nano titanium oxide, in the hope of obtain a kind of safety non-toxic, can degradable organic pollutant the long-acting broad-spectrum antibacterial water-borne coatings.Found that by in conventional water-borne coatings, adding a kind of nano titanium dioxide photocatalyst of special preparation, can prepare the long-acting broad-spectrum antibacterial water-borne coatings that satisfies above-mentioned performance requriements.The present invention just is being based on above-mentioned discovery and is being accomplished.
Therefore, the purpose of this invention is to provide a kind of safety non-toxic, can degradable organic pollutant the long-acting broad-spectrum antibacterial water-based paint compositions, it has been got rid of substantially because the problem that the pigment/filler improper use causes photocatalysis to reduce, and not limited by light source, all can bring into play the function of antibiotic, deodorizing, degradable organic pollutant.
The invention provides the long-acting broad-spectrum antibacterial water-based paint compositions that a kind of safety non-toxic, degradation of organic substances dye thing, it comprises coating emulsion, water, is dispersed in wherein conventional additives and filler and a kind of special nano titanium dioxide photocatalyst.
This purpose of the present invention and other purposes, feature and advantage will be easy to be understood by those of ordinary skill after integral body is considered the present invention.
Detailed Description Of The InventionThe coating emulsion that is used for long-acting broad-spectrum antibacterial water-based paint compositions of the present invention can be paint field any emulsion commonly used, for example acrylic ester emulsion, latex of copolymer in cinnamic acrylic ester, aqueous polyvinyl acetate emulsion, vinyl acetate-dibutyl maleate copolymer contg emulsion, vinyl acetate-acrylate copolymer emulsion, vinyl chloride-vinylidene chloride copolymer emulsion, pure acrylic acid ester copolymer emulsion and vinyl acetate-tertiary ethylene carbonate copolymer emulsion etc.Its consumption is a 20-60% weight based on the gross weight of water-borne coatings of the present invention, preferred 20-55% weight, more preferably 24-51% weight.For example for high lac varnish, emulsion content is generally about 50%; For sub-gloss varnish, emulsion content is generally about 25%; And for flat enamel, emulsion content is generally about 40%.
To can be used for additive in the long-acting broad-spectrum antibacterial water-based paint compositions of the present invention and filler without any particular restriction, condition is the above-mentioned advantageous property that can influence water-based paint compositions of the present invention sharply.For example, these additives can be paint field any additives commonly used, as oxidation inhibitor, dispersion agent, defoamer, film coalescence aid, filler etc.Yet mica powder is easy to and electrons excited, hole-recombination owing to containing many free property ions, thereby the photocatalysis to nano titanium dioxide photocatalyst has the weakening effect when using as filler, so it should be foreclosed.In addition,, for example can use also without any restriction for the consumption of above-mentioned additive in water-borne coatings of the present invention with paint field amount commonly used.Particularly, total consumption of described additive and filler is a 25-60% weight based on the gross weight of water-based paint compositions of the present invention, preferred 28-55% weight.
In long-acting broad-spectrum antibacterial water-based paint compositions of the present invention, the consumption of water is not crucial, but preferably its consumption is a 10-30% weight based on the gross weight of described coating composition, more preferably 15-26% weight.
The special nano titanium dioxide photocatalyst that is used for long-acting broad-spectrum antibacterial water-based paint compositions of the present invention is to use the adulterated nano titanium oxide of semiconductor material also further to use the nano titanium dioxide photocatalyst of conjugated system organism surface modification as matrix.In described matrix, used semiconductor material can be those skilled in the art well-known those, the oxide compound of niobium, tungsten, chromium, indium, tin, strontium, iron, vanadium, gallium, germanium and zinc etc. for example, the oxide compound of preferred iron, zinc, vanadium, tin etc.In described matrix, the weight ratio of titanium dioxide and semiconductor material (in metal oxide) is 60: 40-96: 4, preferred 65: 35-90: 10.The matrix used particle size of the present invention is a nano level, in the preferred 100nm, more preferably in the 50nm.
Above-mentioned nm TiO 2-base body is preferably produced by the metastable state chlorination process.Particularly, described metastable state chlorination process comprises the steps:
1) hydrolysis reaction: the titanium tetrachloride raw water is separated the mixing liquid that obtains containing white precipitate;
2) sol gel reaction: in step 1) gained mixing liquid, add compound alone or in combination with oxidation susceptibility and/or reducing property, make the white precipitate dissolving, form uniform reaction soln, heating is slowly evaporated liquid under 50-150 ℃ temperature then, forms sol-gel;
3) filtration washing: filter and water repetitive scrubbing step 2) products therefrom is 6-8 until pH;
4) drying: the step 3) products therefrom is dry under the vacuum tightness of-30 ℃ to 30 ℃ temperature and 5-15mmHg, obtain having of one's own the metastable state TiO 2 precursor of microparticle system; With
5) high-temperature calcination: with step 4) gained presoma temperature lower calcination 0.5-6 hour at 200-1000 ℃; Wherein at the hydrolysis reaction of step 1), in step 2) sol gel reaction or in step 1) and step 2) add the precursor of semiconductor material in the two.
In above-mentioned metastable state chlorination process, step 1) relates to the hydrolysis of raw material titanium tetrachloride.Used raw material can be the technical grade titanium tetrachloride in this step, also can be the pure titanium tetrachloride of reagent.From the cost angle, preferred technical grade titanium tetrachloride.Concentration to titanium tetrachloride there is no particular restriction, but preferably its volumetric molar concentration is controlled at 0.01-30mol/l, and preferred 0.05-10mol/l is more preferably in the scope of 0.09-5mol/l.The hydrolysis reaction of step 1) can carry out under the pH value arbitrarily, and for example the pH value can be about 0-11, preferred 0-8, more preferably 0-5, most preferably 1-3.Preferably use alkali to carry out to a certain degree neutralization in this hydrolysing step, wherein operable alkali comprises for example ammonium hydroxide (NH
4OH), sodium hydroxide (NaOH), potassium hydroxide (KOH) etc., preferably ammonium hydroxide.Also without any restriction, for example its consumption can be the 0.1-10 mole based on every mole of titanium tetrachloride to the consumption of described alkali, preferred 0.5-5 mole, more preferably 1-3 mole.The temperature that hydrolysis reaction carried out is not particularly limited, can under room temperature (about 30 ℃) or low temperature, carries out, but preferably at room temperature carry out.Because therefore the hydrolysis reaction very exothermic of titanium tetrachloride needs to use conventional method of cooling such as cooled with liquid nitrogen, refrigerated bath etc. to cool off.After hydrolysis reaction is finished, obtain containing the mixing liquid of white precipitate.
In above-mentioned metastable state chlorination process, step 2) relates to the formation of sol-gel.Particularly, the compound that will have oxidation susceptibility and/or reducing property under 10-180 ℃, preferred 30-100 ℃ temperature adds in the step 1) gained hydrolysate alone or in combination, white precipitate dissolves, form uniform reaction soln, reacting by heating solution 1-10 hour under 50-150 ℃, preferred 70-100 ℃ temperature then, liquid is slowly evaporated, form sol-gel.The oxidisability and/or the reductibility compound that are used for this step comprise for example hydrochloric acid (HCl), ammonium sulfide ((NH
4)
2S), sulfuric acid (H
2SO
4), nitric acid (HNO
3), perchloric acid (HClO
4), sulfurous acid (H
2SO
3), tin protochloride (SnCl
2), iron protochloride (FeCl
2), Sodium Nitrite (NaNO
2), sodium hyposulfate (Na
2S
2O
42H
2O) etc.The consumption of oxidisability and/or reductibility compound is the 0.01-10 mole based on every mole of titanium tetrachloride in this step, preferred 0.05-5 mole, more preferably 0.1-3 mole.Term used herein " oxidation susceptibility " and " reducing property " are relative concepts, promptly when the element Oxidation Number of compound used therefor hour, it is easy to lose electronics and is defined as reductive agent; And when the element Oxidation Number of compound used therefor was maximum, it was easy to obtain electronics and is defined as oxygenant.
In above-mentioned metastable state chlorination process, step 3) relates to step 2) filtration and the washing of gained sol-gel.The purpose of washing is in order to remove acid group and other impurity.Washing should be carried out repeatedly, is about 6-8 up to the pH of sol-gel value, preferred 6.5-7.5.
In above-mentioned metastable state chlorination process, step 4) relates to the drying that the step 3) gained has washed sol-gel.This step is preferably carried out like this: will wash sol-gel and place under the vacuum tightness of-30 ℃ to 30 ℃ temperature and 5-15mmHg dry 3-6 hour, remove moisture in the colloidal sol and possible solvent thus, obtain having of one's own the metastable state TiO 2 precursor of microparticle system.
In above-mentioned metastable state chlorination process, step 5) relates to the high-temperature calcination of step 4) gained metastable state TiO 2 precursor.This step is more preferably carried out in the calciner of using always in this area under 500-980 ℃ the temperature preferably at 200-1000 ℃.Without any restriction, calcining can be carried out under oxygen or oxygen containing air atmosphere to incinerating atmosphere, also can carry out in the presence of rare gas element such as nitrogen, helium, argon gas etc.Although calcining is optimal under oxygen atmosphere, consider production security, production cost and satisfying property of production, this calcining step adopts air atmosphere to carry out.Calcination time can be 0.5-6 hour.
In addition, in order to obtain the adulterated nm TiO 2-base body of semiconductor material, can be in hydrolysis reaction, the step 2 of step 1)) sol gel reaction or step 1) and step 2) add the precursor of semiconductor material in the two, as the inorganic acid salt or the organic acid salt of niobium, tungsten, chromium, indium, tin, strontium, iron, vanadium, gallium, germanium and zinc etc., for example muriate, bromide, vitriol, nitrate, phosphoric acid salt, acetate etc.Its consumption should make that the weight ratio of titanium dioxide and semiconductor material (in metal oxide) is 60 in the gained matrix of calcining back: 40-96: 4, preferred 65: 35-90: 10.
The present invention's used wording " metastable state " in term " metastable state chlorination process " and " metastable state TiO 2 precursor " is meant in the sol-gel preparation process in the inventive method, gel forms from heterogeneous non-equilibrium, astable system, through filtration, washing, vacuum-drying, form unsettled on the thermodynamics, as to have microparticle system of one's own metastable state TiO 2 precursor.The transformation temperature that this presoma changes to rutile-type from Detitanium-ore-type is less than 1000 ℃, be starkly lower than the transformation temperature (the rutile-type transformation temperature scope of conventional stable state titanium dioxide is about 1100-1400 ℃) of conventional stable state titanium dioxide, this is metastable physical property characteristic.In addition, its X-ray diffraction spectrum presents diffraction peak broadening phenomenon, the large percentage of surface atom, and surperficial unsaturated link(age) is rich or the like, and these illustrate that all nano-TiO 2 precursor of the present invention belongs to the metastable state material.Therefore adopt " metastable state chlorination process " term in this manual, be different from conventional chlorination process.
In the nano titanium dioxide photocatalyst that is used for long-acting broad-spectrum antibacterial water-based paint compositions of the present invention, the conjugated system organism of use is selected from toxilic acid and salt, fumaric acid and salt thereof, alkene sulfonic acid (as vinyl sulfonic acid, propenyl sulfonic acid, allyl sulphonic acid etc.) and salt, Witco 1298 Soft Acid and salt thereof, chooses the vinylformic acid and the salt thereof that replace wantonly.The organic content of described conjugated system is 0.01-20% weight based on the weight of the adulterated nm TiO 2-base body of described semiconductor material, preferred 0.05-15% weight, more preferably 0.1-10% weight.
In the nano titanium dioxide photocatalyst that is used for long-acting broad-spectrum antibacterial water-based paint compositions of the present invention, the primary particle particle diameter is the 5-80 nanometer, preferred 10-30 nanometer, and soft aggregate most probable particle diameter is the 40-100 nanometer, preferred 60-80 nanometer.
After preparing the nm TiO 2-base body as mentioned above, by abundant in proportion mixing in water with this matrix and conjugated system organism, ageing is also dry and carry out the conjugated system organism and coat, and obtains can be used for the nano titanium dioxide photocatalyst in the antibiotic plastic of the present invention thus.Described matrix and the ratio of described organism in water should make the nano titanium dioxide photocatalyst that obtains after the drying contain 0.01-20% weight, preferred 0.05-15% weight, more preferably the conjugated system organism of 0.1-10% weight.Ageing and drying can be carried out 3-20 hour under preferred 95-120 ℃ the temperature at 80-150 ℃, preferred 5-15 hour.
Before above-mentioned nano titanium dioxide photocatalyst being added in the long-acting broad-spectrum antibacterial water-based paint compositions of the present invention, can handle this photocatalyst with tensio-active agent, thereby make itself and the coating emulsion can be compatible well, and in emulsion, reach nano level distribution, show good quantum size photocatalytic effect thus.The tensio-active agent that can be used among the present invention is this area anion surfactant commonly used.This processing is carried out under 20-80 ℃ temperature usually.The consumption of tensio-active agent is a 0.1-10% weight based on the weight of used nano titanium dioxide photocatalyst, preferred 0.5-5% weight.In this treatment step, the concentration of nano titanium dioxide photocatalyst is unimportant, but makes nano titanium dioxide photocatalyst with 20-50% weight usually, and the concentration of preferred 25-40% weight is suspended in the anionic surfactant solution.Through after the stirring of certain hour, ageing is also dry.
After used nano titanium dioxide photocatalyst carries out surface modification through the semiconductor material doping and with the conjugated system organism in the long-acting broad-spectrum antibacterial water-based paint compositions of the present invention, its primary particle particle diameter remains on the 5-80 nanometer, preferred 10-30 nanometer, soft aggregate most probable size distribution is in the 40-100 nanometer, in the scope of preferred 60-80 nanometer.The used nano titanium dioxide photocatalyst of the present invention all shows effect significantly antibiotic and that degradation of organic substances dyes thing under the low-light at daylight, indoor natural light, dark place, and because the organic surface of conjugated system coats, its chemical stability is good, is difficult for causing the efflorescence of coating and wearing out.
In long-acting broad-spectrum antibacterial water-based paint compositions of the present invention, the content of nano titanium dioxide photocatalyst is 0.1-5.0% weight based on the gross weight of water-based paint compositions of the present invention, preferred 0.5-4.0% weight, more preferably 1-3% weight.
Long-acting broad-spectrum antibacterial water-based paint compositions of the present invention can add in the mixture of coating emulsion, water and conventional additives and filler by the nano titanium dioxide photocatalyst that directly will prepare as mentioned above, utilizes the mechanical shearing effect to mix then and prepares.The device that can produce the mechanical shearing effect is a paint field mixing device commonly used, as high speed homogenization mulser (model: HD
3, Beijing China oceangoing voyage economy and trade company limited), JSF-400 stirs sand milling and disperses multi-purpose machine (Shanghai modern environment engineering and technological research institute).
Because the adding of nano titanium dioxide photocatalyst, even that water-based paint compositions of the present invention also can have been given play in the low-light of dark region is antibiotic, the effect of deodorizing and degradable organic pollutant.For example, long-acting broad-spectrum antibacterial water-based paint compositions of the present invention all can reach more than 99% the germ-killing efficiency of intestinal bacteria, streptococcus aureus, the mutation of subtilis black etc., and the organic concentration of indoor high-concentration formaldehyde (300-800ppm) can be degraded in the set quota concentration (80ppm).In addition, the ageing resistance of long-acting broad-spectrum antibacterial water-based paint compositions of the present invention and resistance to chalking can be improved significantly, thereby have prolonged its work-ing life.
Embodiment
The present invention below will be described in more detail by reference example and Comparative Examples, but protection scope of the present invention is not limited to these embodiment.
Reference example The preparation embodiment of nano titanium dioxide photocatalyst Step 1:The preparation of the nm TiO 2-base body of ferric oxide semiconductor doping
At room temperature 49 gram (0.3mol) iron trichlorides (Beijing Raw Materials Company of Chemical Industry) are dissolved in the NH of 1000ml5% (weight/volume)
4In the OH aqueous solution.Adopt refrigerated bath then, 0.6mol technical grade titanium tetrachloride (Tianjin Chemical Plant) slowly is added drop-wise in this aqueous solution, under at the uniform velocity stirring, evenly produce white precipitate.Under agitation add 0.15mol perchloric acid (Beijing chemical industry two factories) then, make the white precipitate dissolving, obtain transparent liquid.Heat this liquid down at 95 ℃ and make its evaporation 2 hours, remove redundant moisture, obtain sol-gel.Filter the gained sol-gel and use 500ml water washing 4 times, making its pH is 7.With the sol-gel after the washing under 20 ℃ and 10mmHg dry 3 hours, obtain white micro mist, i.e. the metastable state TiO 2 precursor.Should the white micro mist in calcining furnace in 800 ℃ of calcinings 1 hour down, obtain the adulterated nm TiO 2-base body of ferric oxide, wherein the part by weight of ferric oxide and titanium dioxide is that the particle diameter of 24: 48 and matrix is 30-60nm.
Step 2:The preparation of nano titanium dioxide photocatalyst
The matrix that obtains in the step 1 is ground, be distributed in 200ml50 ℃ the pure water, add 6.5 gram propenyl sodium sulfonates (Beijing Raw Materials Company of Chemical Industry), fully mixing and dry 18 hours of 100 ℃ of following ageings, grind again, obtain nano-silica titanium photocatalyst of the present invention.The particle diameter of this nano titanium dioxide photocatalyst is 30-60nm and contains the 9 weight % propenyl sodium sulfonates of having an appointment.
Embodiment 1 The preparation of latex outer wall paint 1 and application
Each component as shown in table 1 below is hybridly prepared into latex outer wall paint 1 and tests its sterilization effect (testing method :) with reference to the Quinn test method in GB15979-1995 (appendix B-product antibacterial and bactericidal property and stability test method) and the Ministry of Health of the People's Republic of China 1999 (disinfection technology standard-bacteriostatic test) to intestinal bacteria, streptococcus aureus, the mutation of subtilis black.Found that its sterilizing rate is all more than 99%.
Table 1
Annotate: alcohol ester-12: main component 2,2,4-trimethylammonium-1, the 3-pentanediol mono isobutyrate, Beijing Mei Yahua becomes the AMP-95:2-of company limited amino-2-methyl-1-propyl alcohol, contain 5% water, Beijing Mei Yahua becomes the AT-06 of company limited: polycarboxylic acid, the BC-01 of Dongfang Chemical Plant, Beijing, The East Chemical Plant,Beijing (benzene-third) emulsion: east connection chemical plant, Beijing kaolin: the calcined kaolin (Al of ultra-fine chemical industry company limited is believed in Tianjin, development area, Langfang
2O
3, 1250 orders) and DAP (polycarboxylic acid salt), NXZ (mineral oils), common titanium white (R-930), zinc sulfide white (ZnS.BaSO
4), talcum powder (3MgO.4SiO
2.H
2O): capital clock chemistry painting industry company limited Natvosol: Beijing Mei Yahua becomes company limited
Embodiment 2 The preparation of latex outer wall paint 2 and application
| The component title | Content (weight %) |
| Water | ???22.5 |
| The nano titanium dioxide photocatalyst of reference example | ???1 |
| DAP | ???0.1 |
| AMP-95 | ???0.2 |
| NXZ | ???0.2 |
| Alcohol ester-12 | ???0.8 |
| Ethylene glycol | ???0.8 |
| Common titanium white | ???5 |
| Zinc sulfide white | ???6 |
| Talcum powder | ???17.6 |
| Kaolin | ???6.6 |
| BC-01 (benzene-third) emulsion | ???24.9 |
| 4% Natvosol slurry | ???13.2 |
| AT-06 | ???1.1 |
Each component as shown in table 2 below is hybridly prepared into latex outer wall paint 2 and tests its sterilization effect (testing method :) with reference to the Quinn test method in GB15979-1995 (appendix B-product antibacterial and bactericidal property and stability test method) and the Ministry of Health of the People's Republic of China 1999 (disinfection technology standard-bacteriostatic test) to intestinal bacteria, streptococcus aureus, the mutation of subtilis black.Found that its sterilizing rate is all more than 99%.
Table 2
Annotate: alcohol ester-12: main component 2,2,4-trimethylammonium-1, the 3-pentanediol mono isobutyrate, Beijing Mei Yahua becomes the AMP-95:2-of company limited amino-2-methyl-1-propyl alcohol, contain 5% water, Beijing Mei Yahua becomes the AT-06 of company limited: polycarboxylic acid, the BA-201 of Dongfang Chemical Plant, Beijing, The East Chemical Plant,Beijing (pure third) emulsion: east connection chemical plant, Beijing Natvosol: Beijing Mei Yahua becomes company limited's kaolin: the calcined kaolin (Al of ultra-fine chemical industry company limited is believed in Tianjin, development area, Langfang
2O
3, 1250 orders) and SN-154 (polyether-modified polysiloxane), ordinary titanium powder (R-930), talcum powder (3MgO.4SiO
2.H
2O): capital clock chemistry painting industry company limited 8030: dispersion agent, Henkel KGaA company
| The component title | Content (weight %) |
| Water | ??22.3 |
| The nano titanium dioxide photocatalyst of reference example | ??1.0 |
| 8030 | ??0.1 |
| AMP-95 | ??0.2 |
| SN-154 | ??0.2 |
| Alcohol ester-12 | ??0.85 |
| Ethylene glycol | ??0.95 |
| Common titanium white | ??11 |
| Talcum powder | ??17.6 |
| Kaolin | ??6.5 |
| BA-201 (pure third) emulsion | ??25.0 |
| 4% Natvosol slurry | ??13.2 |
| AT-06 | ??1.1 |
The artificial accelerated aging performance test results is: 300 hours non-foaming, do not peel off, flawless, efflorescence is 0 grade, variable color is 1 grade, and (national chemical building material test center builds worker's test department detection-room temperature: 23 ± 2%, relative humidity: 50 ± 5%, detecting instrument: the BETALM type is congratulated Li Shi xenon lamp aging instrument; SC-80 colour-difference meter etc.; Xenon lamp radiation: 300nm-400nm, rainfall cycle: drenched with rain 18 minutes in per 102 minutes).
Embodiment 3 The preparation of latex outer wall paint 3 and application
Each component as shown in table 3 below is hybridly prepared into latex outer wall paint 3 and tests its sterilization effect (testing method :) with reference to the Quinn test method in GB15979-1995 (appendix B-product antibacterial and bactericidal property and stability test method) and the Ministry of Health of the People's Republic of China 1999 (disinfection technology standard-bacteriostatic test) to intestinal bacteria, streptococcus aureus, the mutation of subtilis black.Found that its sterilizing rate is all more than 99%.
Table 3
Annotate: alcohol ester-12: main component 2,2,4-trimethylammonium-1, the 3-pentanediol mono isobutyrate, Beijing Mei Yahua becomes the AMP-95:2-of company limited amino-2-methyl-1-propyl alcohol, contains 5% water, and Beijing Mei Yahua becomes company limited.AT-06: polycarboxylic acid, the BA-201 of Dongfang Chemical Plant, Beijing, The East Chemical Plant,Beijing (pure third) emulsion: east, Beijing connection chemical plant AS-881 (superfine alumina silicate, SiO
2%:78-82, Al
2O
3%:11-13, Na
2O%＜9,2000 orders, unformed), fine particle calcium carbonate (CaCO
3, 800 orders), talcum powder (3Mgo.4SiO
2.H
2O, 1250 orders): the ultra-fine chemical industry coarse whiting (CaCO of company limited is believed in Tianjin, development area, Langfang
3, 800 orders) and supplier: the SN-154 of Beijing Guoli Ultrafine Powder Co., Ltd (polyether-modified polysiloxane), 612 (polyurethane-modified polyethers), common titanium white (R-930): capital clock chemistry painting industry company limited 8030: dispersion agent, Henkel KGaA company
| The component title | Content (weight %) |
| Water | ??15.8 |
| The nano titanium dioxide photocatalyst of reference example | ??1.0 |
| 8030 | ??0.8 |
| AMP-95 | ??0.3 |
| SN-154 | ??0.1 |
| Alcohol ester-12 | ??2.1 |
| Ethylene glycol | ??2.4 |
| Common titanium white | ??15 |
| Coarse whiting | ??2.1 |
| Fine particle calcium carbonate | ??3.5 |
| Talcum powder | ??4 |
| AS-881 | ??5 |
| AT-06 | ??0.4 |
| 612(50％) | ??0.1 |
| BA-201 (pure third) emulsion | ??47.4 |
The artificial accelerated aging performance test results is: 250 hours non-foaming, do not peel off, flawless, efflorescence is 0 grade, variable color is 1 grade, and (national chemical building material test center builds worker's test department detection-room temperature: 23 ± 2%, relative humidity: 50 ± 5%, detecting instrument: the BETALM type is congratulated Li Shi xenon lamp aging instrument; SC-80 colour-difference meter etc.; Xenon lamp radiation: 300nm-400nm, rainfall cycle: drenched with rain 18 minutes in per 102 minutes).
Embodiment 4 The preparation of latex outer wall paint 4 and application
Each component as shown in table 4 below is hybridly prepared into latex outer wall paint 4 and tests its sterilization effect (testing method :) with reference to the Quinn test method in GB15979-1995 (appendix B-product antibacterial and bactericidal property and stability test method) and the Ministry of Health of the People's Republic of China 1999 (disinfection technology standard-bacteriostatic test) to intestinal bacteria, streptococcus aureus, the mutation of subtilis black.Found that its sterilizing rate is all more than 99%.
Table 4
Annotate: alcohol ester-12: main component 2,2,4-trimethylammonium-1, the 3-pentanediol mono isobutyrate, Beijing Mei Yahua becomes the AMP-95:2-of company limited amino-2-methyl-1-propyl alcohol, contain 5% water, Beijing Mei Yahua becomes the AT-06 of company limited: polycarboxylic acid, the BA-201 of Dongfang Chemical Plant, Beijing, The East Chemical Plant,Beijing (pure third) emulsion: east, Beijing connection chemical plant DAP (polycarboxylic acid salt), 612 (polyurethane-modified polyethers), common titanium white (R-930), SN-154 (polyether-modified polysiloxane): capital clock chemistry painting industry company limited
| The component title | Content (weight %) |
| Water | ????19.9 |
| The nano titanium dioxide photocatalyst of reference example | ????1.0 |
| DAP | ????0.1 |
| AMP-95 | ????0.2 |
| SN-154 | ????0.1 |
| Alcohol ester-12 | ????1.2 |
| Ethylene glycol | ????1.2 |
| Common titanium white | ????25 |
| AT-06 | ????1 |
| 612(50％) | ????0.1 |
| BA-201 (pure third) emulsion | ????50.2 |
The artificial accelerated aging performance test results is: 250 hours non-foaming, do not peel off, flawless, efflorescence is 0 grade, variable color is 1 grade, and (national chemical building material test center builds worker's test department detection-room temperature: 23 ± 2%, relative humidity: 50 ± 5%, detecting instrument: the BETALM type is congratulated Li Shi xenon lamp aging instrument; SC-80 colour-difference meter etc.; Xenon lamp radiation: 300nm-400nm, rainfall cycle: drenched with rain 18 minutes in per 102 minutes).
Claims (10)
1. antibiotic water paint composition, comprise coating emulsion, water, be dispersed in wherein conventional additives and filler and a kind of special nano titanium dioxide photocatalyst, the content of wherein said nano titanium dioxide photocatalyst in described antibiotic water paint composition is 0.1-5.0% weight based on the gross weight of described composition.
2. according to the antibiotic water paint composition of claim 1, the content of wherein said nano titanium dioxide photocatalyst in described antibiotic water paint composition is 0.5-4.0% weight based on the gross weight of described composition.
3. according to the antibiotic water paint composition of claim 2, the content of wherein said nano titanium dioxide photocatalyst in described antibiotic water paint composition is 1.0-3.0% weight based on the gross weight of described composition.
4. according to the antibiotic water paint composition of claim 1, it is 20-60% weight based on the gross weight of described composition that wherein said coating emulsion is selected from acrylic ester emulsion, latex of copolymer in cinnamic acrylic ester, aqueous polyvinyl acetate emulsion, vinyl acetate-dibutyl maleate copolymer contg emulsion, vinyl acetate-acrylate copolymer emulsion, vinyl chloride-vinylidene chloride copolymer emulsion, pure acrylic acid ester copolymer emulsion and vinyl acetate-tertiary ethylene carbonate copolymer emulsion and its content, preferred 20-55% weight; The total content of described additive and filler is a 25-60% weight based on the gross weight of described composition, is preferably 28-55% weight.
5. according to the antibiotic water paint composition of claim 1, wherein the content of water is 10-30% weight based on the gross weight of described composition, preferred 15-26 weight.
6. according to the antibiotic water paint composition of claim 1, wherein said nano titanium dioxide photocatalyst comprises that the adulterated nano titanium oxide of semiconductor material is as matrix and coated conjugated system organism on described matrix surface, wherein the weight ratio of titanium dioxide and semiconductor material (calculating with metal oxide) is 60 in described matrix: 40-96: 4 and the particle size of described matrix be in the 100nm, the organic content of wherein said conjugated system is 0.01-20% weight based on the weight of the adulterated nm TiO 2-base body of described semiconductor material.
7. according to the antibiotic water paint composition of claim 6, wherein the weight ratio of titanium dioxide and semiconductor material (calculating with metal oxide) is 65 in described nm TiO 2-base body: 35-90: 10 and the particle size of described matrix be in the 50nm, the organic content of wherein said conjugated system is 0.05-15% weight based on the weight of the adulterated nm TiO 2-base body of described semiconductor material.
8. according to the antibiotic water paint composition of claim 6 or 7, wherein said nm TiO 2-base body is produced by the metastable state chlorination process.
9. according to the antibiotic water paint composition of claim 6, wherein said semiconductor material is selected from the oxide compound of tungsten, niobium, chromium, indium, tin, strontium, iron, vanadium, gallium, germanium and zinc.
10. according to the antibiotic water paint composition of claim 6, wherein said conjugated system organism is selected from toxilic acid and salt, fumaric acid and salt thereof, alkene sulfonic acid and salt thereof, Witco 1298 Soft Acid and salt thereof, chooses the vinylformic acid and the salt thereof that replace wantonly.