-kind of braided sleeve for cable and production method thereof
The present invention is to be on September 5th, 96 applying date, and application number is 96118338.1, and denomination of invention is dividing an application of braided sleeve for cable and production method application for a patent for invention case thereof.
Technical field
The present invention relates to cable sleeve and production method thereof, particularly a kind of braided sleeve for cable and production method thereof.
Background technology
At present; the mechanical protection cover that is applied to radio, motor, instrument, multiple circuit lead bundle, cloth wire harness all adopts the polyvinyl chloride glass fibre sleeve of GB2731, GB2715; this product becomes under cryogenic conditions and hardens; easy fracture; when temperature surpasses 32 ℃ the surface show be clamminess, the easy defective of adhesion; moreover its weight is heavier; flexibility is poor, is unsuitable for adopting in military weapon device that aerospace, rocket, aviation selects for use and high-precision meter, electronics electromechanical equipment, the radio test set.
Summary of the invention
The purpose of this invention is to provide a kind of braided sleeve for cable and production method thereof, to solve the deficiencies in the prior art part.
Technical scheme of the present invention is achieved like this: a kind of braided sleeve for cable is made up of Polyamide Yarns and diamagnetic metallic fiber mixed weaving.Its production method by make tube, the group of beating, close knit (Polyamide Yarns and diamagnetic metallic fiber), Wrapping formed, technology of the package step is formed; The ratio that it is characterized in that described Polyamide Yarns and diamagnetic metallic fiber is 8: 1.
Braided sleeve for cable provided by the invention has that flexibility is good, light weight, adaptive temperature wide ranges, the advantage of tensile strength and high-strength elimination antistatic property, also have the protection and the advantage of electromagnetic shielding, especially be adapted to adopt in military weapon device that aerospace, rocket, aviation selects for use and high-precision meter, electronics electromechanical equipment, the radio test set.
Description of drawings
Fig. 1 is a structural representation of the present invention.
Wherein S-represents wall thickness, and M-represents count, and Φ represents nominal inside diameter.
Embodiment
A kind of as shown in drawings braided sleeve for cable is formed by the diamagnetic metallic fiber shuffling of 210D Polyamide Yarns and 0.18mm.Wherein the ratio of the diamagnetic metallic fiber of 2l0D Polyamide Yarns and 0.18mm is 8: 1, its production method by make tube, the group of beating, close knit, Wrapping formed, technology of the package step forms, its weaving parameter sees Table 1, the technical standard of its product sees Table 2.
Table 1
Nominal inside diameter φ mm | Wall thickness smm | Count M/cm | The line number splits * root |
????12 | ?0.4±0.1 | ????20±1 | ????64×3 |
????14 | ?0.4±0.1 | ????22±1 | ????64×4 |
????16 | ?0.5±0.1 | ????24±1 | ????64×5 |
????18 | ?0.5±0.1 | ????26±1 | ????72×3 |
????20 | ?0.5±0.1 | ????28±1 | ????72×4 |
????22 | ?0.6±0.1 | ????30±1 | ????72×5 |
????24 | ?0.6±0.1 | ????32±1 | ????72×6 |
????26 | ?0.6±0.1 | ????32±1 | ????84×3 |
????28 | ?0.6±0.1 | ????34±1 | ????84×4 |
????30 | ?0.7±0.1 | ????36±1 | ????84×5 |
????32 | ?0.8±0.1 | ????38±1 | ????84×6 |
????34 | ?0.9±0.1 | ????40±1 | ????96×4 |
????36 | ?0.9±0.1 | ????42±1 | ????96×5 |
Table 2
Project | Reference standard | Standard value | Measured value |
Electrification voltage | QJ1950-90 | -100V-+100V | ????92V |
Surface resistivity | GB2811-89 GB1410-78 | ≤10
9 | ????<5×10
4 |
Line resistance | | | ????20.6Ω/M |