CN1417415A - Making process and product of color vaccum aluminium plating paper as package material - Google Patents
Making process and product of color vaccum aluminium plating paper as package material Download PDFInfo
- Publication number
- CN1417415A CN1417415A CN 01129858 CN01129858A CN1417415A CN 1417415 A CN1417415 A CN 1417415A CN 01129858 CN01129858 CN 01129858 CN 01129858 A CN01129858 A CN 01129858A CN 1417415 A CN1417415 A CN 1417415A
- Authority
- CN
- China
- Prior art keywords
- paper
- acrylic resin
- aluminium
- release coating
- easy release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
In the present invention, polyester film is painted with easy-to-peel coating, sprayed with aluminium and adhered with paper layer, and the polyester film is then peeled and paint containing pigment is painted to the easy-to-peel coating to obtain the product. The easy-to-peel coating consists of nitro cellulose and acrylic resin. The improved easy-to-peel coating has raised organic solvent resistance, can be colored in great area, and is covered with rougher easy-to-peel layer and thus has high smoothness and mirror effect. The aluminum-plating paper can be printed and colored in controlled color difference.
Description
Technical field
The present invention relates to manufacture method of a kind of vacuum aluminum-coated paper composites and products thereof, more particularly, relate to manufacture method of a kind of vaccum aluminium plating paper as package material that on aluminizer, scribbles color layers and products thereof.
Background technology
Vacuum aluminium-plated paper is the packaging material that are applied to packaging industry in recent years, it has preferred metal texture, be applicable to the processing of embossing machine, high-speed crosscutting machine, have lucifuge, every advantages such as wet, degradables, alternative aluminized plastic film, the thin composite of fine aluminium, because it is few with the aluminium amount, have broad prospects, now be widely used in fields such as the packing and decorating of cigarette, food, medicine and brand mark.At present, vacuum aluminium-plated paper with coloring effect all adopts the preceding color method of going up, its process is to coat an easy release coating of being made by NC Nitroncellulose on polyester film, the back is carried out vacuum aluminum-coated on easy release coating, paste a compound ply of paper again and form semi-finished product, then polyester film is peeled off away and obtained the finished product vacuum aluminium-plated paper, its coloring pigment is added in the easy release coating.The vacuum aluminium-plated paper that this process is made has the following disadvantages: make the nitrocellulose element coating on the paper top layer of aluminizing become coarse when peeling off owing to polyester film, the paper poor surface smoothness of aluminizing lacks gloss; Preceding coloring process makes the product aberration be difficult to control; Because the ability of the anti-organic solvent of NC Nitroncellulose, the adaptability of the paper surface printing of making of aluminizing is relatively poor, can't carry out the large tracts of land printing.
Summary of the invention
The object of the present invention is to provide manufacture method of a kind of surface smoothness height, color vaccum aluminium plating paper as package material that anti-organic solvent ability is strong and products thereof.
For achieving the above object, manufacture method of the present invention comprises following steps successively:
A, on polyester film, carry out once such operation at least: apply remover, and 90-140 ℃ of oven dry down, so that form the easy release coating that thickness is every square metre of 0.5-1.8 gram;
B, under vacuum environment with spraying plating behind the metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
C, on the aluminium film of the transfer membrane of aluminizing adhesive coating and paste a compound ply of paper, 60-90 ℃ of oven dry down, the normal temperature cooling curing forms compound semi-finished product again;
D, polyester film is progressively peeled off out the transfer paper of must aluminizing with certain pulling force from compound semi-finished product;
E, the coating that will contain pigment are coated on the easy release coating surface of the above-mentioned transfer paper of aluminizing, and 60-90 ℃ of oven dry down, obtain the color vaccum aluminium plating paper as package material product.
Described remover is that solid content is that the nitro-cellulose solution of 7-10% (weight) and acrylic resin soln that solid content is 16-20% (weight) are pressed 1.5-2.5: 1 weight ratio is mixed and is formed composition.
Described nitro-cellulose solution solvent for use is one or more the composition in acetone, butanone, methyl iso-butyl ketone (MIBK), cyclohexanone, ethyl acetate, propyl acetate, the butyl acetate.
Described acrylic resin soln is made up of following composition and weight ratio:
Acrylic resin 12-15%
Organic solvent 80-84%
Plasticizer 0.5-1%
Levelling agent 0.5-1%
Amino resins 3%
Described organic solvent is one or more the composition in acetone, butanone, methyl iso-butyl ketone (MIBK), cyclohexanone, ethyl acetate, propyl acetate, the butyl acetate.
Can also apply described acrylic resin soln on the described easy release coating, dry down at 90-140 ℃ and form binder course, this joint thickness is every square metre of 0.6-0.8 gram, and the metallic aluminium spraying plating of described B in the step is on this binder course.
Described acrylic resin can be the polymethyl methacrylate PMA.
The painted paper packing material of aluminizing that makes by above-mentioned manufacture method, comprise ply of paper, paste composite aluminium-plated layer on the ply of paper, easy release coating is arranged on the aluminium coated, the composition that described easy release coating is made up of following composition and weight ratio: 3 parts in NC Nitroncellulose 10.5-25 part, acrylic resin 12-15 part, plasticizer 0.5-1 part, levelling agent 0.5-1 part and amino resins have colored film on the described easy release coating.
One binder course of being made up of acrylic resin 12-15 part, plasticizer 0.5-1 part, levelling agent 0.5-1 part, amino resins 3 parts (weight ratio) can also be arranged between described easy release coating and the aluminium coated, and aluminium coated is plated on this binder course.
Commute release coating of the present invention improves, improved anti-organic solvent ability, can carry out large tracts of land on its surface apply painted, dyed layer has covered comparatively coarse easy peel ply, the fineness on paper surface of aluminizing improves greatly, demonstrate mirror effect, and can be once more to the paper printing of aluminizing, in coloring process, can control aberration in real time, make product colour applying customer requirements, do not needing when painted, can easily apply a clear, colorless gloss oil on the release coating, product shows the silvery white effect of light.
Embodiment 1
NC Nitroncellulose is dissolved in cyclohexanone, butanone and the ethyl acetate mixed solvent, and forming solid content is the nitro-cellulose solution of 8% (weight).
By weight, 12 parts of polymethyl methacrylates, 3 parts in amino resins, 0.6 part of poly terephthalic acid dioctyl ester and levelling agent are dissolved in 83.4 parts of cyclohexanone for 1 part, form acrylic resin soln.
Above-mentioned nitro-cellulose solution and acrylic resin soln were uniformly mixed to form remover by weight 1.5: 1.
On the intaglio press above-mentioned remover is being coated on the polyester film, back oven dry in baking oven forms easy release coating, and oven temperature is 90-140 ℃.Repeating the easy release coating thickness that described operation makes formation is every square metre of 1.0-1.8 gram.
On vacuum coating equipment, spraying plating behind the metallic aluminium heating and melting to the easy release coating of above-mentioned polyester film, is got vacuum aluminum-coated transfer membrane, wherein the aluminium film thickness is controlled at the 30-40 nanometer.
On the wet type compounding machine, water-soluble poly vinylacetate adhesive is coated on the aluminium face of above-mentioned vacuum aluminum-coated transfer membrane, fitted with paper then, in 60-90 ℃ baking oven, dry, place at normal temperatures again and solidified 12 hours, form compound semi-finished product.
Laminated polyester film in the above-mentioned compound semi-finished product is mechanically progressively peeled off with certain mechanical pulling force, with polyester film and have the composite sheet of aluminium coated to separate rolling, obtain the transfer paper of aluminizing, at this moment aluminizer bonds on paper, and easily release coating also is pasted on the transfer paper of aluminizing with aluminizer.Polyester film reclaims and uses.
Be applied on the easy release coating of the above-mentioned transfer paper of aluminizing at the polyacrylic acid coating that will add pigment and the good color of adjustment on the intaglio printing press, making the painted paper packing material product of aluminizing after the oven dry in 60-90 ℃ the baking oven.
The product glossiness that the said method step makes is good, and is glossy, and product surface has the effect of minute surface, and product can be adjusted color at any time according to customer requirement, reduces aberration, and the anti-organic solvent properties of product surface is good, can print once more on intaglio press.
Embodiment 2
NC Nitroncellulose is dissolved in ethyl acetate, butyl acetate, the cyclohexanone mixed solvent, and forming solid content is the nitro-cellulose solution of 8% (weight).
14 parts of PMAs, 3 parts in amino resins, 1 part of poly terephthalic acid dioctyl ester, levelling agent are dissolved in 81 parts of cyclohexanone for 1 part, form acrylic resin soln.
Above-mentioned nitro-cellulose solution and acrylic resin soln were uniformly mixed to form easy release coating coating by weight 2.3: 1.
On the intaglio press above-mentioned remover is being coated on the polyester film, back oven dry in baking oven forms easy release coating, and oven temperature is 90-140 ℃, and the easy release coating thickness of formation is every square metre of 0.5-0.7 gram.
On the intaglio press described acrylic resin soln is being coated on the surface of above-mentioned easy release coating, oven dry forms binder course in 90-140 ℃ baking oven, and joint thickness is controlled at every square metre of 0.6-0.8 gram.
On vacuum coating equipment, spraying plating behind the metallic aluminium heating and melting to above-mentioned binder course, is got vacuum aluminum-coated transfer membrane, wherein the aluminium film thickness is controlled at the 30-40 nanometer.
On the wet type compounding machine, water-soluble living polyvinyl acetate glue stick is coated on the aluminium face of above-mentioned vacuum aluminum-coated transfer membrane, fitted with paper then, in 60-90 ℃ baking oven, dry, cooling curing 10 hours at normal temperatures forms compound semi-finished product again.
Laminated polyester film in the above-mentioned compound semi-finished product is mechanically progressively peeled off with certain mechanical pulling force, with polyester film and have the composite sheet of aluminium coated to separate rolling, obtain the transfer paper of aluminizing, at this moment aluminizer bonds on paper, and easily release coating also is pasted on the transfer paper of aluminizing with aluminizer.Polyester film reclaims and uses.
Be applied on the easy release coating of the above-mentioned transfer paper of aluminizing at the polyacrylic acid coating that will add pigment and the good color of adjustment on the intaglio printing press, making the painted paper packing material product of aluminizing after the oven dry in 60-90 ℃ the baking oven.
The product glossiness that the said method step makes is good, glossy, product surface has the effect of minute surface, product can be adjusted color at any time according to customer requirement, reduce aberration, the anti-organic solvent properties of product surface is good, can print once more on intaglio press, and the binder course of increase is strengthened the brightness of product, anti-wear performance.
Claims (8)
1, a kind of manufacture method of color vaccum aluminium plating paper as package material is characterized in that, comprises following steps successively:
A, on polyester film, carry out once such operation at least: apply remover, and 90-140 ℃ of oven dry down, so that form the easy release coating that thickness is every square metre of 0.5-1.8 gram;
B, under vacuum environment with spraying plating behind the metallic aluminium heating and melting on above-mentioned easy release coating, form vacuum aluminum-coated transfer membrane;
C, on the aluminium film of vacuum aluminum-coated transfer membrane adhesive coating and paste a compound ply of paper, 60-90 ℃ of oven dry down, cooling curing under the normal temperature forms compound semi-finished product;
D, polyester film is progressively peeled off out the transfer paper of must aluminizing with certain pulling force from compound semi-finished product;
E, the coating that will contain pigment are coated on the easy release coating surface of the above-mentioned transfer paper of aluminizing, 60-90 ℃ of oven dry down, the color vaccum aluminium plating paper as package material product;
Described remover is that solid content is that the nitro-cellulose solution of 7-10% (weight) and acrylic resin soln that solid content is 16-20% (weight) are pressed 1.5-2.5: 1 weight ratio is mixed and is formed composition;
Described nitro-cellulose solution solvent for use is one or more the composition in acetone, butanone, methyl iso-butyl ketone (MIBK), cyclohexanone, ethyl acetate, propyl acetate, the butyl acetate;
Described acrylic resin soln is made up of following composition and weight ratio:
Acrylic resin 12-15%
Organic solvent 80-84%
Plasticizer 0.5-1%
Levelling agent 0.5-1%
Amino resins 3%
Described organic solvent is one or more the composition in acetone, butanone, methyl iso-butyl ketone (MIBK), cyclohexanone, ethyl acetate, propyl acetate, the butyl acetate.
2, according to the described manufacture method of claim 1, it is characterized in that, also apply described acrylic resin soln on the described easy release coating, dry down at 90-140 ℃ and form binder course, this joint thickness is every square metre of 0.6-0.8 gram, and the metallic aluminium spraying plating of described B in the step is on this binder course.
3, according to claim 1 or 2 described manufacture methods, it is characterized in that described acrylic resin is a polymethyl methacrylate.
4, according to claim 1 or 2 described manufacture methods, it is characterized in that described acrylic resin is a PMA.
5, make the painted paper packing material of aluminizing according to claim 1 or 2 described manufacture methods, comprise ply of paper, paste composite aluminium-plated layer on the ply of paper, easy release coating is arranged on the aluminium coated, it is characterized in that, the composition that described easy release coating is made up of following composition and weight ratio: 3 parts of NC Nitroncellulose 10.5-25 parts, acrylic resin 12-15 part, plasticizer 0.5-1 part, levelling agent 0.5-1 part, amino resins have colored film on the described easy release coating.
6, according to the described painted paper packing material of aluminizing of claim 4, it is characterized in that, also have a binder course of being made up of acrylic resin 12-15 part, plasticizer 0.5-1 part, levelling agent 0.5-1 part and amino resins 3 parts (weight ratio) between described easy release coating and the aluminium coated, the aluminium coated spraying plating is on this binder course.
7, according to claim 1 or 2 described manufacture methods, it is characterized in that described acrylic resin is a polymethyl methacrylate.
8, according to claim 1 or 2 described manufacture methods, it is characterized in that described acrylic resin is a PMA.