CN1396141A - Multi-element borax and its preparing process - Google Patents
Multi-element borax and its preparing process Download PDFInfo
- Publication number
- CN1396141A CN1396141A CN 01138761 CN01138761A CN1396141A CN 1396141 A CN1396141 A CN 1396141A CN 01138761 CN01138761 CN 01138761 CN 01138761 A CN01138761 A CN 01138761A CN 1396141 A CN1396141 A CN 1396141A
- Authority
- CN
- China
- Prior art keywords
- borax
- mentioned
- boric acid
- slip
- mother liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A multi-element borax prepared from the waste liquid generated during preparing boric acid mother liquid by sulfulric acid contains borax, magnisium sulfate, Fe, S, Ca, chloride and water. It is prepared through evaporating mother liquid until boric acid or magnesium sulfate is nearly saturated, then neutralizing, crystallizing, cooling to 20-40 deg.C, deposition and dewatering to obtain the said borax.
Description
Affiliated technical field
The invention belongs to the boronation worker and administer and pollute and the deepening manufacture field of single boron fertilizer, particularly a kind of Production By Sulfuric Acid Process mother liquid of boric acid and borax of utilizing produced multi-element borax and preparation technology field thereof.
Background technology
In the past, the boron fertilizer of China was based on industrial borax, boric acid, and the nutrient of these boron fertilizers is single, and the peasant uses inconvenience.And use cost is higher.And the rate of recovery of boric acid production process is lower, amplification quantity mother liquor side by side, promptly severe contamination environment, wasted ample resources again.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of environmental benefit good, the quality height, and effect of increasing production is obvious, simple multi-element borax of processing method and preparation technology thereof.
Technical solution of the present invention can realize according to following mode:
A kind of multi-element borax is characterized in: contain: borax, sal epsom, iron, sulphur, calcium, muriate, water; The said components weight percentage is followed successively by:
Borax 〉=40%
Sal epsom 〉=50%
Iron 〉=0.3%
Sulphur 〉=7%
Calcium 〉=0.05%
Muriate≤0.03%;
Water＜5%
The preparation technology of above-mentioned multi-element borax is characterized in: carry out successively as follows:
(A) the Production By Sulfuric Acid Process mother liquid of boric acid is sent in the vaporizer evaporated;
(B) reach 80 ℃～120 ℃ when vaporization temperature, it is near when saturated that boric acid or magnesium sulfate concentration have reached, is 80 ℃～120 ℃ with temperature, and concentration is that the borax solution of 380～440g/l neutralizes to above-mentioned slip, makes its PH be controlled at 4～7;
(C) slip that neutralization is finished is sent into to cool in the crystallizer and is carried out crystallization;
When (D) being cooled to 20 ℃～40 ℃, the slip in the crystallizer is put into the natural subsidence groove, carry out sedimentation, expel liquid;
(E) above-mentioned sediment is dewatered;
(F) composition of the above-mentioned dehydrated material of detection;
(G) composition that utilizes the crystallized product of borax and mother liquid of boric acid to adjust above-mentioned material makes borax content meet the component standard of above-mentioned multi-element borax;
(H) weighing, packing.
The vapor pressure of described vaporizer is controlled at 0.1～0.3Mpa.
The present invention has tangible increasing yield and improving quality effect, and its environmental benefit is remarkable, and processing method is simple.
Description of drawings
Fig. 1 is a process flow sheet of the present invention;
Embodiment
Embodiment 1:
A kind of multi-element borax, it contains: borax, sal epsom, iron, sulphur, calcium, muriate, water; The said components weight percentage is followed successively by:
Borax 41%
Sal epsom 50%
Iron 0.7%
Sulphur 7%
Calcium 0.29%
Muriate 0.01%;
The preparation technology of water 1% above-mentioned multi-element borax is characterized in that: carry out successively as follows:
(A) the Production By Sulfuric Acid Process mother liquid of boric acid is sent in the vaporizer evaporated; The vapor pressure of vaporizer is controlled at 0.15Mpa.Vaporizer adopts the shell and tube single-effect evaporator;
(B) reach 80 ℃ when vaporization temperature, it is near when saturated that boric acid or magnesium sulfate concentration have reached, is 80 ℃ with temperature, and concentration is that the borax solution of 380g/l neutralizes to above-mentioned slip, makes its PH be controlled at 5;
(C) slip that neutralization is finished is sent into to cool in the crystallizer and is carried out crystallization;
When (D) being cooled to 30 ℃, the slip in the crystallizer is put into the natural subsidence groove, carry out sedimentation, expel liquid;
(E) above-mentioned sediment is dewatered;
(F) composition of the above-mentioned dehydrated material of detection;
(G) crystallized product that utilizes borax and Production By Sulfuric Acid Process mother liquid of boric acid the to be mixed composition of adjusting above-mentioned material makes borax content meet the component standard of above-mentioned multi-element borax;
(H) weighing, packing.
Embodiment 2:
A kind of multi-element borax is characterized in: contain: borax, sal epsom, iron, sulphur, calcium, muriate, water; The said components weight percentage is followed successively by:
Borax 40%
Sal epsom 50.3%
Iron 0.38%
Sulphur 7.2%
Calcium 0.09%
Muriate 0.03%;
Water 2%
The preparation technology of above-mentioned multi-element borax is characterized in that: carry out successively as follows:
(A) preparation technology of above-mentioned multi-element borax is characterized in: carry out successively as follows: the Production By Sulfuric Acid Process mother liquid of boric acid is sent in the vaporizer evaporated; The vapor pressure of vaporizer can be controlled in 0.25Mpa.
(B) reach 100 ℃ when vaporization temperature, it is near when saturated that boric acid or magnesium sulfate concentration have reached, is 100 ℃ with temperature, and concentration is that the borax solution of 400g/l neutralizes to above-mentioned slip, makes its PH be controlled at 6;
(C) slip that neutralization is finished is sent into to cool in the crystallizer and is carried out crystallization;
When (D) being cooled to 35 ℃, the slip in the crystallizer is put into the natural subsidence groove, carry out sedimentation, expel liquid;
(E) above-mentioned sediment is dewatered;
(F) composition of the above-mentioned dehydrated material of detection;
(G) composition that utilizes the crystallized product of borax and mother liquid of boric acid to adjust above-mentioned material makes borax content meet the component standard of above-mentioned multi-element borax;
(H) weighing, packing.
Embodiment 3:
A kind of multi-element borax is characterized in: contain: borax, sal epsom, iron, sulphur, calcium, muriate, water; The said components weight percentage is followed successively by:
Borax 41.%
Sal epsom 51%
Iron 0.4%
Sulphur 7%
Calcium 0.08%
Muriate 0.02%;
Water 0.5%
The preparation technology of above-mentioned multi-element borax is characterized in: carry out successively as follows:
(A) the Production By Sulfuric Acid Process mother liquid of boric acid is sent in the vaporizer evaporated; The vapor pressure of vaporizer is controlled at 0.2Mpa.
(B) reach 110 ℃ when vaporization temperature, it is near when saturated that boric acid or magnesium sulfate concentration have reached, is 110 ℃ with temperature, and concentration is that the borax solution of 440g/l neutralizes to above-mentioned slip, makes its PH be controlled at 7;
(C) slip that neutralization is finished is sent into to cool in the crystallizer and is carried out crystallization;
When (D) being cooled to 38 ℃, the slip in the crystallizer is put into the natural subsidence groove, carry out sedimentation, expel liquid;
(E) above-mentioned sediment is dewatered;
(F) composition of the above-mentioned dehydrated material of detection;
(G) composition that utilizes the crystallized product of borax and mother liquid of boric acid to adjust above-mentioned material makes borax content meet the component standard of above-mentioned multi-element borax;
(H) weighing, packing.
Embodiment 4:
A kind of multi-element borax is characterized in: contain: borax, sal epsom, iron, sulphur, calcium, muriate, water; The said components weight percentage is followed successively by:
Borax 40.1%
Sal epsom 52.1%
Iron 0.3%
Sulphur 7.1%
Calcium 0.09%
Muriate 0.01%;
Water 0.3%.
The preparation technology of above-mentioned multi-element borax is characterized in: carry out successively as follows:
(A) the Production By Sulfuric Acid Process mother liquid of boric acid is sent in the vaporizer evaporated; The vapor pressure of vaporizer is controlled at 0.18Mpa.
(B) reach 90 ℃ when vaporization temperature, it is near when saturated that boric acid or magnesium sulfate concentration have reached, is 90 ℃ with temperature, and concentration is that the borax solution of 390g/l neutralizes to above-mentioned slip, makes its PH be controlled at 5;
(C) slip that neutralization is finished is sent into to cool in the crystallizer and is carried out crystallization;
When (D) being cooled to 36 ℃, the slip in the crystallizer is put into the natural subsidence groove, carry out sedimentation, expel liquid;
(E) above-mentioned sediment is dewatered;
(F) composition of the above-mentioned dehydrated material of detection;
(G) composition that utilizes the crystallized product of borax and mother liquid of boric acid to adjust above-mentioned material makes borax content meet the component standard of above-mentioned multi-element borax;
(H) weighing, packing.
Claims (3)
1, a kind of multi-element borax is characterized in that: contain: borax, sal epsom, iron, sulphur, calcium, muriate, water; The said components weight percentage is followed successively by:
Borax 〉=40%
Sal epsom 〉=50%
Iron 〉=0.3%
Sulphur 〉=7%
Calcium 〉=0.05%
Muriate≤0.03%;
Water＜5%
2, according to the preparation technology of the described multi-element borax of claim 1, it is characterized in that: carry out successively as follows:
(A) the Production By Sulfuric Acid Process mother liquid of boric acid is sent in the vaporizer evaporated;
(B) reach 80 ℃～120 ℃ when vaporization temperature, it is near when saturated that boric acid or magnesium sulfate concentration have reached, is 80 ℃～120 ℃ with temperature, and concentration is that the borax solution of 380～440g/l neutralizes to above-mentioned slip, makes its PH be controlled at 4～7;
(C) slip that neutralization is finished is sent into to cool in the crystallizer and is carried out crystallization;
When (D) being cooled to 20 ℃～40 ℃, the slip in the crystallizer is put into the natural subsidence groove, carry out sedimentation, expel liquid;
(E) above-mentioned sediment is dewatered;
(F) composition of the above-mentioned dehydrated material of detection;
(G) composition that utilizes the crystallized product of borax and mother liquid of boric acid to adjust above-mentioned material makes borax content meet the standard of claim 1;
(H) weighing, packing.
3, according to the preparation technology of the described multi-element borax of claim 2, it is characterized in that: the vapor pressure of described vaporizer is controlled at 0.1～0.3Mpa.