CN1405112A - Fire-retardant heat-insulation material - Google Patents

Fire-retardant heat-insulation material Download PDF

Info

Publication number
CN1405112A
CN1405112A CN02137686A CN02137686A CN1405112A CN 1405112 A CN1405112 A CN 1405112A CN 02137686 A CN02137686 A CN 02137686A CN 02137686 A CN02137686 A CN 02137686A CN 1405112 A CN1405112 A CN 1405112A
Authority
CN
China
Prior art keywords
component
fire
insulation material
retardant heat
kaolin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN02137686A
Other languages
Chinese (zh)
Other versions
CN1208278C (en
Inventor
黄奕雄
吴梅群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LEYI PETROLEUM CHEMICAL CO Ltd SHANGHAI
Original Assignee
LEYI PETROLEUM CHEMICAL CO Ltd SHANGHAI
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LEYI PETROLEUM CHEMICAL CO Ltd SHANGHAI filed Critical LEYI PETROLEUM CHEMICAL CO Ltd SHANGHAI
Priority to CNB021376867A priority Critical patent/CN1208278C/en
Publication of CN1405112A publication Critical patent/CN1405112A/en
Application granted granted Critical
Publication of CN1208278C publication Critical patent/CN1208278C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The invention discloses a fire-resisting heat-insualting material. Its composition comprises 1.5-2.0 portions of component A and 0.8-1.2 portions of component B, said component A contains (wt%) low-calcium flyash 55-62%, calcium hydroxide 15-22%, kaolin 15-22%, glass fibre 0.6-0.9% and magnesium hdyroxid3 4-7%. Said product possesses excellent fire-resisting and heat-insulating properties, and is a new building material.

Description

Fire-retardant heat-insulation material
Technical field
The present invention relates to a kind of material of construction, specifically, relate to a kind of external wall of building material, relate in particular to a kind of insulating wall material.
Background technology
Along with the continuous development of science and technology, people have higher requirement to material of construction, and it is all not ideal enough on its various performances to be used in the material of construction of exterior wall at present, especially energy-conservation, fire prevention, aspects such as insulation can not satisfy the needs of relevant department, and most external wall of building materials all adopt black cement as cakingagent, than great, be generally about 2.7, thermal conductivity is big, and bond performance is poor, come off easily, constructing operation is difficult for.
Summary of the invention
The technical issues that need to address of the present invention are to disclose a kind of fire-retardant heat-insulation material, to overcome the above-mentioned defective that prior art exists.
Technical scheme of the present invention:
Fire-retardant heat-insulation material of the present invention is a kind of composition, and its component and parts by weight comprise 1.5～2.0 parts A component and 0.8～1.2 part B component;
Wherein: the component and the weight percentage of A component comprise:
Low calcium fly ash 55～62%
Calcium hydroxide 15～22%
Kaolin 15～22%
Glass fibre 0.6～0.9%
Magnesium hydroxide 4～7%
The B component is a pearlstone, according to the present invention, can preferably adopt mixed expanded perlite, is 70～80kg/m as adopting proportion 3The pearlstone mixture, pearlstone is a kind of acidic lava of volcanic eruption, the glassy rock through extremely acute cooling forms has the pearl fissured structure;
Said low calcium fly ash, calcium hydroxide, kaolin are filler, low calcium fly ash is a kind of slightly hydraulic gelling material, no cohesive force own can form the stable and binding agent that have hydraulicity gelling property of conviction behind adding calcium hydroxide and the kaolin, plays cohesive action.
Glass fibre can prevent to ftracture after the material cured;
Magnesium hydroxide is a fire retardant, to improve the flame retardant properties of material;
The main component of said pearlstone is SiO 2, TiO 2, Al 2O 3, Fe 2O 3,, can adopt the commercially available prod for a kind of nonflammable lagging material.
Fire-retardant heat-insulation material of the present invention is to be material of main part with non-flame properties pearlstone, adopt flyash, calcium hydroxide, and inorganic materials such as kaolin are cakingagent, have added that auxiliary agent mixes.Need only during construction A, B component are mixed, and add the water of A, B two component total amounts 200～250%, stir, be mixed into paste and get final product, paste can be constructed in metope by the form of plastering during construction.
Material insulation heat-insulating property of the present invention is good, this material has adopted pearlstone as the insulation main material, make thermal conductivity be reduced to 0.069 greatly, pearlstone is the inorganic non-combustible thing simultaneously, powders such as flyash are silicic acid class inorganics, all belong to incombustible substance, so this material belongs to A level non-combustible material.Adopt the GB/T5464-1999 standard that material of the present invention is carried out fire retardancy test, the result shows, be A level incombustible substance, be specially adapted to the extra high buildings of fire protection requirement, the present invention has replaced black cement traditionally with flyash, not only proportion drops to 0.8 from 2.7, and the thermal conductivity ratio black cement of flyash is much lower, and (black cement is 1.0, flyash is 0.26), easy construction of the present invention, the starting material source is abundant, is the secondary products of dregs series products as flyash, raw material sources are abundant, and cheap, therefore fire-retardant heat-insulation material of the present invention can satisfy the needs of building field, is a kind of insulation, fire-retardant New Building Materials.
Embodiment
Embodiment 1
13 kilograms of flyash, 4 kilograms of calcium hydroxides, 4 kilograms of kaolin, 0.2 kilogram of glass fibre, 1.5 kilograms of magnesium hydroxide mixtures are even, promptly obtain the A component;
In above-mentioned A component, add 14.5 kilograms of B components and 42.5 kg of water, mix, can construct.
Adopt the GB/T5464-1999 standard that above-mentioned materials is carried out fire retardancy test, the result is an A level incombustible substance, adopts GB/T10297-1998 to carry out thermal conductivity and measures, and its thermal conductivity is 0.0686.

Claims (3)

1. a fire-retardant heat-insulation material is a kind of composition, it is characterized in that component and parts by weight comprise 1.5～2.0 parts A component and 0.8～1.2 part B component;
Wherein: the component and the weight percentage of A component comprise:
Low calcium fly ash 55～62%
Calcium hydroxide 15～22%
Kaolin 15～22%
Glass fibre 0.6～0.9%
Magnesium hydroxide 4～7%;
The B component is a pearlstone.
2. fire-retardant heat-insulation material according to claim 1 is characterized in that pearlstone proportion is 70～80kg/m 3
3. a fire-retardant heat-insulation material is a kind of composition, it is characterized in that its component comprises low calcium fly ash, calcium hydroxide, kaolin, glass fibre, magnesium hydroxide and kaolin.
CNB021376867A 2002-10-29 2002-10-29 Fire-retardant heat-insulation material Expired - Fee Related CN1208278C (en)