CN1392193A - Hard polyvinyl-chloride bar section with anti-freezing property and its producing method - Google Patents
Hard polyvinyl-chloride bar section with anti-freezing property and its producing method Download PDFInfo
- Publication number
- CN1392193A CN1392193A CN 02132692 CN02132692A CN1392193A CN 1392193 A CN1392193 A CN 1392193A CN 02132692 CN02132692 CN 02132692 CN 02132692 A CN02132692 A CN 02132692A CN 1392193 A CN1392193 A CN 1392193A
- Authority
- CN
- China
- Prior art keywords
- chloride
- freezing property
- raw material
- hard polyvinyl
- polyvinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The hard polyvinyl chloride section bar is produced with the material including polyvinyl chloride as main material, impact assistant, active carbon carbonate, machining assistant, lubricant and titanium white powder and the production process includes weighing material, hot mixing, cold mixing, curing and extruding at 170-180 deg.c in a extruder to form. The hard polyvinyl chloride section bar may be used in cold weather condition of temperature of minus 20 to minus 30 deg.c without cracking. The formula of the present invention may be used in producing plastic-steel section bar for windows and doors.
Description
Technical field: the present invention relates to a kind of section bar that plastic-steel door and window uses and manufacture method of this section bar made.
Background technology: since the beginning of the eighties, country in a planned way organizes and has applied since the chemical building material, the production of Vybak section bar and plastic door-window and application have obtained bigger development, that the Vybak door and window has is energy-conservation, heat-insulating property, weather resistance, fire resistance, insulating property, sound-proofing properties, waterproof, protection against the tide and resisting wind press capacity etc., be described as after wood, steel, aluminium the 4th generation door and window.Yet the UPVC section bar of domestic each manufacturer production and door and window all are conventional classes, use at cold district to occur crackle easily, so conventional class hard polyvinyl-chloride bar section is not suitable for the use of cold district.
Summary of the invention: the invention provides a kind of hard polyvinyl-chloride bar section and manufacture method thereof with anti-freezing property, it has solved crackle appears in existing hard polyvinyl-chloride bar section easily in the cold district use problem.The present invention is made up of the raw material of following ratio of weight and number: polyvinyl chloride 90～110, impact modifier 9～12, treated carbonates 4～6, processing aid 1.8～2, lubricant 0.8～1.2, titanium dioxide 4～6.The polymerization degree of used polyvinyl chloride is 1100～2000; Used impact modifier is chlorinatedpolyethylene (CPE); Used processing aid is acrylate (ACR); Used lubricant is a stearic acid; Used titanium dioxide is a rutile-type.The manufacture method of hard polyethylene section bar of the present invention is carried out as follows: (1) takes by weighing raw material by following ratio of weight and number: polyvinyl chloride 90～110, impact modifier 9～12, treated carbonates 4～6, processing aid 1.8～2, lubricant 0.8～12, titanium dioxide 4～6; (2) heat is sneaked out journey: above each raw material is mixed, make it rise to 110～130 ℃; (3) the cold journey of sneaking out: the raw material that heat is mixed is cooled to 30～50 ℃ in mixing process; (4) maturing process: mixed raw material placed at normal temperatures carried out slaking in 8～12 hours; (5) moulding process: raw material is carried out extrusion moulding with forcing machine under 170～180 ℃.Hard polyvinyl-chloride bar section of the present invention can satisfy the service requirements under-20～-30 ℃ the harsh climate, does not in use crack, and reach the purpose of heat preservation energy-saving, and weathering resistance is fine.This rigid polyvinyl chloride material prescription can be used for making tubing and sheet material, is more suitable for making the section bar of plastic-steel door and window, and the wall thickness of section bar is at 3.0～3.2mm.Its manufacture method three-waste free discharge, non-environmental-pollution is suitable for large-scale industrial production.This hard polyvinyl-chloride bar section sees the following form at the contrast effect of-20 ℃, 1.5 meters high falling weight impact tests:
| Original section bar | Section bar of the present invention | |
| Intensity N | ??3500 | ??5500 |
| Drop impact-20 ℃, 1.5 meters high | 10 samples are gone bad 8 | 10 samples do not have bad |
Embodiment one: present embodiment is made up of the raw material of following ratio of weight and number: polyvinyl chloride 90～100, impact modifier 9～10, treated carbonates 5～6, processing aid 1.9～2, lubricant 1.0～1.2, titanium dioxide 5～6.Its manufacture method is carried out as follows: (1) takes by weighing raw material by above-mentioned ratio of weight and number: (2) heat is sneaked out journey: above each raw material is mixed, make it rise to 110～130 ℃; (3) the cold journey of sneaking out: the raw material that heat is mixed is cooled to 30～50 ℃ in mixing process; (4) maturing process: mixed raw material placed at normal temperatures carried out slaking in 8～12 hours; (5) moulding process: raw material is carried out extrusion moulding with forcing machine under 170～180 ℃.Section bar after the extrusion moulding is with 10～23 ℃ water cooling, and the workshop temperature is controlled at 10～20 ℃ in the whole process of producing.
Embodiment two: what present embodiment and embodiment one were different is: the raw material by following ratio of weight and number is formed: polyvinyl chloride 100～110, impact modifier 10～12, treated carbonates 4～5, processing aid 1.8～1.9, lubricant 0.8～1.0, titanium dioxide 4～6.Its manufacture method is identical with embodiment one.
Claims (10)
1, the hard polyvinyl-chloride bar section that has anti-freezing property is characterized in that it is made up of the raw material of following ratio of weight and number: polyvinyl chloride 90～110, impact modifier 9～12, treated carbonates 4～6, processing aid 1.8～2, lubricant 0.8～1.2, titanium dioxide 4～6.
2, the hard polyvinyl-chloride bar section with anti-freezing property according to claim 1 is characterized in that it is made up of the raw material of following ratio of weight and number: polyvinyl chloride 90～100, impact modifier 9～10, treated carbonates 5～6, processing aid 1.9～2, lubricant 1.0～1.2, titanium dioxide 5～6.
3, the hard polyvinyl-chloride bar section with anti-freezing property according to claim 1 is characterized in that it is made up of the raw material of following ratio of weight and number: polyvinyl chloride 100～110, impact modifier 10～12, treated carbonates 4～5, processing aid 1.8～1.9, lubricant 0.8～1.0, titanium dioxide 4～6.
4, according to claim 1,2 or 3 described hard polyvinyl-chloride bar sections with anti-freezing property, the polymerization degree that it is characterized in that used polyvinyl chloride is 1100～2000.
5,, it is characterized in that used impact modifier is a chlorinatedpolyethylene according to claim 1,2 or 3 described hard polyvinyl-chloride bar sections with anti-freezing property.
6,, it is characterized in that used processing aid is an acrylate according to claim 1,2 or 3 described hard polyvinyl-chloride bar sections with anti-freezing property.
7,, it is characterized in that used lubricant is a stearic acid according to claim 1,2 or 3 described hard polyvinyl-chloride bar sections with anti-freezing property.
8, the manufacture method that has the hard polyvinyl-chloride bar section of anti-freezing property, it is characterized in that it carries out as follows: (1) takes by weighing raw material by following ratio of weight and number: polyvinyl chloride 90～110, impact modifier 9～12, treated carbonates 4～6, processing aid 1.8～2, lubricant 0.8～1.2, titanium dioxide 4～6; (2) heat is sneaked out journey: above each raw material is mixed, make it rise to 110～130 ℃; (3) the cold journey of sneaking out: the raw material that heat is mixed is cooled to 30～50 ℃ in mixing process; (4) maturing process: mixed raw material placed at normal temperatures carried out slaking in 8～12 hours; (5) moulding process: raw material is carried out extrusion moulding with forcing machine under 170～180 ℃.
9, the manufacture method with hard polyvinyl-chloride bar section of anti-freezing property according to claim 8 is characterized in that section bar after the extrusion moulding is with 10～23 ℃ water cooling.
10, according to Claim 8 or 9 described manufacture method, it is characterized in that the workshop temperature is controlled at 10～20 ℃ in the whole process of producing with hard polyvinyl-chloride bar section of anti-freezing property.