CN1438356A - Multihead ion film-plating method for ceramic product - Google Patents
Multihead ion film-plating method for ceramic product Download PDFInfo
- Publication number
- CN1438356A CN1438356A CN 03113917 CN03113917A CN1438356A CN 1438356 A CN1438356 A CN 1438356A CN 03113917 CN03113917 CN 03113917 CN 03113917 A CN03113917 A CN 03113917A CN 1438356 A CN1438356 A CN 1438356A
- Authority
- CN
- China
- Prior art keywords
- vacuum
- take out
- open
- plated
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a multisphere ion plating method for pottery products. The invention is carried on in multisphere ion vacuum plating machine, includes rinsing, crude drawing, refinery drawing, charging inert gases and nitrogen, generating asc plating.
Description
Technical field
The present invention relates to a kind of surface treatment method of ceramic, relate in particular to a kind of multi-arc ion plating film method of ceramic.
Background technology
Traditional multi-arc ion plating film mainly is to be applied on the plated film of metal products.And traditional ceramic surface decoration mainly is to adopt methods such as decal paper or artificial colored drawing pattern color to decorate, though can play certain decorative effect, but the resistance to persistence of product appearance color is not enough, and the time, long can the generation faded, and influenced decorative effect.Along with socioeconomic fast development, living standards of the people improve constantly, and people also improve constantly requirement daily and the technology porcelain.Not only require product appearance handsome in appearance, practical, and require inner quality good, as resistance to persistence of shock resistance, wear resistance, thermostability, erosion resistance and the appearance luster of product etc. is had higher requirement.
Technical scheme
For overcoming the deficiency of traditional ceramics surface decoration, the trailing that the purpose of this invention is to provide a kind of ceramic, it can make, and product is attractive in appearance, practicality good, the shock resistance of product, wear resistance, thermostability, good corrosion resistance, and the resistance to persistence of product appearance color and luster is good.
The present invention is achieved in that
A kind of multi-arc ion plating film method of ceramic, this method comprises the step of following order:
(1), loads onto cathode material at the negative electrode of multi sphere ion vacuum plating unit;
(2), with organic solvent to being cleaned, dry by the ceramic workpiece that plated, and it is indoor to send into vacuum plating with hanger;
(3), shut the vacuum chamber gate, drive vacuum pump and slightly take out, make vacuum tightness reach 2.5～4Pa;
(4), add rare gas element, as argon gas, and workpiece to be plated bombarded cleaned 6～10 minutes;
(5), when vacuum tightness reaches 1.8～2.2Pa, close and slightly take out valve, open foreline valve, open essence again and take out valve and carry out essence and take out, when vacuum tightness reaches 3 * 10
-2Pa～5 * 10
-2During Pa, charge into rare gas element such as argon gas again, make vacuum tightness reach 1.5 * 10
-1Pa～2 * 10
-1Pa;
(6), drive turn switch, make Workpiece Rotating, and the open arc source switch, striking alone after 30～40 seconds, charges into nitrogen in striking, the control plated film time was at 3～5 minutes;
(7), close the arc source, charge into air, open vacuum film coating chamber, the product behind the plated film is shifted out.
The described cathode material of above-mentioned steps (1) can be wherein a kind of for copper, aluminium, titanium, tungsten, nickel, silver etc.
Use film coating method of the present invention, the ceramic surface-brightening after plating, the rete combination is firm, compact structure, gloss duration is good; The coating process wide ranges can be carried out ion film plating at a lower temperature; Cathode material is selected metallic substance such as cheap copper, aluminium, tungsten, titanium for use, and cost is lower, and can make desirable tones such as imitative gold, imitative silver, bronze, improves product specification; The production efficiency height, and whole process carries out in that vacuum plating is indoor, and pollution-free, noiseless.
Description of drawings
Fig. 1 is the plated film vacuum system synoptic diagram of vacuum plating unit of the present invention.
Embodiment
Below in conjunction with accompanying drawing to the specific embodiment of the present invention further detailed description, so that can more clearly understand the present invention.
Embodiment 1
(1), loads onto titanium at the negative electrode of multi sphere ion vacuum plating unit;
(2), with organic solvent to being cleaned, dry by the ceramic workpiece that plated, send in the vacuum film coating chamber 1 with hanger;
(3), shut the vacuum chamber gate, drive vacuum pump 2 and slightly take out, make vacuum tightness reach 3Pa;
(4), add argon gas and workpiece to be plated bombarded cleaned 8 minutes;
(5), when vacuum tightness reaches 2Pa, close and slightly take out valve 3, open foreline valve 4, open essence again and take out valve 5 and carry out essence and take out, when vacuum tightness reaches 4 * 10
-2During Pa, charge into argon gas again, make vacuum tightness reach 1.8 * 10
-1Pa;
(6), drive turn switch, make Workpiece Rotating, and the open arc source switch, striking alone after 30 seconds, charges into nitrogen in striking, the control plated film time was at 4 minutes;
(7), close the arc source, open inflation valve 6 and charge into air, open vacuum film coating chamber 1, the product behind the plated film is shifted out, like this, just obtain the product of imitative golden plated film.
Embodiment 2
Except step (1) is loaded onto aluminium at the negative electrode of multi sphere ion vacuum plating unit, other step so just obtains the plated film product of imitative silver with embodiment 1.
Claims (2)
1, a kind of multi-arc ion plating film method of ceramic, this method comprises the step of following order:
(1), loads onto cathode material at the negative electrode of multi sphere ion vacuum plating unit;
(2), with organic solvent to being cleaned, dry by the ceramic workpiece that plated, and it is indoor to send into vacuum plating with hanger;
(3), shut the vacuum chamber gate, drive vacuum pump and slightly take out, make vacuum tightness reach 2.5～4Pa;
(4), add rare gas element, as argon gas, and workpiece to be plated bombarded cleaned 6～10 minutes;
(5), when vacuum tightness reaches 1.8～2.2Pa, close and slightly take out valve, open foreline valve, open essence again and take out valve and carry out essence and take out, when vacuum tightness reaches 3 * 10
-2Pa～5 * 10
-2During Pa, charge into rare gas element such as argon gas again, make vacuum tightness reach 1.5 * 10
-1Pa～2 * 10
-1Pa;
(6), drive turn switch, make Workpiece Rotating, and the open arc source switch, striking alone after 30～40 seconds, charges into nitrogen in striking, the control plated film time was at 3～5 minutes;
(7), close the arc source, charge into air, open vacuum film coating chamber, the product behind the plated film is shifted out.
2, method according to claim 1, wherein the described cathode material of step (1) can for copper, aluminium,, titanium, tungsten, nickel, silver etc. be wherein a kind of.