CN1438466A - Corrosion-proof treating method of surface evaporation air-cooling apparatus - Google Patents
Corrosion-proof treating method of surface evaporation air-cooling apparatus Download PDFInfo
- Publication number
- CN1438466A CN1438466A CN 03102146 CN03102146A CN1438466A CN 1438466 A CN1438466 A CN 1438466A CN 03102146 CN03102146 CN 03102146 CN 03102146 A CN03102146 A CN 03102146A CN 1438466 A CN1438466 A CN 1438466A
- Authority
- CN
- China
- Prior art keywords
- equipment
- surface evaporation
- spray
- spraying
- air cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses an antisepsis way for the surface vaporizing air-cooling device. The process is that it firstly sweeps the device with high pressure wind to weep out impurity, secondly to lay the device at angle of 45, to spray background lacquer and to solidify, lastly to spray surface lacquer and to solidify. The present invention solves the problem which is it difficult for the surface vaporizing cooling device to perform reliable antisepsis disposal with other devices antisepsis ways. It has run effectively for 5 years, and antisepsis effect is good.
Description
Technical field
The present invention relates to the metal surface is applied the technology of corrosion resistant coating, specifically, is a kind of large chemical equipment method for anticorrosion treatment, more particularly, is the method for anticorrosion treatment to surface evaporation air cooling equipment.
Background technology
Surface evaporation air cooling equipment is novel large-size chemical cold exchange device, because of its high heat exchange efficiency has been obtained good effect in large scale chemical plant, its operation principle is mainly the moisture film thin layer that the water of spray on tube bank surface forms and can vaporizes rapidly, undergoes phase transition to take away a large amount of heat and realize its high efficiency heat exchange.But the tube bank of surface evaporation air cooling equipment is a carbon steel material, can't use for a long time in the corrosive environment of water and air.Surface evaporation air cooling is restrained not only dense arrangement, quantity is many, and profile is huge, and the aseptic technic of other type equipment is difficult to it is realized reliable preservative treatment, and therefore domestic still unmatchful its outer surface applies the preservative treatment technology of organic corrosion resistant coating at present.The aseptic technic that corrosion inhibiter or pouring are added in the domestic common employing of similar large-size chemical cold exchange device, the former causes the equipment surface fouling easily, and heat-transfer effect significantly reduces; Latter Yi Zaocheng coating covers imperfect to equipment surface and thickness evenness is poor, influences the performance of coating.
Summary of the invention
The objective of the invention is to overcome the shortcoming of prior art, a kind of method for anticorrosion treatment of surface evaporation air cooling equipment of favorable anti-corrosion effect is provided.
Surface evaporation air cooling equipment anticorrosion processing method of the present invention may further comprise the steps:
(1) cleaning equipment
Adopt high-pressure blast to purging inside and outside the surface evaporation air cooling equipment, especially will carefully purge device outer surface from different perspectives, remove its impurity;
(2) place apparatus
Surface evaporation air cooling equipment after the cleaning is tiltedly hung on the straddle truck and moves, and the end that equipment is low is placed on small rack, and the high other end is placed on the trapezoidal big supports that a base angle is 60 degree, and the position of adjusting makes surface evaporation air cooling be miter angle;
(3) spraying priming paint
Perpendicular to 0.5 meter of surface evaporation air cooling equipment, adopt automatic spraying machine from left to right, spray primer for rusted steel LLMTD-1 from top to bottom, 120 ℃ of priming paint spraying temperatures, spraying rate is 35-45g/s, after spraying finishes, surface evaporation air cooling equipment is exchanged at two ends up and down, again spray one time, spray twice altogether, move this equipment with straddle truck then, regulate the position of small rack, making equipment be 60 spends inclination and leaves standstill 1h, with straddle truck it is moved on at last and pull drying room on the trailer into,, be warmed up to 120 ℃ every the halfhour mode of 1h constant temperature with 20 ℃/h, make solidifying priming paint 8h, forming thickness is the priming paint dry film of 60-80 μ m;
(4) spray paint
Haul out step (3) and scribbled the equipment of priming paint from drying room, as requested equipment is fixed, spray paint LLSTD-2 sprays four times, and spraying method is identical with the priming paint of step (3) with curing, and last finish paint build is 120-160 μ m.
Priming paint of the present invention comprises the primer for rusted steel of LLSTD-1, and described finish paint comprises the finish paint of LLSTD-2, and they are the Lanzhou Oil Refinery equipment research and produce.
Flush coater of the present invention, straddle truck all are known devices.
Advantage of the present invention and effect:
The tube bank quantity of surface evaporation air cooling equipment is many and be carbon steel material, in air and aqueous medium, corrosion very easily takes place, not only heat-transfer effect reduces greatly, but also can badly damaged equipment, be 1.73 * 10 with the thick coating thermal resistance of the every 0.1mm of surface evaporation air cooling equipment coating material of technical finesse of the present invention
-4m
2Hr/kcal, thermal conductivity factor are 0.59kcal/mhr ℃, drop into certainly and use 5 years so far, and equipment is still intact.Therefore method of the present invention is not only filled up domestic surface evaporation air cooling anticorrosion technology of equipments, and other large chemical equipment also can be used for reference technology of the present invention.
The specific embodiment
Further specify characteristics of the present invention below by specific embodiment.
Embodiment
Present embodiment is that the surface evaporation air cooling equipment of 3,000,000 tons of/year reformer transformations adopts method for anticorrosion treatment of the present invention.
Handled surface evaporation air cooling equipment is produced by Lanzhou Petro-Chemical Machinery Plant.Have related parameter as follows:
Model: ZP9X3-15/4-557-149-245
Heat exchange area: 557m
2
Design pressure: 2.45Mpa
Appearance and size: 9.7 * 3.5 * 1.15
Material: carbon steel
Tube bank: form by 795 tube banks, totally 15 layers, 53 every layer.
Concrete processing procedure:
1. cleaning equipment
Adopt high-pressure blast to purging inside and outside the surface evaporation air cooling equipment, from different perspectives device outer surface is carefully purged, remove its impurity;
2. place apparatus
Surface evaporation air cooling tiltedly hung on the straddle truck move, the end that equipment is low is placed on the small rack that can regulate front and back position, the other end is placed on the trapezoidal big support that a base angle is 60 degree, regulates the position of small rack, makes surface evaporation air cooling be miter angle.Under this angle, be sprayed on coating in the tube bank and can well evenly be diffused into second half of the tube bank that can't be sprayed onto.
3. coating spraying and curing
Perpendicular to 0.5 meter of surface evaporation air cooling equipment, adopt automatic coating machine from left to right, spray LLWTD-1 priming paint from top to bottom, 120 ℃ of priming paint spraying temperatures, spraying rate is 35-45g/s, after spraying finishes, in order to make all even coating of coating cover the tube bank surface fully, surface evaporation air cooling is exchanged at two ends up and down, spray again one time, move this equipment with straddle truck then, regulate the position of small rack, make equipment be 60 degree and tilt, be beneficial to the diffusion and the levelling of coating, after surface evaporation air cooling leaves standstill 1h, with straddle truck it is moved on the trailer and to pull drying room into,, be warmed up to 120 ℃ every the halfhour mode of 1h constant temperature with 20 ℃/h programming rate, make solidifying priming paint 8h, the priming paint build is 60-80 μ m.Hauling-out equipment from drying room, the requirement fixing according to equipment places equipment, carries out the spraying of finish paint.Finish paint uses LLSTD-2 organic anti-corrosive lacquer, sprays four times, and two ends exchange twice up and down, and spraying method is identical with priming paint with the paint solidification method, and the finish paint build is 120-160 μ m.Surface evaporation air cooling Equipment Inspection result after the preservative treatment:
Outward appearance: color clear, smooth surface;
Solidify: the tube bank surface wiping repeatedly of, middle different parts forward and backward to surface evaporation air cooling equipment, the equal nondiscolouring of cotton-wool with the cotton-wool that dips in solvent.
Claims (1)
1. the method for anticorrosion treatment of a surface evaporation air cooling equipment is characterized in that processing procedure comprises:
(1) cleaning equipment
Adopt high-pressure blast inside and outside face evaporative air-cooling equipment is arranged, to purge, especially will carefully purge device outer surface from different perspectives, remove its impurity;
(2) place apparatus
Surface evaporation air cooling equipment after the cleaning is tiltedly hung on the straddle truck and moves, and the end that equipment is low is placed on small rack, and the high other end is placed on the trapezoidal big supports that a base angle is 60 degree, and the position of adjusting makes surface evaporation air cooling be miter angle;
(3) spraying priming paint
Apart from 0.5 meter of evaporative air-cooling equipment surface, adopt automatic spraying machine from left to right, spray the LLSTD-1 primer for rusted steel from top to bottom, 120 ℃ of priming paint spraying temperatures, spraying rate is 35-45g/s, after spraying finishes, surface evaporation air cooling equipment is exchanged at two ends up and down, again spray one time, spray twice altogether, move this equipment with straddle truck then, regulate the position of small rack, making equipment be 60 spends inclination and leaves standstill 1h, with straddle truck it is moved on at last and pull drying room on the trailer into,, be warmed up to 120 ℃ every the halfhour mode of 1h constant temperature with 20 ℃/h, make solidifying priming paint 8h, forming thickness is the priming paint dry film of 60-80 μ m;
(4) spray paint
Haul out step (3) and scribbled the equipment of priming paint from drying room, as requested equipment is fixed, spray paint LLSTD-2 sprays four times, and spraying method is identical with the priming paint of step (3) with curing, and last finish paint build is 120-160 μ m.